CN113477277A - 金属负载共价有机框架的复合材料及其制备方法和应用 - Google Patents
金属负载共价有机框架的复合材料及其制备方法和应用 Download PDFInfo
- Publication number
- CN113477277A CN113477277A CN202110731539.4A CN202110731539A CN113477277A CN 113477277 A CN113477277 A CN 113477277A CN 202110731539 A CN202110731539 A CN 202110731539A CN 113477277 A CN113477277 A CN 113477277A
- Authority
- CN
- China
- Prior art keywords
- tpma
- preparation
- organic framework
- covalent organic
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于材料制备及环境领域,具体涉及一种金属负载共价有机框架的复合材料及其制备方法及应用。所述复合材料的组分包括金属纳米颗粒和TpMA。制备方法包括先将TpMA、氯金酸和甲醇混合;然后加入硼氢化钠进行反应,即得。本发明制备得到的金属纳米颗粒负载共价有机框架材料是一种制备简单、绿色高效的新型非均相催化剂,其催化活性高、降解速率快、时间短、可催化还原高浓度的污染物。
Description
技术领域
本发明属于材料制备及环境领域,具体涉及一种金属负载共价有机框架的复合材料及其制备方法和应用。
背景技术
硝基化合物是工业废水中常见的有机污染物,而4-硝基酚作为典型的硝基污染物在染料、造纸、制药、农药、石油等工业中广泛使用,也是4-氨基酚的化学前体。4-硝基酚对动植物具有危害作用,且短期暴露会导致人类头痛、恶心和嗜睡。它被美国环境保护署列为114种有机污染物之一,饮用水中最大允许含量为0.43μmol/L。在吸附法、膜分离法、溶剂萃取法、催化还原法等众多方法中,以贵金属纳米颗粒为主的催化还原法被认为是经济有效的方法之一。
贵金属纳米颗粒由于特有的光电和理化性质,在催化、能源、电化学、抗菌等领域得到广泛应用。尤其,具有高面容比和比表面积的贵金属纳米颗粒,如金纳米颗粒(AuNPs)、铂纳米颗粒(Pt NPs)、钯金属纳米颗粒(Pd NPs)等,在多相催化方面展现出较高的催化活性、稳定性和循环利用性。然而,单独的贵金属纳米颗粒因高的比表面能而极易团聚,这容易导致催化过程中催化活性的降低,影响催化剂的回收与重复利用性。因此,为提高贵金属纳米颗粒的分散性,将贵金属纳米颗粒负载在多孔基质上是避免金属纳米颗粒团聚的重要策略。
近年来,COFs材料作为贵金属基质材料的研究受到广泛关注。因溶剂热法制备的COFs具有优异的晶体结构和形貌,所以溶剂热法是制备COFs最常用的一种方法。然而,溶剂热法的实验条件较为苛刻,例如需要高温(85~120℃)、制备时间长(通常持续2~9d)、有机溶剂消耗量多、操作步骤多等。这些严苛的实验条件限制了溶剂热法的工业应用。因此需要寻找一种清洁、方便、高效的制备方法。目前,发展了离子热法、微波辅助法、界面合成法、机械研磨法等多种制备方法。相比于溶剂热法,机械研磨法又称机械化学法,具有更清洁、更高效、更简便的优点。然而还没有研究报道采用机械研磨法制备COFs用于负载贵金属纳米颗粒。
Lu等以含硫醚的COFs作为贵金属纳米颗粒(Pt NPs和Pd NPs)的生长模板制备了PtNPs@COF和PdNPs@COF,硫醚官能团可作为金属沉积和颗粒生长的成核位点以此实现了对贵金属纳米颗粒的尺寸生长控制。PtNPs@COF和PdNPs@COF催化剂对铃木-宫浦偶联反应和硝基酚还原反应展现出优异的催化活性。
但是,当贵金属负载在共价有机框架材料表面时,因贵金属纳米颗粒粒径较大而降低了催化应用,同时贵金属纳米颗粒因表面能较大而极易团聚,造成催化活性的下降,而如何有效平衡贵金属纳米颗粒的粒径和含量是当前研究中的一个难点;此外,在制备贵金属纳米颗粒时,需要用到强还原剂,这对载体的稳定性和抗腐蚀性提出更高的要求,如何选择稳定牢固的共价有机框架材料作为贵金属纳米颗粒的载体,并且保证当贵金属纳米颗粒嵌入到共价有机框架材料内部时不对其自身结构框架造成破坏是另一个需要突破的难点。
