CN113109204A - 一种快速检测浆粕纤维素结构方法 - Google Patents

一种快速检测浆粕纤维素结构方法 Download PDF

Info

Publication number
CN113109204A
CN113109204A CN202110331900.4A CN202110331900A CN113109204A CN 113109204 A CN113109204 A CN 113109204A CN 202110331900 A CN202110331900 A CN 202110331900A CN 113109204 A CN113109204 A CN 113109204A
Authority
CN
China
Prior art keywords
pulp
cellulose
pulp cellulose
samples
wet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202110331900.4A
Other languages
English (en)
Inventor
王培荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Hongtai Dingxin Material Technology Co.,Ltd.
Original Assignee
Hangzhou Rongkaisheng Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Rongkaisheng Technology Co ltd filed Critical Hangzhou Rongkaisheng Technology Co ltd
Priority to CN202110331900.4A priority Critical patent/CN113109204A/zh
Publication of CN113109204A publication Critical patent/CN113109204A/zh
Pending legal-status Critical Current

Abstract

一种快速检测浆粕纤维素结构方法，属于浆粕纤维素检测技术领域。采用湿解离法，准备好实验用的仪器和样品，称取一定量样品用湿解离法测定浆粕纤维素。浆柏纤维素缺少检测方法，而通过该方法对于使用浆柏作为生产原材料的厂家来说，可以较为简便的检测出浆柏纤维素。本发明有效的测定了莱赛尔体系中浆柏纤维素的结构，填补了这一领域中检测方法的空白，而且试验方式较为简便，可以广泛地应用于本行业。

Description

一种快速检测浆粕纤维素结构方法
技术领域
本发明属于浆粕纤维素检测技术领域，涉及一种快速检测浆粕纤维素结构方法。
背景技术
莱赛尔纤维是再生素纤维中的一种，该纤维以植物来源的木浆为原料，经溶剂纺丝方法制成纤维素纤维，再经过纺织成为纺织品从而进入消费市场，其产品能在泥土中完全分解。生产中所使用的NMMO溶剂无毒无污染，可循环使用，整个纤维生产流程环保，溶剂回收率能够达到99％以上，因此莱赛尔纤维被称为“21世纪绿色纤维”。保水值可以说明纤维的润胀程度，从而反映出细纤维化程度，说明了纤维之间结合力的大小。
国内测试保水值的仪器较为单一，且保水值很少作为常规测定项目，因此测试环节薄弱，对于不同种类的浆粕也缺少有效的检测方法。
发明内容
为了克服现有技术的不足,本发明提供一种快速检测浆粕纤维素结构方法。
一种快速检测浆粕纤维素结构方法,含有以下步骤：采用湿解离法，准备好实验用的仪器和样品，称取一定量样品用湿解离法测定浆粕纤维素。
本发明的优点是:目前莱赛尔纤维是一种新材料，浆柏纤维素缺少检测方法，而通过该方法对于使用浆柏作为生产原材料的厂家来说，可以较为简便的检测出浆柏纤维素。
本发明有效的测定了莱赛尔体系中浆柏纤维素的结构，填补了这一领域中检测方法的空白，而且试验方式较为简便，可以广泛地应用于本行业。
具体实施方式
显然，本领域技术人员基于本发明的宗旨所做的许多修改和变化属于本发明的保护范围。
本技术领域技术人员可以理解，除非特意声明，这里使用的单数形式“一”、“一个”、“所述”和“该”也可包括复数形式。应该进一步理解的是，本发明的说明书中使用的措辞“包括”是指存在所述特征、整数、步骤、操作、元件和/或组件，但是并不排除存在或添加一个或多个其他特征、整数、步骤、操作、元件、组件和/或它们的组。应该理解，当称元件、组件被“连接”到另一元件、组件时，它可以直接连接到其他元件或者组件，或者也可以存在中间元件或者组件。这里使用的措辞“和/或”包括一个或更多个相关联的列出项的任一单元和全部组合。
本技术领域技术人员可以理解，除非另外定义，这里使用的所有术语(包括技术术语和科学术语)具有与所属领域中的普通技术人员的一般理解相同的意义。
为便于对实施例的理解，下面将结合做进一步的解释说明，且各个实施例并不构成对本发明的限定。
实施例1：一种快速检测浆粕纤维素结构方法,采用湿解离法，准备好实验用的仪器和样品，称取一定量样品用解离法测定浆粕纤维素。
测定浆柏纤维素采用的湿解离法，检测的主要是莱赛尔生产体系中测定浆粕纤维素，采用离心法测定浆柏纤维素的含量。
一种快速检测浆粕纤维素结构方法,含有以下步骤：准备好仪器设备和样品，称取相当于0.25g绝干浆的浆粕原料，装入滤网中，在25℃的温度下吸水30min，然后取出装有样品的滤网，用离心机于3000g离心力下离心15min，称湿重，在将样品烘干至绝干称重。
按下式计算：
Figure BDA0002996438570000031
WRV％：保水值，以％表示，
W1:烘前质量，单位为g，
W2：烘后质量，单位为g。
序号 烘前质量g 烘后质量g WRV％
1 0.9641 0.2511 284
2 0.9602 0.2494 285
3 0.9633 0.2501 285
4 0.9520 0.2468 286
5 0.9710 0.2552 280
如上所述，对本发明的实施例进行了详细地说明，但是只要实质上没有脱离本发明的发明点及效果可以有很多的变形，这对本领域的技术人员来说是显而易见的。因此，这样的变形例也全部包含在本发明的保护范围之内。

Claims (3)

1.一种快速检测浆粕纤维素结构方法,其特征在于采用湿解离法，准备好实验用的仪器和样品，称取一定量样品用湿解离法测定浆粕纤维素。
2.根据权利要求1所述的一种快速检测浆粕纤维素结构方法，其特征在于测定浆柏纤维素采用的湿解离法，检测的主要是莱赛尔生产体系中测定浆粕纤维素，采用离心法测定浆柏纤维素的含量。
3.根据权利要求1所述的一种快速检测浆粕纤维素结构方法，其特征在于还含有以下步骤：准备好仪器设备和样品，称取相当于0.25g绝干浆的浆粕原料，装入滤网中，在25℃的温度下吸水30min，然后取出装有样品的滤网，用离心机于3000g离心力下离心15min，称湿重，在将样品烘干至绝干称重。
CN202110331900.4A 2021-03-29 2021-03-29 一种快速检测浆粕纤维素结构方法 Pending CN113109204A (zh)