CN109772356A - 一种丙烯腈催化剂及其制备方法和应用 - Google Patents
一种丙烯腈催化剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN109772356A CN109772356A CN201910173069.7A CN201910173069A CN109772356A CN 109772356 A CN109772356 A CN 109772356A CN 201910173069 A CN201910173069 A CN 201910173069A CN 109772356 A CN109772356 A CN 109772356A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- acrylonitrile
- acrylonitrile catalyst
- preparation
- carrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种丙烯腈催化剂及其制备方法和应用。所述丙烯腈催化剂,其包含具有下述通式(1)所示的金属氧化物,BiaFebNicMgdCeeAfBgChMo12Ox(1)其中:A选自由锂、钠、钾、铷、铯组成的组中的一种或两种以上的元素;B选自由镨、铕、铽、镝组成的组中的一种或两种以上的元素;C选自由钒、镉组成的组中的一种或两种的元素;a、b、c、d、e、f、g和h表示各元素的原子个数;a为1.2~3.0;b为1.0~2.7;c为3~8;d为0.3~1.6;e为0.4~1.8;f、g和h含量分别为0.01~0.4;x为用于满足其它元素化合价所需的氧原子数。本发明的丙烯腈催化剂具有以下效果:1)可满足工业化扩能装置高催化剂负荷的要求;2)降低了羰基化合物丙烯醛、丙烯酸的生成量,提高了装置运行周期。
Description
技术领域
本发明涉及一种丙烯腈催化剂及其制备方法和应用,属于催化剂领域。
背景技术
丙烯腈(AN)是用于合成纤维腈纶的原料单体,也是ABS、SAN等热塑性合成树酯、丁腈橡胶、己二腈、丙烯酰胺及其他衍生物的原料,是石油化工重要产品之一。丙烯氨氧化生产丙烯腈的工艺技术已日趋成熟,研制性能优良的丙烯腈催化剂是丙烯腈行业关注的热点。
对于催化剂稳定性,目前催化剂在流化床反应器中可连续运转4-5年不必整体更换,比过去仅能用1-1.5年即需更换新催化剂有了明显的提高。从催化剂本身来说,某种组分的挥发损失是造成使用寿命不长的主要原因。钼系催化剂主要是钼组分的挥发。最早解决这些问题的方法是将催化剂从反应器中卸出,补加流失的组分并活化后再加入到反应器内,当然,这种方法是不经济的,因为工厂停车将造成很大经济损失。一种改进的方法是连续向反应器内加入易挥发的组分,以补充和减少催化剂中某些组分的流失。例如加入含有氧化钼的硅胶以解决钼的挥发,就可以不必停车以保持工厂有较长的年开工时数。但是,这种方法也存在一些缺点,主要是补充加入的物质与反应器内催化剂不同,长期使用会使反应器内催化剂组成发生变化。
另外,丙烯腈催化剂的技术指标中还有一项流动性或结块倾向的指标,通常用休止角来描述催化剂的流动性。通常测定流动性是在冷态下进行,不能代表催化剂在反应器内的高温下的流动状态。如果在高温下催化剂流动状态变差就会造成旋风分离器料腿或空气、丙烯-氨分布器被堵塞而无法正常运转。对于钼系催化剂,发生这种现象的原因可能是在催化剂表面出现过量氧化钼造成的。如果过量氧化钼出现且在催化剂表面沉积就会使微粒相互粘结而造成堵塞。催化剂采用低氧比条件可以显著提高反应器生产能力,是当前研究工作者追求的方向。但是氧比过低时,催化剂中的某些高价态元素会被过度还原而产生大量的过量氧化钼。因此,降低反应温度,减少活性组分钼的升华,延缓催化剂的寿命是新型催化剂研发的趋势。
