CN108824031B - 具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺 - Google Patents
具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺 Download PDFInfo
- Publication number
- CN108824031B CN108824031B CN201810716564.3A CN201810716564A CN108824031B CN 108824031 B CN108824031 B CN 108824031B CN 201810716564 A CN201810716564 A CN 201810716564A CN 108824031 B CN108824031 B CN 108824031B
- Authority
- CN
- China
- Prior art keywords
- fabric
- dyeable polyester
- dyeing
- cationic
- polyester fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，具有以下步骤：①将阳离子可染涤纶织物浸在染液中，加酸调节pH为4.0～5.0，然后在110℃～135℃染色处理20min～60min；②将织物依次进行热水洗、还原清洗以及酸中和；③将织物先进行脱水、烘干，然后浸轧后整理液，最后焙烘定型。本发明的方法针对阳离子可染涤纶织物选择特殊的紫外线吸收剂，尤其是将抗紫外功能化与染色同时进行，而后整理环节只进行防蚊功能化与凉爽功能化，该特殊的功能化处理方式尤其能获得较好的抗紫外线功能，最终能够使得阳离子可染涤纶织物同时具备效果较好的抗紫外线、凉爽触感、防蚊三种功能。
Description
技术领域
本发明属于纺织印染技术领域，具体涉及一种具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺。
背景技术
随着纺织面料功能加工技术的日益成熟，对纺织面料功能的要求也越来越高。单一功能的纺织面料已经无法满足特定领域的需求，复合功能纺织面料存在广阔市场。
织物的功能化主要有以下两种途径：
（1）先制备功能化纤维，再制备功能化织物。
该途径主要适用于化学纤维，优点是功能化效果较好，缺点则是工艺设备要求较高，生产成本较高。
（2）对普通织物进行功能化后整理。
该途径主要适用于天然纤维，也即，对于天然纤维的功能化效果较好，而对于化学纤维的功能化效果不佳，尤其是复合功能化效果更不理想。
发明内容
本发明的目的在于解决上述问题，提供一种工艺设备简单、生产成本较低、功能化效果较好的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺。
实现本发明目的的技术方案是：一种具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，具有以下步骤：
①将阳离子可染涤纶织物浸在染液中，加酸调节pH为4.0～5.0，然后在110℃～135℃的温度下染色处理20min～60min；
所述染液是每升含有0.5g～3.0g精炼乳化剂、0.5g～3.0g沉淀防止剂、3.0g～8.0g元明粉、1.0g～4.0g紫外线吸收剂以及0.1g～8.0g阳离子染料的水溶液，并且阳离子染料的总重量为织物重量的0.1%～8.0%；
②将经过步骤①染色处理后的织物先进行50℃～70℃的热水洗8min～15min，再进行85℃～95℃的还原清洗15min～30min，最后进行10℃～40℃的酸中和5min～30min；
③将经过步骤②处理后的织物先进行脱水、烘干，然后浸轧后整理液，最后在110℃～150℃焙烘定型100～150秒。
上述步骤①中所述的精炼乳化剂的主要成分为聚氧乙烯壬基酚醚；所述的沉淀防止剂的主要成分为脂肪醇聚氧乙烯醚；所述的阳离子染料为阳离子黑染料Sunacryl BlackCD-BR H/C和/或阳离子藏青色染料Sunacryl Navy Blue SDR。
上述步骤①中所述的紫外线吸收剂的主要成分为聚氧乙烯山梨醇酐月桂酸酯。
