CN108914612A - A kind of processing method of warp knitting ultra-soft grid knitted polyester fabric - Google Patents

A kind of processing method of warp knitting ultra-soft grid knitted polyester fabric Download PDF

Info

Publication number
CN108914612A
CN108914612A CN201811050892.0A CN201811050892A CN108914612A CN 108914612 A CN108914612 A CN 108914612A CN 201811050892 A CN201811050892 A CN 201811050892A CN 108914612 A CN108914612 A CN 108914612A
Authority
CN
China
Prior art keywords
yarn
fabric
cloth
coiled hair
primer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811050892.0A
Other languages
Chinese (zh)
Inventor
金佳明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Xinzhao Textile Co Ltd
Original Assignee
Zhejiang Xinzhao Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Xinzhao Textile Co Ltd filed Critical Zhejiang Xinzhao Textile Co Ltd
Priority to CN201811050892.0A priority Critical patent/CN108914612A/en
Publication of CN108914612A publication Critical patent/CN108914612A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of processing methods of warp knitting ultra-soft grid knitted polyester fabric, include the following steps：S1, drawnwork：Yarn is extracted out by process by the chemical grain of rice, and determines the fineness degree of a yarn, factory generally directly buys yarn cake；Warping：The yarn cake of dispersion is focused on coiled hair, coiled hair number is related to the lines of yarn；Doubling：The yarn of two or more coiled hair, which is merged on a coiled hair 600D yarn such as, to be merged by two 300D yarns；S2, sizing：Upper pulp-water, keeps yarn firmer after doubling.Has following advantages compared with prior art：Common knitted fabric often with pillar stitch, warp plain stitch, satin, tiltedly organized etc. to weave.There are many fancy knitted fabric type, common are mesh fabric, knop cloth, horizontal tuck, pluse cloth, weft inserted fabric etc..Knitted fabric has lengthwise dimensional stability good, and fabric is well-pressed, and laddering is small, will not crimping, the advantages that good permeability, there is good promotional value.

Description

A kind of processing method of warp knitting ultra-soft grid knitted polyester fabric
Technical field
The present invention relates to a kind of production technologies, more specifically more particularly to a kind of warp knitting ultra-soft grid knitted polyester fabric Processing method.
Background technique
Weaving process includes woven（Also referred to as tatting）, knitting, braiding and non-woven, wherein knitting is divided into warp knit and latitude again It compiles.Warp knit is to belong to a kind of textile technology in knitting field.With one group or several groups of yarns arranged in parallel, in through to feeding machine All working needle on, while lopping and form knitted fabric, this method is known as warp knit, and the knitted fabric of formation is referred to as woven Object.
But traditional warp knit organization method haves the shortcomings that complicated for operation, maintenance cost is high and complicated for operation, serious shadow Production efficiency is rung, while increasing energy consumption, is not suitable for being widely popularized, for this purpose, it is proposed that a kind of warp knitting ultra-soft grid knitted polyester face The processing method of material.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the one kind proposed is warp knitting ultra-soft grid knitted The processing method of polyester fabric, common knitted fabric often with pillar stitch, warp plain stitch, satin, tiltedly organized etc. to weave. There are many fancy knitted fabric type, common are mesh fabric, knop cloth, horizontal tuck, pluse cloth, weft inserted fabric Deng.Knitted fabric has lengthwise dimensional stability good, and fabric is well-pressed, and laddering is small, will not crimping, the advantages that good permeability.
To achieve the above object, the present invention provides the following technical solutions：A kind of warp knitting ultra-soft grid knitted polyester fabric adds Work method, includes the following steps：
S1, drawnwork：Yarn is extracted out by process by the chemical grain of rice, and determines the fineness degree of a yarn, factory generally directly buys yarn cake； Warping：The yarn cake of dispersion is focused on coiled hair, coiled hair number is related to the lines of yarn；Doubling：Two or more The yarn of coiled hair, which is merged on a coiled hair 600D yarn such as, to be merged by two 300D yarns；
S2, sizing：Upper pulp-water, keeps yarn firmer after doubling；Lease making：Warp thread is set to be staggered in interval up and down by machine, so as to latitude Yarn passes through；Woven fabric：There are two kinds of knitting, plain weave, is mainly reflected in the difference of lines；
S3, wrinkle dye：It is generally used for terylene, is dyed by moving cloth, dyestuff simultaneously；Shaping：Shaping is set to make to wrinkle by shaping The cloth of folding is smooth, and prevents cloth crooked；
S4, starching：To one layer of glue on veil, keep its stronger；Press polish, sanding：Press polish is in order to the hair pressure on veil surface Flat, sanding is then to make veil wildness；
S5, cold pressing：Production raw rubber bottom is pressed again, after primer is carried out, so that primer is closed veil by physics, chemical action and is combined further It rises；Hot pressing：Primer is pressed when dissolving, and is generally pressed by temperature, the gluing of PU/AC/ PU primer；
S6, frictioning：By fixing a roller bearing, moving cloth, miscellaneous idler wheel glues and rotates in cloth contact, thus on cloth Primer.
Preferably, gluing process is generally in calender, foaming machine, lathering machine（It is completed on PU machine）, either pressure PVC is still PU glue is crossed, upper paste is all essential process, and processing is bad, and finished fabric just will appear degumming phenomenon.
Technical effect and advantage of the invention：Common knitted fabric is often with pillar stitch, warp plain stitch, satin, warp Tiltedly tissue etc. weaves.There are many fancy knitted fabric type, common are mesh fabric, knop cloth, horizontal tuck, plush and knit Object, weft inserted fabric etc..Knitted fabric have lengthwise dimensional stability it is good, fabric is well-pressed, and laddering is small, will not crimping, gas permeability The advantages that good.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not For limiting the present invention.Based on the embodiments of the present invention, those of ordinary skill in the art are not before making creative work Every other embodiment obtained is put, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of processing method of warp knitting ultra-soft grid knitted polyester fabric, includes the following steps：
S1, drawnwork：Yarn is extracted out by process by the chemical grain of rice, and determines the fineness degree of a yarn, factory generally directly buys yarn cake； Warping：The yarn cake of dispersion is focused on coiled hair, coiled hair number is related to the lines of yarn；Doubling：Two or more The yarn of coiled hair, which is merged on a coiled hair 600D yarn such as, to be merged by two 300D yarns；
S2, sizing：Upper pulp-water, keeps yarn firmer after doubling；Lease making：Warp thread is set to be staggered in interval up and down by machine, so as to latitude Yarn passes through；Woven fabric：There are two kinds of knitting, plain weave, is mainly reflected in the difference of lines；
S3, wrinkle dye：It is generally used for terylene, is dyed by moving cloth, dyestuff simultaneously；Shaping：Shaping is set to make to wrinkle by shaping The cloth of folding is smooth, and prevents cloth crooked；
S4, starching：To one layer of glue on veil, keep its stronger；Press polish, sanding：Press polish is in order to the hair pressure on veil surface Flat, sanding is then to make veil wildness；
S5, cold pressing：Production raw rubber bottom is pressed again, after primer is carried out, so that primer is closed veil by physics, chemical action and is combined further It rises；Hot pressing：Primer is pressed when dissolving, and is generally pressed by temperature, the gluing of PU/AC/ PU primer；
S6, frictioning：By fixing a roller bearing, moving cloth, miscellaneous idler wheel glues and rotates in cloth contact, thus on cloth Primer.
Gluing process is generally in calender, foaming machine, lathering machine（It is completed on PU machine）, either PVC is pressed still to cross PU glue, Upper paste is all essential process, and processing is bad, and finished fabric just will appear degumming phenomenon.
In summary：The processing method of a kind of warp knitting ultra-soft grid knitted polyester fabric provided by the invention, with prior art It compares, has following advantages：Common knitted fabric often with pillar stitch, warp plain stitch, satin, tiltedly organized etc. to weave. There are many fancy knitted fabric type, common are mesh fabric, knop cloth, horizontal tuck, pluse cloth, weft inserted fabric Deng.Knitted fabric has lengthwise dimensional stability good, and fabric is well-pressed, and laddering is small, will not crimping, the advantages that good permeability.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features, All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention Within protection scope.

