CN1086710C - 冰箱、冷柜壳体 - Google Patents

冰箱、冷柜壳体 Download PDF

Info

Publication number
CN1086710C
CN1086710C CN98111227A CN98111227A CN1086710C CN 1086710 C CN1086710 C CN 1086710C CN 98111227 A CN98111227 A CN 98111227A CN 98111227 A CN98111227 A CN 98111227A CN 1086710 C CN1086710 C CN 1086710C
Authority
CN
China
Prior art keywords
refrigerator
component
housing
pattern
catalyzer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN98111227A
Other languages
English (en)
Other versions
CN1197918A (zh
Inventor
陈国民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN98111227A priority Critical patent/CN1086710C/zh
Publication of CN1197918A publication Critical patent/CN1197918A/zh
Application granted granted Critical
Publication of CN1086710C publication Critical patent/CN1086710C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

一种冰箱、冷柜壳体，由化工塑料制成，该化工塑料是一种A、B双组份硬质聚氨脂，A组份是由单体聚醚加入稳定剂、发泡剂、催化剂混合而成，各量的百分比是：单体聚醚(72.5～84.0)%；发泡剂(12.6～14.5)%；稳定剂(1.7～2.2)%；催化剂(1.7～10.8)%；B组份是多苯基多次甲基多异氰酸酯，也可以是二苯基甲烷二异氰酸酯，A∶B的量比为0.9～1.4∶1。

Description

冰箱、冷柜壳体
本发明涉及一种冰箱、冷柜壳体，主要是壳体的材料及应用该材料来制造壳体的方法。
传统的冰箱、冷柜壳体的材料是金属薄板、应用冲压等工艺来制作。应用黑色金属薄板，则会带来由于气氛而腐蚀及比重较大等问题。也有人提出过应用常规塑料来制造。这也有刚、强度不足的问题。
本发明的任务是提出一种冰箱壳体的新的化工塑料，重度小，刚、强度韧性好且耐腐。
本发明的技术方案是冰箱、冷柜壳体，由化工塑料制成，该化工塑料是一种A、B双组份硬质聚氨脂。A组分是由单体聚醚加入稳定剂、发泡剂、催化剂混合而成，各量的百分比是：单体聚醚(72.5～84.0)％；发泡剂(12.6～14.5)％；稳定剂(1.7～2.2)％；催化剂(1.7～10.8)％；B组分是多苯基多次甲基多异氰酸酯，也可以是二苯基甲烷二异氰酸酯。A∶B的量比为0.9～1.4∶1。它的制造方法是：一、将A组份、B组份按量比混合，二、浇注入冰箱、冷柜壳体的型模腔内，三、合模，在型模腔内发泡、固化、稳定，四、加温熟化，五、冷却脱模取出成品。
本发明技术方案完成了发明任务
图一是本发明冰箱、冷柜壳体的制造方法流程图。
以下结合附图详细叙述本发明
本发明冰箱、冷柜壳体由化工塑料制成，该化工塑料是一种A、B双组份硬质聚氨脂，A组份是由单体聚醚加入稳定剂、发泡剂、催化剂混合而成，各量的百分比是：单体聚醚(72.5～84.0)％；发泡剂(12.6～14.5)％；稳定剂(1.7～2.2)％；催化剂(1.7～10.8)％；B组份是多苯基多次甲基多异氰酸酯，也可以是二苯基甲烷二异氰酸酯，A∶B的量比为0.9～14∶1。
冰箱、冷柜壳体的制造方法是：一、将A组份、B组份按量比混合，二、浇注入冰箱、冷柜壳体的型模腔内，三、合模，在型模腔内发泡、固化、稳定，四、加热熟化，五、冷却脱模取出成品。
在将双组份材料浇注入冰箱、冷柜壳体的型模前，型模有预热工艺，双组份材料浇入时，型模内腔温度应不小于50℃。
A、B组份混合时，可以加入较短的玻璃丝或尼龙丝等纤维物，以提高壳体的强度及韧性。
在A、B组份浇注入型模前，型模腔内可预先放置组装嵌件。
A组份材料中稳定剂是硅油，发泡剂可以是141B，也可以是环戊烷；催化剂是胺类催化剂。
胺类催化剂可以是二甲基环己胺，也可以是三乙醇胺，也可以是2、4、6-二甲胺基甲基苯酚，也可以是三乙稀二胺。
A组份中的单体聚醚是由起始剂、催化剂、环氧丙烷、甘油四者聚合成的高分子聚合物，催化剂是碱性催化剂氢氧化钾，起始剂是含羟基化合物。
起始剂、催化剂、环氧丙烷、甘油的含量的百分比是：起始剂(10.3～18.8)％，催化剂(0.2～0.3)％，环氧丙烷(60.2～81.1)％，甘油(8.4～20.7)％。
作为起始剂的含羟基化合物可以是木糖醇，也可以是季戊四醇，也可以是己三醇，也可以是甘露醇。
在A、B组份混合时，可加入有各种颜色的色浆及阻燃剂，阻燃剂的加入量可以是总量的(10～15)％，阻燃剂可以是含磷、含氯、含溴的磷酸脂。色浆可根据壳体需要的颜色来决定加入的数量及种类。阻燃剂的加入提高了壳体的阻燃性。
实施例1、A组份制作：取单体聚醚840克，稳定剂硅油17克，发泡剂141B126克，催化剂二甲基环己胺17克，混合搅拌，制成A组份材料待用。
实施例2、A组份制作：取单体聚醚725克，稳定剂硅油22克，发泡剂环戊烷145克，催化剂二甲胺基甲基苯酚108克混合搅拌，制成A组份材料待用。
实施例3、A组份制作：取单体聚醚780克，稳定剂硅油20克，发泡剂环戊烷130克，催化剂三乙醇胺70克混合搅拌，制成A组份材料待用。
实施例4、按量比0.9∶1取由例1制备好的A组份，取B组份多苯基多次甲基多异氰酸酯，混合搅拌时加入玻璃丝后浇注入型模腔内，型模腔内温度为72℃，合模后发泡固化，稳定后加热熟化，加热温度140℃140分钟后，冷却至常温，脱模取出成品。
实施例5、按量比14∶1取由上例3制备好的A组份，取B组份为二苯基甲烷二异氰酸酯，加入阻燃剂12％，混合搅拌后浇注入型模腔内，型模腔内温度78℃，合模后发泡固化，稳定后加热熟化，加热温度150℃二小时后，冷却至常温，脱模取出成品。
实施例6、按量比1∶1取由例2制备好的A组份、B组份为二苯基甲烷二异氰酸脂，混合搅拌，加入尼龙丝，再添加阻燃剂10％，浇注入型模腔内，型模温度81℃，合模后发泡、固化、稳定后加热熟化，加热温度120℃100分钟后，冷却至常温，脱模取出样品。
将取出的样品作各种测试，得测试结果：
比    重      g/cm3：      0.4～1.2
冲击强度      kJ/m2：      ＞10
弯曲强度      MPa：         ＞30
阻  燃性      级：          V-O
收  缩率      ％：          0.25～0.4
热变形温度    ℃            87
吸 水 量      g/cm3：      0.001～0.01
为了脱模方便，在浇注前，型模可涂复脱模剂，只是脱模后要在成品上清除脱模剂。
为使产品美观，脱模的成品可再加修整及涂复漆层。

