CN113620333A - 一种偏钛酸合成复合硫酸钡的方法 - Google Patents
一种偏钛酸合成复合硫酸钡的方法 Download PDFInfo
- Publication number
- CN113620333A CN113620333A CN202111018197.8A CN202111018197A CN113620333A CN 113620333 A CN113620333 A CN 113620333A CN 202111018197 A CN202111018197 A CN 202111018197A CN 113620333 A CN113620333 A CN 113620333A
- Authority
- CN
- China
- Prior art keywords
- metatitanic acid
- barium sulfate
- tio2
- composite
- sulfuric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及钛白粉合成技术领域，尤其是指一种偏钛酸合成复合硫酸钡的方法，包括以下步骤：S1，采用硫酸法钛白生产工艺，取工艺中的偏钛酸备用；S2，取步骤S1中得到的偏钛酸，根据产品需要加入定量的98％硫酸溶解，再加入碳酸钡浆液反应；S3，将步骤S2中反应完成的产品经过洗涤、煅烧和粉碎得到复合硫酸钡钛白粉。本发明可以根据需要，随时调整硫酸的用量，来生产稳定性高的复合硫酸钡钛白粉。
Description
技术领域
本发明涉及钛白粉合成技术领域，尤其是指一种偏钛酸合成复合硫酸钡的方法。
背景技术
钛白粉是最好的白色颜料，但是具有光催化性能。在紫外光下，钛白粉具有光催化性，将有机物分解为二氧化碳和水。导致钛白粉生产的产品出现不耐晒的问题。同时二氧化钛是两性，与酸、碱都会发生分解反应。
硫酸钡粉体在自然界中非常稳定，难溶于水，与酸碱都不反应。硫酸钡同时具有高光泽、高白度的特点。
为了提高钛白粉的利用率，市场上出现了大量复合钛白。市场上的复合钛白多数采用碳酸钙、滑石粉、膨润土、硫酸钡等粉体与钛白粉直接物理混合而来。虽然大量文献有以低价的原料为核，在表面包覆二氧化钛的工艺技术，但是均未实现工业化生产。因此需要提供一种合成复合硫酸钡钛白粉的方法来解决上述问题。
发明内容
本发明要解决的技术问题是提供一种偏钛酸合成复合硫酸钡的方法，可以根据需要，随时调整硫酸的用量，来生产稳定性高的复合硫酸钡钛白粉。
为了解决上述技术问题，本发明采用如下技术方案：
一种偏钛酸合成复合硫酸钡的方法，包括以下步骤：
S1，采用硫酸法钛白生产工艺，取工艺中的偏钛酸备用；
S2，取步骤S1中得到的偏钛酸，根据产品需要加入定量的98％硫酸溶解，再加入碳酸钡浆液反应；
S3，将步骤S2中反应完成的产品经过洗涤、煅烧和粉碎得到复合硫酸钡钛白粉。
优选地，步骤S1中的偏钛酸的制备方法如下：用硫酸将钛精矿酸解成钛液，将钛液沉淀过滤去除酸不溶物，冷冻结晶过滤去除硫酸亚铁，得到精钛液，然后将精钛液进行水解得到偏钛酸。
优选地，取偏钛酸以TiO2计200g，加入98％硫酸800g，与1600g碳酸钡反应得到含TiO2为10％、BaSO4为90％的复合钛白粉。
优选地，取偏钛酸以TiO2计200g，加入98％硫酸350g，与700g碳酸钡反应得到含TiO2为20％、BaSO4为80％的复合钛白粉。
优选地，取偏钛酸以TiO2计200g，加入98％硫酸200g，与400g碳酸钡反应得到含TiO2为30％、BaSO4为70％的复合钛白粉。
