CN110327939A - 一种酯化-皂化反应催化剂的制备方法及应用 - Google Patents
一种酯化-皂化反应催化剂的制备方法及应用 Download PDFInfo
- Publication number
- CN110327939A CN110327939A CN201910589375.9A CN201910589375A CN110327939A CN 110327939 A CN110327939 A CN 110327939A CN 201910589375 A CN201910589375 A CN 201910589375A CN 110327939 A CN110327939 A CN 110327939A
- Authority
- CN
- China
- Prior art keywords
- esterification
- cnms
- saponification
- silicon
- saponification catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种酯化‑皂化反应催化剂的制备方法及应用,本发明方法将溶胶凝胶法制得的CNMS(手性向列型介孔硅)在一定浓度的硫酸下浸渍,使得CNMS表面的硅羟基被磺酸基所取代形成CNMS‑SO3H催化剂,之后在浸渍液中再加入Al2O3经超声处理,过滤,洗涤,干燥,煅烧后制得Al2O3/CNMS‑SO3H催化剂;将上述所制得的催化剂应用在松节油酯化反应中,得到具有较高产率的龙脑;该方法原料成本低,条件温和,设备条件要求低,将所制备催化剂用于松节酯化反应可高转化率、较高选择性的获得龙脑。
Description
技术领域
本发明涉及一种酯化-皂化反应催化剂的制备方法及应用,属于化工领域。
背景技术
中国是松节油的主要生产国,产量居世界第一。松节油在我国的分布较为广泛,南方各省区均有生产,其主要产地集中在广东、广西、云南、江西和福建等地。松节油是一种可再生精油,含有多种萜烯,主要成分为α-蒎烯和β-蒎烯,两种互为同分异构体,其中α-蒎烯的含量达90%以上。松节油可直接应用于医药和用作溶剂,但更主要的是进行精细化学利用,如合成日化香料、药理活性物质、农用及家用生物活性物质及功能材料等,松节油经酯化-皂化反应可获得高价值的龙脑;龙脑可以加工成日用品,如:香料、龙脑精油、女性化妆品等,有通透肌肤和灭菌消炎的作用,在一定程度上促进人体的新陈代谢,净化环境、去除灰尘和螨虫的奇特功效。
目前,关于α-蒎烯合成龙脑的研究多集中于催化剂及酯化剂的选择。现有α-蒎烯合成龙脑的催化剂或多或少存在一些不足,例如常见的催化剂主要集中于含硼类、含钛类、硼钛复合类、固体超强酸类及其他类型如离子液体等,常用的酯化剂为甲酸、乙酸、草酸、氯乙酸、邻苯二甲酸等。硼酐和偏硼酸类催化剂是工业上最常用的,生产工艺成熟,但反应过程中放热剧烈,不容易控制,且草酸需要分批投入,龙脑的产率不理想,收率在40%~50%左右。偏钛酸类催化剂性能较平稳,但草酸消耗较大,对设备要求高。据目前报道,采用沉淀法制备的固体超强酸S2O8 2-/ZrO2-NiO催化剂,以无水草酸为酯化剂,通过酯化-皂化两步法合成龙脑,龙脑的收率高达55.8%,但是采用S2O8 2-为活性组分存在安全隐患,易发生爆炸,不利于实现工业化;利用固体超强酸SO4 2-/TiO2为催化剂,以氯乙酸为酯化剂,得到龙脑的产率达45%,其中正龙脑的含量在97%以上,但是采用氯乙酸为酯化剂对环境造成了污染,不符合环保的要求,不利于实现工业化。
