CN109336464A - 一种钙钛矿锰氧化物的制备方法 - Google Patents
一种钙钛矿锰氧化物的制备方法 Download PDFInfo
- Publication number
- CN109336464A CN109336464A CN201811115381.2A CN201811115381A CN109336464A CN 109336464 A CN109336464 A CN 109336464A CN 201811115381 A CN201811115381 A CN 201811115381A CN 109336464 A CN109336464 A CN 109336464A
- Authority
- CN
- China
- Prior art keywords
- titanium ore
- preparation
- calcium titanium
- oxide
- ore manganose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种钙钛矿锰氧化物的制备方法,包括:以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在780‑870℃煅烧2‑4h,研磨后在900‑1000℃煅烧3‑5h,研磨后在1150‑1250℃煅烧7‑10h,研磨后得前驱粉;将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混匀,加入环氧树脂搅匀,烘干、压制成型、固化。本发明提出的钙钛矿锰氧化物的制备方法,其过程简单,条件温和,避免了两相间的界面扩散,得到的钙钛矿锰氧化物力学性能好,低场磁电阻高。
Description
技术领域
本发明涉及钙钛矿锰氧化物技术领域,尤其涉及一种钙钛矿锰氧化物的制备方法。
背景技术
信息技术的飞速发展及器件的小型化对存储设备提出了更高的要求,促使材料物理工作者不断地发掘和探索新型的功能材料,以适应高密度信息存储和快速读写的需要。因为庞磁电阻(CMR)效应在磁传感、磁记录、随机存储器等方面有着诱人的应用前景,近年来,激发了人们对钙钛矿结构氧化物的研究热情。
具有庞磁电阻效应(CMR)的稀土掺杂钙钛矿锰氧化物属于强关联电子体系,表现出许多复杂的物理效应,在电荷-自旋-轨道-晶格之间存在各种相互作用,从而诱发绝缘体-金属相变、有序化和相分离等一系列奇异效应,是近年来凝聚态物理和材料物理领域的一个热点课题。
现有的稀土掺杂钙钛矿锰氧化物通常是采用高温烧结方法制备的,传统的烧结方法使得两相之间的界面扩散反应是难以避免的,即烧结工艺不可能制备绝对没有扩散的复合相样品,因此寻找与传统烧结方法不同的新方法是目前急需解决的问题。
发明内容
基于背景技术存在的技术问题,本发明提出了一种钙钛矿锰氧化物的制备方法,其过程简单,条件温和,避免了两相间的界面扩散,得到的钙钛矿锰氧化物力学性能好,低场磁电阻高。
本发明提出的一种钙钛矿锰氧化物的制备方法,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在780-870℃煅烧2-4h,研磨后在900-1000℃下煅烧3-5h,研磨后在1150-1250℃下煅烧7-10h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物。
优选地,在S2中,环氧树脂固化剂的重量为前驱粉重量的0.8-1.7wt%。
优选地,在S2中,所述环氧树脂固化剂按照以下工艺进行制备:将对苯二酚、碳酸钾、二甲基甲酰胺和甲苯混合均匀,在氮气的保护下升温至65-80℃,搅拌5-10h,加入4,4′-二氟二苯甲酮,搅拌反应5-8h,反应结束后蒸发、洗涤、干燥得到物料A;将聚甲基三乙氧基硅烷、二丁基二异辛酸锡与水混合,搅拌升温至75-85℃,加入硅烷偶联剂KH-560,在75-85℃下搅拌反应2-3h,然后在90-95℃下搅拌3-5h,加入线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A和2-乙基-4-甲基咪唑,在125-135℃下搅拌反应2-3h,反应结束后干燥得到所述环氧树脂固化剂。
优选地,在环氧树脂固化剂的制备过程中,对苯二酚、4,4′-二氟二苯甲酮的重量比为15-30:13-21。
优选地,在环氧树脂固化剂的制备过程中,聚甲基三乙氧基硅烷、硅烷偶联剂KH-560、线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A的重量比为30-45:20-40:10-21:3-9:4-12。
优选地,在S2中,所述绝缘体氧化物为Sb2O3、Fe2O3、Bi2O3、CuO中的一种。
优选地,在S2中,绝缘体氧化物的重量为前驱粉重量的2-5wt%。
优选地,在S2中,所述环氧树脂的重量为前驱粉重量的3-8wt%;所述环氧树脂为双酚A型环氧树脂。
优选地,在S2中,烘干的温度为75-110℃。
优选地,在S2中,压制成型的压力为400-550MPa;固化的温度为25-30℃。
