CN108978255A - A kind of fine works with the antibacterial flame-retardant function not material manufacturing technique of falling flannelette - Google Patents

A kind of fine works with the antibacterial flame-retardant function not material manufacturing technique of falling flannelette Download PDF

Info

Publication number
CN108978255A
CN108978255A CN201811150476.8A CN201811150476A CN108978255A CN 108978255 A CN108978255 A CN 108978255A CN 201811150476 A CN201811150476 A CN 201811150476A CN 108978255 A CN108978255 A CN 108978255A
Authority
CN
China
Prior art keywords
yarn
fiber
fabric
fine works
flannelette
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811150476.8A
Other languages
Chinese (zh)
Inventor
陶聪
陶菊明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiaxing Huachuo Textile Co Ltd
Original Assignee
Jiaxing Huachuo Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiaxing Huachuo Textile Co Ltd filed Critical Jiaxing Huachuo Textile Co Ltd
Priority to CN201811150476.8A priority Critical patent/CN108978255A/en
Publication of CN108978255A publication Critical patent/CN108978255A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of fine works with antibacterial flame-retardant function not material manufacturing techniques of falling flannelette, wherein the weight ratio of cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber is 65:10:12:13, fine works do not fall velvet fabric production method the following steps are included: carried out shaping based on step (1), step (2) and step (3) to fabric by tricot machine, the fabric after sizing is dyed, open-width, plucking, hot light, cropping and clot is dehydrated and processes；Fabric surface layer is subjected to gluing, and bonds nylon velvet on glue-line.The present invention passes through using cotton fiber as A yarn, polyester fiber is as B yarn, for bamboo charcoal fiber as C yarn, as D yarn, as raw material, fabric is made using warp knit mode in aramid fiber, then again in the surface layer of fabric coating epoxy resin as viscose, it bonds one layer of nylon fiber and is used as not suede, keep whole fabric surface layer smooth, and have the effect of antibacterial flame-retardant, fabric dimensional structure is stablized simultaneously, convenient for permanent use.