发明内容
本发明的目的在于提供一种酯化-皂化反应催化剂的制备方法,本发明方法将CNMS作为载体,硫酸中的硫酸基取代CNMS上的硅羟基,再将Al2O3负载在CNMS-SO3H上,得到酯化-皂化反应催化剂(Al2O3/CNMS-SO3H催化剂)。
本发明方法包括以下步骤:
(1)将微晶纤维素(MCC)放入质量浓度60~80%的硫酸溶液中超声处理,然后在搅拌、35~45℃下水解25~35min,超声再处理1~4h,在混合物中添加水后超声处理,静置,离心收集上清液,上清液透析至pH为2.3~2.8,收集带内液体得到纳晶纤维素(NCC)悬浮液;
所述步骤(1)中超声超声处理25~35min,加水超声处理25~35min,静置时间20~30h;
所述微晶纤维素与硫酸溶液的质量比为1:9~15,水的添加量为混合物质量的4~8倍;
(2)将硅源和助结构导向剂加入无水乙醇中混匀后,将混合液倒入纳晶纤维素悬浮液中,在搅拌、40~50℃水浴条件自组装2~4h,之后取出在45~60℃下干燥12~24h,制得NCC-硅复合膜;NCC-硅复合膜采用煅烧的方式除去模板剂,制得手性向列型介孔硅CNMS;
所述硅源为正硅酸甲酯、正硅酸乙酯中的一种,助结构导向剂为3-氨丙基三甲氧基硅烷、3-氨丙基三乙氧基硅烷中的一种;
所述微晶纤维素:硅源:助结构导向剂:无水乙醇的体积比为(500~600):(30~40):1:(125~250);
所述煅烧是按2℃/min升温到100℃,并在100℃下保持2h,然后2℃/min升温到540℃,并保持4~6h;
(3)将手性向列型介孔硅CNMS浸渍在浓度为1~4mol/L的硫酸溶液中,浸渍12~24h后在浸渍液中再加入Al2O3,继续超声浸渍12h,过滤,滤渣洗涤,干燥,煅烧后制得酯化-皂化反应催化剂Al2O3/CNMS-SO3H;
所述Al2O3与手性向列型介孔硅CNMS的质量比为1:2~4;
所述煅烧是在400~500℃下处理2~4h。
本发明另一目的是将上述方法制得的酯化-皂化反应催化剂应用在松节油酯化-皂化合成龙脑中,将酯化-皂化反应催化剂与松节油按质量比6~10%的比例加入反应器中,然后加入无水草酸,使松节油中α-蒎烯与无水草酸的摩尔比为1:0.4~0.6,然后在60~100℃油浴中加热回流反应6~10h,得到酯化产物;将酯化产物与NaOH醇溶液进行皂化反应,酯化产物与NaOH的摩尔比为1:4~6,制得龙脑。
所述NaOH醇溶液为NaOH质量浓度为20%的无水乙醇溶液。
本发明所述的技术方案具有以下优点:
(1)手性向列型介孔硅CNMS具有酸位、离子交换性、骨架硅羟基可取代性、孔道高选择性及具有较大比表面积等特性,能够为其在酯化反应中有效地构建催化活性,创造材料基础;
(2)Al元素在松节油酯化反应中具有一定的优势,且Al2O3价格要比La元素等应用在α-蒎烯酯化生成龙脑中便宜很多;
(3)采用通过直接在硫酸中浸渍CNMS而取代骨架表面的硅羟基,而没有用带有磺酸基的有机物等制备,价格大大降低,制作工艺简单,对环境友好;
(4)本发明中使用Al2O3直接添加在浸渍液中,然后经过滤干燥煅烧即得催化剂,制备工艺简单,步骤少,可有效缩小生产成本,降低设备要求。
具体实施方式
下面通过实施例对本发明作进一步详述,但本发明保护范围不局限于所述内容。
实施例1:本酯化-皂化反应催化剂的制备方法及应用如下:
