CN114163600A - 一种透气抗菌记忆绵及其制备方法 - Google Patents
一种透气抗菌记忆绵及其制备方法 Download PDFInfo
- Publication number
- CN114163600A CN114163600A CN202111497813.2A CN202111497813A CN114163600A CN 114163600 A CN114163600 A CN 114163600A CN 202111497813 A CN202111497813 A CN 202111497813A CN 114163600 A CN114163600 A CN 114163600A
- Authority
- CN
- China
- Prior art keywords
- sponge
- foaming
- parts
- memory foam
- conveying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种透气抗菌记忆绵，由以下重量份的组分组成：聚醚多元醇90‑110份、MDI或TDI 30‑70份、链延长剂0‑0.5份、高效海绵稳定剂0.5‑5份、高效复合催化剂0.1‑1.0份、外发泡剂0‑6份、水1‑5份、氧化锌0.1‑2份；还涉及一种透气抗菌记忆绵的制备方法。本发明的优点在于：本发明的透气抗菌记忆绵，通过在组分中加入一定量的氧化锌，利用氧化锌来直接破坏细菌的结构，从根本上解决了细菌的问题，而且起效快，杀菌效果好，大大提高了记忆绵的抗菌效果。
Description
技术领域
本发明涉及一种记忆绵，特别涉及一种透气抗菌记忆绵，以及上述透气抗菌记忆绵的制备方法。
背景技术
记忆绵由许许多多个细小的粒子组成，记忆绵材料具有良好的温感性，能够根据人体的不同部位的温度提供适合的软硬程度；记忆绵又称慢回弹，它是指当记忆绵受压而下陷时，不会表现出强烈的反弹力，而是当压力移除后慢慢恢复原状，这样可以很好的将人体与其接触点的压力均衡分散，达到最舒适的状态。记忆绵还具有重量轻、成本低、形变量大、赋形容易、生产原料广、配方可调性大、形状记忆选择范围广等优点，适应于挤压、注射成型、涂层、铸造等成型工艺，能满足较多场合的需要。但是，因为记忆绵的材质决定了记忆绵的透气性能差，记忆绵产品容易滋生霉菌。
随着生活水平的提高，人们也日益注重生活质量，研发既能保持记忆绵材料的柔软舒适，又具有广谱抗菌除臭、绿色环保、天然健康功能的替代材料，将具有很好的实用性和市场前景。
而在专利CN112142942A中就提到了一种可水洗抗菌防霉记忆绵，其技术方案要点,由包含以下重量份的原料制备而成：普通聚醚多元醇60-85份、慢回弹聚醚多元醇10-35份、仿乳胶聚醚10-20份、疏水多元醇聚醚10-20份、改性聚合物多元醇5-10份、温感聚醚8-12份、链扩展剂0.5-1.2份、扩链交联剂0.3-1份、催化剂0.8-1.5份、发泡剂1.5-3份、匀泡剂0.5-1份、硅油0.8-1.6份、异氰酸酯40-65份、抗菌防霉剂0.3-1.2份。
上述的方案中，通过在记忆绵中加入抗菌防霉剂来达到抗菌效果，其抗菌防霉剂采用的是吡啶硫酮锌抗菌防霉剂，而吡啶硫酮锌在进行抗菌时，是通过将细菌所需的营养离子带出细菌而饿死细菌的方式，来实现抗菌的目的的，这种方式，起效的时间慢，而且其并不快速的杀死细菌，即无法直接从根本上解决细菌的问题，抗菌效果并不是很好。
发明内容
本发明要解决的技术问题是提供一种透气抗菌记忆绵及其制作工艺，能够生产出抗菌效果好的记忆绵。
为解决上述技术问题，本发明的技术方案为：一种透气抗菌记忆绵，其创新点在于：由以下重量份的组分组成：