优选地，取偏钛酸以TiO2计200g，加入98％硫酸90g，与175g碳酸钡反应得到含TiO2为50％、BaSO4为50％的复合钛白粉。
本发明的有益效果：
在实际使用情景中，控制复合硫酸钡钛白粉中硫酸钡的含量低于70％时，能有效的提高复合钛白粉的稳定性、光泽度等性能，且不影响复合钛白粉的遮盖力。
附图说明
图1为本发明的1-3号产品遮盖力测试结果示意图；
图2为本发明的4-6号产品遮盖力测试结果示意图。
附图标记：
1-100％硫酸钡；2-90％硫酸钡；3-80％硫酸钡；4-70％硫酸钡；5-50％硫酸钡；6-0％硫酸钡。
具体实施方式
为了便于本领域技术人员的理解，下面结合实施例与附图对本发明作进一步的说明，实施方式提及的内容并非对本发明的限定。
实施例1
取偏钛酸(Ti(OH)4)以TiO2计200g，加入98％硫酸800g，与1600g碳酸钡反应得到含TiO2为10％、BaSO4为90％的复合钛白粉2。
实施例2
取偏钛酸(Ti(OH)4)以TiO2计200g，加入98％硫酸350g，与700g碳酸钡反应得到含TiO2为20％、BaSO4为80％的复合钛白粉3。
实施例3
取偏钛酸(Ti(OH)4)以TiO2计200g，加入98％硫酸200g，与400g碳酸钡反应得到含TiO2为30％、BaSO4为70％的复合钛白粉4。
实施例3
取偏钛酸(Ti(OH)4)以TiO2计200g，加入98％硫酸90g，与175g碳酸钡反应得到含TiO2为50％、BaSO4为50％的复合钛白粉5。
将实施例1-4进行遮盖力测试，所有对比试验结果如图1-2所示。
由测试卡纸测试结果可以看出硫酸钡含量低于70％时遮盖力与100％钛白粉一致。因此，控制复合硫酸钡钛白粉中硫酸钡的含量低于70％时，能有效的提高复合钛白粉的稳定性、光泽度等性能，且不影响复合钛白粉的遮盖力。
遮盖力的测定：基于GB 1726-1979《涂料遮盖力测定法》进行测定。
最后需要说明，上述描述仅为本发明的优选实施例，本领域的技术人员在本发明的启示下，在不违背本发明宗旨及权利要求的前提下，可以做出多种类似的表示，这样的变换均落入本发明的保护范围之内。
Claims (6)
1.一种偏钛酸合成复合硫酸钡的方法，其特征在于：包括以下步骤：
S1，采用硫酸法钛白生产工艺，取工艺中的偏钛酸备用；
S2，取步骤S1中得到的偏钛酸，根据产品需要加入定量的98％硫酸溶解，再加入碳酸钡浆液反应；
S3，将步骤S2中反应完成的产品经过洗涤、煅烧和粉碎得到复合硫酸钡钛白粉。
2.根据权利要求1所述的一种偏钛酸合成复合硫酸钡的方法，其特征在于：步骤S1中的偏钛酸的制备方法如下：用硫酸将钛精矿酸解成钛液，将钛液沉淀过滤去除酸不溶物，冷冻结晶过滤去除硫酸亚铁，得到精钛液，然后将精钛液进行水解得到偏钛酸。
3.根据权利要求1所述的一种偏钛酸合成复合硫酸钡的方法，其特征在于：取偏钛酸以TiO2计200g，加入98％硫酸800g，与1600g碳酸钡反应得到含TiO2为10％、BaSO4为90％的复合钛白粉。
4.根据权利要求1所述的一种偏钛酸合成复合硫酸钡的方法，其特征在于：取偏钛酸以TiO2计200g，加入98％硫酸350g，与700g碳酸钡反应得到含TiO2为20％、BaSO4为80％的复合钛白粉。
5.根据权利要求1所述的一种偏钛酸合成复合硫酸钡的方法，其特征在于：取偏钛酸以TiO2计200g，加入98％硫酸200g，与400g碳酸钡反应得到含TiO2为30％、BaSO4为70％的复合钛白粉。
6.根据权利要求1所述的一种偏钛酸合成复合硫酸钡的方法，其特征在于：取偏钛酸以TiO2计200g，加入98％硫酸90g，与175g碳酸钡反应得到含TiO2为50％、BaSO4为50％的复合钛白粉。