CN108705820A - 一种抗菌铝箔复合材料及其制造方法 - Google Patents
一种抗菌铝箔复合材料及其制造方法 Download PDFInfo
- Publication number
- CN108705820A CN108705820A CN201810601418.6A CN201810601418A CN108705820A CN 108705820 A CN108705820 A CN 108705820A CN 201810601418 A CN201810601418 A CN 201810601418A CN 108705820 A CN108705820 A CN 108705820A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- aluminium foil
- aluminum foil
- antibacterial aluminum
- plastic film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于软包装技术领域，具体涉及一种抗菌铝箔复合材料及其制造方法，所述复合材料包括塑料薄膜和铝箔，所述塑料薄膜和铝箔之间通过胶粘剂相互连接，增强材料的柔软性，方便操作，所述铝箔表面设有抗菌铝膜层，所述抗菌铝膜层内设有抗菌剂，使得其能够杀死细菌，防止细菌的侵入导致产品变质，本发明的抗菌铝箔复合材料制造方法工艺简单、操作方便、制造成本低廉，抗菌物质沉积均匀、牢固稳定，抗菌铝箔复合材料的抗菌杀菌作用持续时间长且抗菌杀菌率高达99.99％。多孔氧化铝膜提高了抗菌铝箔复合材料的耐腐蚀性能，电解沉积液长期使用也不会析出不溶性沉积，非常稳定。
Description
技术领域
本发明属于软包装技术领域，具体涉及一种抗菌铝箔复合材料及其制造方法。
背景技术
铝箔因其优良的特性，广泛用于食品、饮料、香烟、药品、家庭日用品等，通常用作其包装材料。铝箔包装发展前景十分广泛；复合铝箔材料包装具有高阻隔性能、轻量化、抗紫外、常温保质期长等优势，在方便食品，熟食，药品等包装中的应用越来越广泛，近年来，因技术进步，人类对健康的关注和环保意识的增强，包装材料向着更安全、更全面和无污染的方向发展，世界包装材料正向多元化、多样化、着重安全、顺应环保的趋势发展。然而，目前的包装材料通常不具有杀菌功能，容易使得细菌侵入食品或药品，造成食品或药品变质，滋生细菌，威胁着人们的健康安全。
随着人们生活水平的提高，人们对卫生和健康的要求越来越高，符合卫生和健康要求的包装材料，目前也取得了一定成果。
如专利号CN201710576596.3公开了一种抗菌聚酯/铝箔复合包装膜及其制备方法，该制备方法包括：1)将铝箔进行预处理，然后置于电镀液中进行电镀以使得铝箔的表面形成电镀层以制得电镀铝箔；2)将聚酯、乙烯-甲基丙烯酸共聚物、氧化钙、凡士林、对苯二酚、松香、二苯基硅二醇、麻黄、柴胡、牛蒡子、羌活和白芷进行混炼以制得混炼物；3)将粘结剂涂覆于电镀铝箔的一面，接着干燥以形成粘结层，然后将混炼物热压于粘结层的上方形成聚酯层以制得抗菌聚酯/铝箔复合包装膜；其中，电镀液的pH为4-5.5，并且含有Ag+、Pd2+、Cu2+和Ti4+，电镀阳极含有Ag、Pd、Cu和Ti。该抗菌聚酯/铝箔复合包装膜具有优异的抗菌性能，同时该制备方法具有工序简单和原料易得优点，但是所述的抗菌聚酯/铝箔复合包装膜通过一步电镀和涂覆制得的抗菌层易脱落，抗菌持久性差。
发明内容
为了解决上述包装材料不具有杀菌功能或抗菌层易脱落，造成细菌侵入食品或药品，导致食品或药品变质而影响健康等问题，本发明提供一种抗菌铝箔复合材料及其制造方法。
