CN108530034A - 一种满釉陶瓷及其制备方法 - Google Patents

一种满釉陶瓷及其制备方法 Download PDF

Info

Publication number
CN108530034A
CN108530034A CN201810678626.6A CN201810678626A CN108530034A CN 108530034 A CN108530034 A CN 108530034A CN 201810678626 A CN201810678626 A CN 201810678626A CN 108530034 A CN108530034 A CN 108530034A
Authority
CN
China
Prior art keywords
parts
glaze
green body
glazing
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201810678626.6A
Other languages
English (en)
Other versions
CN108530034B (zh
Inventor
张节成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Dehua Tao Yuan Ming Ceramic Culture Co Ltd
Original Assignee
Fujian Dehua Tao Yuan Ming Ceramic Culture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Dehua Tao Yuan Ming Ceramic Culture Co Ltd filed Critical Fujian Dehua Tao Yuan Ming Ceramic Culture Co Ltd
Priority to CN201810678626.6A priority Critical patent/CN108530034B/zh
Publication of CN108530034A publication Critical patent/CN108530034A/zh
Application granted granted Critical
Publication of CN108530034B publication Critical patent/CN108530034B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种满釉陶瓷及其制备方法，釉料包括以下重量份的原料：钾长石25‑28份、石英46‑52份、蒙脱石30‑35份、磁铁矿15‑18份、瓷石8‑12份、高温熔块6‑10份、白云石3‑5份、木鱼石2‑5份；高温熔块的化学百分含量为：SiO2：46‑50％、Al2O3：10‑15％、MgO：6‑8％、CaCO3：4‑5.6％、Na2O：3.2‑3.8％、Fe2O3：5.4‑6.2％、La2O3：1.5‑2.8％、BaO：1.8‑2.4％、ZnO：4.2‑4.8％、TiO2：0.8‑1.8％、Li2O：3.5‑4.2％、I.L：4‑5％，制得的陶瓷釉面光滑、不易伤到桌面，且不沾污垢、不吸味，易清洗。

