CN110117187A - 一种具有保鲜功能的陶瓷制品及其制备方法 - Google Patents

一种具有保鲜功能的陶瓷制品及其制备方法 Download PDF

Info

Publication number
CN110117187A
CN110117187A CN201811306387.8A CN201811306387A CN110117187A CN 110117187 A CN110117187 A CN 110117187A CN 201811306387 A CN201811306387 A CN 201811306387A CN 110117187 A CN110117187 A CN 110117187A
Authority
CN
China
Prior art keywords
ceramic
powder
hours
fresh
keeping function
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811306387.8A
Other languages
English (en)
Inventor
杨史奋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811306387.8A priority Critical patent/CN110117187A/zh
Publication of CN110117187A publication Critical patent/CN110117187A/zh
Pending legal-status Critical Current

Abstract

本发明属于陶瓷制品领域，具体涉及一种具有保鲜功能的陶瓷制品及其制作方法，将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉煅烧；煅烧后的物料粉碎后，与棕榈纤维、竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过筛，湿法球磨、真空练泥，制成陶瓷制品的坯件；坯件干燥后，进行烧结。本发明提供的一种具有保鲜功能的陶瓷制品及其制备方法，具有抗氧化、抑菌功能，陶瓷制品可以多元化设计，即可以用于食物的存储、运输，也可以用于保健产品。