为实现上述目的，本发明所采用的技术方案是：一种抗菌铝箔复合材料，所述复合材料包括塑料薄膜和铝箔，所述塑料薄膜和铝箔之间通过胶粘剂相互连接，所述铝箔表面设有抗菌铝膜层，所述抗菌铝膜层内设有抗菌剂。
进一步的，塑料薄膜的材质为PE或PP或PET，所述塑料薄膜的厚度为0.03-2mm。
进一步的，胶粘剂为聚氨酯，其厚度为0.005-0.01mm。
进一步的，铝箔的厚度为0.01-0.25mm。
进一步的，抗菌剂为抗菌金属包括银、氧化银、铜或氧化铜中的任意组合。
一种抗菌铝箔复合材料的制造方法，制造上述的抗菌铝箔复合材料，其步骤如下：
1)往基材塑料薄膜表面涂覆一层胶粘剂；
2)将铝箔通过热压粘结于塑料薄膜表面；
3)将步骤二中的复合材料作为阳极，放入电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
4)将步骤三中制得的具有多孔氧化铝膜的铝箔复合材料作为阴极，放入电解液溶液进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得抗菌铝箔复合材料；
5)将步骤四中制得的抗菌铝箔复合材料进行清洗和封孔；
或其步骤如下：
1)将铝箔作为阳极，放入电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
2)将步骤一中制得的具有多孔氧化铝膜的铝箔作为阴极，放入电解液溶液进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得抗菌铝箔材料；
3)将步骤二中制得的抗菌铝箔材料进行清洗和封孔；
4)往基材塑料薄膜表面涂覆一层胶粘剂；
5)将抗菌铝箔材料通过热压粘结于塑料薄膜表面，制得抗菌铝箔复合材料。
进一步的，铝箔阳极氧化反应的电解液为硫酸，氧化锌，草甘膦中的一种或多种的组合物。
进一步的，着色和沉积抗菌金属的电解液为色素、硝酸银、铜绿、硫酸镁、络合剂，所述络合剂为甘氨酸或丙氨酸或有机羟基羧酸中一种。
进一步的，封孔反应的封孔剂为二氧化钛或碘和碘的化合物中的一种或多种。
本发明提供一种抗菌铝箔复合材料，所述复合材料包括塑料薄膜和铝箔，所述塑料薄膜和铝箔之间通过胶粘剂相互连接，增强材料的柔软性，方便包装，所述铝箔表面设有抗菌铝膜层，所述抗菌铝膜层内设有抗菌剂，使得其能够杀死细菌，防止细菌的侵入导致产品变质，本发明的抗菌铝箔复合材料制造方法工艺简单、操作方便、制造成本低廉，抗菌金属沉积均匀、牢固稳定，抗菌铝箔复合材料的抗菌杀菌作用持续时间长且抗菌杀菌率高达99.99％。多孔氧化铝膜提高了抗菌铝箔复合材料的耐腐蚀性能，电解沉积液长期使用也不会析出不溶性沉积，非常稳定。
附图说明
图1为单面抗菌铝箔复合材料的结构示意图；
图2为抗菌铝箔表面沉积有抗菌金属的多孔氧化铝膜；
图3为双面抗菌铝箔复合材料的结构示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。
实施例一
如图1和图2所示，一种抗菌铝箔复合材料，所述复合材料包括塑料薄膜1和铝箔2，所述塑料薄膜1的材质为PET，其厚度为1mm，所述铝箔2的厚度为0.01mm，所述塑料薄膜1和铝箔2之间通过胶粘剂相互连接成单面铝箔的复合材料，增强材料的柔软性，方便包装，所述铝箔2表面设有抗菌铝膜层21，所述抗菌铝膜层21内设有抗菌剂22，所述抗菌剂22为抗菌金属包括银、氧化银、铜或氧化铜中的任意组合，使得其能够杀死细菌，防止细菌的侵入导致产品变质。
一种抗菌铝箔复合材料的制造方法，制造上述的抗菌铝箔复合材料，其步骤如下：
1)往基材塑料薄膜表面涂覆一层胶粘剂；
2)将铝箔通过热压粘结于塑料薄膜表面，形成单面抗菌铝箔复合材料；
