CN114395434A - Sts脱水防锈油及其制备方法 - Google Patents

Sts脱水防锈油及其制备方法 Download PDF

Info

Publication number
CN114395434A
CN114395434A CN202111594841.6A CN202111594841A CN114395434A CN 114395434 A CN114395434 A CN 114395434A CN 202111594841 A CN202111594841 A CN 202111594841A CN 114395434 A CN114395434 A CN 114395434A
Authority
CN
China
Prior art keywords
sts
kerosene
rust preventive
stirring
preventive oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN202111594841.6A
Other languages
English (en)
Inventor
张静波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou City Hushuguan Chemical Additives Co ltd
Original Assignee
Suzhou City Hushuguan Chemical Additives Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou City Hushuguan Chemical Additives Co ltd filed Critical Suzhou City Hushuguan Chemical Additives Co ltd
Priority to CN202111594841.6A priority Critical patent/CN114395434A/zh
Publication of CN114395434A publication Critical patent/CN114395434A/zh
Withdrawn legal-status Critical Current

Abstract

本发明揭示了STS脱水防锈油及其制备方法，方法包括以下步骤，将石油磺酸钡、液体石蜡加入反应釜中，温度控制120℃，搅拌2h；加入十二烯基丁二酸，降温至80℃，搅拌2h；加入煤油、硫代硫酸银，常温搅拌2h，制得STS脱水防锈油。本发明实现了防锈油的成膜性能稳定，具有抗菌防锈环保的特点。

Description

STS脱水防锈油及其制备方法
技术领域
本发明属于防锈油制备技术领域，尤其涉及一种STS脱水防锈油及其制备方法。
背景技术
腐蚀是金属件破坏的主要形式之一，对机械设备会造成很大的损失，为避免紧固件等金属制件发生锈蚀和减少其带来的损失，通常会涂刷防锈油。现有专利号为CN201911082782.7一种防锈油及其制备方法包括如下的组分：十二烯基丁二酸；石油磺酸钡；三乙醇胺；机油；棕榈酸；4-甲基苯骈三氮唑；十二烷基苯磺酸钠；缓冲溶液；水。现有防锈油公开了组分内包含抗菌剂，抗菌剂需要额外制备成本较高，含水乳液型的防锈油的防腐蚀性能较弱，针对户外工况，当金属表面发生形变，形变的断纹处防锈油的防护性能失效，遭到腐蚀破坏，其成膜的稳定性受到破坏。
发明内容
本发明的目的是为了解决上述技术问题，而提供STS脱水防锈油及其制备方法，从而实现防锈油的成膜性能稳定，具有抗菌防锈环保的特点。为了达到上述目的，本发明技术方案如下：
STS脱水防锈油，包括如下质量百分比的组分，石油磺酸钡55-57％、液体石蜡14-16％、十二烯基丁二酸14-16％、煤油8-10％、硫代硫酸银5％。
具体的，所述石油磺酸钡的钡含量不小于7％，其平均分子量为900-1200。
具体的，所述液体石蜡的分子量为300-500。
具体的，所述煤油的初馏点140-158℃，终馏点192-200℃。
具体的，所述煤油的密度为0.78-0.88kg/m3，20℃。
具体的，所述煤油的粘度为1.21-1.32mm2/s，40℃。
具体的，包括如下质量百分比的组分，石油磺酸钡55％、液体石蜡16％、十二烯基丁二酸14％、煤油10％、硫代硫酸银5％。
STS脱水防锈油制备方法，包括以下步骤：
将一定质量比例的石油磺酸钡、液体石蜡加入反应釜中，温度控制120℃；
加入十二烯基丁二酸，降温至80℃，搅拌；
加入煤油、硫代硫酸银，常温搅拌，制得STS脱水防锈油。
具体的，所述石油磺酸钡、液体石蜡加入反应釜中搅拌2h，再加入十二烯基丁二酸，搅拌2h，再加入煤油、硫代硫酸银搅拌2h。
与现有技术相比，本发明STS脱水防锈油及其制备方法的有益效果主要体现在：
通过将石油磺酸钡、液体石蜡脱水搅拌后加入十二烯基丁二酸、煤油，保证制备的防锈油具有良好的成膜性能，与金属表面粘附性好，分子间作用力结合牢固，当膜层出现形变压力时，其内部应力适用变化，防锈膜层具有一定强度，能长时间防止腐蚀情况发生；组分中加入硫代硫酸银作为溶剂油，提高整体组分的聚合力，同时作为一种杀菌抑制剂，能消灭微生物细菌，降低腐坏的发生，为金属表层提供安全防护。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整的描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例1：
本实施例为STS脱水防锈油的制备方法，包括以下步骤：
将石油磺酸钡55kg、液体石蜡16kg加入反应釜中，温度控制120℃，搅拌2h；加入十二烯基丁二酸14kg，降温至80℃，搅拌2h；加入煤油10kg、硫代硫酸银5kg，常温搅拌2h，制得STS脱水防锈油。
石油磺酸钡选自济南金隅化工，牌号T701，作为防锈添加剂，石油磺酸钡为棕褐色、半透明、半固体，适用于防锈油脂中作防锈剂，石油磺酸钡的静态腐蚀试验情况较好，对钢、黄铜、紫铜、铝合金、锌等多种金属无腐蚀作用，加热后油溶性好，能吸附于金属表面形成保护膜，防止对金属的腐蚀和锈蚀，对黑色和有色金属有良好的防锈性能。石油磺酸钡中钡含量不小于7％，石油磺酸钡的平均分子量为900。石油磺酸钡的水份不大于0.3％。
液体石蜡选自茂名市润华石油化工，牌号5#白油，作为润滑剂，液体石蜡的分子量为300，其对酸、光、热的性能稳定，具有有无色无味，不易燃特点，化学性能较好。
十二烯基丁二酸选自金坛市建春宝胶鞋，牌号T746，作为防锈添加剂，总酸值235(mgK0H/g)，其pH值不小于4.2。
煤油选自茂名市环海精细化工，牌号T404，作为溶剂油，煤油的初馏点140℃，终馏点192℃。煤油的密度为0.78kg/m3，20℃。煤油的粘度为1.21mm2/s，40℃。
硫代硫酸银选自苏州鑫正化工，牌号STS，作为溶剂油。
实施例2：
与实施例1的区别在于：
将石油磺酸钡57kg、液体石蜡14kg加入反应釜中，温度控制120℃，搅拌2h；加入十二烯基丁二酸14kg，降温至80℃，搅拌2h；加入煤油8kg、硫代硫酸银5kg，常温搅拌2h，制得STS脱水防锈油。
石油磺酸钡的平均分子量为1200。液体石蜡的分子量为500。煤油的初馏点158℃，终馏点200℃。煤油的密度为0.88kg/m3，20℃。煤油的粘度为1.32mm2/s，40℃。
实施例1-2制备的防锈油分别进行符合国标的湿热试验，均为合格，将防锈油涂刷在金属材料表面，置于室外33天未见明显锈迹。
应用上述实施例时，通过将石油磺酸钡、液体石蜡脱水搅拌后加入十二烯基丁二酸、煤油，保证制备的防锈油具有良好的成膜性能，与金属表面粘附性好，分子间作用力结合牢固，当膜层出现形变压力时，其内部应力适用变化，防锈膜层具有一定强度，能长时间防止腐蚀情况发生；组分中加入硫代硫酸银作为溶剂油，提高整体组分的聚合力，同时作为一种杀菌抑制剂，能消灭微生物细菌，降低腐坏的发生，为金属表层提供安全防护。
在本发明的描述中，术语“安装”、“相连”、“连接”、“固定”等均应做广义理解，例如，“连接”可以是固定连接，也可以是可拆卸连接，或一体地连接；可以是直接相连，也可以通过中间媒介间接相连。对于本领域的普通技术人员而言，可以根据具体情况理解上述术语在本发明中的具体含义。
在本说明书的描述中，术语“一个实施例”、“一些实施例”、“具体实施例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不一定指的是相同的实施例或实例。而且，描述的具体特征、结构、材料或特点可以在任何的一个或多个实施例或示例中以合适的方式结合。
虽然本发明所揭露的实施方式如上，但所述的内容仅为便于理解本发明而采用的实施方式，并非用以限定本发明。任何本发明所属领域内的技术人员，在不脱离本发明所揭露的精神和范围的前提下，可以在实施的形式及细节上进行任何的修改与变化，但本发明的专利保护范围，仍须以所附的权利要求书所界定的范围为准。