对于清洁性问题,由于在目前丙烯腈反应产物中有丙烯醛、丙烯酸等杂质,它们大部分是在系统中通过聚合除去,如果系统中聚合物积累将堵塞管线和设备,装置必须停工清洗,影响运行周期,因此工厂希望使用的催化剂能尽量减少丙烯醛、丙烯酸的生成。清洁性差的催化剂羰基化合物丙烯醛、丙烯酸的生成量较大。鉴于羰基化合物丙烯醛、丙烯酸的存在对外排污水及装置运行周期都有直接影响。为此要开展降低反应过程中丙烯醛、丙烯酸的工作,实现低温反应是提高丙烯腈催化剂清洁环保性能的关键技术措施。
对于选择性问题,由于丙烯氨氧化反应不受热力学平衡的控制,而完全受动力学因素控制,关键在于催化剂性能,因此随着对丙烯氨氧化耦合反应网络系统研究的深入,催化剂表面结构更多信息的获取以及各组分氧化物催化剂体系设计能力的提高,将丙烯腈单程收率继续提升的空间还是存在的。随着市场的变化,对丙烯腈生产过程中的副产物氢氰酸、乙腈的需求也发生了变化,应当研究副产物的选择性,以满足不同使用单位的需要。
对于催化剂负荷低的问题,高负荷催化剂对一定规模的生产装置而言,可减少催化剂装填量。高丙烯负荷、高反应压力条件可以提高丙烯腈产量和反应器的处理能力,并可使反应器扩能,这样厂家可根据市场需求适当提高生产能力。耐高压催化剂还可以满足日益提高的环保要求。因此研制出在高负荷、高压条件下仍保持高反应性能的催化剂是目前的一个研究方向,它将使丙烯腈生产形成规模经济效益成为可能。由于一些丙烯腈装置大部分都进行了扩能改造,生产能力在原有基础上增加了60%,这些装置主体设备没有改变。由于负荷的增加,反应压力增加了,反应器负荷也增加了,因此从生产实际角度,提高国产丙烯腈催化剂高压下的选择性和活性、提高国产丙烯腈催化剂的重时空速也是目前亟待解决的技术问题。
发明内容
发明要解决的问题
鉴于现在技术中的丙烯腈催化剂所存在的问题,本申请首先提供了一种丙烯腈催化剂。具体而言,本发明的丙烯腈催化剂可以在较低反应温度下反应有效防止活性组分升华,提高丙烯腈催化剂的稳定性;能够在较低反应温度下反应减少羰基化合物的产生,提高丙烯腈催化剂的清洁性。可以提高丙烯腈和氢氰酸的单程收率、降低乙腈收率,更好满足市场需求。能够在高重量空速下反应,减少丙烯腈催化剂装填量,更好满足扩能装置的需求。
进一步地,本发明还提供一种原料易于获取,制备方法简单易行的丙烯腈催化剂的制备方法。
用于解决问题的方案
本发明提供一种丙烯腈催化剂,其包含具有下述通式(1)所示的金属氧化物,
BiaFebNicMgdCeeAfBgChMo12Ox (1)
其中:
A选自由锂、钠、钾、铷、铯组成的组中的一种或两种以上的元素;
B选自由镨、铕、铽、镝组成的组中的一种或两种以上的元素;
C选自由钒、镉组成的组中的一种或两种的元素;
a、b、c、d、e、f、g和h表示各元素的原子个数;
a为1.2~3.0;
b为1.0~2.7;
c为3~8;
d为0.3~1.6;
e为0.4~1.8;
f、g和h含量分别为0.01~0.4;
x为用于满足其它元素化合价所需的氧原子数。
根据本发明的丙烯腈催化剂,其中,所述丙烯腈催化剂含有载体,所述金属氧化物负载于所述载体上;优选地,所述载体为二氧化硅。
