CN110451515A - 一种锂基膨润土 - Google Patents
一种锂基膨润土 Download PDFInfo
- Publication number
- CN110451515A CN110451515A CN201910720296.7A CN201910720296A CN110451515A CN 110451515 A CN110451515 A CN 110451515A CN 201910720296 A CN201910720296 A CN 201910720296A CN 110451515 A CN110451515 A CN 110451515A
- Authority
- CN
- China
- Prior art keywords
- bentonite
- lithiumation
- heating stirring
- swelling soil
- filtered
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种锂基膨润土，所述膨润土制备工艺为：将膨润土矿中开采的膨润土原料进行筛选提纯去除杂质，得到膨润土原材加水，形成膨润土膏浆。往膨润土膏浆内加入酸化剂进行酸化。将酸化的膨润土膏浆进行水洗、过滤，直至洗液呈中性停止。向膨润土膏体内加入锂化剂，并进行加热搅拌。将膨润土膏浆进行干燥、磨粉。向膨润土内加入锂化剂，并进行加热搅拌。将加热搅拌均匀的膨润土进行陈化、过滤。将过滤后的膨润土进行干燥，磨粉，包装。本发明通过添加酸化剂对膨润土进行酸化增加活性，并且添加两次锂化剂加热搅拌进行改型，干法和湿法相结合，提高了膨润土的锂化效果和锂化效率，工艺简单。
Description
技术领域
本发明涉及膨润土制造领域，尤其涉及一种锂基膨润土。
背景技术
锂基膨润土在水溶剂和醇溶剂条件下都具有很好的分散性和悬浮性，在建筑涂料、铸造涂料、陶瓷涂料中得到了越来越广泛的应用。通常在对锂基膨润土进行制造时，通常采用的是干法和湿法两种方法，目前的制备工艺在制备时，制造出来的锂基膨润土锂化性能不强，改型效率底下，因此解决这个问题就变得很重要了。
发明内容
本发明的目的是提供一种锂基膨润土，通过对膨润土进行酸化，提高膨润土活性，通过两次锂化剂，提高膨润土改性效率，提高改型效果，解决了锂化性能差和改型效率低的问题。
本发明提供一种锂基膨润土，所述膨润土制备工艺为：
步骤一：将膨润土矿中开采的膨润土原料进行筛选提纯去除杂质，得到膨润土原材加水，形成膨润土膏浆；
步骤二：往膨润土膏浆内加入酸化剂进行酸化；
步骤三：将酸化的膨润土膏浆进行水洗、过滤，直至洗液呈中性停止；
步骤四：将膨润土膏浆进行干燥、磨粉；
步骤五：向膨润土内加入锂化剂，并进行加热搅拌；
步骤六：将加热搅拌均匀的膨润土进行陈化、过滤；
步骤七：将过滤后的膨润土进行干燥，磨粉，包装。
进一步改进在于：酸化剂采用盐酸、硫酸中的一种。
进一步改进在于：锂化剂采用碳酸锂溶液和氯化锂溶液中的一种，锂化剂的用量不超过膨润土用量5%。
进一步改进在于：加热搅拌温度50~100℃，干燥温度低于120℃。
本发明的有益效果：通过对膨润土进行酸化，提高膨润土活性，通过采用湿法进行锂化改型和干法进行锂化改型，提高了锂化的效率和锂化效果；在锂化时进行加热搅拌，提高了锂化改型的效率。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