Description

A kind of fine works with the antibacterial flame-retardant function not material manufacturing technique of falling flannelette
Technical field
The present invention relates to a kind of fabric production technology, in particular to a kind of fine works with antibacterial flame-retardant function not fall flannelette Material manufacturing technique.
Background technique
It is divided into knitting, braiding and non-woven in fabric production process, wherein knitting is divided into warp knit and weft knitting again, warp knit is to belong to A kind of textile technology in knitting field, with one group or several groups of yarns arranged in parallel, in through all working to feeding machine On needle, at the same lopping and form knitted fabric, this method is known as warp knit, and the knitted fabric of formation is known as knitted fabric, and knitting is shape At a kind of method of fabric, it is formed by fabric and is known as knitted fabric, knitted fabric is as made of the mutual snare of coil, according to yarn Knitted fabric can be divided into knitted fabric and weft-knitted fabric by the lopping direction of line in the fabric, and warp knit and weft-knitted title come from machine It knits, in knitted fabric, same one thread is along fabric through forming coil one by one to (longitudinal direction), and general fabric is using knitting Function only as reinforcing the effect of comfort level afterwards, however fabric dimensional structure itself is not sufficiently stable, and does not have the function of antibacterial flame-retardant Can, it is not easy to being used for a long time for fabric.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the defect of the prior art, provide a kind of with antibacterial flame-retardant function The fine works not material manufacturing technique of falling flannelette, by the way that using cotton fiber as A yarn, polyester fiber is as B yarn, and bamboo charcoal fiber is as C yarn, virtue Synthetic fibre fiber, as raw material, carries out that fabric is made using warp knit mode as D yarn, then coats epoxy resin on the surface layer of fabric again As viscose, bonds upper one layer of nylon fiber and be used as not suede, keep whole fabric surface layer smooth, and the effect with antibacterial flame-retardant Fruit, while fabric dimensional structure is stablized, convenient for permanent use.
In order to solve the above-mentioned technical problems, the present invention provides the following technical solutions:
A kind of fine works with antibacterial flame-retardant function of the present invention not material manufacturing technique of falling flannelette, the fine works not velvet fabric It include cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber, wherein cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber are fine The weight ratio of dimension be 65:10:12:13, the fine works fall velvet fabric production method the following steps are included:
(1) is first using cotton fiber as A yarn, and polyester fiber is as B yarn, and bamboo charcoal fiber is as C yarn, and aramid fiber is as D Yarn, by the yarn arrays mode of cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber according to 1A1C1A1B1A1D1C1A1C1A1B1C1B1C1B1C1D1C1D1C, 20 stringer one cycles through tricot machine and is arranged；
(2) is by the band yarn digital manner of A yarn and B yarn according to GB4:0-0-0-0/3-3-3-3//arrange；By C yarn Band yarn digital manner according to GB5:1-0-0-0/0-1-1-1//arranged；By the band yarn digital manner of D yarn according to GB12: 1-0-1-l/1-2-2-2/2-3-3-3/3-4-4-4/4--5-5-5/5-6-6-6/6-7-7-7/7-8-8-8/8-9-9-9/9- 10-10-10/10-11-11-11/11-12-12-12/12-13-13-13/13-14-14-14/14-15-15-15/15-16- l6-16/16-17-17-17/17-18-18-18/17-16-16-16/17-18-18-18/17-l6-16-16/16-15-15- 15/15-l4-14-14/14-13-13-13/13-12-12-12/12-ll-l1-11/11-10-10-10//10-9-9--9/9- 8-8-8/8-7-7-7/7-6-6-6/6-5-5-5/5-4-4-4/4-3-3-3/3-2-2-2/2-1-1-l/1-0-1-1/l-2-2- 2//arranged；
(3) its warp run-in of are as follows:
GB4:1200；
GB5:2000；
GB12:1700；Indulging close is 7 rows/cm, and warp run-in unit is mm/rack；
(4) carries out shaping fabric based on step (1), step (2) and step (3) by tricot machine, after sizing Fabric dyed, be dehydrated open-width, plucking, hot light, cropping and clot and processed；
(5) the fabric surface layer after last clot processing is carried out gluing by, and one layer of nylon velvet is bonded on glue-line.
As a preferred technical solution of the present invention, tricot machine model of the step (1) into step (4) is SRM510 tricot machine.
As a preferred technical solution of the present invention, first cloth is warming up in the dyeing course in the step (4) 60 DEG C, dyestuff, auxiliary agent is added, keeps the temperature 30 minutes after being warming up to 130 DEG C, then cool down to 60 DEG C, cloth is put into water It washes cloth in wash pool.
As a preferred technical solution of the present invention, during the plucking in the step (4) regulation speed 25 meters/ Point, temperature is 160 DEG C during the hot light in the step (4), and it is identical as during plucking to control vehicle.
Compared with prior art, beneficial effects of the present invention are as follows:
The present invention is by the way that using cotton fiber as A yarn, polyester fiber is made as B yarn, bamboo charcoal fiber as C yarn, aramid fiber It is D yarn as raw material, carries out that fabric is made using warp knit mode, then again in the surface layer of fabric coating epoxy resin as glutinous Glue bonds upper one layer of nylon fiber and is used as not suede, keeps whole fabric surface layer smooth, and have the effect of antibacterial flame-retardant, simultaneously Fabric dimensional structure is stablized, convenient for permanent use.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
The present invention provides a kind of fine works with the antibacterial flame-retardant function not material manufacturing technique of falling flannelette, and fine works does not fall velvet fabric It include cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber, wherein cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber are fine The weight ratio of dimension be 65:10:12:13, fine works fall velvet fabric production method the following steps are included:
