CN110081701A - 一种具有耐磨陶瓷衬板的粮食烘干机 - Google Patents

一种具有耐磨陶瓷衬板的粮食烘干机 Download PDF

Info

Publication number
CN110081701A
CN110081701A CN201910349238.8A CN201910349238A CN110081701A CN 110081701 A CN110081701 A CN 110081701A CN 201910349238 A CN201910349238 A CN 201910349238A CN 110081701 A CN110081701 A CN 110081701A
Authority
CN
China
Prior art keywords
parts
weight
drying device
foodstuff drying
lining plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910349238.8A
Other languages
English (en)
Inventor
陈文新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jiutai Agricultural Equipment Co Ltd
Original Assignee
Anhui Jiutai Agricultural Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jiutai Agricultural Equipment Co Ltd filed Critical Anhui Jiutai Agricultural Equipment Co Ltd
Priority to CN201910349238.8A priority Critical patent/CN110081701A/zh
Publication of CN110081701A publication Critical patent/CN110081701A/zh
Pending legal-status Critical Current

Abstract

本发明属于粮食烘干机技术领域，具体涉及一种具有耐磨陶瓷衬板的粮食烘干机，包括粮食烘干机本体和提升机，所述提升机的顶端与粮食烘干机本体的顶端连通，所述提升机的底端一侧设置有进料斗，所述提升机远离进料斗的一侧连接有连接部，所述连接部通过固定螺栓固定安装在粮食烘干机本体的外壁上，所述粮食烘干机本体的底端内部设置有绞龙，所述绞龙的一端位于连接部内部，所述绞龙位于连接部内部的一端外侧固设有拨片，克服了现有技术的不足，在连接部的内壁上固定设置耐磨的陶瓷衬板，避免了粮食外壳直接对连接部内壁造成损伤，降低了设备的维修成本，延长了设备的使用寿命。

