CN109354481A - 一种制作卧坐品酒人物形象的陶瓷的方法 - Google Patents

一种制作卧坐品酒人物形象的陶瓷的方法 Download PDF

Info

Publication number
CN109354481A
CN109354481A CN201811083243.0A CN201811083243A CN109354481A CN 109354481 A CN109354481 A CN 109354481A CN 201811083243 A CN201811083243 A CN 201811083243A CN 109354481 A CN109354481 A CN 109354481A
Authority
CN
China
Prior art keywords
glaze
parts
image
tire
porcelain
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811083243.0A
Other languages
English (en)
Inventor
杨根成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811083243.0A priority Critical patent/CN109354481A/zh
Publication of CN109354481A publication Critical patent/CN109354481A/zh
Pending legal-status Critical Current

Abstract

本发明涉及人物形象钧瓷的制作方法，具体涉及一种制作卧坐品酒人物形象的陶瓷的制作方法，包括胎瓷和釉料，胎瓷的原料包括高岭土、粘土、石英砂等，第一釉料包括钾长石、钠长石、石英等，第二釉料包括钾长石、石英、瓷石和透辉石等，将胎瓷制成泥料后人工捏制形象，使用钢刷等工具修饰边缘，使用粘合剂粘合各个部分后对其修饰打磨，最终针对性的施以第一釉料和第二釉料，烧制成型，最终形成一种具有国画风格的人物形象钧瓷产品，高温烧制之后，第二釉料浆料会形成乳白色，人物形象像是披了一件厚实的外袍一般，使观赏者能感受到人物形象所在的环境，十分美观。

