CN104496555B - 仿金属陶瓷艺术釉及其制备和使用方法 - Google Patents

仿金属陶瓷艺术釉及其制备和使用方法 Download PDF

Info

Publication number
CN104496555B
CN104496555B CN201410723931.4A CN201410723931A CN104496555B CN 104496555 B CN104496555 B CN 104496555B CN 201410723931 A CN201410723931 A CN 201410723931A CN 104496555 B CN104496555 B CN 104496555B
Authority
CN
China
Prior art keywords
parts
glaze
frit
ceramic metal
imitative
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410723931.4A
Other languages
English (en)
Other versions
CN104496555A (zh
Inventor
叶紫琳
徐建中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HOU XIAODONG
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410723931.4A priority Critical patent/CN104496555B/zh
Publication of CN104496555A publication Critical patent/CN104496555A/zh
Application granted granted Critical
Publication of CN104496555B publication Critical patent/CN104496555B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种仿金属陶瓷艺术釉，由以下重量分数的各组分组成：熔块45～52份，硅灰石15～17份，托帕石4～6份，云母6～7份，氧化铜3.5～4份，滑石6～7份，二氧化钛1～2份，二氧化锰3～4份，氧化镍5～7份，氧化铝8～10份，其中，所述熔块由以下重量分数的各组分组成：石英47～49份，高岭土8～13份，碳酸钙7～9份，碳酸钠1～4份，铅丹22～24份，焦宝石2～3份，摩根石1～2份。本发明还涉及所述仿金属陶瓷艺术釉的制备和使用方法，用其制备出来的仿金属艺术陶瓷产品，其釉面呈金黄色，金属光泽强烈，呈镜面反射，可媲美金属制品。

Description

仿金属陶瓷艺术釉及其制备和使用方法
技术领域
本发明涉及陶瓷釉料领域，更具体地，涉及一种仿金属陶瓷艺术釉及其制备和使用方法。
背景技术
金属釉是陶瓷产业釉料中的一种特殊艺术釉，主要施于仿古砖瓷砖上，也有施于日用陈设瓷的瓶罐上，花瓶或艺术瓷上。施加金属釉的瓷砖表面呈现出金属质感的光泽，并能呈现出各种颜色，红、黄、银、蓝、黑等。目前金属艺术釉的技艺尚不成熟。
发明内容
本发明的目的是针对上述的问题，提供一种仿金属陶瓷艺术釉及其制备和使用方法。
本发明目的通过以下技术方案予以实现：
提供一种仿金属陶瓷艺术釉，由以下重量分数的各组分组成：熔块45～52份，硅灰石15～17份，托帕石4～6份，云母6～7份，氧化铜3.5～4份，滑石6～7份，二氧化钛1～2份，二氧化锰3～4份，氧化镍5～7份，氧化铝8～10份，其中，所述熔块由以下重量分数的各组分组成：石英47～49份，高岭土8～13份，碳酸钙7～9份，碳酸钠1～4份，铅丹22～24份，焦宝石2～3份，摩根石1～2份。
优选地，所述仿金属陶瓷艺术釉由以下重量分数的各组分组成：熔块48份，硅灰石16份，托帕石5份，云母6份，氧化铜3.5份，滑石6份，二氧化钛2份，二氧化锰4份，氧化镍6份，氧化铝9份，其中，所述熔块由以下重量分数的各组分组成：石英48份，高岭土10份，碳酸钙8份，碳酸钠3份，铅丹23份，焦宝石2份，摩根石1份。
本发明还提供了所述仿金属陶瓷艺术釉的制备方法，包括以下步骤：
S1．按熔块配方称取，混合均匀装入坩埚，在硅碳棒电炉中熔融2h，倒入冷水中淬冷成细小颗粒，烘干破碎，球磨过300目筛，得到熔块备用；
S2．按黄金釉配方称取，以料：球：水=1：2：0.5～0.7入球磨研磨2h，出磨后250目筛筛余0.1%，得到仿金属陶瓷艺术釉。
本发明还提供了所述仿金属陶瓷艺术釉的使用方法：在坯件上淋釉，施釉厚度0.3～0.4mm，入隧道窑氧化焰烧成，烧成温度1190～1200℃，烧成周期2h，温度降至950～1050℃，保温30min后自然冷却，得到仿金属艺术陶瓷。
实验表明，各种原材料的配比及烧成工艺等对釉面效果影响极大。
与现有技术相比，本发明具有以下有益效果：
本发明提供了一种仿金属陶瓷艺术釉，用其制备出来的仿金属艺术陶瓷产品，其釉面呈金黄色，金属光泽强烈，呈镜面反射，外观可媲美金属制品。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1
本实施例公开了一种仿金属陶瓷艺术釉，由以下重量分数的各组分组成：熔块48份，硅灰石16份，托帕石5份，云母6份，氧化铜3.5份，滑石6份，二氧化钛2份，二氧化锰4份，氧化镍6份，氧化铝9份，其中，所述熔块由以下重量分数的各组分组成：石英48份，高岭土10份，碳酸钙8份，碳酸钠3份，铅丹23份，焦宝石2份，摩根石1份。
实施例2
本实施例公开了一种仿金属陶瓷艺术釉，由以下重量分数的各组分组成：熔块45份，硅灰石15份，托帕石4份，云母7份，氧化铜4份，滑石7份，二氧化钛1份，二氧化锰3份，氧化镍5份，氧化铝8份，其中，所述熔块由以下重量分数的各组分组成：石英47份，高岭土8份，碳酸钙7份，碳酸钠4份，铅丹22份，焦宝石3份，摩根石2份。
实施例3
本实施例公开了一种仿金属陶瓷艺术釉，由以下重量分数的各组分组成：熔块52份，硅灰石17份，托帕石6份，云母6份，氧化铜3.8份，滑石6份，二氧化钛2份，二氧化锰4份，氧化镍7份，氧化铝10份，其中，所述熔块由以下重量分数的各组分组成：石英49份，高岭土13份，碳酸钙9份，碳酸钠1份，铅丹24份，焦宝石2份，摩根石1份。
实施例4
本实施例公开了一种仿金属陶瓷艺术釉，由以下重量分数的各组分组成：熔块50份，硅灰石16.5份，托帕石5份，云母6.2份，氧化铜4份，滑石6.5份，二氧化钛1.5份，二氧化锰3.5份，氧化镍5.9份，氧化铝8份，其中，所述熔块由以下重量分数的各组分组成：石英48.5份，高岭土11份，碳酸钙7.5份，碳酸钠2份，铅丹23份，焦宝石2.5份，摩根石1.5份。
实施例5
取实施例1～4任意实施例的重量组分制备仿金属陶瓷艺术釉，制备步骤如下：
S1．按熔块配方称取，混合均匀装入坩埚，在硅碳棒电炉中熔融2h，倒入冷水中淬冷成细小颗粒，烘干破碎，球磨过300目筛，得到熔块备用；
S2．按黄金釉配方称取，以料：球：水=1：2：0.5入球磨研磨2h，出磨后250目筛筛余0.1%，得到仿金属陶瓷艺术釉。
实施例6
取实施例1～4任意实施例的重量组分制备仿金属陶瓷艺术釉，制备步骤如下：
S1．按熔块配方称取，混合均匀装入坩埚，在硅碳棒电炉中熔融2h，倒入冷水中淬冷成细小颗粒，烘干破碎，球磨过300目筛，得到熔块备用；
S2．按黄金釉配方称取，以料：球：水=1：2：0.7入球磨研磨2h，出磨后250目筛筛余0.1%，得到仿金属陶瓷艺术釉。
实施例7
取实施例1～4任意实施例的重量组分制备仿金属陶瓷艺术釉，制备步骤如下：
S1．按熔块配方称取，混合均匀装入坩埚，在硅碳棒电炉中熔融2h，倒入冷水中淬冷成细小颗粒，烘干破碎，球磨过300目筛，得到熔块备用；
S2．按黄金釉配方称取，以料：球：水=1：2：0.6入球磨研磨2h，出磨后250目筛筛余0.1%，得到仿金属陶瓷艺术釉。
实施例8
实施例5～7任意实施例制备的仿金属陶瓷艺术釉，使用方法如下：
在坯件上淋釉，施釉厚度0.3～0.4mm，入隧道窑氧化焰烧成，烧成温度1190～1200℃，烧成周期2h，温度降至950～1050℃，保温30min后自然冷却，得到仿金属艺术陶瓷，其釉面呈金黄色，金属光泽强烈，呈镜面反射，可媲美高档金属制品。

