CN109773956B - 无模具装饰混凝土制作方法及转印基膜 - Google Patents
无模具装饰混凝土制作方法及转印基膜 Download PDFInfo
- Publication number
- CN109773956B CN109773956B CN201811581270.0A CN201811581270A CN109773956B CN 109773956 B CN109773956 B CN 109773956B CN 201811581270 A CN201811581270 A CN 201811581270A CN 109773956 B CN109773956 B CN 109773956B
- Authority
- CN
- China
- Prior art keywords
- base film
- mortar
- concrete
- pattern
- retarder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无模具装饰混凝土制作方法和转印基膜,解决了目前无法在立面、斜面或曲面的构件的基础上制备装饰混凝土的问题。技术方案包括将缓凝剂按图案转印在基膜上,所述基膜上均匀分布有多个气孔;将砂浆涂抹在构件上;在砂浆表面贴上印有缓凝剂图案的基膜,有图案的一面与砂浆接触并贴平,将接触面的气体推至气孔排出;养护一段时间,得到硬化的混凝土基体;将基膜从混凝土基体上撕下;用水冲洗混凝土基体表面,使得骨料露出得到图案。本发明转印基膜,所述基膜上均匀分布有若干气孔,与砂浆的接触面转印有缓凝剂。本发明方法简单、操作难度低、可在具有立面、斜面或曲面的构件上制作装饰混凝土,具有良好的图案精细程度。
Description
技术领域
本发明涉及混凝土装饰领域,具体涉及一种无模具装饰混凝土制作方法及转印基膜。
背景技术
转印混凝土是一种通过缓凝技术使得混凝土表面图案部分的骨料露出从而形成图案的装饰混凝土。其特征在于图案精细复杂,可随意变化,相比于普通装饰材料,转印混凝土能给建筑设计师极大的创造空间,能达到极好的艺术效果。所以转印混凝土的发展越来越迅速,应用范围越来越大。
现有常用的转印混凝土的制作方法是将缓凝剂按一定图案印在基膜上,在基膜上浇筑混凝土,待混凝土硬化后揭开基膜,用水冲刷混凝土表面得到相应图案。目前已经有部分学者对转印混凝土进行了研究。姜熙提出,可以将缓凝剂按设计的图案喷涂到PVC薄膜上,将薄膜有图案的一面朝上浇筑混凝土,待混凝土浆料凝固后,拆模并撕扯PVC薄膜,用水枪冲洗混凝土表面,使其露出图案。
目前的转印混凝土都是通过模具水平浇筑混凝土从而得到表面图案,这种方法在工程实践中应用有限,当需要对已有建筑进行装饰,如具有垂直面或倾斜面、曲面的墙面等,现有的装饰混凝土的制作方法难以实现混凝土与建筑面完全吻合。
发明内容
本发明的目的是为了解决上述问题,提供一种工艺简单、操作难度低、图案精细程度高、适用现有立面、斜面或曲面的构件上制作装饰混凝土、吻合程度高的无模具装饰混凝土制作方法。
本发明还提供一种结构简单、使用方便、用于无模具装饰混凝土的转印基膜。
技术方案包括以下步骤:
a、制备转印膜:将缓凝剂按图案转印在基膜上,所述基膜上均匀分布有若干气孔;
b、涂抹砂浆:将砂浆涂抹在构件上并找平;
c、贴上基膜:在砂浆表面贴上印有缓凝剂图案的基膜,有图案的一面与砂浆接触并贴平,将接触面的气体推至气孔排出;
d、养护:养护一段时间,待混凝土基体硬化;
e、揭开基膜:将基膜从混凝土基体上撕下;
f、水冲洗:用水冲洗混凝土基体表面,使得部分骨料露出得到图案。
所述构件具有立面、斜面或曲面的表面。
所述基膜与砂浆的接触面为磨砂面。
所述气孔的直径在0.1mm以下。
所述砂浆流动度小于120mm。
单片基膜面积不大于3m2。
用于无模具装饰混凝土制作方法的转印基膜,包括基膜,所述基膜上均匀分布有若干气孔,与砂浆的接触面转印有缓凝剂。
所述气孔的直径在0.1mm以下。
所述基膜与砂浆的接触面为磨砂面。针对背景技术中存在的问题,发明人对现有技术进行了深入研究,对工艺方法和转印基膜都进行了改进,取消模具水平浇筑,而是将砂浆直接涂抹在现有建筑物表面,然后在砂浆表面贴上有缓凝剂图案的基膜,待砂浆硬化后,揭开基膜,用水枪冲洗砂浆表面使骨料露出而呈现出图案,整个工艺过程无需模具。