Description

一种制作卧坐品酒人物形象的陶瓷的方法
技术领域
本发明涉及人物形象钧瓷的制作方法，具体涉及一种制作卧坐品酒人物形象的陶瓷的方法。
背景技术
中国是瓷器的故乡，瓷器是中国的瑰宝，是中华民族的一个重要的创造，据考证，早在商代和西周就已经出现了具有瓷器基本特征的青釉器。目前我国具有钧瓷、汝瓷、青花瓷等多种瓷器，其中钧瓷发端于东汉，是宋代五大名窑瓷器之一，也是中国传统制瓷工艺中的珍品，钧瓷以其独特的窑变艺术而著称于世，有“入窑一色出窑千彩”的说法，钧瓷的釉色窑变艺术效果不是人为的，而是在窑内炉火的高温下自然形成的，钧瓷入窑是没有任何色彩，一体素净，钧瓷表面形成的绚丽色彩和自然画面都是在烧制过程中在窑内形成的，其原理就是釉料矿物在高温下呈色的物理化学现象，窑变现象是温度、釉料、烧制位置以及炉窑品质等多种因素的结合，窑变结果是自然形成的，在人们对窑变现象有了相当认识和了解的今天，窑变结果也并非完全掌握的，往往招之不来、不期而遇，这大大增添了钧瓷艺术震撼人心的魅力，所以每一件瓷器的形成都是可遇不可求的。钧瓷烧制釉色的不可控，是钧瓷的魅力所在，也是烧制工艺上难以控制的技术难题，钧瓷釉色的呈色与釉料的元素种类及含量、烧制气氛以及烧制温度都有很大关系，釉质配方不同，烧制结果也是千差万异，即使同种釉料，施釉方式不同也会烧制出不同的结果。
钧瓷品中也有不少例如人物形象、动物形象或者植物形象的珍品，有些形象的产品对釉色要求很高，产品整体一色光鲜亮丽且釉料均匀，就像油画一般，有些产品对釉料的施釉方式要求很高，具有自然美感，多种釉料的位置以及量需要施釉人自己把握，通过色彩釉和无色釉的合理分配，像国画山水一样，表现形式不局限与产品本身，观赏者脑海里会自然形成一幅画卷。
发明内容
本发明目的是为提供一种制作卧坐品酒人物形象的陶瓷的方法，包括胎瓷和釉料，胎瓷经过多步加工后制成泥料，人工捏制成各部分的形象，使用粘合剂粘合，合理施釉烧制，最终形成一种具有国画风格的人物形象钧瓷产品。
本发明为解决上述问题提供的是一种制作卧坐品酒人物形象的陶瓷的方法，包括胎瓷和釉料，按照重量比，胎瓷原料包括高岭土30-40份、粘土30-38份、石英砂8-10份、瓷石5-9份、紫木节2-7份、黄长石15-21份、铁矿石3-5份以及氧化铝4-7份；釉料包括第一釉料和第二釉料，第一釉料原料包括钾长石20-27份、钠长石22-28份、木灰2-5份、钛矿石5-9份、滑石2-3份、石英2-3份、氧化锌1-3份和硅灰石1-2份，第二釉料原料包括钾长石20-25份、石英5-7份、瓷石2-5份、木灰2-4份、方解石6-7份和透辉石2-5份。
进一步的，一种制作卧坐品酒人物形象的陶瓷的方法包括以下步骤：
步骤一、将胎瓷原料混合加水搅拌后放入球磨机中球磨，胎瓷原料：球=1：2，球磨24-30小时后烘干过100-200目网筛得到胎瓷粉料，向胎瓷粉料中加水搅拌成胎瓷泥料，搅拌过程中加入乙醇和工业油；
步骤二、将两部分釉料原料分别放入球磨机中加水进行湿磨，其中釉料原料：球：水=1:2:0.5，球磨30-36小时后取出烘干过100-300目网筛分别得到第一釉料粉料和第二釉料粉料，向其中分别加水搅拌均匀分别得到第一釉料浆料和第二釉料浆料；
步骤三、取部分胎瓷泥料分别人工捏制成一个矩形的底板和多个鹅的形象，再去部分胎瓷泥料人工捏制成卧坐的人物形象的身躯，再取胎瓷泥料人工捏制成人物头部形象和举杯的手的形象且用毛刷和钢刷分别进行修饰，使用粘接剂将人物头部形象和手部形象粘接在人物形象的身躯上，将人物形象和多个鹅的形象粘接在底板上并烘干最终制成钧瓷素胎；
步骤四、对钧瓷素胎表面进行打磨，对钧瓷素胎表面刷涂第二釉料浆料，待浆料风干后入窑在100℃-300℃温度下预烧制1-3小时；
步骤五、在人物形象身躯部分和鹅形象表面刷涂多层第一釉料浆料，风干后入窑烧制，冷却出窑后得卧坐品酒的人物形象的钧瓷品。
进一步的，所述步骤一中加入乙醇和工业油的量分别为胎瓷原料10%-15%以及6%-7%。
进一步的，所述步骤三中捏制的鹅形象的数量为两个。
进一步的，所述步骤四中第一釉料浆料刷涂在人物形象身躯部分的背面以及正面两侧。
有益效果
1、本发明的目的是制作一种卧坐品酒的人物形象的钧瓷作品，包括胎瓷和釉料，胎瓷经过球磨加水、乙醇和工业油等搅拌制成胎瓷泥料，然后人工捏制成卧坐举杯品酒的人物形象、动物以及底板等，人物形象的须眉、手部细节、衣服下摆纹理以及发饰等通过钢刷修饰，将人物形象部分和动物通过粘合剂粘合在底板上，覆涂一层不具有颜色添加效果的第二釉料浆料进行预烧制，冷却后在人物背部及正面两侧边和动物身上刷涂第一釉料浆料，高温烧制之后，第二釉料浆料会形成乳白色，人物形象像是披了一件厚实的外袍一般，使观赏者能感受到人物形象所在的环境，本发明示例的动物为两只鹅，乳白色的釉色刚好作为鹅的羽毛色彩，动物为其他种类时还需专门配置表现其色彩的第三中釉料。
