CN1676227A - 纳米TiO2载银抗菌薄膜的制造方法 - Google Patents

纳米TiO2载银抗菌薄膜的制造方法 Download PDF

Info

Publication number
CN1676227A
CN1676227A CN 200510031492 CN200510031492A CN1676227A CN 1676227 A CN1676227 A CN 1676227A CN 200510031492 CN200510031492 CN 200510031492 CN 200510031492 A CN200510031492 A CN 200510031492A CN 1676227 A CN1676227 A CN 1676227A
Authority
CN
China
Prior art keywords
silver
oleic acid
acetone
film
product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510031492
Other languages
English (en)
Other versions
CN1311915C (zh
Inventor
潘俊明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN TAIXIN CERAMICS CO Ltd
Original Assignee
HUNAN TAIXIN CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN TAIXIN CERAMICS CO Ltd filed Critical HUNAN TAIXIN CERAMICS CO Ltd
Priority to CNB2005100314921A priority Critical patent/CN1311915C/zh
Publication of CN1676227A publication Critical patent/CN1676227A/zh
Application granted granted Critical
Publication of CN1311915C publication Critical patent/CN1311915C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及纳米TiO2载银抗菌薄膜的制造方法。方法之一是将制好的银溶液加入钛溶胶中制成载银溶胶并以该溶胶对产品涂膜；方法之二是先将产品在钛溶胶中涂膜，干燥后再在银溶液中涂膜。上述银溶液是将适量硝酸银先溶于微量水，再加入适量油酸和丙酮经充分搅拌而成。单独的银溶液稳定时间在3个月以上，而载银溶胶的稳定期也在1个月以上。依本发明方法获得的带纳米TiO2载银薄膜的制品抗菌能力强，对大肠杆菌、金色葡萄球菌的杀菌率均在90％以上；且本法中抗菌物料消耗较少，整个生产工艺的生产成本也低。

Description

纳米TiO2载银抗菌薄膜的制造方法
技术领域
本发明涉及纳米TiO2载银抗菌薄膜的制造方法。
背景技术
在所有金属离子中，Ag+是最低抑菌浓度值最小的品种之一，加上它无色无毒，十分适用于抗菌剂制备。但是，由于银盐具有很强的光敏反应能力，遇光或长期保存极易变色，这就给银盐的添加使用带来很多麻烦，而往钛溶胶中添加时更是如此。
发明内容
本发明的目的是采用保护包覆改性法，让银离子吸附一保护层而避免光的直接照射，从而使纳米TiO2载银抗菌薄膜的制造成为可能。
纳米TiO2载银抗菌薄膜的制造方法，其特征是在钛溶胶中加入银溶液后再行涂膜，具体步骤：A、制备银溶液，按Ag+/TiO2＝3～6％的比例准备硝酸银，先以微量水溶解，再加入油酸和丙酮充分搅拌0.5小时，注意所用油酸和丙酮的体积比为1∶1或1∶2，且油酸和丙酮的总量为20毫升，B、将银溶液加入钛溶胶并充分搅拌0.5小时，以该溶胶对产品涂膜、干燥、煅烧后即得载银涂膜制品，涂膜时采用提拉法，干燥温度80～150℃，时间1小时，煅烧温度450～550℃，时间2小时。
纳米TiO2载银抗菌薄膜的又一制造方法，其特征是产品在钛溶胶中涂膜干燥后再在银溶液中浸涂，具体步骤：A、制品在钛溶胶中涂膜后于80～150℃下干燥20分钟；B、按Ag+/TiO2＝3～6％的比例准备硝酸银，先以微量水溶解，再加入油酸和丙酮充分搅拌0.5小时，所用油酸和丙酮的体积比为1∶1或1∶2，且二者的总量为20毫升；C、将A步骤所得制品于B步骤所得银溶液中提拉浸涂后于80～150℃下干燥1小时，再于450～550℃下煅烧2小时即可。
依本发明方法制得的单一银溶液，其稳定期在三个月以上，而混合涂膜液的稳定期也在一个月以上，可见是一种实用的方法。
依本发明方法得到的纳米TiO2载银抗菌薄膜，对大肠杆菌、金色葡萄球菌的杀菌率均在90％以上；同时在本法中抗菌物料的消耗也较低，这当然就降低了成本。
具体实施方式
一、按Ag+/TiO2＝3～6％的比例准备硝酸银，先以微量水溶解硝酸银，再加入油酸和丙酮充分搅拌半小时即得银溶液，注意所用油酸和丙酮的体积比为1∶1，且所用总量为20毫升。若是油酸量不足，则溶液稳定时间短；油酸量过多，又会使薄膜的透明度差。将制得的银溶液加入钛溶胶液中搅拌半小时可获载银溶胶，以该溶胶对制品涂膜后，于100～120℃下干燥1小时，再于500～550℃下煅烧2小时即可。
二、先将制品在钛溶胶中涂膜后于80～120℃下干燥20分钟，然后在银溶液中提拉涂膜，所述银溶液中Ag+量为TiO2的3％，按此比例称取硝酸银，先以微量水溶解，再加入油酸、丙酮搅拌半小时，注意所用油酸和丙酮的体积比为1∶2，且二者的总量为20毫升；将银溶液中涂膜后的制品于80～100℃干燥1小时，再于500～550℃下煅烧2小时即可。

Claims (2)

1、纳米TiO2载银抗菌薄膜的制造方法，其特征是在钛溶胶中加入银溶液后再行涂膜，具体步骤如下：
A、制备银溶液，按Ag+/TiO2＝3～6％的比例准备硝酸银，先以微量水溶解，再加入油酸和丙酮充分搅拌0.5小时，注意所用油酸和丙酮的体积比为1∶1或1∶2，且油酸和丙酮的总量为20毫升；
B、将制好的银溶液加入钛溶胶并充分搅拌0.5小时即得载银溶胶，用该溶胶对产品涂膜、干燥、煅烧后即得有载银抗菌涂膜层的产品，涂膜时使用提拉法，干燥温度80～150℃，时间1小时，煅烧温度450～550℃，时间2小时。
2、纳米TiO2载银抗菌薄膜的制造方法，其特征是产品在钛溶胶中涂膜干燥后再在银溶液中浸涂，具体步骤如下：
A、制品在钛溶胶中涂膜后于80～150℃下干燥20分钟；
B、按Ag+/TiO2＝3～6％的比例准备硝酸银，先以微量水溶解，再加入油酸和丙酮充分搅拌0.5小时，注意所用油酸和丙酮的体积比为1∶1或1∶2，且二者的总量为20毫升；
C、将A步骤所得制品于B步骤所得银溶液中提拉涂膜后于80～150℃下干燥1小时，再于450～550℃下煅烧2小时即可。
CNB2005100314921A 2005-04-28 2005-04-28 纳米TiO2载银抗菌薄膜的制造方法 Expired - Fee Related CN1311915C (zh)