(1)取10g微晶纤维素(MCC)放入100g 质量浓度60%的硫酸中超声处理30min,超声温度不超过40℃,然后在磁力搅拌、水浴恒温40℃下水解30min,超声再处理1h,超声温度不超过40℃;在混合物中添加500mL超纯水超声处理30min温度不超过40℃,静置24h,离心收集上清液,上清液置于透析袋中在超纯水中透析至袋内pH为2.5,收集带内液体得到纳晶纤维素(NCC)悬浮液;
(2)以正硅酸甲酯(TMOS)为硅源,3-氨丙基三甲氧基硅烷(APS)为助结构导向剂,将硅源和助结构导向剂加入无水乙醇中混匀,其中微晶纤维素:硅源:助结构导向剂:无水乙醇的体积比为500:30:1:125,将混合液倒入搅拌的纳晶纤维素悬浮液中,在搅拌、水浴恒温45℃下缓慢挥发自组装3h,之后取出放进45℃的鼓风干燥箱继续缓慢挥干持续24h,制得手性向列型NCC-硅复合膜;NCC-硅复合膜按2℃/min升温到100℃,并在100℃下保持2h,然后2℃/min升温到540℃,并保持6h进行煅烧,得到左旋手性结构的手性向列型介孔硅CNMS;
(3)将CNMS浸渍在2mol/L的硫酸溶液中12h后,CNMS与硫酸溶液的质量体积比g:mL
为1:50;然后在浸渍液中加入Al2O3继续超声浸渍12h,其中Al2O3与手性向列型介孔硅CNMS的质量比为1:2,过滤,水洗涤滤渣,干燥,500℃煅烧2h后制得酯化-皂化反应催化剂Al2O3/CNMS-SO3H;
(4)将酯化-皂化反应催化剂与松节油按质量比7%的比例加入反应器中,然后加入无水草酸,使松节油中α-蒎烯与无水草酸的摩尔比为1:0.5,然后在100℃下油浴中加热回流反应6h,得到酯化产物;将酯化产物与NaOH醇溶液(质量浓度为20%的无水乙醇溶液)进行皂化反应,酯化产物与NaOH的摩尔比为1:5,制得龙脑;松节油的转化率为100%,龙脑的总选择性为53.94%。
实施例2:本酯化-皂化反应催化剂的制备方法及应用如下:
(1)取7g微晶纤维素(MCC)放入100g 质量浓度65%的硫酸中超声处理25min,超声温度不超过40℃,然后在磁力搅拌、水浴恒温45℃下水解25min,超声再处理2h,超声温度不超过40℃;在混合物中添加600mL超纯水超声处理35min温度不超过40℃,静置25h,离心收集上清液,上清液置于透析袋中在超纯水中透析至带内pH为2.5,收集带内液体得到纳晶纤维素(NCC)悬浮液;
(2)以正硅酸甲酯(TMOS)为硅源,3-氨丙基三甲氧基硅烷(APS)为助结构导向剂,将硅源和助结构导向剂加入无水乙醇中混匀,其中微晶纤维素:硅源:助结构导向剂:无水乙醇的体积比为550:35:1:150,将混合液倒入搅拌的纳晶纤维素悬浮液中,在搅拌、水浴恒温40℃下缓慢挥发自组装4h,之后取出放进50℃的鼓风干燥箱继续缓慢挥干持续20h,制得手性向列型NCC-硅复合膜;NCC-硅复合膜按2℃/min升温到100℃,并在100℃下保持2h,然后2℃/min升温到540℃,并保持5h进行煅烧,得到左旋手性结构的手性向列型介孔硅CNMS;
(3)将CNMS浸渍在1mol/L的硫酸溶液中20h后,CNMS与硫酸溶液的质量体积比g:mL
为1:50;然后在浸渍液中加入Al2O3继续超声浸渍12h,其中Al2O3与手性向列型介孔硅CNMS的质量比为1:4,过滤,水洗涤滤渣,干燥,400℃煅烧4h后制得酯化-皂化反应催化剂Al2O3/CNMS-SO3H;
(4)将酯化-皂化反应催化剂与松节油按质量比6%的比例加入反应器中,然后加入无水草酸,松节油中α-蒎烯与无水草酸的摩尔比为1:0.4,然后在60℃下油浴中加热回流反应10h,得到酯化产物;将酯化产物与NaOH醇溶液(质量浓度为20%的无水乙醇溶液)进行皂化反应,酯化产物与NaOH的摩尔比为1:4,制得龙脑;松节油的转化率为92.55%,龙脑的总选择性为38.94%。