2、本发明中由于胎瓷的原料要求没有釉料的原料要求高，故胎瓷原料的预处理精度要低于釉料原料的预处理精度，第二釉料主要起保护作用，对打磨过的钧瓷素胎表面施以第二釉料，钧瓷烧制后还会呈现原本的素色，但结构强度和稳定性都会有所提升；第一釉料起着色作用，且釉料浓度高，而且人物形象上刷涂的釉料较多，边缘处自然流落，高温烧制后在人物背面以及鹅身形成一层乳白色的釉色，人身上的釉色边缘位置会显现一种自然的美感，乳白色的釉色相对与其他部位的素色，像初春时身披一件厚实的白袍一般，具有美感。
附图说明
图1是本发明卧坐品酒的人物形象陶瓷的成品示意图。
具体实施方式
实施例1
一种制作卧坐品酒人物形象的陶瓷的方法，包括胎瓷和釉料，按照重量比，胎瓷原料包括高岭土30份、粘土30份、石英砂8份、瓷石5份、紫木节2份、黄长石15份、铁矿石3份以及氧化铝4份；釉料包括第一釉料和第二釉料，第一釉料原料包括钾长石20份、钠长石22份、木灰2份、钛矿石5份、滑石2份、石英2份、氧化锌1份和硅灰石1份，第二釉料原料包括钾长石20份、石英5份、瓷石2份、木灰2份、方解石6份和透辉石2份。
一种制作卧坐品酒人物形象的陶瓷的方法包括以下步骤：
步骤一、将胎瓷原料混合加水搅拌后放入球磨机中球磨，胎瓷原料：球=1：2，球磨24小时后烘干过100目网筛得到胎瓷粉料，向胎瓷粉料中加水搅拌成胎瓷泥料，搅拌过程中加入瓷胎原料重量10%乙醇和和瓷胎重量6%工业油；
步骤二、将两部分釉料原料分别放入球磨机中加水进行湿磨，其中釉料原料：球：水=1:2:0.5，球磨30小时后取出烘干过100目网筛分别得到第一釉料粉料和第二釉料粉料，向其中分别加水搅拌均匀分别得到第一釉料浆料和第二釉料浆料；
步骤三、取部分胎瓷泥料分别人工捏制成一个矩形的底板和两个鹅的形象，再去部分胎瓷泥料人工捏制成卧坐的人物形象的身躯，再取胎瓷泥料人工捏制成人物头部形象和举杯的手的形象且用毛刷和钢刷分别进行修饰，使用粘接剂将人物头部形象和手部形象粘接在人物形象的身躯上，将人物形象和多个鹅的形象粘接在底板上并烘干最终制成钧瓷素胎；
步骤四、对钧瓷素胎表面进行打磨，对钧瓷素胎表面的人物形象身躯部分的背面和正面两侧刷涂第二釉料浆料，待浆料风干后入窑在100℃温度下预烧制3小时；
步骤五、在人物形象身躯部分和鹅形象表面刷涂多层第一釉料浆料，风干后入窑烧制，冷却出窑后得卧坐品酒的人物形象的钧瓷品。
实施例2
一种制作卧坐品酒人物形象的陶瓷的方法，其特征在于：包括胎瓷和釉料，按照重量比，胎瓷原料包括高岭土40份、粘土38份、石英砂10份、瓷石9份、紫木节7份、黄长石21份、铁矿石5份以及氧化铝7份；釉料包括第一釉料和第二釉料，第一釉料原料包括钾长石27份、钠长石28份、木灰5份、钛矿石9份、滑石3份、石英3份、氧化锌3份和硅灰石2份，第二釉料原料包括钾长石25份、石英7份、瓷石5份、木灰4份、方解石7份和透辉石5份。
一种制作卧坐品酒人物形象的陶瓷的方法包括以下步骤：
步骤一、将胎瓷原料混合加水搅拌后放入球磨机中球磨，胎瓷原料：球=1：2，球磨30小时后烘干过200目网筛得到胎瓷粉料，向胎瓷粉料中加水搅拌成胎瓷泥料，搅拌过程中加入瓷胎原料重量15%的乙醇和瓷胎原料重量7%的工业油；
步骤二、将两部分釉料原料分别放入球磨机中加水进行湿磨，其中釉料原料：球：水=1:2:0.5，球磨36小时后取出烘干过300目网筛分别得到第一釉料粉料和第二釉料粉料，向其中分别加水搅拌均匀分别得到第一釉料浆料和第二釉料浆料；
步骤三、取部分胎瓷泥料分别人工捏制成一个矩形的底板和两个鹅的形象，再去部分胎瓷泥料人工捏制成卧坐的人物形象的身躯，再取胎瓷泥料人工捏制成人物头部形象和举杯的手的形象且用毛刷和钢刷分别进行修饰，使用粘接剂将人物头部形象和手部形象粘接在人物形象的身躯上，将人物形象和两个鹅的形象粘接在底板上并烘干最终制成钧瓷素胎；
步骤四、对钧瓷素胎表面进行打磨，对钧瓷素胎表面刷涂第二釉料浆料，待浆料风干后入窑在300℃温度下预烧制1小时；
步骤五、在人物形象身躯部分的背面和正面两侧边以及鹅形象表面刷涂多层第一釉料浆料，风干后入窑烧制，冷却出窑后得卧坐品酒的人物形象的钧瓷品。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (5)