上述步骤②中所述的还原清洗采用的是每升含有1.0g～4.0g酸性还原剂的水溶液；上述步骤②中所述的酸中和采用的是每升含有0.5g～1.0g柠檬酸的水溶液。
所述的酸性还原剂的主要成分为亚硫酸氢钠。
上述步骤③中所述的后整理液是每升含有100g～160g防蚊剂、35g～75g交联剂以及30g～70g凉爽触感加工剂的水溶液，并加酸调节pH为4.0～5.5。
所述的防蚊剂的主要成分为（苄）氯菊酯；所述的交联剂的主要成分为自交联水性丙烯酸分散液；所述的凉爽触感加工剂的主要成分为异氰酸酯。
上述步骤①中所述的阳离子可染涤纶织物为100%阳离子可染涤纶织物、或者阳离子可染涤纶与氨纶的交织/混纺织物、或者阳离子可染涤纶与（普通）涤纶的交织/混纺织物、或者阳离子可染涤纶与（普通）涤纶以及氨纶的交织/混纺织物。
本发明具有的积极效果：本发明的方法针对阳离子可染涤纶织物选择特殊的紫外线吸收剂，尤其是将抗紫外功能化与染色同时进行，而后整理环节只进行防蚊功能化与凉爽功能化，该特殊的功能化处理方式尤其能获得较好的抗紫外线功能，最终能够使得阳离子可染涤纶织物同时具备效果较好的抗紫外线、凉爽触感、防蚊三种功能。
具体实施方式
（实施例1）
本实施例的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺具有以下步骤：
①将阳离子可染涤纶织物浸在染液中，加酸调节pH为4.5，然后在120℃的温度下染色处理30min。
该染液是每升含有1.4g精炼乳化剂、0.9g沉淀防止剂、5.0g元明粉、2.0g紫外线吸收剂以及3.2g阳离子染料的水溶液；并且阳离子染料的总重量为织物重量的3.2%。
其中，精炼乳化剂采用的是信守化工股份有限公司生产的SEM-35N精炼乳化剂，其主要成分为聚氧乙烯壬基酚醚；沉淀防止剂采用的是江苏德旺化工工业有限公司生产的沉淀防止剂HT-77，其主要成分为脂肪醇聚氧乙烯醚。
紫外线吸收剂采用的是苏州维明化学工业有限公司生产的Hipom UV-330，其主要成分为聚氧乙烯山梨醇酐月桂酸酯（也即吐温-20）。
阳离子染料采用的是江苏德旺化工工业有限公司生产的阳离子黑染料SunacrylBlack CD-BR H/C和阳离子藏青色染料Sunacryl Navy Blue SDR；其中，阳离子黑染料Sunacryl Black CD-BR H/C的重量为织物重量的2.2%，阳离子藏青色染料Sunacryl NavyBlue SDR的重量为织物重量的1.0%。
本实施例采用的阳离子可染涤纶织物为100%阳离子可染涤纶针织物。
②将经过步骤①染色处理后的织物先进行60℃×10min的热水洗，再进行90℃×20min的还原清洗，最后进行20℃×10min的酸中和。
其中，还原清洗采用的是每升含有3.0g酸性还原剂的水溶液，酸中和采用的是每升含有0.7g柠檬酸的水溶液。
其中，酸性还原剂采用的是苏州市鸿辰化工有限公司生产的HC007酸性还原剂，其主要成分为亚硫酸氢钠。
③将经过步骤②处理后的织物先进行脱水、烘干，然后浸轧后整理液，采用二浸二轧，轧余率为80～85%，最后在130℃焙烘定型120秒。
该后整理液是每升含有140g防蚊剂、50g交联剂以及60g凉爽触感加工剂的水溶液，并加酸调节pH为4.5。
其中，防蚊剂采用的是拓纳贸易（上海）有限公司生产的EULAN SPA 01，其主要成分为（苄）氯菊酯；交联剂采用的是拓纳贸易（上海）有限公司生产的EDOLAN AB，其主要成分为自交联水性丙烯酸分散液；凉爽触感加工剂采用的是昆山洺家助剂有限公司生产的Sincool SN-802凉爽触感加工剂，其主要成分为异氰酸酯。
（实施例2～实施例5）
各实施例的染整工艺与实施例1基本相同，不同之处见表1。
表1
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 阳离子可染涤纶织物 | 100%阳离子可染涤纶针织物 | 50%阳离子可染涤纶+50%涤纶交织针织物 | 45%阳离子可染涤纶+45%涤纶+10%氨纶交织弹力针织物 | 95%阳离子可染涤纶+5%氨纶交织弹力针织物 | 50%阳离子可染涤纶+40%涤纶+10%氨纶交织弹力针织物 |