根据本发明的丙烯腈催化剂,其中,以所述丙烯腈催化剂的总质量计,所述载体的加入量为30%-70%,优选为40%-55%。
根据本发明的丙烯腈催化剂,其中,所述丙烯腈催化剂的松密度为0.88~1.12g/mL,紧密度为1.04~1.28g/mL;和/或,所述丙烯腈催化剂的孔容为0.20~0.30mL/g,比表面积为30.0m2/g以上。
根据本发明的丙烯腈催化剂,其中,30%以下的所述丙烯腈催化剂的粒径为大于90μm,30-50%的所述丙烯腈催化剂的粒径为大于20μm且在45μm以下,7%以下的所述丙烯腈催化剂的粒径为20μm以下。
本发明还提供一种根据本发明的丙烯腈催化剂的制备方法,包括以下步骤:
制备工序:取制备所述丙烯腈催化剂的原料溶于水后与载体混合,获得前体浆料;
干燥工序:将所述前体浆料干燥,得到干燥颗粒;
焙烧工序:对所述干燥颗粒进行活化焙烧,得到焙烧产物。
根据本发明的丙烯腈催化剂的制备方法,其中,所述载体为二氧化硅,所述二氧化硅是以硅溶胶的形式加入的;优选地,以所述硅溶胶的总质量计,SiO2的含量为35.1~49.5%;和/或,Cl-的含量为11~17ppm;更优选地,所述硅溶胶中包含有稳定剂,所述稳定剂为氨水。
根据本发明的丙烯腈催化剂的制备方法,其中,所述硅溶胶的粘度为6~14cP,pH值为9.0~9.6,密度为1.19~1.325g/mL;和/或,所述硅溶胶中的SiO2的粒径为17~25nm。
根据本发明的丙烯腈催化剂的制备方法,其中,所述干燥工序中,所述干燥的温度为130℃-400℃,优选为150℃-350℃;所述焙烧工序中,所述焙烧的温度为500℃-700℃,优选为580℃-680℃,所述焙烧的时间为1h-5h,优选为1h-3h;在进行焙烧时通入空气,所述空气的通入量为100-400Nm3/吨丙烯腈催化剂,优选为150-300Nm3/吨丙烯腈催化剂。
本发明还提供一种根据本发明的丙烯腈催化剂或本发明的制备方法制备得到的丙烯腈催化剂在丙烯氨氧化制备丙烯腈中的应用。
发明的效果
本发明的丙烯腈催化剂具有以下效果:
1)可满足工业化扩能装置高催化剂负荷的要求;
2)降低了羰基化合物丙烯醛、丙烯酸的生成量,提高了装置运行周期。
3)在实际生产中,可以使用较低的操作温度,例如418℃~425℃,有利于延长催化剂寿命,催化剂使用寿命超过10年或更长;
4)丙烯转化率高,降低了吸收塔尾气治理的负荷;
5)在较低的反应温度条件下还可使丙烯腈的单程收率可以达到83.0%或者更高;
6)本发明的催化剂更重要的优点是主要成分成本低而且催化剂的制备很简单。
具体实施方式
以下将详细说明本发明的各种示例性实施例、特征和方面。在这里专用的词“示例性”意为“用作例子、实施例或说明性”。这里作为“示例性”所说明的任何实施例不必解释为优于或好于其它实施例。
另外,为了更好地说明本发明,在下文的具体实施方式中给出了众多的具体细节。本领域技术人员应当理解,没有某些具体细节,本发明同样可以实施。在另外一些实例中,对于本领域技术人员熟知的方法、手段、器材和步骤未作详细描述,以便于凸显本发明的主旨。
如无特殊声明,本发明所使用的单位均为国际标准单位,并且本发明中出现的数值,数值范围,均应当理解为包含了工业生产中所不可避免的系统性误差。
第一实施方式
本发明的第一实施方式提供了一种丙烯腈催化剂,包含具有下述通式(1)所示的金属氧化物,
BiaFebNicMgdCeeAfBgChMo12Ox (1)
其中:
A选自由锂、钠、钾、铷、铯组成的组中的一种或两种以上的元素;
B选自由镨、铕、铽、镝组成的组中的一种或两种以上的元素;