本发明钙钛矿锰氧化物的制备方法中,以La2O3、SrCO3、Dy2O3和MnO2为原料,并控制反应的条件,得到了La0.6Dy0.1Sr0.3MnO3母体,其Tc为308K,CMR较大,在6T磁场下,MR为74%,之后选择特定的环氧树脂和固化剂作为粘结剂,使其与绝缘体氧化物复合,并控制了复合的条件,避免了反应过程中两相之间的扩散,与传统的烧结方法相比,得到的钙钛矿氧化物具有更好的力学性能和可加工性,且室温低场磁电阻高,其在室温附近在0.3T外场下得到磁电阻MR>20%;优选方式环氧树脂固化剂的制备过程中,首先将对苯二酚、碳酸钾、二甲基甲酰胺和甲苯混合均匀,在氮气的保护与4,4′-二氟二苯甲酮进行反应,通过控制反应的条件,使对苯二酚中的羟基与4,4′-二氟二苯甲酮中的氟发生了反应,得到了含羟基的物料A;以聚甲基三乙氧基硅烷与硅烷偶联剂KH-560为原料,通过控制反应的条件,使聚甲基三乙氧基硅烷与硅烷偶联剂KH-560发生了水解缩合反应,得到了含环氧基的物质,加入线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A后,控制反应的条件,使得到的含环氧基的物质中的环氧基与线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A中的羟基发生了缩合反应,得到了环氧树脂固化剂,将其加入体系中,因引入了多羟基的聚硅氧烷,一方面,其中的Si-O-Si键柔韧性强于C-C键,起到了增韧作用,提高了材料的冲击韧性,使所得钙钛矿锰氧化物抗冲击、不易碎,另一方面,其中的Si-O键键能强于C-C键,提高了材料的交联强度,同时在体系中引入了联苯结构,使材料在后续的烘干、固化过程中更加稳定,同时所述环氧树脂固化剂加入体系中,对前驱粉和绝缘体氧化物具有包裹作用,使本发明在不使用偶联剂的情况下得到了高粘结强度的材料,使得到的钙钛矿锰氧化物具有高的力学性能。
具体实施方式
下面,通过具体实施例对本发明的技术方案进行详细说明。
实施例1
本发明提出的一种钙钛矿锰氧化物的制备方法,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在780℃煅烧4h,研磨后在900℃下煅烧5h,研磨后在1150℃下煅烧10h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物。
实施例2
本发明提出的一种钙钛矿锰氧化物的制备方法,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在870℃煅烧2h,研磨后在1000℃下煅烧3h,研磨后在1250℃下煅烧7h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物。
实施例3
本发明提出的一种钙钛矿锰氧化物的制备方法,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在850℃煅烧3h,研磨后在980℃下煅烧3.5h,研磨后在1230℃下煅烧8h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物;
其中,在S2中,环氧树脂固化剂的重量为前驱粉重量的1.7wt%;
在S2中,所述环氧树脂固化剂按照以下工艺进行制备:将对苯二酚、碳酸钾、二甲基甲酰胺和甲苯混合均匀,在氮气的保护下升温至65℃,搅拌10h,加入4,4′-二氟二苯甲酮,搅拌反应5h,反应结束后蒸发、洗涤、干燥得到物料A;将聚甲基三乙氧基硅烷、二丁基二异辛酸锡与水混合,搅拌升温至85℃,加入硅烷偶联剂KH-560,在75℃下搅拌反应3h,然后在90℃下搅拌5h,加入线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A和2-乙基-4-甲基咪唑,在125℃下搅拌反应3h,反应结束后干燥得到所述环氧树脂固化剂;
在环氧树脂固化剂的制备过程中,对苯二酚、4,4′-二氟二苯甲酮的重量比为15:21;
在环氧树脂固化剂的制备过程中,聚甲基三乙氧基硅烷、硅烷偶联剂KH-560、线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A的重量比为30:40:10:9:4;
在S2中,所述绝缘体氧化物为Sb2O3;
在S2中,绝缘体氧化物的重量为前驱粉重量的5wt%;
在S2中,所述环氧树脂的重量为前驱粉重量的3wt%;所述环氧树脂为双酚A型环氧树脂;
在S2中,烘干的温度为110℃;
在S2中,压制成型的压力为400MPa;固化的温度为30℃。
实施例4
本发明提出的一种钙钛矿锰氧化物的制备方法,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在790℃煅烧3.5h,研磨后在950℃下煅烧4.3h,研磨后在1180℃下煅烧9.3h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物;
其中,在S2中,环氧树脂固化剂的重量为前驱粉重量的0.8wt%;
在S2中,所述环氧树脂固化剂按照以下工艺进行制备:将对苯二酚、碳酸钾、二甲基甲酰胺和甲苯混合均匀,在氮气的保护下升温至80℃,搅拌5h,加入4,4′-二氟二苯甲酮,搅拌反应8h,反应结束后蒸发、洗涤、干燥得到物料A;将聚甲基三乙氧基硅烷、二丁基二异辛酸锡与水混合,搅拌升温至75℃,加入硅烷偶联剂KH-560,在85℃下搅拌反应2h,然后在95℃下搅拌3h,加入线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A和2-乙基-4-甲基咪唑,在135℃下搅拌反应2h,反应结束后干燥得到所述环氧树脂固化剂;
在环氧树脂固化剂的制备过程中,对苯二酚、4,4′-二氟二苯甲酮的重量比为30:13;
在环氧树脂固化剂的制备过程中,聚甲基三乙氧基硅烷、硅烷偶联剂KH-560、线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A的重量比为45:20:21:3:12;