Claims (10)

1、一种冰箱、冷柜壳体，由化工塑料制成，其特征是：该化工塑料是一种A、B双组份硬质聚氨脂，A组份是由单体聚醚加入稳定剂、发泡剂、催化剂混合而成，各量的百分比是：单体聚醚(72.5～84.0)％；发泡剂(12.6～14.5)％；稳定剂(1.7～2.2)％；催化剂(1.7～10.8)％；B组份是多苯基多次甲基多异氰酸酯，也可以是二苯基甲烷二异氰酸酯，A∶B的量比为0.9～1 4∶1。
2、由权利要求1所述的冰箱、冷柜壳体，其特征是：它的制造方法是：一、将A组份、B组份按量比混合，二、浇注入冰箱、冷柜壳体的型模腔内，三、合模，在型模腔内发泡、固化、稳定，四、加热熟化，五、冷却脱模取出成品。
3、由权利要求2所述的冰箱、冷柜壳体，其特征是：在将双组份材料浇注入冰箱、冷柜壳体的型模前，型模有预热工艺，双组份材料浇入时，型模内腔温度应不小于50℃。
4、由权利要求2所述的冰箱、冷柜壳体，其特征是：在A、B组份浇注入型模前，型模腔内可预先放置组装嵌件。
5、由权利要求1所述的冰箱、冷柜壳体，其特征是：A组份材料中稳定剂是硅油，发泡剂可以是141B，也可以是环戊烷；催化剂是胺类催化剂。
6、由权利要求5所述的冰箱、冷柜壳体，其特征是：胺类催化剂可以是二甲基环己胺，也可以是三乙醇胺，也可以是2、4、6一二甲胺基甲基苯酚，也可以是三乙稀二胺。
7、由权利要求1所述的冰箱、冷柜壳体，其特征是：A组份中的单体聚醚是由起始剂、催化剂、环氧丙烷、甘油四者聚合成的高分子聚合物，催化剂是碱性催化剂氢氧化钾，起始剂是含羟基化合物。
8、由权利要求7所述的冰箱、冷柜壳体，其特征是：起始剂、催化剂、环氧丙烷、甘油的含量的百分比是起始剂(10.3～18.8)％，催化剂(0.2～0.3)％，环氧丙烷(60.2～81.1)％，甘油(8.4～20.7)％。
9、由权利要求7所述的冰箱、冷柜壳体，其特征是：作为起始剂的含羟基化合物可以是木糖醇，也可以是季戊四醇，也可以是己三醇，也可以是甘露醇。
10、由权利要求2所述的冰箱、冷柜壳体，其特征是：在A、B组份混合时，可加入有各种颜色的色浆及阻燃剂，阻燃剂的加入量可以是总量的(10～15)％，阻燃剂可以是含磷、含氯、含溴的磷酸脂。
CN98111227A 1998-04-03 1998-04-03 冰箱、冷柜壳体 Expired - Lifetime CN1086710C (zh)