C选自由钒、镉组成的组中的一种或两种的元素;
a、b、c、d、e、f、g和h表示各元素的原子个数;
a为1.2~3.0;
b为1.0~2.7;
c为3~8;
d为0.3~1.6;
e为0.4~1.8;
f、g和h含量分别为0.01~0.4;
x为用于满足其它元素化合价所需的氧原子数。
本实施方式的目的之一在于提高催化剂的稳定性,主要解决催化剂结构畸变问题和催化剂的主要活性物钼的流失问题,解决催化剂结构畸变关键要求催化剂有合理的元素组成,解决活性物质钼的流失主要是通过降低反应温度,达到减少钼流失的目的。
本实施方式通过引入钼、铋、镍、镁和铁作为必需成分。本实施方式一方面通过元素合理搭配,充分发挥了元素之间的“协同作用”,使催化剂结构畸变变得缓和减少活性物质钼的流失;通过引入碱金属元素,调整催化剂表面酸碱度,使催化剂在较低温度下对反应原料有好的吸附能力,保证催化剂在低温条件下有很高的丙烯腈收率和丙烯转化率。另外,本实施方式还引入元素铈,不仅降低了反应副产物生成量,而且使催化剂在较高负荷下具有良好的丙烯腈收率和选择性及稳定性。
进一步,本实施方式通过引入镨、铕、铽和/或镝等元素,可以提高催化剂的选择性,提高丙烯腈收率,提高氢氰酸收率,降低乙腈收率;还可以降低反应的温度,减缓催化剂活性衰减的速度,延长催化剂的寿命;提高催化剂的处理能力,满足装置扩能的需求。本实施方式通过引入钒和/或镉等元素,可以降低羰基化合物的生成量,提高催化剂的清洁性,减少有机物的聚合,提高装置的运行周期。本发明的丙烯腈催化剂,可以提高丙烯的转化率,并且有利于催化剂长周期高效运行,可以提高催化剂选择性及稳定性。
本发明的催化剂中的钼,可以使用任何氧化物形式的钼,如氧化钼或者钼酸盐。较优选的是可水溶性的钼酸盐,最优选起始物料为七钼酸铵。
催化剂中的碱金属,可以用氧化物形式,也可以用经焙烧能产生氧化物的盐,例如硝酸盐或氯化盐。硝酸盐或氯化盐易于获得和容易溶解。
催化剂中的铁、镍、镁、铈、铋,可以用氧化物形式,也可以使用在焙烧时能够生成氧化物的任何化合物,较优选的是可水溶性的盐,最优选的是水合硝酸盐或硝酸盐。
催化剂中的镨、铕、铽和镝,可以用氧化物形式,也可以使用在焙烧时能够生成氧化物的任何化合物,较优选的是可水溶性的盐,最优选的是水合硝酸盐或硝酸盐。
催化剂中的钒、镉,可以用氧化物形式,也可以使用在焙烧时能够生成氧化物的任何化合物,较优选的是可水溶性的盐。具体而言,钒优选以硝酸双氧钒的方式引入;镉优选以水合硝酸盐或硝酸盐的方式引入。
本发明的丙烯腈催化剂可以仅由活性组分组成,在无载体的情况下使用也可显示出优良的性能。为了优化技术方案,可以与载体结合使用,所述金属氧化物负载于所述载体上。所述载体优选的是二氧化硅,以所述丙烯腈催化剂的总质量计,载体占催化剂重量的30%-70%;优选的,载体占催化剂总重量的40%-55%。
在本发明中,所述丙烯腈催化剂的松密度为0.88~1.12g/mL,紧密度为1.04~1.28g/mL;和/或,所述丙烯腈催化剂的孔容为0.20~0.30mL/g,比表面积为30.0m2/g以上。
另外,在本发明中,以所述丙烯腈催化剂的质量计,所述丙烯腈催化剂的磨损率为4%以下。
在本发明中,30%以下的所述丙烯腈催化剂的粒径为大于90μm,30-50%的所述丙烯腈催化剂的粒径为大于20μm且在45μm以下,7%以下的所述丙烯腈催化剂的粒径为20μm以下。
本发明的丙烯腈催化剂具有优异的催化性能,催化效率高。具体地,丙烯腈(AN)的收率为80%以上,乙腈(ACN)的收率为4%以下,氢氰酸(HCN)的收率为6%左右。