Description

一种具有保鲜功能的陶瓷制品及其制备方法
技术领域
本发明属于陶瓷制品领域，具体涉及一种具有保鲜功能的陶瓷制品及其制作方法。
背景技术
保鲜陶瓷制品一直是陶瓷产品研发的一个重要领域，早期的比如远红外陶瓷材料被研发出来，这种材料可以根据需要制造出能发射各种不同波段范围的远红外线，而8-15μm范围内的远红外线应用范围较广。比如采用瑾青石或莫来石与Si3N4合成方法制备能发射远红外线的材料；还有以Al2O3、SiO2，苏州土、滑石、Fe2O3、ZrO2等为原料，经多次烧结粉碎制得。这次陶瓷制品具有一定的保鲜功能，但是抑菌等反面有所欠缺，因此保鲜的时间较短。
发明内容
针对上述技术问题，本发明提供一种既有保鲜、又具有良好抑菌效果的陶瓷制品及其制备方法。
具体的技术方案为：
一种具有保鲜功能的陶瓷制品，由以下原料按照质量份数制成：电气石粉60-70、绿泥石30-40、海泡石12-15、硅藻土12-15、高岭土12-16、活性乌金碳8-12、天青泥2-4、黑胆石4-6、碳酸氢钠3-5、食品级氧化镁1-2、氧化锌1-2、负离子粉2-3、氧化钛1-2、粗孔硅胶2-4、稻壳粉6-8、竹炭粉3-5、甘蔗糖蜜1-2、棕榈纤维2-4、玉米粉1-3、酚醛树脂3-5、环氧大豆油4-6、蜂蜡1-2、抑菌剂6-7。
具体的，所述的抑菌剂由以下原料按照质量份数制成：锗石粉20-30、玉石粉15-18、石英8-12、纳米银碳分子筛3-5、纳米氧化锌1-3、过硫酸钾1-2、月桂基葡萄糖苷0.5-1、柠檬酸35-45。
该抑菌剂的制备方法为：将锗石粉、玉石粉、石英在850-880℃下煅烧1-2小时后粉碎研磨成粉，然后和纳米银碳分子筛、纳米氧化锌、过硫酸钾混合均匀，再加入月桂基葡萄糖苷、柠檬酸搅拌1-1.5小时，然后过滤取出；用蒸馏水清洗3-4次，烘干即得。
本发明还提供该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2-3小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1-2小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30-40分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨8～16小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；
(4)坯件干燥后，进行烧结。
优选地，将步骤(3)中的浆料的pH到6.2-6.4，在送入模具后，采用微波处理100-150min；经过了微波处理的最终产品会形成表面的均匀、细致和非常好的紧密性，这个步骤是本发明的最终产品具有抗摔性的最重要步骤之一，在微波处理过程中，需要结合调节合适的pH值来配合，发明人经过许多次实验，如果不调节pH值则会导致最终产品并没有形成表面强度的增加，反而会变脆而导致易碎(虽然质地会变硬)，所以需要严格控制，发明人在做实验过程中发现处于此pH值范围内的工艺得到的产品的强度差别并不特别大。这是发明人对本发明最大的贡献技术点，经过此技术得到产品具有表面非常致密的结构和均匀的厚度，使得本发明在原有配方和工艺的基础上的产品效果更进一步，具有致密光滑的表面，不容易使得细菌孳生，达到通过以材料改进的方式实现抑菌和保鲜的作用。
其中，所述的步骤(4)中烧结曲线为：
先在以5-8℃/min速度升温250-280℃烧结，保温1-2小时；
然后，以4-6℃/min速度升温至750-800℃烧结，保温2-3小时；
再以8-10℃/min速率升温至1150-1250℃烧结，保温4-5小时；
自然冷却。此处应该明示，烧结曲线为发明人最重要的发明点之一，利用这个经过发明人数十次烧结实验的温度曲线，可以得到非常好的产品。
本发明提供的一种具有保鲜功能的陶瓷制品及其制备方法，具有抗氧化、抑菌功能，陶瓷制品可以多元化设计，即可以用于食物的存储、运输，也可以用于保健产品。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种具有保鲜功能的陶瓷制品，由以下原料按照质量份数制成：电气石粉63、绿泥石35、海泡石15、硅藻土12、高岭土14、活性乌金碳9、天青泥3、黑胆石4、碳酸氢钠5、食品级氧化镁1、氧化锌2、负离子粉2、氧化钛1、粗孔硅胶3、稻壳粉7、竹炭粉6、甘蔗糖蜜1、棕榈纤维5、玉米粉2、酚醛树脂4、环氧大豆油5、蜂蜡1、抑菌剂6。
所述的抑菌剂由以下原料按照质量份数制成：锗石粉25、玉石粉16、石英9、纳米银碳分子筛4、纳米氧化锌2、过硫酸钾1、月桂基葡萄糖苷0.8、柠檬酸38。
该抑菌剂的制备方法为：将锗石粉、玉石粉、石英在850-880℃下煅烧2小时后粉碎研磨成粉，然后和纳米银碳分子筛、纳米氧化锌、过硫酸钾混合均匀，再加入月桂基葡萄糖苷、柠檬酸搅拌1小时，然后过滤取出；用蒸馏水清洗3次，烘干即得。
该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2.5小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1.5小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨10小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；
(4)坯件干燥后，进行烧结，烧结曲线为：
先在以5-8℃/min速度升温280℃烧结，保温2小时；
然后，以4-6℃/min速度升温至800℃烧结，保温3小时；
再以8-10℃/min速率升温至1250℃烧结，保温4小时；
自然冷却。
实施例2
与实施例1基本过程一样，区别在于，陶瓷制品，由以下原料按照质量份数制成：电气石粉67、绿泥石38、海泡石14、硅藻土14、高岭土15、活性乌金碳12、天青泥3、黑胆石6、碳酸氢钠4、食品级氧化镁1.5、氧化锌1.8、负离子粉2.5、氧化钛1.5、粗孔硅胶3.5、稻壳粉8、竹炭粉4、甘蔗糖蜜1.5、棕榈纤维4、玉米粉1、酚醛树脂5、环氧大豆油5、蜂蜡2、抑菌剂7。
抑菌剂由以下原料按照质量份数制成：锗石粉24、玉石粉17、石英12、纳米银碳分子筛5、纳米氧化锌1、过硫酸钾2、月桂基葡萄糖苷0.8、柠檬酸42。
该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2.5小时，过滤后用清水洗至近中性，于80℃干燥，于800℃煅烧1.5小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨10小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；