Claims (4)

1.一种仿金属陶瓷艺术釉，其特征在于，由以下重量份数的各组分制成：熔块45～52份，硅灰石15～17份，托帕石4～6份，云母6～7份，氧化铜3.5～4份，滑石6～7份，二氧化钛1～2份，二氧化锰3～4份，氧化镍5～7份，氧化铝8～10份，其中，所述熔块由以下重量份数的各组分制成：石英47～49份，高岭土8～13份，碳酸钙7～9份，碳酸钠1～4份，铅丹22～24份，焦宝石2～3份，摩根石1～2份。
2. 根据权利要求1所述的仿金属陶瓷艺术釉，其特征在于，由以下重量份数的各组分制成：熔块48份，硅灰石16份，托帕石5份，云母6份，氧化铜3.5份，滑石6份，二氧化钛2份，二氧化锰4份，氧化镍6份，氧化铝9份，其中，所述熔块由以下重量份数的各组分制成：石英48份，高岭土10份，碳酸钙8份，碳酸钠3份，铅丹23份，焦宝石2份，摩根石1份。
3.根据权利要求1或2所述仿金属陶瓷艺术釉的制备方法，其特征在于，包括以下步骤：
S1．按熔块配方称取，混合均匀装入坩埚，在硅碳棒电炉中熔融2h，倒入冷水中淬冷成细小颗粒，烘干破碎，球磨过300目筛，得到熔块备用；
S2．按仿金属陶瓷艺术釉配方称取，以料：球：水=1：2：0.5～0.7的比例球磨2h，出磨后250目筛筛余0.1%，得到仿金属陶瓷艺术釉。
4.根据权利要求1或2所述仿金属陶瓷艺术釉的使用方法，其特征在于，在坯件上淋釉，施釉厚度0.3～0.4mm，入隧道窑氧化焰烧成，烧成温度1190～1200℃，烧成周期2h，温度降至950～1050℃，保温30min后自然冷却，得到仿金属艺术陶瓷。
CN201410723931.4A 2014-12-04 2014-12-04 仿金属陶瓷艺术釉及其制备和使用方法 Expired - Fee Related CN104496555B (zh)