发明内容
针对现有技术存在的不同,本发明提供一种贵金属负载共价有机框架的复合材料及其制备方法,制备的金纳米颗粒负载共价有机框架材料可用于催化剂,是一种制备简单、绿色高效的新型非均相催化剂,其催化活性高、降解速率快、时间短、可催化还原高浓度的污染物。
本发明的目的是通过以下技术方案实现的:
一种金属负载共价有机框架的复合材料,复合材料的组分包括金属纳米颗粒和TpMA。
优选地,所述金属纳米颗粒为金、银或铂的纳米颗粒中的一种;优选为金纳米颗粒。
优选地,所述复合材料的制备原料包括TpMA和氯金酸,所述TpMA和氯金酸的质量比为10:1-5。
本发明的再一目的是提供一种金属负载共价有机框架复合材料的制备方法,包括如下步骤:
(1)将TpMA、氯金酸和甲醇混合,搅拌;
(2)将硼氢化钠加入到步骤(1)的反应体系中反应,即得。
优选地,步骤(1)中TpMA、氯金酸和甲醇的质量比为10:1-5:0.5-1.5。
优选地,步骤(1)中所述搅拌为在室温下搅拌,所述搅拌的时间为20h以上;优选为24-26h,更优选为24h。
优选地,所述氯金酸和硼氢化钠的质量摩尔比为1-5g:0.4mol,所述硼氢化钠的浓度为1.5-2.5mol/L。
优选地,步骤(2)中所述反应1-3h,反应完成后,先用二氯甲烷洗涤,然后用甲醇洗涤,最后真空60-70℃烘干即得。
优选地,步骤(1)中TpMA的制备方法包括如下步骤:
A.先将对甲苯磺酸和三聚氰胺混合研磨12-30min;
B.然后将1,3,5-三甲酰间苯三酚加入到步骤A的反应体系中,研磨2-4h;
C.最后加0.1-0.5mL水到步骤B的反应体系中,研磨,用DMF洗涤2-3次,真空干燥即得。
优选地,所述对甲苯磺酸、三聚氰胺和1,3,5-三甲酰间苯三酚的用量比为0.5-1.5mL:320-360mg:370-390mg;
优选地,步骤C中所述研磨的时间为4-6h;所述真空干燥的温度为55-65℃。
本发明还有一个目的是提供上述贵金属负载共价有机框架复合材料在污染物吸附催化降解中的应用。
本发明的有益效果:
1)本发明制备得到的负载TpMA共价有机框架材料,有效平衡负载在共价有机框架材料表面的贵金属纳米颗粒的粒径和含量,并且合成超细贵金属纳米颗粒(<5nm)且克服其极易团聚的缺点,极大的提高催化性能。
2)本发明制备得到的TpMA共价有机框架材料稳定性优异,作为多孔有机材料为AuNPs的负载提供了稳定的结构支撑,使其Au NPs在TpMA中分散性良好、稳定存在。除此之外,金纳米颗粒的嵌入也不会破坏共价有机框架的结构。
3)通过控制HAuCl4的用量可自主调节Au@TpMA催化剂中Au NPs的粒径和密度。经研究发现了最佳的HAuCl4用量。
4)本发明在制备TpMA共价有机框架材料时,对反应进行深入研究,先将对甲苯磺酸和三聚氰胺混合,产生质子化反应,以形成对甲苯磺酸-胺盐作为反应的模板;再加入1,3,5-三甲酰间苯三酚,产生去质子化过程和基于三聚氰胺和1,3,5-三甲酰基间苯三酚的缩合反应,最后形成稳定性优良的共价有机框架材料(COFs)。
附图说明
图1为实施例1制备得到的Au@TpMA的TEM图;
图2为实施例2制备得到的Au@TpMA的TEM图;
图3为实施例3制备得到的Au@TpMA的TEM图;
图4为实施例4制备得到的Au@TpMA的TEM图;
图5为实施例5制备得到的Au@TpMA的TEM图;
图6为TpMA和Au@TpMA的XRD图谱;
图7为TpMA和Au@TpMA的FTIR光谱。
具体实施方式
下面结合具体实施例进一步阐述本发明。
实施例1
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1mL对甲苯磺酸催化剂和340mg三聚氰胺(MA),然后将混合物在300rpm下研磨15min。
(2)将378mg 1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.5mL水加入到混合物中并研磨5h。
(3)用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和氯金酸(HAuCl4)40mg置于烧杯中,加入10mL甲醇,在室温下搅拌24h。
(2)将配制的硼氢化钠(NaBH4)溶液(2mL,2mol/L)加入到上述混合液中,继续搅拌2h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)。其催化剂Au@TpMA中Au的粒径为3.09±0.75nm。