Description

一种满釉陶瓷及其制备方法
技术领域
本发明属于陶瓷制备领域，具体涉及一种满釉陶瓷及其制备方法。
背景技术
陶瓷在我国有着十分悠久的历史，现如今已被应用在很多领域，特别是在日用品中，陶瓷制品更是随处可见，其制备工艺也早已在全世界范围内广泛使用，日用陶瓷俨然已成为人们日常生活中不可或缺的一部分，形形色色的餐具、茶具、各类洁具等随处可见，这些陶瓷大多美观大方，造型多样，传统的陶瓷有部分并未上釉，形象不美观，容易损伤桌面，或者陶瓷的表面上釉，但是底部并未上釉，且上釉技术中，由于釉料的质量不稳定，导致上釉后的陶瓷不美观，容易造成废品，不符合低碳环保的观念，有待进一步改进。
发明内容
本发明的目的是克服现有技术的缺点，提供一种釉料质量稳定，形象美观的满釉陶瓷，另一目的是提供一种制备上述满釉陶瓷的方法。
本发明采用如下技术方案：
一种满釉陶瓷，包括坯体和釉料，所述釉料包括以下重量份的原料：钾长石25-28份、石英46-52份、蒙脱石30-35份、磁铁矿15-18份、瓷石8-12份、高温熔块6-10份、白云石3-5份、木鱼石2-5份；
所述高温熔块的化学百分含量为：SiO2：46-50％、Al2O3：10-15％、MgO：6-8％、CaCO3：4-5.6％、Na2O：3.2-3.8％、Fe2O3：5.4-6.2％、La2O3：1.5-2.8％、BaO：1.8-2.4％、ZnO：4.2-4.8％、TiO2：0.8-1.8％、Li2O：3.5-4.2％、I.L：4-5％。
进一步的，所述坯体包括以下重量份的原料：长石18-25份、石英52-58份、高岭土25-28份、长辉石15-18份、方解石8-12份、电气石6-10份、盐土3-5份、竹粉2-4份、氧化铝5-8份、五氧化二钒3-5份、碳酸钙1-3份、氧化铈0.5-1.2份。
如上所述的一种满釉陶瓷的制备方法，包括如下步骤：
(1)、将釉料原料中的钾长石、石英和蒙脱石先自然风化5-7天，然后与其他原料按配比称重混合，经破碎机破碎，过筛后，湿球磨制得釉料；
(2)、将未施釉的坯体送入窑炉中，在760-800℃的温度下素烧；
(3)、对素烧后的坯体表面进行打磨、烘干；
(4)、在烘干后的坯体表面进行一次施釉，然后送入窑炉中，在1250-1280℃的温度下进行一次烧制，烧制时间为12.5-13.5h；
(5)、待一次烧制后的坯体冷却至室温后，进行二次施釉，并送入窑炉中，在1050-1080℃的温度下进行二次烧制，烧制时间为9.5-10.5h，冷却至室温，得满釉陶瓷。
进一步的，所述步骤(1)中，釉料湿球磨的条件为：料：球：水＝1:2-2.4:1.8-2，球磨时间为20-24h。
进一步的，所述坯体的制备方法包括如下步骤：
(1)、将坯体的原料按其配比称重后，混合破碎，过筛得粉料；
(2)、将制得粉料进行湿球磨，其中料：球：水＝1:1.6-2:1.2-1.6，球磨18-22小时制得泥料；
(3)、将泥料进行除气、陈泥后，干燥制成粗坯；
(4)、将粗坯经过粗修、细修、精修后得坯体。
进一步的，所述一次施釉的施釉方式为浸釉。
进一步的，所述二次施釉的施釉方式为浸釉。
进一步的，所述一次施釉的釉面层厚度为0.6-0.8mm。
进一步的，所述二次施釉的釉面层厚度为0.3-0.5mm。
由上述对本发明的描述可知，与现有技术相比，本发明的有益效果是：釉料以钾长石、石英和蒙脱石为基料，以高温熔块、磁铁矿、瓷石、白云石和木鱼石为辅，钾长石是熔剂原料，石英是瘠性原料，蒙脱石是可塑性原料，通过高温熔块保证制得的釉料在高温烧制时的质量稳定，使得烧制而成的陶瓷釉面光滑、不易伤到桌面，且不沾污垢、不吸味，易清洗。
具体实施方式
以下通过具体实施方式对本发明作进一步的描述。
一种满釉陶瓷，包括坯体和釉料；
釉料包括以下重量份的原料：钾长石25-28份、石英46-52份、蒙脱石30-35份、磁铁矿15-18份、瓷石8-12份、高温熔块6-10份、白云石3-5份、木鱼石2-5份；
具体的，高温熔块的化学百分含量为：SiO2：46-50％、Al2O3：10-15％、MgO：6-8％、CaCO3：4-5.6％、Na2O：3.2-3.8％、Fe2O3：5.4-6.2％、La2O3：1.5-2.8％、BaO：1.8-2.4％、ZnO：4.2-4.8％、TiO2：0.8-1.8％、Li2O：3.5-4.2％、I.L：4-5％。
坯体包括以下重量份的原料：长石18-25份、石英52-58份、高岭土25-28份、长辉石15-18份、方解石8-12份、电气石6-10份、盐土3-5份、竹粉2-4份、氧化铝5-8份、五氧化二钒3-5份、碳酸钙1-3份、氧化铈0.5-1.2份。
一种满釉陶瓷的制备方法，包括如下步骤：
(1)、将釉料原料中的钾长石、石英和蒙脱石先自然风化5-7天，然后与其他原料按配比称重混合，经破碎机破碎，过筛后，湿球磨制得釉料，其中，料：球：水＝1:2-2.4:1.8-2，球磨时间为20-24h；
(2)、将未施釉的坯体送入窑炉中，在760-800℃的温度下素烧2-4h；
(3)、对素烧后的坯体表面进行打磨、烘干；
(4)、在烘干后的坯体表面进行一次施釉，然后送入窑炉中，在1250-1280℃的温度下进行一次烧制，烧制时间为12.5-13.5h，其中，一次施釉的施釉方式为浸釉，釉面层厚度为0.6-0.8mm；
(5)、待一次烧制后的坯体冷却至室温后，进行二次施釉，并送入窑炉中，在1050-1080℃的温度下进行二次烧制，烧制时间为9.5-10.5h，冷却至室温，得满釉陶瓷，其中，二次施釉的施釉方式为浸釉，二次施釉的釉面层厚度为0.3-0.5mm。