第二实施方式
本发明的第二实施方式提供了一种第一实施方式的丙烯腈催化剂的制备方法,具体包括以下步骤:
制备工序:取制备丙烯腈催化剂的原料溶于水后与载体混合,获得前体浆料;
干燥工序:将所述前体浆料干燥,得到干燥颗粒;
焙烧工序:对所述干燥颗粒进行焙烧,得到焙烧产物;
优选地,所述水的电导率为小于1μs/cm。
本发明可以通过使用沙滤、活性炭吸附、膜渗透过滤的方式,使水的电导率小于1μs/cm。
具体地,所述制备步骤中,可以将可溶性的活性组分原料溶解到一定量的电导率小于1μs/cm的纯水中,制成混合溶液,然后与载体混合做成浆液。
进一步地,所述载体为二氧化硅,二氧化硅是以硅溶胶形式加入的;优选地,以所述硅溶胶的总质量计,SiO2的含量为35.1~49.5%;和/或,Cl-的含量为11~17ppm。
在本发明中,所述硅溶胶中包含有稳定剂,所述稳定剂为氨水。在硅溶胶中,NH3的含量为0.15-0.27%。
在本发明中,所述硅溶胶的粘度为6~14cP,pH值为9.0~9.6,密度为1.19~1.325g/mL;和/或,所述硅溶胶中的SiO2的粒径为17~25nm。
在干燥工序中,在130℃~400℃下将配置好的浆液喷雾干燥成型,得到干燥颗粒,优选喷雾成型温度为150℃~350℃,喷雾干燥器可用压力式或离心转盘式,优选离心转盘式,能保证制成的丙烯腈催化剂有良好的粒度分布。
在焙烧工序中,通常在500℃~700℃条件下,将喷雾成型后的干燥颗粒进行焙烧活化,焙烧时间1h~5h或更长时间,优选的焙烧温度580℃~680℃,焙烧时间1h~3h,焙烧过程中可以通入空气,空气通入量为100~400Nm3/吨丙烯腈催化剂,优选通入量为150~300Nm3/吨丙烯腈催化剂。
另外,本申请的丙烯腈催化剂的制备方法还包括三废处理的步骤,将生产过程中的尾气进行回收,废水经蒸发后达标排放,废渣经压滤后进行处理。
第三实施方式
本发明的第三实施方式提供了一种本发明的第一实施方式的丙烯腈催化剂或第二实施方式的制备方法制备得到的丙烯腈催化剂在丙烯氨氧化制备丙烯腈中的应用。
具体地,本发明的丙烯腈催化剂可以使用流化床制造丙烯腈。丙烯腈催化剂可以用于连续的生产过程,也可以用于间歇生产过程,但在使用大型反应器时最好选择连续的生产过程。此外,希望对丙烯腈催化剂进行周期性再生或活化,例如在一定温度下通入空气以实现这一过程。
利用本发明的丙烯腈催化剂制备丙烯腈所需反应物为氧、氨、丙烯及它们的混合物。所需氧可以用纯氧、富氧空气,但从经济、资源方便考虑,使用空气作为氧源更为合理;氨可用肥料级液氨;丙烯可以和饱和烃如乙烷、丙烷、丁烷、戊烷的混合物形式存在。但从经济角度考虑,丙烯含量应大于85%(体积)。
反应原料中的氨与丙烯的摩尔比最好为(0.5~1.5):1,氨与丙烯的摩尔比超过1.5:1对反应没有明显影响,氨与丙烯的摩尔比为(1.0~1.2):1时,氨的利用率最高,大大降低了反应器流出物中未反应氨的含量,从而减少了用于中和未反应氨硫酸的用量。
反应原料中的空气与丙烯的摩尔比为(8.5~9.8):1,最佳空气与丙烯的摩尔比为(9.0~9.5):1。
这样低的氨、空气与丙烯配比,有利于提高反应器的效率,反应器的生产能力可提高5%。
催化剂负荷(即WWH,指每吨催化剂每小时处理丙烯的吨数)为0.04~0.20,最佳为0.06~0.10,并且在实际生产中可以保证WWH=0.08~0.085时长期稳定运行。在相同反应器催化剂使用量条件下,可提高原料丙烯的投料量,相应提高反应器的生产能力10~15%。