实施例2
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1.5mL对甲苯磺酸催化剂和360mg三聚氰胺(MA),然后将混合物在300rpm下研磨30min。
(2)将390mg 1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.2mL水加入到混合物中并研磨6h。
(3)用DMF洗涤3次,然后在65℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和氯金酸(HAuCl4)10mg置于烧杯中,加入8mL甲醇,在室温下搅拌22h。
(2)将配制的硼氢化钠(NaBH4)溶液(3mL,1.5mol/L)加入到上述混合液中,继续搅拌1h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)备用。
其催化剂Au@TpMA中Au的粒径为4.32±1.39nm。
实施例3
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入0.5mL对甲苯磺酸催化剂和320mg三聚氰胺(MA),然后将混合物在300rpm下研磨12min。
(2)将370mg1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2h。随后,将0.5mL水加入到混合物中并研磨4h。
(3)用DMF洗涤2次,然后在55℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和氯金酸(HAuCl4)50mg置于烧杯中,加入16mL甲醇,在室温下搅拌26h。
(2)将配制的硼氢化钠(NaBH4)溶液(2mL,2.5mol/L)加入到上述混合液中,继续搅拌3h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)备用。其催化剂Au@TpMA中Au的粒径为2.50±0.55nm。
实施例4
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1mL对甲苯磺酸催化剂和340mg三聚氰胺(MA),然后将混合物在300rpm下研磨15min。
(2)将378mg1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.3mL水加入到混合物中并研磨5h。
(3)用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和氯金酸(HAuCl4)20mg置于烧杯中,加入10mL甲醇,在室温下搅拌24h。
(2)将配制的硼氢化钠(NaBH4)溶液(2mL,2mol/L)加入到上述混合液中,继续搅拌2h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)备用。其催化剂Au@TpMA中Au的粒径为3.43±0.87nm。
实施例5
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1mL对甲苯磺酸催化剂和340mg三聚氰胺(MA),然后将混合物在300rpm下研磨15min。
(2)将378mg1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.5mL水加入到混合物中并研磨5h。
(3)用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和氯金酸(HAuCl4)33mg置于烧杯中,加入10mL甲醇,在室温下搅拌24h。
(2)将配制的硼氢化钠(NaBH4)溶液(2mL,2mol/L)加入到上述混合液中,继续搅拌2h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)备用。其催化剂Au@TpMA中Au的粒径为3.24±0.69nm。
实施例6
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1mL对甲苯磺酸催化剂和340mg三聚氰胺(MA),然后将混合物在300rpm下研磨15min。