3)将步骤二中的复合材料作为阳极，放入含有硫酸，草甘膦的组合物电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
4)将步骤三中制得的具有多孔氧化铝膜的铝箔复合材料作为阴极，放入含有色素、硝酸银、铜绿、硫酸镁、甘氨酸络合剂的电解液溶液中，进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得单面抗菌铝箔复合材料；
5)将步骤四中制得的抗菌铝箔复合材料进行清洗，清洗完成后浸入含有二氧化钛封孔剂的溶液中，进行封孔反应。
实施例二
如图1和图2所示，一种抗菌铝箔复合材料，所述复合材料包括塑料薄膜1和铝箔2，所述塑料薄膜1的材质为PET，其厚度为1mm，所述铝箔2的厚度为0.01mm，所述塑料薄膜和铝箔之间通过胶粘剂相互连接成单面铝箔的复合材料，增强材料的柔软性，方便包装，所述铝箔2表面设有抗菌铝膜层21，所述抗菌铝膜层21内设有抗菌剂22，所述抗菌剂22为抗菌金属包括银、氧化银、铜或氧化铜中的任意组合，使得其能够杀死细菌，防止细菌的侵入导致产品变质。
一种抗菌铝箔复合材料的制造方法，制造上述的抗菌铝箔复合材料，其步骤如下：
1)将铝箔作为阳极，放入含有硫酸，草甘膦的组合物电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
2)将步骤一中制得的具有多孔氧化铝膜的铝箔作为阴极，放入含有色素、硝酸银、铜绿、硫酸镁、甘氨酸络合剂的电解液溶液进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得抗菌铝箔材料；
3)将步骤二中制得的抗菌铝箔材料进行清洗，清洗完成后浸入含有二氧化钛封孔剂的溶液中，进行封孔反应；
4)往基材塑料薄膜表面涂覆一层胶粘剂；
5)将抗菌铝箔材料通过热压粘结与塑料薄膜表面，制得单面抗菌铝箔复合材料。
实施例三
如图2和图3所示，一种抗菌铝箔复合材料，所述复合材料包括塑料薄膜1和铝箔2，所述塑料薄膜1的材质为PET，其厚度为1mm，所述铝箔2的厚度为0.01mm，所述塑料薄膜和铝箔之间通过胶粘剂相互连接成双面铝箔的复合材料，增强材料的柔软性，方便包装，所述铝箔2表面设有抗菌铝膜层21，所述抗菌铝膜层21内设有抗菌剂22，所述抗菌剂22为抗菌金属包括银、氧化银、铜或氧化铜中的任意组合，使得其能够杀死细菌，防止细菌的侵入导致产品变质。
一种抗菌铝箔复合材料的制造方法，制造上述的抗菌铝箔复合材料，其步骤如下：
1)往基材塑料薄膜表面涂覆一层胶粘剂；
2)将铝箔通过热压粘结于塑料薄膜表面，形成双面抗菌铝箔复合材料；
3)将步骤二中的复合材料作为阳极，放入含有硫酸，草甘膦的组合物电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
4)将步骤三中制得的具有多孔氧化铝膜的铝箔复合材料作为阴极，放入含有色素、硝酸银、铜绿、硫酸镁、甘氨酸络合剂的电解液溶液中，进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得双面抗菌铝箔复合材料；
5)将步骤四中制得的抗菌铝箔复合材料进行清洗，清洗完成后浸入含有二氧化钛封孔剂的溶液中，进行封孔反应。
实施例四
如图2和图3所示，一种抗菌铝箔复合材料，所述复合材料包括塑料薄膜1和铝箔2，所述塑料薄膜1的材质为PET，其厚度为1mm，所述铝箔2的厚度为0.01mm，所述塑料薄膜和铝箔之间通过胶粘剂相互连接成双面铝箔的复合材料，增强材料的柔软性，方便包装，所述铝箔2表面设有抗菌铝膜层21，所述抗菌铝膜层21内设有抗菌剂22，所述抗菌剂22为抗菌金属包括银、氧化银、铜或氧化铜中的任意组合，使得其能够杀死细菌，防止细菌的侵入导致产品变质。