实施例一
本实施例提供一种锂基膨润土，所述膨润土制备工艺为：
步骤一：将膨润土矿中开采的膨润土原料进行筛选提纯去除杂质，得到膨润土原材加水，形成膨润土膏浆。
步骤二：往膨润土膏浆内加入酸化剂进行酸化。
步骤三：将酸化的膨润土膏浆进行水洗、过滤，直至洗液呈中性停止。
步骤四：向膨润土膏体内加入锂化剂，并进行加热搅拌。
步骤五：将膨润土膏浆进行干燥、磨粉。
步骤六：向膨润土内加入锂化剂，并进行加热搅拌。
步骤七：将加热搅拌均匀的膨润土进行陈化、过滤。
步骤八：将过滤后的膨润土进行干燥，磨粉，包装。
所述酸化剂采用盐酸；所述锂化剂采用碳酸锂溶液，锂化剂的用量为膨润土用量1%；加热搅拌温度50℃，干燥温度为70℃。
实施例二
本实施例提供一种锂基膨润土，所述膨润土制备工艺为：
步骤一：将膨润土矿中开采的膨润土原料进行筛选提纯去除杂质，得到膨润土原材加水，形成膨润土膏浆；
步骤二：往膨润土膏浆内加入酸化剂进行酸化；
步骤三：将酸化的膨润土膏浆进行水洗、过滤，直至洗液呈中性停止；
步骤四：向膨润土膏体内加入锂化剂，并进行加热搅拌；
步骤五：将膨润土膏浆进行干燥、磨粉；
步骤六：向膨润土内加入锂化剂，并进行加热搅拌；
步骤七：将加热搅拌均匀的膨润土进行陈化、过滤；
步骤八：将过滤后的膨润土进行干燥，磨粉，包装。
所述酸化剂采用硫酸；所述锂化剂采用碳酸锂溶液，锂化剂的用量为膨润土用量3%；加热搅拌温度75℃，干燥温度为90℃。
实施例三
本实施例提供一种锂基膨润土，所述膨润土制备工艺为：
步骤一：将膨润土矿中开采的膨润土原料进行筛选提纯去除杂质，得到膨润土原材加水，形成膨润土膏浆。
步骤二：往膨润土膏浆内加入酸化剂进行酸化。
步骤三：将酸化的膨润土膏浆进行水洗、过滤，直至洗液呈中性停止。
步骤四：向膨润土膏体内加入锂化剂，并进行加热搅拌。
步骤五：将膨润土膏浆进行干燥、磨粉。
步骤六：向膨润土内加入锂化剂，并进行加热搅拌。
步骤七：将加热搅拌均匀的膨润土进行陈化、过滤。
步骤八：将过滤后的膨润土进行干燥，磨粉，包装。
所述酸化剂采用硫酸；所述锂化剂采用氯化锂溶液，锂化剂的用量为膨润土用量5%；加热搅拌温度100℃，干燥温度为120℃。
本实施例先通过酸化对膨润土进行改性，提高膨润土活性；在通过湿法锂化和干法锂化结合，在锂化的同时进行加热，提高膨润土改型效率和锂化性能。
Claims (4)
1.一种锂基膨润土，其特征在于：所述膨润土制备工艺为：
步骤一：将膨润土矿中开采的膨润土原料进行筛选提纯去除杂质，得到膨润土原材加水，形成膨润土膏浆；
步骤二：往膨润土膏浆内加入酸化剂进行酸化；
步骤三：将酸化的膨润土膏浆进行水洗、过滤，直至洗液呈中性停止；
步骤四：向膨润土膏体内加入锂化剂，并进行加热搅拌；
步骤五：将膨润土膏浆进行干燥、磨粉；
步骤六：向膨润土内加入锂化剂，并进行加热搅拌；
步骤七：将加热搅拌均匀的膨润土进行陈化、过滤；
步骤八：将过滤后的膨润土进行干燥，磨粉，包装。
2.如权利要求1所述的一种锂基膨润土，其特征在于：酸化剂采用盐酸、硫酸中的一种。
3.如权利要求1所述的一种锂基膨润土，其特征在于：锂化剂采用碳酸锂溶液和氯化锂溶液中的一种，锂化剂的用量不超过膨润土用量的5%。
4.如权利要求1所述的一种锂基膨润土，其特征在于：加热搅拌温度50~100℃，干燥温度低于120℃。