上述方法中,由于基膜被贴在砂浆表面,在贴上基膜的过程中极易出现或大或小的气泡,而基膜表面印有缓凝剂,过度大面积推挤排气会造成缓凝剂图案的变形位移,降低图案精细度,对此发明人巧妙的对基膜进行改进,设计多个均匀分布的气孔,接触面局部的气体能够由最近的气孔中快速排出,保证基膜与砂浆表面的密实贴合,避免排气过程中缓凝剂的移位,解决了先砂浆涂抹再覆膜时存在的难点,图案精细程度好。优选地,所述气孔的直径在1mm以下,过大会导致砂浆从气孔流出。
由于本发明中的构件具有立面、斜面或曲面,非水平状态下,基膜受重力作用,可能会下滑移位,因此所述基膜与砂浆的接触面(即印刷图案面)为磨砂面,提高与浆砂的磨擦力,避免覆膜后的移动,能够进一步提高图案的精细程度。
为保证砂浆与基膜的粘附效果,应在涂抹砂浆后尽快贴膜,故应控制基膜面积,优选单片基膜面积不大于3m2,以便于抹面后及时贴膜。若有面积大于3m2的图案,则分区涂抹砂浆、分区贴膜并分区冲洗;为保证区域交界处的图案完整,应等待上一区域冲洗完毕后再涂抹下一区域的砂浆。
由于砂浆需要直接涂抹在构件上,因此应考虑砂浆选用具有快干、易成型功能的组分,优选掺入快干快硬水泥拌制砂浆,如硫铝酸盐水泥,所述砂浆的砂胶比优选大于1.4,流动度小于120mm,本领域技术人员可根据上述条件合理选择合适的砂浆配比,此为现有技术,不作详述。
所述基膜优选基膜自重小、表面不吸水的塑性材料,如PVC薄板、覆膜铜版纸等;所述构件可以为墙面、柱状面、斜坡、弧面等。
综上,本发明基膜结构简单、易于操作;本发明方法简单、操作难度低、制得的图案轮廓清晰、可在具有立面、斜面或曲面的构件上制作装饰混凝土,具有良好的图案精细程度。
说明书附图
图1为发明砂浆表面贴上基膜的状态示意图。
1-构件、2-砂浆、3-缓凝剂、4-基膜、5-气孔。
具体实施方式
参见图1,本发明转印基膜结构为:包括基膜4,所述基膜4上均匀分布有若干直径在0.1mm以下的气孔5,与砂浆的接触面为磨砂面且转印有缓凝剂3,单片基膜4面积不大于3m2。
工艺实施例:
a、制备转印膜:将缓凝剂3按图案转印在基膜4上,所述基膜4上均匀分布有多个直径在1mm以下的气孔5,所述基膜4与砂浆的接触面为磨砂面;
b、涂抹砂浆:将砂浆2涂抹在构件1上并找平,优选所述砂浆的砂胶质量比大于1.4,所述砂浆的流动度小于120mm;
c、贴上基膜:在砂浆2表面贴上印有缓凝剂图案的基膜4,有图案的一面与砂浆2接触并贴平,将接触面的气体推至气孔5排出;
d、养护:养护一段时间,得到硬化的混凝土基体;
e、揭开基膜:将基膜4从混凝土基体上撕下;
f、水冲洗:用水冲洗混凝土基体表面,使得部分骨料露出得到图案。
采用上述方法的实施例1-5的参数及效果详见表1,对比例6-10的参数及效果详见表2。
其中,面积变化率(ACP)通过Eq.(1).计算
ACP=(P1-P0)/P0×100% (1)
式中P0表示设计图案面积,P1表示转印混凝土图案面积。当面积变化率为正值时,转印图案大于设计图案;当面积变化率为负值时,转印图案小于设计图案;当面积变化率为0时,转印图案等于设计图案。
表1实施例
表2对比实施例
Claims (8)
1.一种无模具装饰混凝土制作方法,其特征在于,包括以下步骤:
a、制备转印膜:将缓凝剂按图案转印在基膜上,所述基膜上均匀分布有若干气孔;
b、涂抹砂浆:将砂浆涂抹在构件上并找平,所述砂浆流动度小于120mm,所述构件具有立面、斜面或曲面的表面;
c、贴上基膜:在砂浆表面贴上印有缓凝剂图案的基膜,有图案的一面与砂浆接触并贴平,将接触面的气体推至气孔排出;
d、养护:养护一段时间,得到硬化的混凝土基体;
e、揭开基膜:将基膜从混凝土基体上撕下;
f、水冲洗:用水冲洗混凝土基体表面,使得部分骨料露出得到图案。
2.如权利要求1所述的无模具装饰混凝土制作方法,其特征在于:所述基膜与砂浆的接触面为磨砂面。
3.如权利要求1所述的无模具装饰混凝土制作方法,其特征在于:所述气孔的直径在0.1mm以下。
4.如权利要求1所述的无模具装饰混凝土制作方法,其特征在于:单片基膜面积不大于3m2。
5.一种用于无模具装饰混凝土制作方法的转印基膜,包括基膜,其特征在于,所述基膜上均匀分布有若干气孔,与砂浆的接触面转印有缓凝剂。
6.如权利要求5所述的转印基膜,其特征在于:所述气孔的直径在0.1mm以下。
7.如权利要求5或6所述的转印基膜,其特征在于:所述基膜与砂浆的接触面为磨砂面。
8.如权利要求5或6所述的转印基膜,其特征在于:单片基膜面积不大于3m2。