一种抗菌铝箔复合材料的制造方法，制造上述的抗菌铝箔复合材料，其步骤如下：
1)将铝箔作为阳极，放入含有硫酸，草甘膦的组合物电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
2)将步骤一中制得的具有多孔氧化铝膜的铝箔作为阴极，放入含有色素、硝酸银、铜绿、硫酸镁、甘氨酸络合剂的电解液溶液进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得抗菌铝箔材料；
3)将步骤二中制得的抗菌铝箔材料进行清洗，清洗完成后浸入含有二氧化钛封孔剂的溶液中，进行封孔反应；
4)往基材塑料薄膜表面涂覆一层胶粘剂；
5)将抗菌铝箔材料通过热压粘结与塑料薄膜表面，制得双面抗菌铝箔复合材料。
本发明的抗菌铝箔复合材料制造方法工艺简单、操作方便、制造成本低廉，抗菌金属沉积均匀、牢固稳定，抗菌铝箔复合材料的抗菌杀菌作用持续时间长且抗菌杀菌率高达99.99％。多孔氧化铝膜提高了抗菌铝箔复合材料的耐腐蚀性能，电解沉积液长期使用也不会析出不溶性沉积，非常稳定。
上述仅为本发明的优选具体实施方式，但本发明的设计构思并不局限于此，凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的行为。
Claims (9)
1.一种抗菌铝箔复合材料，其特征在于：所述复合材料包括塑料薄膜和铝箔，所述塑料薄膜和铝箔之间通过胶粘剂相互连接，所述铝箔表面设有抗菌铝膜层，所述抗菌铝膜层内设有抗菌剂。
2.根据权利要求1所述的抗菌铝箔复合材料，其特征在于：所述塑料薄膜的材质为PE或PP或PET，所述塑料薄膜的厚度为0.03-2mm。
3.根据权利要求1所述的抗菌铝箔复合材料，其特征在于：所述胶粘剂为聚氨酯，其厚度为0.005-0.01mm。
4.根据权利要求1所述的抗菌铝箔复合材料，其特征在于：所述铝箔的厚度为0.01-0.25mm。
5.根据权利要求1所述的抗菌铝箔复合材料，其特征在于：所述抗菌剂为抗菌金属包括银、氧化银、铜或氧化铜中的一种或者其任意组合。
6.一种抗菌铝箔复合材料的制造方法，其特征在于：制造权利要求1所述的抗菌铝箔复合材料，其步骤如下：
1)往基材塑料薄膜表面涂覆一层胶粘剂；
2)将铝箔通过热压粘结于塑料薄膜表面；
3)将步骤二中的复合材料作为阳极，放入电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
4)将步骤三中制得的具有多孔氧化铝膜的铝箔复合材料作为阴极，放入电解液溶液进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得抗菌铝箔复合材料；
5)将步骤四中制得的抗菌铝箔复合材料进行清洗和封孔；
或其步骤如下：
1)将铝箔作为阳极，放入电解液溶液中进行氧化反应，铝箔表面制得多孔氧化铝膜；
2)将步骤一中制得的具有多孔氧化铝膜的铝箔作为阴极，放入电解液溶液进行着色和沉积反应，使得多孔氧化铝膜的孔道中电解沉积抗菌金属，制得抗菌铝箔材料；
3)将步骤二中制得的抗菌铝箔材料进行清洗和封孔；
4)往基材塑料薄膜表面涂覆一层胶粘剂；
5)将抗菌铝箔材料通过热压粘结于塑料薄膜表面，制得抗菌铝箔复合材料。
7.根据权利要求6所述的抗菌铝箔复合材料的制造方法，其特征在于：所述铝箔阳极氧化反应的电解液为硫酸，氧化锌，草甘膦中的一种或多种的组合物。
8.根据权利要求6所述的抗菌铝箔复合材料的制造方法，其特征在于：所述着色和沉积抗菌金属的电解液为色素、硝酸银、铜绿、硫酸镁、络合剂，所述络合剂为甘氨酸或丙氨酸或有机羟基羧酸中一种。
9.根据权利要求6所述的抗菌铝箔复合材料的制造方法，其特征在于：所述封孔反应的封孔剂为二氧化钛或碘及碘的化合物中一种或多种。