1.一种制作卧坐品酒人物形象的陶瓷的方法，其特征在于：包括胎瓷和釉料，按照重量比，胎瓷原料包括高岭土30-40份、粘土30-38份、石英砂8-10份、瓷石5-9份、紫木节2-7份、黄长石15-21份、铁矿石3-5份以及氧化铝4-7份；釉料包括第一釉料和第二釉料，第一釉料原料包括钾长石20-27份、钠长石22-28份、木灰2-5份、钛矿石5-9份、滑石2-3份、石英2-3份、氧化锌1-3份和硅灰石1-2份，第二釉料原料包括钾长石20-25份、石英5-7份、瓷石2-5份、木灰2-4份、方解石6-7份和透辉石2-5份。
2.如权利要求1所述的一种制作卧坐品酒人物形象的陶瓷的方法，其特征在于：包括以下步骤：
步骤一、将胎瓷原料混合加水搅拌后放入球磨机中球磨，胎瓷原料：球=1：2，球磨24-30小时后烘干过100-200目网筛得到胎瓷粉料，向胎瓷粉料中加水搅拌成胎瓷泥料，搅拌过程中加入乙醇和工业油；
步骤二、将两部分釉料原料分别放入球磨机中加水进行湿磨，其中釉料原料：球：水=1:2:0.5，球磨30-36小时后取出烘干过100-300目网筛分别得到第一釉料粉料和第二釉料粉料，向其中分别加水搅拌均匀分别得到第一釉料浆料和第二釉料浆料；
步骤三、取部分胎瓷泥料分别人工捏制成一个矩形的底板和多个鹅的形象，再去部分胎瓷泥料人工捏制成卧坐的人物形象的身躯，再取胎瓷泥料人工捏制成人物头部形象和举杯的手的形象且用毛刷和钢刷分别进行修饰，使用粘接剂将人物头部形象和手部形象粘接在人物形象的身躯上，将人物形象和多个鹅的形象粘接在底板上并烘干最终制成钧瓷素胎；
步骤四、对钧瓷素胎表面进行打磨，对钧瓷素胎表面刷涂第二釉料浆料，待浆料风干后入窑在100℃-300℃温度下预烧制1-3小时；
步骤五、在人物形象身躯部分和鹅形象表面刷涂多层第一釉料浆料，风干后入窑烧制，冷却出窑后得卧坐品酒的人物形象的钧瓷品。
3.如权利要求2所述的一种制作卧坐品酒人物形象的陶瓷的方法，其特征在于：所述步骤一中加入乙醇和工业油的量分别为胎瓷原料10%-15%以及6%-7%。
4.如权利要求2所述的一种制作卧坐品酒人物形象的陶瓷的方法，其特征在于：所述步骤三中捏制的鹅形象的数量为两个。
5.如权利要求2所述的一种制作卧坐品酒人物形象的陶瓷的方法，其特征在于：所述步骤四中第一釉料浆料刷涂在人物形象身躯部分的背面以及正面两侧。
CN201811083243.0A 2018-09-17 2018-09-17 一种制作卧坐品酒人物形象的陶瓷的方法 Pending CN109354481A (zh)