聚醚多元醇90-110份、MDI或TDI 30-70份、链延长剂0-0.5份、高效海绵稳定剂0.5-5份、高效复合催化剂0.1-1.0份、外发泡剂0-6份、水1-5份、氧化锌0.1-2份。
进一步的，所述聚醚多元醇为适用于发泡的所有聚醚多元醇，所述链延长剂为多元醇或二胺类的低分子化合物，所述高效海绵稳定剂为有机硅海绵稳定剂或聚硅氧烷-聚氧化烯烃镶嵌共聚物，所述高效复合催化剂为锡类催化剂或胺类催化剂。
一种透气抗菌记忆绵的制备方法，其创新点在于：包括下述步骤；
S1聚合：首先，准备好制备透气抗菌记忆绵所需的原料，然后将聚醚多元醇与MDI或TDI进行聚合，在聚合的过程中，再加入链延长剂、高效海绵稳定剂、高效复合催化剂、外发泡剂、水、氧化锌，从而制备出发泡所需的原料；
S2发泡：将原料通过管道输送的方式输送给发泡机，由发泡机机头进行开放连续式低压平泡发泡，将聚合后的物料通过发泡机的发泡喷嘴喷至设置在发泡机的出料端处的降落板上，在降落板的后侧设置有输送带，在降落板上还铺设有牛皮纸，发泡喷嘴将海绵喷至牛皮纸上，牛皮纸随着输送带向前运动，从而带动海绵一起向前移动，边发泡边输送，在发泡时，通过预先设置在发泡机上侧的空调对发泡机机头进行温度调节，从而提供发泡所需的温度；
S3整形：发泡后的海绵在输送带上进行输送，在输送带的两侧设置有竖直设置的侧面板，侧面板由独立的直线驱动器驱动进行水平移动，从而对海绵的宽度进行调整；通过原料的输入量的控制和输送带的输送速度的配合，从而对海绵的密度进行控制；降落板由数块板子共同拼装而成，各块板子由对应的直线驱动器驱动进行上下升降，从而控制海绵的顶部高度以及控制海绵顶端面的弧度；
S4切割：输送带上输送的海绵经过整形后固化定型，最后通过海绵切割机异形切割成所需的透气抗菌记忆绵产品。
进一步的，所述步骤S2中，发泡喷嘴喷射原料的流量控制在80-400kg/min，步骤S3中，输送带的输送速度控制在2-6m/min。
进一步的，所述步骤S3中，发泡后的海绵在输送带上进行输送时，在发泡机头的后侧位于输送带的上方还设置有一压辊，该压辊由一升降机构带动进行上下升降，在海绵通过压辊时，利用压辊对通过输送带的海绵进行挤压，由压辊将海绵向下压8－20CM，利用外力提高海绵开孔率，增加海绵透气性，防止海绵闭孔收缩。
本发明的优点在于：本发明的透气抗菌记忆绵，通过在组分中加入一定量的氧化锌，利用氧化锌来直接破坏细菌的结构，从根本上解决了细菌的问题，而且起效快，杀菌效果好，大大提高了记忆绵的抗菌效果。
本发明的制备方法，通过混合、发泡、整形、切割等工序的配合来制备记忆绵，并通过在原料中加入氧化锌来实现抗菌的目的，通过氧化锌直接破坏细菌的结构，从而根本上杀死细菌，使得最终生产出的记忆绵具备优良的抗菌效果。
在对海绵进行整形时，通过侧面板、输送带的输送速度、原料的输入量控制、降落板的升降高度以及降落板的板型等多方面的控制来实现对海绵的宽度、密度、高度、顶面形状的多方面的控制，确保海绵整形后能够满足多项需求，减少后续的二次整形。
通过在输送带上增设一压辊，当海绵透气率不高，开孔性不够的时候，出模后海绵体内未能排放出来的热空气冷却收缩，外界压力大于海绵未充分开孔的海绵体的压力时，最后会导致海绵收缩，因此通过增设的压辊，利用外力提高海绵开孔率，增加海绵透气性，防止海绵闭孔收缩。
具体实施方式
下面的实施例可以使本专业的技术人员更全面地理解本发明，但并不因此将本发明限制在所述的实施例范围之中。
实施例一
本发明的透气抗菌记忆绵由以下重量份的组分组成：
聚醚多元醇100份、MDI(二苯基甲烷二异氰酸酯)55份、链延长剂0.3份、有机硅海绵稳定剂3份、胺类催化剂0.6份、外发泡剂3份、水3份、氧化锌0.1份。
实施例二
本发明的透气抗菌记忆绵由以下重量份的组分组成：