催化剂反应压力一般为0.01~0.20MPa,优选为0.05~0.14MPa。本催化剂在反应压力大于0.10MPa时,丙烯腈的收率仍然可以达到81.0%,在较低压力下反应效果更好,对催化剂效率起关键因素是反应原料与催化剂的接触时间,通常接触时间为0.1~30秒,优选接触时间为0.5~18秒。
实际生产时,反应温度为380℃~590℃,优选为418℃~425℃,此时,丙烯腈的收率仍然可以达到83.0%以上,并且可以保证在此温度下长期稳定运行,可减缓催化剂中活性物质钼的损失,有利于提高催化剂的使用寿命。
一般来说,向反应原料加水可以提高反应的选择性和丙烯腈的收率。但在本发明中,不需要向原料中加水,因为在反应过程中有水生成。
由于采用多种元素组合,优化了催化剂表面的电负性,使得催化剂在反应器内高速气流冲击下产生较小量静电,使流失到急冷塔的细小颗粒催化剂不被急冷塔管壁吸附,延长了该装置使用周期,提高了生产效率。
实施例
下面将结合实施例对本发明的实施方案进行详细描述,但是本领域技术人员将会理解,下列实施例仅用于说明本发明,而不应视为限定本发明的范围。实施例中未注明具体条件者,按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者,均为可以通过市购获得的常规产品。
实施例中,对催化剂考察评价的具体条件为:
反应器:流化床反应器,内径
催化剂填装量:440克
反应器顶压力:0.08MPa(表压)
反应温度:435℃
反应时间:4小时
原料比:烯烃/氨/空气=1/1.2/9.5(摩尔比)
WWH:0.085小时-1
反应产物用0℃酸液和水吸收,用气相色谱和化学分析结合分析产物。并计算碳平衡,当碳平衡在(95~105)%时为有效数据。
烯烃转化率、不饱和腈收率和丙烯腈选择性的定义为:
实施例1
将388.43g(NH4)6Mo7O24·4H2O加入到75℃热水中,搅拌使其全部溶解,再加入2684.1g二氧化硅含量为40%(wt)的硅溶胶(牌号;NALCO 2327CH),制成物料A。
将125.93g Fe(NO3)3·9H2O加入到80℃热水中,搅拌使其全部溶解,再加入177.87g Bi(NO3)3·5H2O,287.91g Ni(NO3)2·6H2O,28.21g Mg(NO3)2·6H2O,63.69g Ce(NO3)3·6H2O,制成物料B。
将1.5g NaCl,2.22g KNO3,9.57g Pr(NO3)3·6H2O,4.52g Cd(NO3)2加入80℃热水中溶解后,将其加入到物料B中,形成物料C。
将物料C在快速搅拌下滴加于物料A中,并于80℃恒温老化4h后,用直径50mm雾化盘,转速12000转/min,160℃下,喷雾干燥成型,将干燥成型的催化剂放置到回转焙烧炉中,600℃下焙烧活化3h,得到成品催化剂,其中催化剂活性组分组成见表2。
实施例2~6
制备方法同实施例1,但起始用料按表1加入。催化剂活性组分组成见表2,其引入方式与实施例1相同。
对比例1~6
制备方法同实施例1,但起始用料按表1加入。催化剂活性组分组成见表2,其引入方式与实施例1相同。
表2催化剂活性组分组成表
性能测试
1、样品初活性评价
取实施例1获得催化剂中的三个样品(各440g)置于流化床催化剂评价装置中,升温并反应温度控制在435℃,稳定90min后取样,利用气相色谱和液相色谱分析,进行样品初活性评价,具体结果如下表3所示。
表3实施例1的丙烯腈催化剂的样品初活性评价表