Description

一种具有耐磨陶瓷衬板的粮食烘干机
技术领域
本发明属于粮食烘干机技术领域，具体涉及一种具有耐磨陶瓷衬板的粮食烘干机。
背景技术
粮食烘干机随着粮种的改进、单产的提高和国家对粮食烘干设备的投资增加，建设大、中、小型粮食烘干设施的越来越多。能否选配质量高、使用寿命长、经济实用、可靠性好和自动化程度高的烘干机至关重要。
粮食烘干机中采用绞龙将粮食传输到提升机中进行循环烘干，在烘干外壳较硬的粮食时，绞龙与提升机连接的连接部内壁被粮食不断冲刷，长时间使用会影响对连接部造成损伤，增加设备的维修和维护成本，影响设备的使用寿命。
发明内容
本发明的目的在于提供一种具有耐磨陶瓷衬板的粮食烘干机，克服了现有技术的不足，在连接部的内壁上固定设置耐磨的陶瓷衬板，避免了粮食外壳直接对连接部内壁造成损伤，降低了设备的维修成本，延长了设备的使用寿命。
为解决上述问题，本发明所采取的技术方案如下：
一种具有耐磨陶瓷衬板的粮食烘干机，包括粮食烘干机本体和提升机，所述提升机的顶端与粮食烘干机本体的顶端连通，所述提升机的底端一侧设置有进料斗，所述提升机远离进料斗的一侧连接有连接部，所述连接部通过固定螺栓固定安装在粮食烘干机本体的外壁上，所述粮食烘干机本体的底端内部设置有绞龙，所述绞龙的一端位于连接部内部，所述绞龙位于连接部内部的一端外侧固设有拨片，所述连接部的内壁上设置有多个陶瓷衬板，所述陶瓷衬板通过螺丝固定在连接部的内壁上。
进一步，所述拨片采用陶瓷衬板相同的原料加工处理得到。
进一步，所述陶瓷衬板采用如下原料制备：高岭土100-200重量份、氧化铝20-40重量份、氧化锌10-20重量份、氧化钙6-8重量份、石英10-20重量份、菱镁矿20-40重量份、锆石10-20重量份、氧化锆5-15重量份、氧化镧2-8重量份、氧化钇1-3重量份、氧化锡1-8重量份、粘结剂3-20重量份、辅料2-10质量份。
进一步，所述陶瓷衬板的生产包括以下步骤：
S1：利用球磨机将高岭土100-200重量份、氧化铝20-40重量份、氧化锌10-20重量份、氧化钙6-8重量份、石英10-20重量份、菱镁矿20-40重量份、锆石10-20重量份、氧化锆5-15重量份、氧化镧2-8重量份、氧化钇1-3重量份、氧化锡1-8重量份、辅料2-10质量份磨制成粉末，过100-300目筛，得到粉料；
S2：将所述粉料与3-20重量份粘结剂混合，利用用喷雾机进行喷雾造粉，然后送入陶瓷压机进行压制成型，得到砖坯；
S3：将所述砖坯经过脱粘烧结后磨边，抛光，得到陶瓷衬板。
进一步，所述陶瓷压机的压力为80MPa，压制三次。
进一步，所述所述脱粘的方式为氮气氛围中脱粘。
进一步，所述烧结具体为升温至1800℃保温2-8小时，缓慢降至1480℃并保温2-4小时。
本发明与现有技术相比较，具有以下有益效果：
本发明所述一种具有耐磨陶瓷衬板的粮食烘干机，通过设置连接部、陶瓷衬板和拨片，避免粮食外壳直接对连接部内壁造成损伤，方便对陶瓷衬板和拨片进行更换，降低了使用成本，延长了设备的使用寿命；通过在陶瓷衬板生产过程中加入氧化镧和氧化钇，提高陶瓷衬板本身的耐磨性，延长陶瓷衬板的使用时间，降低了维修和维护的成本。
本发明设计新颖，使用成本低，在连接部的内壁上固定设置耐磨的陶瓷衬板，避免了粮食外壳直接对连接部内壁造成损伤，降低了设备的维修成本，延长了设备的使用寿命。
附图说明
图1为一种具有耐磨陶瓷衬板的粮食烘干机的结构示意图。
图2为一种具有耐磨陶瓷衬板的粮食烘干机中连接部的结构示意图。
图中：1-粮食烘干机本体；2-提升机；3-进料斗；4-连接部；5-陶瓷衬板；6-绞龙；7-拨片。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
如图所示，本发明一种具有耐磨陶瓷衬板的粮食烘干机，包括粮食烘干机本体1和提升机2，提升机2的顶端与粮食烘干机本体1的顶端连通，提升机2的底端一侧设置有进料斗3，提升机2远离进料斗3的一侧连接有连接部4，连接部4通过固定螺栓固定安装在粮食烘干机本体1的外壁上，粮食烘干机本体1的底端内部设置有绞龙6，绞龙6的一端位于连接部4内部，绞龙6位于连接部4内部的一端外侧固设有拨片7，连接部4的内壁上设置有多个陶瓷衬板5，陶瓷衬板5通过螺丝固定在连接部4的内壁上。
实施例2：
在实施例1的基础上，陶瓷衬板5的生产包括以下步骤：
S1：利用球磨机将高岭土100重量份、氧化铝20重量份、氧化锌10重量份、氧化钙6重量份、石英10重量份、菱镁矿20重量份、锆石10重量份、氧化锆5重量份、氧化镧2重量份、氧化钇1重量份、氧化锡1重量份、辅料2质量份磨制成粉末，过200目筛，得到粉料；
S2：将所述粉料与20重量份粘结剂混合，利用用喷雾机进行喷雾造粉，然后送入陶瓷压机进行压制成型，得到砖坯；
S3：将所述砖坯经过脱粘烧结后磨边，抛光，得到陶瓷衬板。
所述陶瓷压机的压力为80MPa，压制三次；所述所述脱粘的方式为氮气氛围中脱粘；所述烧结具体为升温至1800℃保温4小时，缓慢降至1480℃并保温3小时。
实施例3：
在实施例1的基础上，陶瓷衬板5的生产包括以下步骤：
S1：利用球磨机将高岭土200重量份、氧化铝40重量份、氧化锌20重量份、氧化钙8重量份、石英20重量份、菱镁矿40重量份、锆石20重量份、氧化锆15重量份、氧化镧8重量份、氧化钇3重量份、氧化锡8重量份、辅料10质量份磨制成粉末，过200目筛，得到粉料；
S2：将所述粉料与20重量份粘结剂混合，利用用喷雾机进行喷雾造粉，然后送入陶瓷压机进行压制成型，得到砖坯；
S3：将所述砖坯经过脱粘烧结后磨边，抛光，得到陶瓷衬板。
所述陶瓷压机的压力为80MPa，压制三次；所述所述脱粘的方式为氮气氛围中脱粘；所述烧结具体为升温至1800℃保温4小时，缓慢降至1480℃并保温3小时。
实施例4：
在实施例1的基础上，陶瓷衬板5的生产包括以下步骤：
S1：利用球磨机将高岭土150重量份、氧化铝30重量份、氧化锌15重量份、氧化钙7重量份、石英15重量份、菱镁矿30重量份、锆石15重量份、氧化锆10重量份、氧化镧6重量份、氧化钇2重量份、氧化锡6重量份、辅料8质量份磨制成粉末，过200目筛，得到粉料；
S2：将所述粉料与20重量份粘结剂混合，利用用喷雾机进行喷雾造粉，然后送入陶瓷压机进行压制成型，得到砖坯；
S3：将所述砖坯经过脱粘烧结后磨边，抛光，得到陶瓷衬板。
所述陶瓷压机的压力为80MPa，压制三次；所述所述脱粘的方式为氮气氛围中脱粘；所述烧结具体为升温至1800℃保温4小时，缓慢降至1480℃并保温3小时。
综上，本发明所述一种具有耐磨陶瓷衬板的粮食烘干机，通过设置连接部4、陶瓷衬板5和拨片7，避免粮食外壳直接对连接部4内壁造成损伤，方便对陶瓷衬板5和拨片7进行更换，降低了使用成本，延长了设备的使用寿命；通过在陶瓷衬板5生产过程中加入氧化镧和氧化钇，提高陶瓷衬板5本身的耐磨性，延长陶瓷衬板5的使用时间，降低了维修和维护的成本。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。

