CN109537274A - 一种服装面料的生产工艺 - Google Patents

一种服装面料的生产工艺 Download PDF

Info

Publication number
CN109537274A
CN109537274A CN201811215953.4A CN201811215953A CN109537274A CN 109537274 A CN109537274 A CN 109537274A CN 201811215953 A CN201811215953 A CN 201811215953A CN 109537274 A CN109537274 A CN 109537274A
Authority
CN
China
Prior art keywords
mass parts
garment material
production technology
drying
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811215953.4A
Other languages
English (en)
Inventor
朱建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Hecheng Textile Co Ltd
Original Assignee
Nantong Hecheng Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Hecheng Textile Co Ltd filed Critical Nantong Hecheng Textile Co Ltd
Priority to CN201811215953.4A priority Critical patent/CN109537274A/zh
Publication of CN109537274A publication Critical patent/CN109537274A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种服装面料的生产工艺，包括如下步骤：在20‑50质量份去离子水中投入1～5质量份丙烯酸、3质量份胍类抗菌剂、5质量份聚氧乙烯多胺、2质量份聚丙二醇混合，搅拌均匀；再同时缓慢加入1质量份失水山梨醇脂肪酸酯、2质量份荆芥挥发油、3质量份四羟甲基氯化磷、1质量份芦荟大黄苷，继续搅拌，至充分混合均匀，制得整理液；然后进行抗菌处理。本发明帽子服装面料的后生产工艺，其整理后的面料具有优异的阻燃、抗菌、抗皱、防静电性能，且耐洗性强，且能够提高面料的抗菌性能，抗菌效果好，使用时间长。

Description

一种服装面料的生产工艺
技术领域
本发明属于纺织技术领域，具体涉及一种服装面料的生产工艺。
背景技术
随着社会的不断发展，技术水平的不断提高，人们在着装方面的要求也在不断提高，特别是对服装面料的各种性能有了新的要求，如抗静电、抗菌、抗病毒、环保、健康等等。目前对于服装面料的抗静电性能研究己经有了初步的成果，但对于其抗菌、抗病毒处理的研究还处于萌芽状态。
发明内容
发明目的：本发明针对现有技术中的不足，提出一种具有优异的阻燃、抗菌、抗皱、防静电性能，且耐洗性强，且能够提高面料的抗菌性能，抗菌效果好的服装面料的生产工艺。
技术方案：本发明所述的一种服装面料的生产工艺，包括如下步骤：
1）在 20 -50质量份去离子水中投入 1～5质量份丙烯酸、3质量份胍类抗菌剂、5质量份聚氧乙烯多胺、2质量份聚丙二醇混合，搅拌均匀；
2）再同时缓慢加入 1质量份失水山梨醇脂肪酸酯、2 质量份荆芥挥发油、3 质量份四羟甲基氯化磷、1质量份芦荟大黄苷，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干；
4）第一次抗菌处理 ：将服装面料脱水处理，然后浸入纳米抗菌液中，升温至 40-60℃，浸泡 1-3小时，然后再升温至 60-90℃，浸泡 5-8 小时 ；
5）第二次抗菌处理 ：将抗菌整理液涂覆在服装面料的表面，然后在 60-90℃的温度下进行烘干成型，烘干时间为 2-5 分钟，接着在 100-160℃的温度下进行烘焙交联，时间为5-10分钟 ；
6）还原清洗处理 ：将服装面料放入清洗溶液中进行清洗 ；
7）后处理：依次进行脱水、松式烘干、拉幅定形和检验。
进一步的，所述纳米抗菌液是由纳米氯化银分散液以及纳米银离子粘结剂制成。
进一步的，所述抗菌整理液由竹醋液、涂层剂和添加剂混合制成。
进一步的，所述步骤6）中的服装面料先通过拉幅烘干机烘干，再通过热定型机烘焙交联。
进一步的，所述步骤7）中的清洗溶液的 ph 值为 5-5.5，清洗温度为 40-55℃，清洗时间为 10-20 分钟。
有益效果：本发明全棉服装面料的后生产工艺，其整理后的面料具有优异的阻燃、抗菌、抗皱、防静电性能，且耐洗性强，且能够提高面料的抗菌性能， 抗菌效果好，使用时间长。
具体实施方式
下面结合具体实施例对本发明作进一步说明：
实施例1
一种服装面料的生产工艺，包括如下步骤：
1）在 20 质量份去离子水中投入 1质量份丙烯酸、3质量份胍类抗菌剂、5质量份聚氧乙烯多胺、2质量份聚丙二醇混合，搅拌均匀；
2）再同时缓慢加入 1质量份失水山梨醇脂肪酸酯、2 质量份荆芥挥发油、3 质量份四羟甲基氯化磷、1质量份芦荟大黄苷，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干；
4）第一次抗菌处理 ：将服装面料脱水处理，然后浸入纳米抗菌液中，升温至 40℃， 浸泡 1小时，然后再升温至 60℃，浸泡 5小时 ；
5）第二次抗菌处理 ：将抗菌整理液涂覆在服装面料的表面，然后在 60℃的温度下进行烘干成型，烘干时间为 2 分钟，接着在 100℃的温度下进行烘焙交联，时间为 5分钟 ；
6）还原清洗处理 ：将服装面料放入清洗溶液中进行清洗 ；
7）后处理：依次进行脱水、松式烘干、拉幅定形和检验。
进一步的，所述纳米抗菌液是由纳米氯化银分散液以及纳米银离子粘结剂制成。
进一步的，所述抗菌整理液由竹醋液、涂层剂和添加剂混合制成。
进一步的，所述步骤6）中的服装面料先通过拉幅烘干机烘干，再通过热定型机烘焙交联。
进一步的，所述步骤7）中的清洗溶液的 ph 值为 5-5.5，清洗温度为 40℃，清洗时间为 10分钟。
实施例2
一种服装面料的生产工艺，包括如下步骤：
1）在 50质量份去离子水中投入5质量份丙烯酸、3质量份胍类抗菌剂、5质量份聚氧乙烯多胺、2质量份聚丙二醇混合，搅拌均匀；
2）再同时缓慢加入 1质量份失水山梨醇脂肪酸酯、2 质量份荆芥挥发油、3 质量份四羟甲基氯化磷、1质量份芦荟大黄苷，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干；
4）第一次抗菌处理 ：将服装面料脱水处理，然后浸入纳米抗菌液中，升温至 60℃， 浸泡 3小时，然后再升温至 90℃，浸泡8小时 ；
5）第二次抗菌处理 ：将抗菌整理液涂覆在服装面料的表面，然后在 90℃的温度下 进行烘干成型，烘干时间为 5 分钟，接着在 160℃的温度下进行烘焙交联，时间为 10分钟 ；
6）还原清洗处理 ：将服装面料放入清洗溶液中进行清洗 ；
7）后处理：依次进行脱水、松式烘干、拉幅定形和检验。
进一步的，所述纳米抗菌液是由纳米氯化银分散液以及纳米银离子粘结剂制成。
进一步的，所述抗菌整理液由竹醋液、涂层剂和添加剂混合制成。
进一步的，所述步骤6）中的服装面料先通过拉幅烘干机烘干，再通过热定型机烘焙交联。
进一步的，所述步骤7）中的清洗溶液的 ph 值为 5-5.5，清洗温度为 55℃，清洗时间为 20 分钟。
实施例3
一种服装面料的生产工艺，包括如下步骤：
1）在 30质量份去离子水中投入 3质量份丙烯酸、3质量份胍类抗菌剂、5质量份聚氧乙烯多胺、2质量份聚丙二醇混合，搅拌均匀；
2）再同时缓慢加入 1质量份失水山梨醇脂肪酸酯、2 质量份荆芥挥发油、3 质量份四羟甲基氯化磷、1质量份芦荟大黄苷，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干；
4）第一次抗菌处理 ：将服装面料脱水处理，然后浸入纳米抗菌液中，升温至 50℃， 浸泡2小时，然后再升温至80℃，浸泡6小时 ；
5）第二次抗菌处理 ：将抗菌整理液涂覆在服装面料的表面，然后在75℃的温度下 进行烘干成型，烘干时间为3分钟，接着在130℃的温度下进行烘焙交联，时间为8分钟 ；
6）还原清洗处理 ：将服装面料放入清洗溶液中进行清洗 ；
7）后处理：依次进行脱水、松式烘干、拉幅定形和检验。
进一步的，所述纳米抗菌液是由纳米氯化银分散液以及纳米银离子粘结剂制成。
进一步的，所述抗菌整理液由竹醋液、涂层剂和添加剂混合制成。
进一步的，所述步骤6）中的服装面料先通过拉幅烘干机烘干，再通过热定型机烘焙交联。
进一步的，所述步骤7）中的清洗溶液的 ph 值为 5-5.5，清洗温度为45℃，清洗时间为15分钟。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (5)