实施例3:本酯化-皂化反应催化剂的制备方法及应用如下:
(1)取8g微晶纤维素(MCC)放入100g 质量浓度70%的硫酸中超声处理35min,超声温度不超过40℃,然后在磁力搅拌、水浴恒温35℃下水解35min,超声再处理3h,超声温度不超过40℃;在混合物中添加600mL超纯水超声处理25min温度不超过40℃,静置25h,离心收集上清液,上清液置于透析袋中在超纯水中透析至带内pH为2.3,收集带内液体得到纳晶纤维素(NCC)悬浮液;
(2)以正硅酸甲酯(TMOS)为硅源,3-氨丙基三甲氧基硅烷(APS)为助结构导向剂,将硅源和助结构导向剂加入无水乙醇中混匀,其中微晶纤维素:硅源:助结构导向剂:无水乙醇的体积比为580:40:1:200,将混合液倒入搅拌的纳晶纤维素悬浮液中,在搅拌、水浴恒温50℃下缓慢挥发自组装2h,之后取出放进55℃的鼓风干燥箱继续缓慢挥干持续15h,制得手性向列型NCC-硅复合膜;NCC-硅复合膜按2℃/min升温到100℃,并在100℃下保持2h,然后2℃/min升温到540℃,并保持6h进行煅烧,得到左旋手性结构的手性向列型介孔硅CNMS;
(3)将CNMS浸渍在4mol/L的硫酸溶液中12h后,CNMS与硫酸溶液的质量体积比g:mL
为1:50;然后在浸渍液中加入Al2O3继续超声浸渍12h,其中Al2O3与手性向列型介孔硅CNMS的质量比为1:3,过滤,水洗涤滤渣,干燥,450℃煅烧3h后制得酯化-皂化反应催化剂Al2O3/CNMS-SO3H;
(4)将酯化-皂化反应催化剂与松节油按质量比10%的比例加入反应器中,然后加入无水草酸,松节油中α-蒎烯与无水草酸的摩尔比为1:0.6,然后在80℃下油浴中加热回流反应8h,得到酯化产物;将酯化产物与NaOH醇溶液(质量浓度为20%的无水乙醇溶液)进行皂化反应,酯化产物与NaOH的摩尔比为1:6,制得龙脑;松节油的转化率为94.85%,龙脑的总选择性为42.67%。
实施例4:本酯化-皂化反应催化剂的制备方法及应用如下:
(1)取10g微晶纤维素(MCC)放入100g 质量浓度75%的硫酸中超声处理25min,超声温度不超过40℃,然后在磁力搅拌、水浴恒温40℃下水解25min,超声再处理1.5h,超声温度不超过40℃;在混合物中添加600mL超纯水超声处理30min温度不超过40℃,静置30h,离心收集上清液,上清液置于透析袋中在超纯水中透析至带内pH为2.8,收集带内液体得到纳晶纤维素(NCC)悬浮液;
(2)以正硅酸乙酯为硅源,3-氨丙基三乙氧基硅烷为助结构导向剂,将硅源和助结构导向剂加入无水乙醇中混匀,其中微晶纤维素:硅源:助结构导向剂:无水乙醇的体积比为500:40:1:250,将混合液倒入搅拌的纳晶纤维素悬浮液中,在搅拌、水浴恒温45℃下缓慢挥发自组装3h,之后取出放进60℃的鼓风干燥箱继续缓慢挥干持续12h,制得手性向列型NCC-硅复合膜;NCC-硅复合膜按2℃/min升温到100℃,并在100℃下保持2h,然后2℃/min升温到540℃,并保持4h进行煅烧,得到左旋手性结构的手性向列型介孔硅CNMS;
(3)将CNMS浸渍在2mol/L的硫酸溶液中15h后,CNMS与硫酸溶液的质量体积比g:mL
为1:50;然后在浸渍液中加入Al2O3继续超声浸渍12h,其中Al2O3与手性向列型介孔硅CNMS的质量比为1:2.5,过滤,水洗涤滤渣,干燥,500℃煅烧3h后制得酯化-皂化反应催化剂Al2O3/CNMS-SO3H;