Claims (7)

1.一种具有耐磨陶瓷衬板的粮食烘干机，包括粮食烘干机本体（1）和提升机（2），其特征在于：所述提升机（2）的顶端与粮食烘干机本体（1）的顶端连通，所述提升机（2）的底端一侧设置有进料斗（3），所述提升机（2）远离进料斗（3）的一侧连接有连接部（4），所述连接部（4）通过固定螺栓固定安装在粮食烘干机本体（1）的外壁上，所述粮食烘干机本体（1）的底端内部设置有绞龙（6），所述绞龙（6）的一端位于连接部（4）内部，所述绞龙（6）位于连接部（4）内部的一端外侧固设有拨片（7），所述连接部（4）的内壁上设置有多个陶瓷衬板（5），所述陶瓷衬板（5）通过螺丝固定在连接部（4）的内壁上。
2.根据权利要求1所述的一种具有耐磨陶瓷衬板的粮食烘干机，其特征在于：所述拨片（7）采用陶瓷衬板（5）相同的原料加工处理得到。
3.根据权利要求1所述的一种具有耐磨陶瓷衬板的粮食烘干机，其特征在于：所述陶瓷衬板（5）采用如下原料制备：
高岭土100-200重量份、氧化铝20-40重量份、氧化锌10-20重量份、氧化钙6-8重量份、石英10-20重量份、菱镁矿20-40重量份、锆石10-20重量份、氧化锆5-15重量份、氧化镧2-8重量份、氧化钇1-3重量份、氧化锡1-8重量份、粘结剂3-20重量份、辅料2-10质量份。
4.根据权利要求1所述的一种具有耐磨陶瓷衬板的粮食烘干机，其特征在于：所述陶瓷衬板（5）的生产包括以下步骤：
S1：利用球磨机将高岭土100-200重量份、氧化铝20-40重量份、氧化锌10-20重量份、氧化钙6-8重量份、石英10-20重量份、菱镁矿20-40重量份、锆石10-20重量份、氧化锆5-15重量份、氧化镧2-8重量份、氧化钇1-3重量份、氧化锡1-8重量份、辅料2-10质量份磨制成粉末，过100-300目筛，得到粉料；
S2：将所述粉料与3-20重量份粘结剂混合，利用用喷雾机进行喷雾造粉，然后送入陶瓷压机进行压制成型，得到砖坯；
S3：将所述砖坯经过脱粘烧结后磨边，抛光，得到陶瓷衬板。
5.根据权利要求4所述的一种具有耐磨陶瓷衬板的粮食烘干机，其特征在于：所述陶瓷压机的压力为80MPa，压制三次。
6.根据权利要求4所述的一种具有耐磨陶瓷衬板的粮食烘干机，其特征在于：所述所述脱粘的方式为氮气氛围中脱粘。
7.根据权利要求4所述的一种具有耐磨陶瓷衬板的粮食烘干机，其特征在于：所述烧结具体为升温至1800℃保温2-8小时，缓慢降至1480℃并保温2-4小时。
CN201910349238.8A 2019-04-28 2019-04-28 一种具有耐磨陶瓷衬板的粮食烘干机 Pending CN110081701A (zh)