1.一种服装面料的生产工艺，其特征在于：包括如下步骤：
1）在 20 -50质量份去离子水中投入 1～5质量份丙烯酸、3质量份胍类抗菌剂、5质量份聚氧乙烯多胺、2质量份聚丙二醇混合，搅拌均匀；
2）再同时缓慢加入 1质量份失水山梨醇脂肪酸酯、2 质量份荆芥挥发油、3 质量份四羟甲基氯化磷、1质量份芦荟大黄苷，继续搅拌，至充分混合均匀，制得整理液；
3）将面料在整理液中浸轧处理，取出后恒温烘干；
4）第一次抗菌处理 ：将服装面料脱水处理，然后浸入纳米抗菌液中，升温至 40-60℃，浸泡 1-3小时，然后再升温至 60-90℃，浸泡5-8小时 ；
5）第二次抗菌处理 ：将抗菌整理液涂覆在服装面料的表面，然后在 60-90℃的温度下进行烘干成型，烘干时间为 2-5 分钟，接着在 100-160℃的温度下进行烘焙交联，时间为5-10分钟；
6）还原清洗处理 ：将服装面料放入清洗溶液中进行清洗 ；
7）后处理：依次进行脱水、松式烘干、拉幅定形和检验。
2.根据权利要求1所述的一种服装面料的生产工艺，其特征在于：所述纳米抗菌液是由纳米氯化银分散液以及纳米银离子粘结剂制成。
3.根据权利要求1所述的一种服装面料的生产工艺，其特征在于：所述抗菌整理液由竹醋液、涂层剂和添加剂混合制成。
4.根据权利要求1所述的一种服装面料的生产工艺，其特征在于：所述步骤6）中的服装面料先通过拉幅烘干机烘干，再通过热定型机烘焙交联。
5.根据权利要求1所述的一种服装面料的生产工艺，其特征在于：所述步骤7）中的清洗溶液的 ph 值为 5-5.5，清洗温度为 40-55℃，清洗时间为 10-20 分钟。
CN201811215953.4A 2018-10-18 2018-10-18 一种服装面料的生产工艺 Pending CN109537274A (zh)