在S2中,所述绝缘体氧化物为Fe2O3;
在S2中,绝缘体氧化物的重量为前驱粉重量的2wt%;
在S2中,所述环氧树脂的重量为前驱粉重量的8wt%;所述环氧树脂为双酚A型环氧树脂;
在S2中,烘干的温度为75℃;
在S2中,压制成型的压力为550MPa;固化的温度为25℃。
实施例5
本发明提出的一种钙钛矿锰氧化物的制备方法,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在850℃煅烧3h,研磨后在950℃下煅烧4h,研磨后在1200℃下煅烧8h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物;
其中,在S2中,环氧树脂固化剂的重量为前驱粉重量的1.3wt%;
在S2中,所述环氧树脂固化剂按照以下工艺进行制备:将对苯二酚、碳酸钾、二甲基甲酰胺和甲苯混合均匀,在氮气的保护下升温至72℃,搅拌7.5h,加入4,4′-二氟二苯甲酮,搅拌反应6.5h,反应结束后蒸发、洗涤、干燥得到物料A;将聚甲基三乙氧基硅烷、二丁基二异辛酸锡与水混合,搅拌升温至80℃,加入硅烷偶联剂KH-560,在78℃下搅拌反应2.5h,然后在93℃下搅拌4h,加入线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A和2-乙基-4-甲基咪唑,在130℃下搅拌反应2.5h,反应结束后干燥得到所述环氧树脂固化剂;
在环氧树脂固化剂的制备过程中,对苯二酚、4,4′-二氟二苯甲酮的重量比为19:17;
在环氧树脂固化剂的制备过程中,聚甲基三乙氧基硅烷、硅烷偶联剂KH-560、线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A的重量比为38:30:17:6:8;
在S2中,所述绝缘体氧化物为CuO;
在S2中,绝缘体氧化物的重量为前驱粉重量的3wt%;
在S2中,所述环氧树脂的重量为前驱粉重量的5wt%;所述环氧树脂为双酚A型环氧树脂;
在S2中,烘干的温度为85℃;
在S2中,压制成型的压力为480MPa;固化的温度为27℃。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种钙钛矿锰氧化物的制备方法,其特征在于,包括以下步骤:
S1、以La2O3、SrCO3、Dy2O3和MnO2为原料,将La2O3、SrCO3、Dy2O3和MnO2按分子式La0.6Dy0.1Sr0.3MnO3的化学计量比进行配备原料;将配备的原料研磨后在780-870℃煅烧2-4h,研磨后在900-1000℃下煅烧3-5h,研磨后在1150-1250℃下煅烧7-10h,研磨后得到前驱粉;
S2、将前驱粉和环氧树脂固化剂加入丙酮中,加入绝缘体氧化物混合均匀,然后加入环氧树脂搅拌均匀,烘干后压制成型,固化后得到所述钙钛矿锰氧化物。
2.根据权利要求1所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,环氧树脂固化剂的重量为前驱粉重量的0.8-1.7wt%。
3.根据权利要求1或2所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,所述环氧树脂固化剂按照以下工艺进行制备:将对苯二酚、碳酸钾、二甲基甲酰胺和甲苯混合均匀,在氮气的保护下升温至65-80℃,搅拌5-10h,加入4,4′-二氟二苯甲酮,搅拌反应5-8h,反应结束后蒸发、洗涤、干燥得到物料A;将聚甲基三乙氧基硅烷、二丁基二异辛酸锡与水混合,搅拌升温至75-85℃,加入硅烷偶联剂KH-560,在75-85℃下搅拌反应2-3h,然后在90-95℃下搅拌3-5h,加入线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A和2-乙基-4-甲基咪唑,在125-135℃下搅拌反应2-3h,反应结束后干燥得到所述环氧树脂固化剂。
4.根据权利要求3所述钙钛矿锰氧化物的制备方法,其特征在于,在环氧树脂固化剂的制备过程中,对苯二酚、4,4′-二氟二苯甲酮的重量比为15-30:13-21。
5.根据权利要求3或4所述钙钛矿锰氧化物的制备方法,其特征在于,在环氧树脂固化剂的制备过程中,聚甲基三乙氧基硅烷、硅烷偶联剂KH-560、线性酚醛树脂、3,3’,5,5’-四甲基-4,4’-联苯二酚、物料A的重量比为30-45:20-40:10-21:3-9:4-12。
6.根据权利要求1-5中任一项所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,所述绝缘体氧化物为Sb2O3、Fe2O3、Bi2O3、CuO中的一种。
7.根据权利要求1-6中任一项所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,绝缘体氧化物的重量为前驱粉重量的2-5wt%。
8.根据权利要求1-7中任一项所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,所述环氧树脂的重量为前驱粉重量的3-8wt%;所述环氧树脂为双酚A型环氧树脂。
9.根据权利要求1-8中任一项所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,烘干的温度为75-110℃。
10.根据权利要求1-9中任一项所述钙钛矿锰氧化物的制备方法,其特征在于,在S2中,压制成型的压力为400-550MPa;固化的温度为25-30℃。