Claims (2)

1. a kind of processing method of warp knitting ultra-soft grid knitted polyester fabric, it is characterised in that：Include the following steps：
S1, drawnwork：Yarn is extracted out by process by the chemical grain of rice, and determines the fineness degree of a yarn, factory generally directly buys yarn cake； Warping：The yarn cake of dispersion is focused on coiled hair, coiled hair number is related to the lines of yarn；Doubling：Two or more The yarn of coiled hair, which is merged on a coiled hair 600D yarn such as, to be merged by two 300D yarns；
S2, sizing：Upper pulp-water, keeps yarn firmer after doubling；Lease making：Warp thread is set to be staggered in interval up and down by machine, so as to latitude Yarn passes through；Woven fabric：There are two kinds of knitting, plain weave, is mainly reflected in the difference of lines；
S3, wrinkle dye：It is generally used for terylene, is dyed by moving cloth, dyestuff simultaneously；Shaping：Shaping is set to make to wrinkle by shaping The cloth of folding is smooth, and prevents cloth crooked；
S4, starching：To one layer of glue on veil, keep its stronger；Press polish, sanding：Press polish is in order to the hair pressure on veil surface Flat, sanding is then to make veil wildness；
S5, cold pressing：Production raw rubber bottom is pressed again, after primer is carried out, so that primer is closed veil by physics, chemical action and is combined further It rises；Hot pressing：Primer is pressed when dissolving, and is generally pressed by temperature, the gluing of PU/AC/ PU primer；
S6, frictioning：By fixing a roller bearing, moving cloth, miscellaneous idler wheel glues and rotates in cloth contact, thus on cloth Primer.
2. a kind of processing method of warp knitting ultra-soft grid knitted polyester fabric according to claim 1, it is characterised in that：Gluing Process is generally in calender, foaming machine, lathering machine（It is completed on PU machine）, either press PVC still to cross PU glue, upper paste is all must not The process that can lack, processing is bad, and finished fabric just will appear degumming phenomenon.
CN201811050892.0A 2018-09-10 2018-09-10 A kind of processing method of warp knitting ultra-soft grid knitted polyester fabric Pending CN108914612A (en)