聚醚多元醇100份、MDI(二苯基甲烷二异氰酸酯)55份、链延长剂0.3份、有机硅海绵稳定剂3份、胺类催化剂0.6份、外发泡剂3份、水3份、氧化锌2份。
实施例三
本发明的透气抗菌记忆绵由以下重量份的组分组成：
聚醚多元醇100份、MDI(二苯基甲烷二异氰酸酯)55份、链延长剂0.3份、有机硅海绵稳定剂3份、胺类催化剂0.6份、外发泡剂3份、水3份、氧化锌1份。
本发明的透气抗菌记忆绵，通过在组分中加入一定量的氧化锌，利用氧化锌来直接破坏细菌的结构，从根本上解决了细菌的问题，而且起效快，杀菌效果好，大大提高了记忆绵的抗菌效果。
本发明的透气抗菌记忆绵的制备方法，通过下述步骤得以实现；
S1聚合：首先，准备好制备透气抗菌记忆绵所需的原料，然后将聚醚多元醇与MDI或TDI进行聚合，在聚合的过程中，再加入链延长剂、高效海绵稳定剂、高效复合催化剂、外发泡剂、水、氧化锌，从而制备出发泡所需的原料。
S2发泡：将原料通过管道输送的方式输送给发泡机，由发泡机机头进行开放连续式低压平泡发泡，将聚合后的物料通过发泡机的发泡喷嘴喷至设置在发泡机的出料端处的降落板上，发泡喷嘴喷射原料的流量控制在80-400kg/min，在降落板的后侧设置有输送带，在降落板上还铺设有牛皮纸，发泡喷嘴将海绵喷至牛皮纸上，牛皮纸随着输送带向前运动，从而带动海绵一起向前移动，边发泡边输送，在发泡时，通过预先设置在发泡机上侧的空调对发泡机机头进行温度调节，从而提供发泡所需的温度。
S3整形：发泡后的海绵在输送带上进行输送，在输送带的两侧设置有竖直设置的侧面板，侧面板由独立的直线驱动器驱动进行水平移动，从而对海绵的宽度进行调整。在本实施例中，直线驱动器可以采用液压油缸、电动推杆或类似的驱动。
发泡后的海绵在输送带上进行输送时，在发泡机头的后侧位于输送带的上方还设置有一压辊，该压辊由一升降机构带动进行上下升降，在本实施例中，升降机构包括一升降支架，在升降支架上安装有一升降油缸，压辊由升降油缸驱动进行上下升降，从而靠近或远离输送带，在海绵通过压辊时，利用压辊对通过输送带的海绵进行挤压，由压辊将海绵向下压8－20CM，利用外力提高海绵开孔率，增加海绵透气性，防止海绵闭孔收缩。通过在输送带上增设一压辊，当海绵透气率不高，开孔性不够的时候，出模后海绵体内未能排放出来的热空气冷却收缩，外界压力大于海绵未充分开孔的海绵体的压力时，最后会导致海绵收缩，因此通过增设的压辊，利用外力提高海绵开孔率，增加海绵透气性，防止海绵闭孔收缩。
通过原料的输入量的控制和输送带的输送速度的配合，从而对海绵的密度进行控制，原料的输入量的控制通过各个原料桶内的电机来进行调节，输送带的输送速度的控制则通过驱动输送带工作的电机来进行调节，输送带的正常输送速度为2-6m/min。
降落板由数块板子共同拼装而成，各块板子由对应的直线驱动器驱动进行上下升降，控制海绵的涨势，从而控制海绵的顶部高度以及控制海绵顶端面的弧度。在本实施例中，直线驱动器可以采用液压油缸、电动推杆或类似的驱动。
在对海绵进行整形时，通过侧面板、输送带的输送速度、原料的输入量控制、降落板的升降高度以及降落板的板型等多方面的控制来实现对海绵的宽度、密度、高度、顶面形状的多方面的控制，确保海绵整形后能够满足多项需求，减少后续的二次整形。
S4切割：输送带上输送的海绵经过整形后固化定型，最后通过海绵切割机异形切割成所需的透气抗菌记忆绵产品。
下面，对记忆绵进抗菌活性测试，参考试验方法ASTM E 2149-13a，测定动态接触条件下固定化抗菌剂抗微生物活性，在测试前，无需对记忆绵进行灭菌，洗脱液：磷酸缓冲液，接触时间：24小时，培养时间：24小时，培养基：培养计数琼脂，测试菌种：大肠杆菌、金黄色葡萄球菌、白色念珠菌，测试样品：实施例一配比制得的记忆绵、实施例二配比制得的记忆绵、实施例三配比制得的记忆绵、对比样一、对比样二、对比样三，其中，对比样一的记忆绵的组分中，氧化锌的加入量为0.05份，其余组分均和实施例一相同，对比样二的记忆绵的组分中，氧化锌的加入量为3份，其余组合均和实施例一相同，对比样三的记忆绵的组合中，不加入氧化锌，其余组分和实施例一相同。