(4)坯件干燥后，进行烧结，烧结曲线为：
先在以5-8℃/min速度升温250℃烧结，保温2小时；
然后，以4-6℃/min速度升温至750℃烧结，保温2小时；
再以8-10℃/min速率升温至1250℃烧结，保温5小时；
自然冷却。
实施例3
与实施例1基本过程一样，陶瓷制品，由以下原料按照质量份数制成：电气石粉68、绿泥石30、海泡石14、硅藻土14、高岭土14、活性乌金碳10、天青泥3、黑胆石5、碳酸氢钠4、食品级氧化镁1、氧化锌2、负离子粉3、氧化钛2、粗孔硅胶3、稻壳粉7、竹炭粉4、甘蔗糖蜜2、棕榈纤维4、玉米粉1、酚醛树脂3、环氧大豆油6、蜂蜡1、抑菌剂7。
抑菌剂由以下原料按照质量份数制成：锗石粉29、玉石粉16、石英12、纳米银碳分子筛3、纳米氧化锌1、过硫酸钾1、月桂基葡萄糖苷0.5、柠檬酸45。
该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2.5小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1.5小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨10小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；
(4)坯件干燥后，进行烧结，烧结曲线为：
先在以5-8℃/min速度升温250℃烧结，保温2小时；
然后，以4-6℃/min速度升温至750℃烧结，保温3小时；
再以8-10℃/min速率升温至1250℃烧结，保温5小时；
自然冷却。
实施例4
与实施例1基本过程一样，陶瓷制品，由以下原料按照质量份数制成：电气石粉68、绿泥石30、海泡石14、硅藻土14、高岭土14、活性乌金碳10、天青泥3、黑胆石5、碳酸氢钠4、食品级氧化镁1、氧化锌2、负离子粉3、氧化钛2、粗孔硅胶3、稻壳粉7、竹炭粉4、甘蔗糖蜜2、棕榈纤维4、玉米粉1、酚醛树脂3、环氧大豆油6、蜂蜡1、抑菌剂7。
抑菌剂由以下原料按照质量份数制成：锗石粉29、玉石粉16、石英12、纳米银碳分子筛3、纳米氧化锌1、过硫酸钾1、月桂基葡萄糖苷0.5、柠檬酸45。
该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2.5小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1.5小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨10小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；将所述浆料的pH到6.4，在送入模具后，采用微波处理150min。
(4)坯件干燥后，进行烧结，烧结曲线为：
先在以5-8℃/min速度升温250℃烧结，保温2小时；
然后，以4-6℃/min速度升温至750℃烧结，保温3小时；
再以8-10℃/min速率升温至1250℃烧结，保温5小时；
自然冷却。
实施例5
与实施例1基本过程一样，陶瓷制品，由以下原料按照质量份数制成：电气石粉68、绿泥石30、海泡石14、硅藻土14、高岭土14、活性乌金碳10、天青泥3、黑胆石5、碳酸氢钠4、食品级氧化镁1、氧化锌2、负离子粉3、氧化钛2、粗孔硅胶3、稻壳粉7、竹炭粉4、甘蔗糖蜜2、棕榈纤维4、玉米粉1、酚醛树脂3、环氧大豆油6、蜂蜡1、抑菌剂7。
抑菌剂由以下原料按照质量份数制成：锗石粉29、玉石粉16、石英12、纳米银碳分子筛3、纳米氧化锌1、过硫酸钾1、月桂基葡萄糖苷0.5、柠檬酸45。
该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2.5小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1.5小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨10小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；将所述浆料的pH到6.2，在送入模具后，采用微波处理100min。
(4)坯件干燥后，进行烧结，烧结曲线为：
先在以5-8℃/min速度升温250℃烧结，保温2小时；
然后，以4-6℃/min速度升温至750℃烧结，保温3小时；
再以8-10℃/min速率升温至1250℃烧结，保温5小时；
自然冷却。
实施例6
与实施例1基本过程一样，陶瓷制品，由以下原料按照质量份数制成：电气石粉68、绿泥石30、海泡石14、硅藻土14、高岭土14、活性乌金碳10、天青泥3、黑胆石5、碳酸氢钠4、食品级氧化镁1、氧化锌2、负离子粉3、氧化钛2、粗孔硅胶3、稻壳粉7、竹炭粉4、甘蔗糖蜜2、棕榈纤维4、玉米粉1、酚醛树脂3、环氧大豆油6、蜂蜡1、抑菌剂7。
抑菌剂由以下原料按照质量份数制成：锗石粉29、玉石粉16、石英12、纳米银碳分子筛3、纳米氧化锌1、过硫酸钾1、月桂基葡萄糖苷0.5、柠檬酸45。
该具有保鲜功能的陶瓷制品的制备方法，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2.5小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1.5小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、料孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨10小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；将所述浆料的pH到6.3，在送入模具后，采用微波处理120min。
(4)坯件干燥后，进行烧结，烧结曲线为：
先在以5-8℃/min速度升温250℃烧结，保温2小时；
然后，以4-6℃/min速度升温至750℃烧结，保温3小时；
再以8-10℃/min速率升温至1250℃烧结，保温5小时；
自然冷却。
对以上实施例所得的陶瓷制品制得保鲜容器，进行相关性能检测，在常温(25摄氏度左右)，蔬菜的保鲜时间10-12天，香蕉保鲜时间7-9天，大米保鲜时间100-120天，测试时间到后，开启保鲜装置，均没有发生霉变、腐烂等现象，水果和蔬菜依然外观新鲜。测试结果显示，该陶瓷制品具有良好的抑菌、保鲜性能。其中，实施例4-6的产品对食物的保质期平均超过实施例1-3中的20％左右。