Claims (9)

1.STS脱水防锈油，其特征在于：包括如下质量百分比的组分，石油磺酸钡55-57％、液体石蜡14-16％、十二烯基丁二酸14-16％、煤油8-10％、硫代硫酸银5％。
2.根据权利要求1所述的STS脱水防锈油，其特征在于：所述石油磺酸钡的钡含量不小于7％，其平均分子量为900-1200。
3.根据权利要求1所述的STS脱水防锈油，其特征在于：所述液体石蜡的分子量为300-500。
4.根据权利要求1所述的STS脱水防锈油，其特征在于：所述煤油的初馏点140-158℃，终馏点192-200℃。
5.根据权利要求1所述的STS脱水防锈油，其特征在于：所述煤油的密度为0.78-0.88kg/m3，20℃。
6.根据权利要求1所述的STS脱水防锈油，其特征在于：所述煤油的粘度为1.21-1.32mm2/s，40℃。
7.根据权利要求1所述的STS脱水防锈油，其特征在于：包括如下质量百分比的组分，石油磺酸钡55％、液体石蜡16％、十二烯基丁二酸14％、煤油10％、硫代硫酸银5％。
8.STS脱水防锈油制备方法，其特征在于，包括以下步骤：
将一定质量比例的石油磺酸钡、液体石蜡加入反应釜中，温度控制120℃；
加入十二烯基丁二酸，降温至80℃，搅拌；
加入煤油、硫代硫酸银，常温搅拌，制得STS脱水防锈油。
9.根据权利要求8所述的STS脱水防锈油制备方法，其特征在于：所述石油磺酸钡、液体石蜡加入反应釜中，搅拌2h，再加入十二烯基丁二酸，搅拌2h，再加入煤油、硫代硫酸银，搅拌2h。
CN202111594841.6A 2021-12-24 2021-12-24 Sts脱水防锈油及其制备方法 Withdrawn CN114395434A (zh)