由表3中数据可以看出,一般而言,丙烯腈催化剂的标准评价条件中的反应温度是440℃,而本发明催化剂样品的评价温度是435℃,在反应温度低5℃的情况下取得了上述反应成绩,从数据上看:
(1)反应温度较标准评价条件低5℃,在实际生产的工业装置上的反应温度可降至418℃,比国内催化剂低8℃,比英力士公司的C49MC催化剂低12℃,是一种低温型催化剂。较低的反应温度会减少活性组分的挥发,提高催化剂的寿命;较低的反应温度反应器产生的杂质量会减少,利于产品质量的控制。
(2)羰基化合物丙烯醛收率在0.2%左右、丙烯酸在1.5%左右,均处于较低的水平,在工业装置上将会减少四效外排污水污染物的含量,减少回收精制系统聚合问题的发生,提高产品的收率,增长装置的运行周期。
(3)主要产物丙烯腈的收率可以超过83%,说明本发明丙烯腈催化剂是一种高选择性催化剂。
(4)由于本发明催化剂的催化剂催化效能高,在工业装置上可以降低重量空速,利于扩能装置的生产。
2、样品初活性与XYA-5催化剂的对比评价
按照上述样品初活性评价的方法,取实施例1获得催化剂中的三个样品和XYA-5催化剂的三个样品(各440g),置于流化床催化剂评价装置中,升温并反应温度控制在435℃,稳定90min后取样,利用气相色谱和液相色谱分析,进行样品初活性对比评价,具体结果如下表4所示:
表4实施例1的丙烯腈催化剂的样品初活性与XYA-5催化剂的对比评价表
从上表4中可以看出:
(1)本发明的丙烯腈催化剂有良好的稳定性能和较高的丙烯腈单收,AN收率可以超过83%,比XYA-5催化剂的AN收率高约2.5个百分点,在工业生产时其初活性将超过85%,是一种高效的催化剂。
(2)本发明的丙烯腈催化剂在反应过程中生成的杂质少,丙烯醛单收在0.2%左右,且丙烯酸的含量较XYA-5有大幅度的降低。这样使主副产品质量易于控制,也使丙烯腈生产装置操作更加容易,丙烯腈装置各系统将更加清洁,将降低操作者劳动强度,提高生产装置的精制回收率,也将提高装置的经济效益。
(3)副产品乙腈的收率有所下降,氢氰酸的收率有所上升。在工业装置上,催化剂进入平衡态后,氢氰酸的收率将在6%左右,将提高甲酯产业链的经济效益。
3、催化剂活性评价
取实施例1-6和对比例1-6获得的催化剂(各440g)置于流化床催化剂评价装置中,升温并反应温度控制在435℃,稳定90min后取样,利用气相色谱和液相色谱分析,进行催化剂活性评价,评价结果由表5所示。
表5催化剂活性评价结果
表5为催化剂活性评价结果,从表5中可以看出:本发明实施例的催化剂在丙烯转化率,丙烯腈选择性,丙烯腈收率上,均比对比例的测试结果有显著的提高,表现出较好的效果。
4、催化剂稳定性评价
按实施例1和对比例1的制备方法及加入量制备相应的催化剂,每次各取实施例1和对比例1得到的催化剂各440g,置于流化床催化剂评价装置中,升温至435℃,连续运行1000h,并按下表6中的试验时间分别稳定90min,利用气相色谱和液相色谱分析,进行催化剂稳定性评价,评价结果由表6所示。
表6实施例1和对比例1的丙烯腈催化剂稳定性试验结果
表6为实施例1和对比例1的丙烯腈催化剂稳定性的试验结果。从表6可以看出:实施例1的丙烯腈催化剂的稳定性试验进行1000h的丙烯腈收率比进行4h的丙烯腈收率降低了1.62%,下降不明显;进行1000h的丙烯腈选择性比进行4h的丙烯腈选择性低了0.86%,变化不明显;而对比例1催化剂的稳定性试验进行1000h的丙烯腈收率比4h的丙烯腈收率降低了2.88%,降低幅度大,丙烯腈选择性比4h的丙烯腈选择性低了1.90%,明显降低。