Claims (5)

1.一种具有保鲜功能的陶瓷制品，其特征在于，由以下原料按照质量份数制成：电气石粉60-70、绿泥石30-40、海泡石12-15、硅藻土12-15、高岭土12-16、活性乌金碳8-12、天青泥2-4、黑胆石4-6、碳酸氢钠3-5、食品级氧化镁1-2、氧化锌1-2、负离子粉2-3、氧化钛1-2、粗孔硅胶2-4、稻壳粉6-8、竹炭粉3-5、甘蔗糖蜜1-2、棕榈纤维2-4、玉米粉1-3、酚醛树脂3-5、环氧大豆油4-6、蜂蜡1-2、抑菌剂6-7。
2.根据权利要求1所述的一种具有保鲜功能的陶瓷制品，其特征在于，所述的抑菌剂由以下原料按照质量份数制成：锗石粉20-30、玉石粉15-18、石英8-12、纳米银碳分子筛3-5、纳米氧化锌1-3、过硫酸钾1-2、月桂基葡萄糖苷0.5-1、柠檬酸35-45。
3.根据权利要求2所述的一种具有保鲜功能的陶瓷制品，其特征在于，所述的抑菌剂的制备方法为：将锗石粉、玉石粉、石英在850-880℃下煅烧1-2小时后粉碎研磨成粉，然后和纳米银碳分子筛、纳米氧化锌、过硫酸钾混合均匀，再加入月桂基葡萄糖苷、柠檬酸搅拌1-1.5小时，然后过滤取出；用蒸馏水清洗3-4次，烘干即得。
4.根据权利要求1到3任一项所述的一种具有保鲜功能的陶瓷制品的制备方法，其特征在于，包括以下步骤：
(1)将电气石粉、绿泥石、海泡石、硅藻土、高岭土、活性乌金碳、天青泥、黑胆石、稻壳粉混合后加入适量的水，搅拌均匀后浸泡2-3小时，过滤后用清水洗至近中性，于80℃～100℃干燥，于600℃～800℃煅烧1-2小时，冷却粉碎；
(2)将棕榈纤维粉碎，与竹炭粉、粗孔硅胶、甘蔗糖蜜、玉米粉、酚醛树脂、环氧大豆油、蜂蜡，在40-50℃下混合搅拌30-40分钟；
(3)将步骤(1)中粉碎后的物料、步骤(2)中的混合物、抑菌剂、碳酸氢钠、食品级氧化镁、氧化锌、氧化钛混合，研磨后，过200～500目筛，湿法球磨8～16小时，料∶球∶水的比例为1∶2∶1.5，然后制成浆料，真空练泥，送入模具制成陶瓷制品的坯件；
(4)坯件干燥后，进行烧结。
5.根据权利要求4所述的一种具有保鲜功能的陶瓷制品的制备方法，其特征在于，所述的步骤(4)中烧结曲线为：
先在以5-8℃/min速度升温250-280℃烧结，保温1-2小时；
然后，以4-6℃/min速度升温至750-800℃烧结，保温2-3小时；
再以8-10℃/min速率升温至1150-1250℃烧结，保温4-5小时；
自然冷却。
CN201811306387.8A 2018-11-05 2018-11-05 一种具有保鲜功能的陶瓷制品及其制备方法 Pending CN110117187A (zh)