CN1131175A - 干粉压坯胶的制备方法 - Google Patents

干粉压坯胶的制备方法 Download PDF

Info

Publication number
CN1131175A
CN1131175A CN 95115778 CN95115778A CN1131175A CN 1131175 A CN1131175 A CN 1131175A CN 95115778 CN95115778 CN 95115778 CN 95115778 A CN95115778 A CN 95115778A CN 1131175 A CN1131175 A CN 1131175A
Authority
CN
China
Prior art keywords
preparation
formula
water
raw materials
emulsification
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 95115778
Other languages
English (en)
Other versions
CN1054618C (zh
Inventor
邱顺恩
孙益成
王长强
计红专
彭少将
陈军
赵政
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Chemical Fibre & Chemical Industry Co Ltd
Original Assignee
Jiangxi Chemical Fibre & Chemical Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Chemical Fibre & Chemical Industry Co Ltd filed Critical Jiangxi Chemical Fibre & Chemical Industry Co Ltd
Priority to CN95115778A priority Critical patent/CN1054618C/zh
Publication of CN1131175A publication Critical patent/CN1131175A/zh
Application granted granted Critical
Publication of CN1054618C publication Critical patent/CN1054618C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于一种高分子聚合物即陶瓷添加剂——干粉压坯胶的制备方法。它包括：原料配比(配方)→预乳化→保护胶的配制→聚合反应等。其中反应釜的反应温度控制在80℃～85℃，反应时间为3～5小时，在氮气保护下(常压工作条件)即可完成聚合反应生成所需产品。该方法具有原料配比合理、工艺简单、成本低等优点。采用该方法所制产品，具有良好的粘结、增强、柔塑及分散等综合性能，成坯率高。

Description

干粉压坯胶的制备方法
本发明涉及化学高分子聚合技术领域，属于一种陶瓷添加剂的制备方法。
干粉压坯胶是陶瓷坯体成形生产工艺中所需的一种添加剂，它对于墙地砖、高档日用陶瓷等产品(等静压成型类)其成坯工艺性能具有极其重要的作用，近年来已引起国内外陶瓷行业的关注。
在现有技术中，有关干粉压坯胶的制备包括：聚合反应和混合配制等方法。例如西德生产的EV—12型产品，该产品虽具有较好的粘结、增强及柔塑性能，但由于需采用诸如乙烯等气体用料及其高压条件，其工艺复杂、投资大、成本高。其它制备方法，虽说比较简单，但所制压坯胶功能单一，性能欠佳，无法满足坯体生产工艺的实际要求，成坯率低，质量难以保证。
本发明的目的就是针对现有技术中存在的问题与不足，提出一种工艺简单、成本低、性能好，可在常压普通工作条件下进行聚合反应的制备方法。
本发明的具体内容详细描述如下：该方法包括原料配比(配方)→预乳化→保护胶的配制→聚合反应等。
原料配比：总配方为(重量％)，水50～60，醋酸乙烯25～35、丙烯酸丁脂4～8、OP-10 0.5～1.4、十二烷基硫酸钠0.4～0.8、丙烯酸0.2～0.8、邻苯二甲酸二丁脂2～6、氢氧化钠0.1～0.2、聚丙烯酸钠1～4、聚乙二醇1～4、聚乙烯醇2～8、过硫酸铵0.1～0.3。(总配方＝配方I＋配方II)。配方I(预乳化)为：水10～15、OP-100.4～0.8、十二烷基硫酸钠0.2～0.6、醋酸乙烯25～35、丙烯酸丁脂4～8、丙烯酸0.2～0.8、氢氧化钠0.1～0.2。配方II(保护胶)为：水35～50、聚乙烯醇2～8、聚乙二醇1～4、聚丙烯酸钠1～4、邻苯二甲酸二丁脂2～6、OP-10 0.4～1.2，十二烷基硫酸钠0.2～0.6。
预乳化：按照配方I(重量％)备料，在进行预乳化工艺时，应先把水加入反应釜中，开动搅拌，同时加入OP-10和十二烷基硫酸钠、分别加入醋酸乙烯、丙烯酸丁脂，再将丙烯酸和氢氧化钠混合且加入搅拌，在常温下预乳化二小时即可。取出10％～20％的乳化液作为种子液，剩余乳化液均打入高位槽待用。
保护胶的配制：按照配方II(重量％)备料，在进行配制时，应先把水加入反应釜开动搅拌，加入聚乙烯醇，升温至90℃保温1小时，降温至80℃将聚乙二醇和聚丙烯酸钠分别加入，同时还应把OP-10、十二烷基硫酸钠及邻苯二甲酸二丁脂加入反应釜中即可留用。
聚合反应：在釜内温度为80℃±2℃时，首先加入种子液和过硫酸铵的1/3，充入氮气；当冷凝器其回流减少时开始滴加已预乳化的单体并每隔15分钟加一次过硫酸铵(适量)，反应釜其温度保持在80℃～85℃，经过3～5小时滴加完毕，将剩余的过硫酸铵一次加入，保温熟化1小时后，降温至40℃出料即可获取干粉压坯胶制品。
本发明与现有技术相比，它不仅具有合理的原料配比，简单可行的工艺，而且能有效地降低生产成本，便于各地大中小厂家实施。采用该方法制备的干粉压坯胶适合添加于含水率为2～6％的各种陶瓷干粉坯料，具有良好的粘结、增强、柔塑及分散等综合性能，成坯率显著提高。

Claims (2)

1、一种陶瓷添加剂——干粉压坯胶的制备方法，它包括原料配比(配方)→预乳化→保护胶的配制→聚合反应等其特征在于：
a).预乳化需按照配方I(重量％)：水10～15、OP-100.4～0.8、十二烷基硫酸钠0.2～0.6、醋酸乙烯25～35、丙烯酸丁脂4～8、丙烯酸0.2～0.8、氢氧化钠0.1～0.2下料投入反应釜中搅拌，在常温下预乳化2小时即可并取出10％～20％的乳化液作为种子液，剩余乳化液均打入高位槽待用；
b).保护胶的配制需按照配方II(重量％)：水35～50、聚乙烯醇2～8、聚乙二醇1～4、聚丙烯酸钠1～4、邻苯二甲酸二丁脂2～6、OP-10 0.4～1.2、十二烷基硫酸钠0.2～0.6备料，开始先把水加入反应釜，开动搅拌再加入聚乙烯醇，升温至90℃保温1小时，降温至80℃将其余备料加入反应釜即可留用；
c).将种子液，过硫酸铵及乳化液依序掺入反应釜且充入氮气进行聚合反应，反应温度控制在80～85℃，反应时间控制在3～5小时。
2、按照权利要求1所述干粉压坯胶的制备方法，其特征在于配方I加配方II即可组成原料总配方(重量％)：水              50～60    醋酸乙烯25～35丙烯酸丁脂      4～8      OP-10   0.5～1.4十二烷基硫酸钠  0.4～0.8  丙烯酸  0.2～0.8邻苯二甲酸二丁脂2～6      氢氧化钠0.1～0.2聚丙烯酸钠      1～4      聚乙二醇1～4聚乙烯醇        2～8      过硫酸铵0.1～0.3
CN95115778A 1995-10-06 1995-10-06 干粉压坯胶的制备方法 Expired - Fee Related CN1054618C (zh)