(4)将酯化-皂化反应催化剂与松节油按质量比9%的比例加入反应器中,然后加入无水草酸,松节油中α-蒎烯与无水草酸的摩尔比为1:0.5,然后在90℃下油浴中加热回流反应7h,得到酯化产物;将酯化产物与NaOH醇溶液(质量浓度为20%的无水乙醇溶液)进行皂化反应,酯化产物与NaOH的摩尔比为1:5,制得龙脑;松节油的转化率为95.58%,龙脑的总选择性为42.58%。
Claims (9)
1.一种酯化-皂化反应催化剂的制备方法,其特征在于,包括以下步骤:
(1)将微晶纤维素放入质量浓度60~80%的硫酸溶液中超声处理,然后在搅拌、35~45℃下水解25~35min,超声再处理1~4h,在混合物中添加水后超声处理,静置,离心收集上清液,上清液透析至pH为2.3~2.8,收集带内液体得到纳晶纤维素悬浮液;
(2)将硅源和助结构导向剂加入无水乙醇中混匀后,将混合液倒入纳晶纤维素悬浮液中,在搅拌、40~50℃水浴条件自组装2~4h,之后取出在45~60℃下干燥12~24h,制得NCC-硅复合膜;NCC-硅复合膜采用煅烧的方式除去模板剂,制得手性向列型介孔硅CNMS;
(3)将手性向列型介孔硅CNMS浸渍在浓度为1~4mol/L的硫酸溶液中,浸渍12~24h后在浸渍液中再加入Al2O3,继续超声浸渍12h,过滤,滤渣洗涤,干燥,煅烧后制得酯化-皂化反应催化剂Al2O3/CNMS-SO3H。
2.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:步骤(1)中超声处理时间25~35min,加水超声处理25~35min,静置时间20~30h。
3.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:微晶纤维素与硫酸溶液的质量比为1:9~15,水的添加量为混合物质量的4~8倍。
4.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:硅源为正硅酸甲酯、正硅酸乙酯中的一种,助结构导向剂为3-氨丙基三甲氧基硅烷、3-氨丙基三乙氧基硅烷中的一种。
5.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:步骤(2)中微晶纤维素:硅源:助结构导向剂:无水乙醇的体积比为(500~600):(30~40):1:(125~250)。
6.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:步骤(2)中煅烧是按2℃/min升温到100℃,并在100℃下保持2h,然后2℃/min升温到540℃,并保持4~6h。
7.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:Al2O3与介孔硅CNMS的质量比为1:2~4。
8.根据权利要求1所述的酯化-皂化反应催化剂的制备方法,其特征在于:步骤(3)中煅烧是在400~500℃下处理2~4h。
9.权利要求1-8中任一项所述的酯化-皂化反应催化剂的制备方法制得的酯化-皂化反应催化剂在松节油酯化-皂化合成龙脑中的应用,其特征在于:将酯化-皂化反应催化剂与松节油按质量比6~10%的比例加入反应器中,然后加入无水草酸,使松节油中α-蒎烯与无水草酸的摩尔比为1:0.4~0.6,然后在60~100℃油浴中加热回流反应6~10h,得到酯化产物;将酯化产物与NaOH醇溶液进行皂化反应,酯化产物与NaOH的摩尔比为1:4~6,制得龙脑。