表1为金黄色葡萄球菌的测试结果对比表：
表1
表2为大肠杆菌的测试结果对比表：
表2
表3为白色念珠菌的测试结果对比表：
表3
通过表1、表2及表3的试验数据对比可以看出，在记忆绵中加入氧化锌能够明显的提高抗菌效果，而对于记忆绵中计入的氧化锌的量控制0.1-2份为最佳，当加入的氧化锌的量少于0.1份时，起到的抗菌效果明显的降低了，即抑菌率会降低，而加入的氧化锌的量多于2份时，所提高的抗菌效果并不会得到明显的提升，抑菌率基本保持不变，会造成氧化锌资源的浪费。
本发明的制备方法，通过混合、发泡、整形、切割等工序的配合来制备记忆绵，并通过在原料中加入氧化锌来实现抗菌的目的，通过氧化锌直接破坏细菌的结构，从而根本上杀死细菌，使得最终生产出的记忆绵具备优良的抗菌效果。
本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (5)
1.一种透气抗菌记忆绵，其特征在于：由以下重量份的组分组成：
聚醚多元醇90-110份、MDI或TDI 30-70份、链延长剂0-0.5份、高效海绵稳定剂0.5-5份、高效复合催化剂0.1-1.0份、外发泡剂0-6份、水1-5份、氧化锌0.1-2份。
2.根据权利要求1所述的透气抗菌记忆绵，其特征在于：所述聚醚多元醇为适用于发泡的所有聚醚多元醇，所述链延长剂为多元醇或二胺类的低分子化合物，所述高效海绵稳定剂为有机硅海绵稳定剂或聚硅氧烷-聚氧化烯烃镶嵌共聚物，所述高效复合催化剂为锡类催化剂或胺类催化剂。
3.一种根据权利要求1所述的透气抗菌记忆绵的制备方法，其特征在于：包括下述步骤；
S1聚合：首先，准备好制备透气抗菌记忆绵所需的原料，然后将聚醚多元醇与MDI或TDI进行聚合，在聚合的过程中，再加入链延长剂、高效海绵稳定剂、高效复合催化剂、外发泡剂、水、氧化锌，从而制备出发泡所需的原料；
S2发泡：将原料通过管道输送的方式输送给发泡机，由发泡机机头进行开放连续式低压平泡发泡，将聚合后的物料通过发泡机的发泡喷嘴喷至设置在发泡机的出料端处的降落板上，在降落板的后侧设置有输送带，在降落板上还铺设有牛皮纸，发泡喷嘴将海绵喷至牛皮纸上，牛皮纸随着输送带向前运动，从而带动海绵一起向前移动，边发泡边输送，在发泡时，通过预先设置在发泡机上侧的空调对发泡机机头进行温度调节，从而提供发泡所需的温度；
S3整形：发泡后的海绵在输送带上进行输送，在输送带的两侧设置有竖直设置的侧面板，侧面板由独立的直线驱动器驱动进行水平移动，从而对海绵的宽度进行调整；通过原料的输入量的控制和输送带的输送速度的配合，从而对海绵的密度进行控制；降落板由数块板子共同拼装而成，各块板子由对应的直线驱动器驱动进行上下升降，从而控制海绵的顶部高度以及控制海绵顶端面的弧度；
S4切割：输送带上输送的海绵经过整形后固化定型，最后通过海绵切割机异形切割成所需的透气抗菌记忆绵产品。
4.根据权利要求3所述的透气抗菌记忆绵的制备方法，其特征在于：所述步骤S2中，发泡喷嘴喷射原料的流量控制在80-400kg/min，步骤S3中，输送带的输送速度控制在2-6m/min。
5.根据权利要求3所述的透气抗菌记忆绵的制备方法，其特征在于：所述步骤S3中，发泡后的海绵在输送带上进行输送时，在发泡机头的后侧位于输送带的上方还设置有一压辊，该压辊由一升降机构带动进行上下升降，在海绵通过压辊时，利用压辊对通过输送带的海绵进行挤压，由压辊将海绵向下压8－20CM，利用外力提高海绵开孔率，增加海绵透气性，防止海绵闭孔收缩。