(1) is first using cotton fiber as A yarn, and polyester fiber is as B yarn, and bamboo charcoal fiber is as C yarn, and aramid fiber is as D Yarn, for bamboo charcoal fiber as C yarn, aramid fiber makes its fabric have good antibacterial and flame retardant effect as D yarn, by cotton fiber, The yarn arrays mode of polyester fiber, bamboo charcoal fiber and aramid fiber according to 1A1C1A1B1A1D1C1A1C1A1B1C1B1C1B1C1D1C1D1C, 20 stringer one cycles through tricot machine and is arranged；
(2) is by the band yarn digital manner of A yarn and B yarn according to GB4:0-0-0-0/3-3-3-3//arrange；By C yarn Band yarn digital manner according to GB5:1-0-0-0/0-1-1-1//arranged；By the band yarn digital manner of D yarn according to GB12: 1-0-1-l/1-2-2-2/2-3-3-3/3-4-4-4/4--5-5-5/5-6-6-6/6-7-7-7/7-8-8-8/8-9-9-9/9- 10-10-10/10-11-11-11/11-12-12-12/12-13-13-13/13-14-14-14/14-15-15-15/15-16- l6-16/16-17-17-17/17-18-18-18/17-16-16-16/17-18-18-18/17-l6-16-16/16-15-15- 15/15-l4-14-14/14-13-13-13/13-12-12-12/12-ll-l1-11/11-10-10-10//10-9-9--9/9- 8-8-8/8-7-7-7/7-6-6-6/6-5-5-5/5-4-4-4/4-3-3-3/3-2-2-2/2-1-1-l/1-0-1-1/l-2-2- 2//arranged；
(3) its warp run-in of are as follows:
GB4:1200；
GB5:2000；
GB12:1700；Indulging close is 7 rows/cm, and warp run-in unit is mm/rack；
(4) carries out shaping fabric based on step (1), step (2) and step (3) by tricot machine, A yarn, B yarn, C yarn and D yarn are able to maintain good dimensional stability through editorial afterword, the fabric after sizing is dyed, be dehydrated open-width, plucking, Hot light, cropping and clot are processed, and the semi-finished product water content after dyeing is too high, keep fabric-surface water content uniform after dehydration, It is ready for rear road plucking process；
(5) the fabric surface layer after last clot processing is carried out gluing by, and one layer of nylon velvet is bonded on glue-line, Upper one layer of epoxy resin adhesive glue will be coated on the surface layer of fabric after fabric clot processing, then by under the action of adhesive glue, Nylon fiber is bonded in web surface and forms not suede.
Tricot machine model of the step (1) into step (4) is SRM510 tricot machine.
Cloth is first warming up to 60 DEG C in dyeing course in step (4), dyestuff, auxiliary agent is added, is protected after being warming up to 130 DEG C Temperature 30 minutes, then cool down to 60 DEG C, cloth is put into washing pool and is washed cloth.
Regulation speed temperature during the hot light in 25 ms/min, step (4) is 160 during plucking in step (4) DEG C, and control vehicle is identical as during plucking, improves the exterior quality of fabric, has enhanced the applicability of product.
Specifically, (1), first using cotton fiber as A yarn, polyester fiber is as B yarn, and for bamboo charcoal fiber as C yarn, aramid fiber is fine Dimension be used as D yarn, by the yarn arrays mode of cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber according to 1A1C1A1B1A1D1C1A1C1A1B1C1B1C1B1C1D1C1D1C, 20 stringer one cycles through tricot machine and is arranged； (2) is by the band yarn digital manner of A yarn and B yarn according to GB4:0-0-0-0/3-3-3-3//arrange；By the band yarn number of C yarn Code mode is according to GB5:1-0-0-0/0-1-1-1//arranged；By the band yarn digital manner of D yarn according to GB12:1-0-1-l/ 1-2-2-2/2-3-3-3/3-4-4-4/4-5-5-5/5-6-6-6/6-7-7-7/7-8-8-8/8-9-9-9/9-10-10-10/ 10-11-11-11/11-12-12-12/12-13-13-13/13-14-14-14/14-15-15-15/15-16-l6-16/16- 17-17-17/17-18-18-18/17-16-16-16/17-18-18-18/17-l6-16-16/16-15-15-15/15-l4- 14-14/14-13-13-13/13-12-12-12/12-ll-l1-11/11-10-10-10//10-9-9-9/9-8-8-8/8-7- 7-7/7-6-6-6/6-5-5-5/5-4-4-4/4-3-3-3/3-2-2-2/2-1-1-l/1-0- 1-1/l-2-2-2//arranged Column form tortuous strip fabric；(3) its warp run-in of are as follows: GB4:1200；GB5:2000；GB12:1700；Indulge it is close be 7 rows/ Cm, warp run-in unit are mm/rack；(4) by tricot machine based on step (1), step (2) and step (3) to fabric into Row sizing, A yarn, B yarn, C yarn and D yarn are able to maintain good dimensional stability through editorial afterword, the fabric after sizing is dyed, Dehydration open-width, plucking, hot light, cropping and clot are processed, and the semi-finished product water content after dyeing is too high, and cloth is kept after dehydration Face moisture content is uniform, is ready for rear road plucking process；(5) applies the fabric surface layer after last clot processing Glue, and one layer of nylon velvet is bonded on glue-line, upper one layer of epoxy resin will be coated on the surface layer of fabric after fabric clot processing Adhesive glue, then by nylon fiber being bonded in web surface and forms not suede, by being made with cotton fiber under the action of adhesive glue For A yarn, polyester fiber as B yarn, bamboo charcoal fiber as C yarn, aramid fiber as D yarn as raw material, using warp knit mode into The obtained fabric of row bonds upper one layer of nylon fiber and is used as not fall then again in the surface layer of fabric coating epoxy resin as viscose Suede keeps whole fabric surface layer smooth, and has the effect of antibacterial flame-retardant, while fabric dimensional structure is stablized, and makes convenient for permanent With.
The present invention is by the way that using cotton fiber as A yarn, polyester fiber is made as B yarn, bamboo charcoal fiber as C yarn, aramid fiber It is D yarn as raw material, carries out that fabric is made using warp knit mode, then again in the surface layer of fabric coating epoxy resin as glutinous Glue bonds upper one layer of nylon fiber and is used as not suede, keeps whole fabric surface layer smooth, and have the effect of antibacterial flame-retardant, simultaneously Fabric dimensional structure is stablized, convenient for permanent use.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention, Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features. All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention Within protection scope.