(2)将378mg 1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.5mL水加入到混合物中并研磨5h。
(3)用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)银纳米颗粒(Ag NPs)负载共价有机框架材料的制备方法
(1)将研磨法制备的100mg TpMA、17.98mg的硝酸银(AgNO3)置于30mL的甲醇溶液里,在黑暗中混合搅拌24h;
(2)加入硼氢化钠(NaBH4)(2mol/L,2mL)继续搅拌2h;
(3)随后,收集沉淀,并用二氯甲烷和超纯水清洗2次,真空(65℃)干燥,即得,
其催化剂Ag@TpMA中Ag粒径为3.24±0.64nm。
对比例1
本对比例与实施例1的区别是氯金酸的用量不同。具体操作如下:
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1mL对甲苯磺酸催化剂和340mg三聚氰胺(MA),然后将混合物在300rpm下研磨15min。
(2)将378mg1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.5mL水加入到混合物中并研磨5h。
(3)用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和氯金酸(HAuCl4)60mg置于烧杯中,加入10mL甲醇,在室温下搅拌24h。
(2)将配制的硼氢化钠(NaBH4)溶液(2mL,2mol/L)加入到上述混合液中,继续搅拌2h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)备用
其催化剂Au@TpMA的粒径为2.97±0.68nm,氯金酸浓度高时,制得的催化剂Au@TpMA粒径虽小,但是极易团聚,其催化效果不佳。
对比例2
本对比例与实施例1的区别是硼氢化钠的用量、浓度不同,具体操作如下:
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
(1)在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入1mL对甲苯磺酸催化剂和340mg三聚氰胺(MA),然后将混合物在300rpm下研磨15min。
(2)将378mg1,3,5-三甲酰间苯三酚(TP)加入到混合物中,并通过利用研磨球和研磨罐之间的动能继续研磨2.75h。随后,将0.5mL水加入到混合物中并研磨5h。
(3)用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和不同质量的氯金酸(HAuCl4)40mg置于烧杯中,加入10mL甲醇,在室温下搅拌24h。
(2)将配制的硼氢化钠(NaBH4)溶液(1mL,3mol/L)加入到上述混合液中,继续搅拌2h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)备用。其催化剂Au@TpMA的粒径为3.50±0.62nm。
对比例3
本对比例与实施例1的区别是共价有机框架材料TpMA的制备方法不同。具体操作如下:
1)共价有机框架材料TpMA的制备方法
使用行星式球磨机(AM400,Ant Source Scientific Instruments(北京)有限公司,中国北京)。具体步骤如下:
在50mL氧化锆研磨罐添加5个5mm直径和15个7mm直径的研磨球。向研磨罐中加入378mg 1,3,5-三甲酰间苯三酚(TP)和340mg三聚氰胺(MA)混合均匀,然后加入1mL对甲苯磺酸催化剂,通过利用研磨球和研磨罐之间的动能研磨3h,随后,将0.5mL水加入到混合物中并研磨5h。用DMF洗涤2次,然后在60℃真空干燥,收集TpMA。
2)金纳米颗粒(Au NPs)负载共价有机框架材料的制备方法
(1)称取100mg TpMA(球磨法制备)和不同质量的氯金酸(HAuCl4)40mg置于烧杯中,加入10mL甲醇,在室温下搅拌24h。
(2)将配制的硼氢化钠(NaBH4)溶液(2mL,2mol/L)加入到上述混合液中,继续搅拌2h。
(3)用二氯甲烷和甲醇洗涤,真空(65℃)烘干,收集催化剂(Au@TpMA)。其催化剂Au@TpMA的粒径为3.09±0.75nm。