| 阳离子黑染料SunacrylBlack CD-BRH/C | 2.2% | 2.0% | 1.0% | 4.0% | 2.3% |
| 阳离子藏青色染料SunacrylNavy Blue SDR | 1.0% | 0.5% | 1.0% | / | 0.5% |
| 紫外线防护系数（UPF） | 58.7 | 53.3 | 55.2 | 52.9 | 56.5 |
| 接触凉感系数qmax（J/cm2·s） | 0.165 | 0.157 | 0.160 | 0.158 | 0.161 |
其中，接触凉感系数qmax参照GB/T 35263-2017《纺织品 接触瞬间凉感性能的检测和评价》，测试条件为：温度20±0.2℃，湿度65±2%，△T=15℃。评价指标为≥0.15J/cm2·s。
（对比例1～对比例3）
各对比例的染整工艺与实施例1基本相同，不同之处见表2。
表2
| 实施例1 | 对比例1 | 对比例2 | 对比例3 | |
| 紫外线吸收剂种类 | Hipom UV-330 | UV-P | UV-531 | Hipom UV-330 |
| 紫外线吸收剂处理方式 | 步骤①染液中 | 步骤①染液中 | 步骤①染液中 | 步骤③后整理液中 |
| 紫外线防护系数（UPF） | 58.7 | 37.2 | 40.6 | 43.2 |
Claims (6)
1.一种具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，其特征在于具有以下步骤：
①将阳离子可染涤纶织物浸在染液中，加酸调节pH为4.0～5.0，然后在110℃～135℃的温度下染色处理20min～60min；
所述染液是每升含有0.5g～3.0g精炼乳化剂、0.5g～3.0g沉淀防止剂、3.0g～8.0g元明粉、1.0g～4.0g紫外线吸收剂以及0.1g～8.0g阳离子染料的水溶液，并且阳离子染料的总重量为织物重量的0.1%～8.0%；
所述的紫外线吸收剂为Hipom UV-330；
②将经过步骤①染色处理后的织物先进行50℃～70℃的热水洗8min～15min，再进行85℃～95℃的还原清洗15min～30min，最后进行10℃～40℃的酸中和5min～30min；
③将经过步骤②处理后的织物先进行脱水、烘干，然后浸轧后整理液，最后在110℃～150℃焙烘定型100～150秒；所述的后整理液是每升含有100g～160g防蚊剂、35g～75g交联剂以及30g～70g凉爽触感加工剂的水溶液，并加酸调节pH为4.0～5.5；
所述的防蚊剂为EULAN SPA 01；
所述的交联剂为EDOLAN AB；
所述的凉爽触感加工剂为Sincool SN-802凉爽触感加工剂。
2.根据权利要求1所述的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，其特征在于：上述步骤①中所述的精炼乳化剂的主要成分为聚氧乙烯壬基酚醚；所述的沉淀防止剂的主要成分为脂肪醇聚氧乙烯醚。
3.根据权利要求1所述的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，其特征在于：上述步骤①中所述的阳离子染料为阳离子黑染料SunacrylBlack CD-BR H/C和/或阳离子藏青色染料Sunacryl Navy Blue SDR。
4.根据权利要求1所述的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，其特征在于：上述步骤②中所述的还原清洗采用的是每升含有1.0g～4.0g酸性还原剂的水溶液；上述步骤②中所述的酸中和采用的是每升含有0.5g～1.0g柠檬酸的水溶液。
5.根据权利要求4所述的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，其特征在于：所述的酸性还原剂的主要成分为亚硫酸氢钠。
6.根据权利要求1所述的具有抗紫外线、凉爽触感、防蚊复合功能的阳离子可染涤纶织物染整工艺，其特征在于：上述步骤①中所述的阳离子可染涤纶织物为100%阳离子可染涤纶织物、或者阳离子可染涤纶与氨纶的交织/混纺织物、或者阳离子可染涤纶与涤纶的交织/混纺织物、或者阳离子可染涤纶与涤纶以及氨纶的交织/混纺织物。