Claims (4)

1. a kind of fine works with antibacterial flame-retardant function not material manufacturing technique of falling flannelette, which is characterized in that the fine works does not fall suede Fabric includes cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber, wherein cotton fiber, polyester fiber, bamboo charcoal fiber and virtue The weight ratio of synthetic fibre fiber be 65:10:12:13, the fine works fall velvet fabric production method the following steps are included:
(1) is first using cotton fiber as A yarn, polyester fiber as B yarn, bamboo charcoal fiber as C yarn, aramid fiber as D yarn, By the yarn arrays mode of cotton fiber, polyester fiber, bamboo charcoal fiber and aramid fiber according to 1A1C1A1B1A1D1C1A1C1A1B1C1B1C1B1C1D1C1D1C, 20 stringer one cycles through tricot machine and is arranged；
(2) is by the band yarn digital manner of A yarn and B yarn according to GB4:0-0-0-0/3-3-3-3//arrange；By the pad of C yarn Yarn digital manner is according to GB5:1-0-0-0/0-1-1-1//arranged；By the band yarn digital manner of D yarn according to GB12:1-0- 1-l/1-2-2-2/2-3-3-3/3-4-4-4/4--5-5-5/5-6-6-6/6-7-7-7/7-8-8-8/8-9-9-9/9-10-10- 10/10-11-11-11/11-12-12-12/12-13-13-13/13-14-14-14/14-15-15-15/15-16-l6-16/ 16-17-17-17/17-18-18-18/17-16-16-16/17-18-18-18/17-l6-16-16/16-15-15-15/15- l4-14-14/14-13-13-13/13-12-12-12/12-ll-l1-11/11-10-10-10//10-9-9--9/9-8-8-8/ 8-7-7-7/7-6-6-6/6-5-5-5/5-4-4-4/4-3-3-3/3-2-2-2/2-1-1-l/ 1-0-1-1/l-2-2-2//progress Arrangement；
(3) its warp run-in of are as follows:
GB4:1200；
GB5:2000；
GB12:1700；Indulging close is 7 rows/cm, and warp run-in unit is mm/rack；
(4) carries out shaping fabric based on step (1), step (2) and step (3) by tricot machine, by the face after sizing Material is dyed, is dehydrated open-width, plucking, hot light, cropping and clot and is processed；
(5) the fabric surface layer after last clot processing is carried out gluing by, and one layer of nylon velvet is bonded on glue-line.
2. a kind of fine works with antibacterial flame-retardant function according to claim 1 not material manufacturing technique of falling flannelette, feature It is, tricot machine model of the step (1) into step (4) is SRM510 tricot machine.
3. a kind of fine works with antibacterial flame-retardant function according to claim 1 not material manufacturing technique of falling flannelette, feature It is, cloth is first warming up to 60 DEG C in the dyeing course in the step (4), dyestuff, auxiliary agent is added, after being warming up to 130 DEG C Heat preservation 30 minutes, then cool down to 60 DEG C, cloth is put into washing pool and is washed cloth.
4. a kind of fine works with antibacterial flame-retardant function according to claim 1 not material manufacturing technique of falling flannelette, feature It is, regulation speed is at 25 ms/min during the plucking in the step (4), temperature during the hot light in the step (4) It is 160 DEG C, and it is identical as during plucking to control vehicle.
CN201811150476.8A 2018-09-29 2018-09-29 A kind of fine works with the antibacterial flame-retardant function not material manufacturing technique of falling flannelette Pending CN108978255A (en)