试验例1金纳米颗粒负载共价有机框架材料(Au@TpMA)的表征
对实施例1-5制备得到的金纳米颗粒负载共价有机框架材料(Au@TpMA)进行表征,结果见图1-5,对实施例1进行XRD、FTIR分析,金纳米颗粒的嵌入没有破坏共价有机框架的结构,保证了共价有机框架材料的完整性。结果见图6-7。
由图1-5可以看到,球磨法制备的共价有机框架TpMA是褶皱的片状结构,为金纳米颗粒的负载提供了丰富的位点。金纳米颗粒在TpMA表面分散良好,表明TpMA的引入良好的避免了金纳米颗粒的聚集。金纳米颗粒的密度和粒径可以根据HAuCl4的用量来进行调节,当HAuCl4用量(10mg、20mg)较低时,Au NPs密度低,分布相对均匀;当HAuCl4用量(33mg、40mg、50mg)逐渐增加时,Au NPs密度逐渐升高,并且有团聚现象,表明TpMA可负载的金纳米颗粒数量是有限的,过多的团聚会降低Au@TpMA的催化活性。当HAuCl4用量在10-50mg时,可以有效平衡负载在共价有机框架材料表面的贵金属纳米颗粒的粒径和含量,并且合成超细贵金属纳米颗粒(<5nm)且克服极易团聚的缺点,极大的提高了催化性能。
试验例2贵金属纳米颗粒负载共价有机框架材料的催化性能研究
以4-硝基酚催化还原为4-氨基酚的模型反应评价复合催化剂的催化性能。
将100μL 4-硝基酚(3.53×10-3mol/L)、0.25mL NaBH4、3mL去离子水依次加入到石英比色皿中,接着加入500μL Au@TpMA催化剂(1mg/mL)来引发还原反应。随着反应的进行,混合溶液的颜色逐渐从黄色转变为无色,采用紫外可见光分光光度计来监测整个反应过程,在特定的时间点测定混合溶液的紫外可见光光谱。
对水污染中4-硝基酚的去除率结果如下表1所述。
表1水污染中4-硝基酚的去除率
分组 | 去除率/% | 去除时间/min |
实施例1 | 100 | 7 |
实施例2 | 95 | 7 |
实施例3 | 98 | 7 |
实施例4 | 96 | 7 |
实施例5 | 98 | 7 |
实施例6 | 99 | 7 |
对比例1 | 91 | 7 |
对比例2 | 93 | 7 |
对比例3 | 90 | 7 |
以上仅为本发明的优选实施例,并非因此限制本发明的专利范围,对于本领域的技术人员来说,本发明可以有各种更改和变化。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包括在本发明的专利保护范围内。
Claims (10)
1.一种金属负载共价有机框架的复合材料,其特征在于,所述复合材料的组分包括金属纳米颗粒和TpMA。
2.根据权利要求1所述的复合材料,其特征在于,所述金属纳米颗粒为金、银或铂的纳米颗粒中的一种;优选为金纳米颗粒。
3.一种权利要求1-2任意一项所述的复合材料的制备方法,其特征在于,包括如下步骤:
(1)将TpMA、氯金酸和甲醇混合,搅拌;
(2)将硼氢化钠加入到步骤(1)的反应体系中反应,即得。
4.根据权利要求3所述的制备方法,其特征在于,步骤(1)中TpMA、氯金酸和甲醇的质量比为10:1-5:0.5-1.5。
5.根据权利要求3所述的制备方法,其特征在于,步骤(1)中所述搅拌的时间为20h以上。
6.根据权利要求3所述的制备方法,其特征在于,所述氯金酸和硼氢化钠的质量摩尔比为1-5g:0.4mol,所述硼氢化钠的浓度为1.5-2.5mol/L。
7.根据权利要求3所述的制备方法,其特征在于,步骤(2)中所述反应的时间为1-3h,反应完成后,先用二氯甲烷洗涤,然后用甲醇洗涤,最后真空60-70℃烘干即得。
8.根据权利要求3所述的制备方法,其特征在于,步骤(1)中TpMA的制备方法包括如下步骤:
A:先将对甲苯磺酸和三聚氰胺混合研磨12-30min;
B:然后将1,3,5-三甲酰间苯三酚加入到步骤A的反应体系中,研磨2-4h;
C:最后加0.1-0.5mL水到步骤B的反应体系中,研磨,用DMF洗涤2-3次,真空干燥即得。
9.根据权利要求8所述制备方法,其特征在于,所述对甲苯磺酸、三聚氰胺和1,3,5-三甲酰间苯三酚的用量比为0.5-1.5mL:320-360mg:370-390mg;
优选地,步骤C中所述研磨的时间为4-6h;所述真空干燥的温度为55-65℃。
10.一种权利要求1-2任意一项所述的贵金属负载共价有机框架的复合材料或权利要求3-9任意一项所述的制备方法制备得到的复合材料在污染物吸附催化降解中的应用。