5、物性测试
对实施例1制备得到的丙烯腈催化剂进行相应的物理性能测试,结果如下表7所示。
表7
由表1可以看出,本申请的丙烯腈催化剂的物性参数合适,满足生产丙烯腈的要求。
本发明的上述实施例仅仅是为清楚地说明本发明所作的举例,而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明权利要求的保护范围之内。
Claims (10)
1.一种丙烯腈催化剂,其特征在于,包含具有下述通式(1)所示的金属氧化物,
BiaFebNicMgdCeeAfBgChMo12Ox (1)
其中:
A选自由锂、钠、钾、铷、铯组成的组中的一种或两种以上的元素;
B选自由镨、铕、铽、镝组成的组中的一种或两种以上的元素;
C选自由钒、镉组成的组中的一种或两种的元素;
a、b、c、d、e、f、g和h表示各元素的原子个数;
a为1.2~3.0;
b为1.0~2.7;
c为3~8;
d为0.3~1.6;
e为0.4~1.8;
f、g和h含量分别为0.01~0.4;
x为用于满足其它元素化合价所需的氧原子数。
2.根据权利要求1所述的丙烯腈催化剂,其特征在于,所述丙烯腈催化剂含有载体,所述金属氧化物负载于所述载体上;优选地,所述载体为二氧化硅。
3.根据权利要求2所述的丙烯腈催化剂,其特征在于,以所述丙烯腈催化剂的总质量计,所述载体的加入量为30%-70%,优选为40%-55%。
4.根据权利要求1-3任一项所述的丙烯腈催化剂,其特征在于,所述丙烯腈催化剂的松密度为0.88~1.12g/mL,紧密度为1.04~1.28g/mL;和/或,所述丙烯腈催化剂的孔容为0.20~0.30mL/g,比表面积为30.0m2/g以上。
5.根据权利要求1-4任一项所述的丙烯腈催化剂,其特征在于,30%以下的所述丙烯腈催化剂的粒径为大于90μm,30-50%的所述丙烯腈催化剂的粒径为大于20μm且在45μm以下,7%以下的所述丙烯腈催化剂的粒径为20μm以下。
6.一种根据权利要求1-5任一项所述的丙烯腈催化剂的制备方法,其特征在于,包括以下步骤:
制备工序:取制备所述丙烯腈催化剂的原料溶于水后与载体混合,获得前体浆料;
干燥工序:将所述前体浆料干燥,得到干燥颗粒;
焙烧工序:对所述干燥颗粒进行活化焙烧,得到焙烧产物。
7.根据权利要求6所述的丙烯腈催化剂的制备方法,其特征在于,所述载体为二氧化硅,所述二氧化硅是以硅溶胶的形式加入的;优选地,以所述硅溶胶的总质量计,SiO2的含量为35.1~49.5%;和/或,Cl-的含量为11~17ppm;更优选地,所述硅溶胶中包含有稳定剂,所述稳定剂为氨水。
8.根据权利要求7所述的丙烯腈催化剂的制备方法,其特征在于,所述硅溶胶的粘度为6~14cP,pH值为9.0~9.6,密度为1.19~1.325g/mL;和/或,所述硅溶胶中的SiO2的粒径为17~25nm。
9.根据权利要求6-8任一项所述的丙烯腈催化剂的制备方法,其特征在于,所述干燥工序中,所述干燥的温度为130℃-400℃,优选为150℃-350℃;所述焙烧工序中,所述焙烧的温度为500℃-700℃,优选为580℃-680℃,所述焙烧的时间为1h-5h,优选为1h-3h;在进行焙烧时通入空气,所述空气的通入量为100-400Nm3/吨丙烯腈催化剂,优选为150-300Nm3/吨丙烯腈催化剂。
10.一种根据权利要求1-5任一项所述的丙烯腈催化剂或权利要求6-9任一项所述的制备方法制备得到的丙烯腈催化剂在丙烯氨氧化制备丙烯腈中的应用。