具体的，坯体的制备方法包括如下步骤：
(1)、将坯体的原料按其配比称重后，混合破碎，过筛得粉料；
(2)、将制得粉料进行湿球磨，其中料：球：水＝1:1.6-2:1.2-1.6，球磨18-22小时制得泥料；
(3)、将泥料进行除气、陈泥后，干燥制成粗坯；
(4)、将粗坯经过粗修、细修、精修后得坯体。
实施例1
一种满釉陶瓷，包括坯体和釉料；
釉料包括以下重量份的原料：钾长石25份、石英52份、蒙脱石30份、磁铁矿18份、瓷石12份、高温熔块6份、白云石5份、木鱼石2份；
具体的，高温熔块的化学百分含量为：SiO2：46％、Al2O3：15％、MgO：6％、CaCO3：5.6％、Na2O：3.2％、Fe2O3：5.4％、La2O3：2.8％、BaO：1.8％、ZnO：4.2％、TiO2：1.8％、Li2O：4.2％、I.L：4％。
坯体包括以下重量份的原料：长石25份、石英52份、高岭土25份、长辉石18份、方解石8份、电气石10份、盐土3份、竹粉4份、氧化铝5份、五氧化二钒5份、碳酸钙1份、氧化铈1.2份。
一种满釉陶瓷的制备方法，包括如下步骤：
(1)、将釉料原料中的钾长石、石英和蒙脱石先自然风化7天，然后与其他原料按配比称重混合，经破碎机破碎，过筛后，湿球磨制得釉料，其中，料：球：水＝1:2:2，球磨时间为24h；
(2)、将未施釉的坯体送入窑炉中，在800℃的温度下素烧2h；
(3)、对素烧后的坯体表面进行打磨、烘干；
(4)、在烘干后的坯体表面进行一次施釉，然后送入窑炉中，在1280℃的温度下进行一次烧制，烧制时间为12.5h，其中，一次施釉的施釉方式为浸釉，釉面层厚度为0.6mm；
(5)、待一次烧制后的坯体冷却至室温后，进行二次施釉，并送入窑炉中，在1080℃的温度下进行二次烧制，烧制时间为9.5h，冷却至室温，得满釉陶瓷，其中，二次施釉的施釉方式为浸釉，二次施釉的釉面层厚度为0.3mm。
具体的，坯体的制备方法包括如下步骤：
(1)、将坯体的原料按其配比称重后，混合破碎，过筛得粉料；
(2)、将制得粉料进行湿球磨，其中料：球：水＝1:2:1.6，球磨22小时制得泥料；
(3)、将泥料进行除气、陈泥后，干燥制成粗坯；
(4)、将粗坯经过粗修、细修、精修后得坯体。
所述满釉陶瓷经试验获得如下的性能参数：
抗弯强度：850MPa；
断裂韧性：35MPa/m；
维氏硬度：93GPa；
通过上述试验数据可知，本发明制得满釉陶瓷强度高、韧性好、硬度高，相比于现有技术的陶瓷相比，强度高、韧性好、硬度高、釉面光滑、不易伤到桌面，且不沾污垢、不吸味，易清洗，其生产成本低，且能达到实际生产应用中所需的各项性能。
实施例2
一种满釉陶瓷，包括坯体和釉料；
釉料包括以下重量份的原料：钾长石28份、石英46份、蒙脱石35份、磁铁矿15份、瓷石8份、高温熔块10份、白云石3份、木鱼石5份；
具体的，高温熔块的化学百分含量为：SiO2：50％、Al2O3：10％、MgO：8％、CaCO3：4％、Na2O：3.8％、Fe2O3：6.2％、La2O3：1.5％、BaO：2.4％、ZnO：4.8％、TiO2：0.8％、Li2O：3.5％、I.L：5％。
坯体包括以下重量份的原料：长石18份、石英58份、高岭土28份、长辉石15份、方解石12份、电气石6份、盐土5份、竹粉2份、氧化铝8份、五氧化二钒3份、碳酸钙3份、氧化铈0.5份。
一种满釉陶瓷的制备方法，包括如下步骤：
(1)、将釉料原料中的钾长石、石英和蒙脱石先自然风化5天，然后与其他原料按配比称重混合，经破碎机破碎，过筛后，湿球磨制得釉料，其中，料：球：水＝1:2.4:1.8，球磨时间为20h；
(2)、将未施釉的坯体送入窑炉中，在760℃的温度下素烧4h；
(3)、对素烧后的坯体表面进行打磨、烘干；
(4)、在烘干后的坯体表面进行一次施釉，然后送入窑炉中，在1250℃的温度下进行一次烧制，烧制时间为13.5h，其中，一次施釉的施釉方式为浸釉，釉面层厚度为0.8mm；
(5)、待一次烧制后的坯体冷却至室温后，进行二次施釉，并送入窑炉中，在1050℃的温度下进行二次烧制，烧制时间为10.5h，冷却至室温，得满釉陶瓷，其中，二次施釉的施釉方式为浸釉，二次施釉的釉面层厚度为0.5mm。
具体的，坯体的制备方法包括如下步骤：
(1)、将坯体的原料按其配比称重后，混合破碎，过筛得粉料；
(2)、将制得粉料进行湿球磨，其中料：球：水＝1:1.6:1.2，球磨18小时制得泥料；
(3)、将泥料进行除气、陈泥后，干燥制成粗坯；
(4)、将粗坯经过粗修、细修、精修后得坯体。
所述满釉陶瓷经试验获得如下的性能参数：
抗弯强度：862MPa；
断裂韧性：37MPa/m；
维氏硬度：92GPa；
通过上述试验数据可知，本发明制得满釉陶瓷强度高、韧性好、硬度高，相比于现有技术的陶瓷相比，强度高、韧性好、硬度高、釉面光滑、不易伤到桌面，且不沾污垢、不吸味，易清洗，其生产成本低，且能达到实际生产应用中所需的各项性能。
实施例3
一种满釉陶瓷，包括坯体和釉料；
釉料包括以下重量份的原料：钾长石26份、石英50份、蒙脱石32份、磁铁矿16份、瓷石10份、高温熔块8份、白云石4份、木鱼石4份；
具体的，高温熔块的化学百分含量为：SiO2：48％、Al2O3：12％、MgO：7％、CaCO3：4.9％、Na2O：3.6％、Fe2O3：5.8％、La2O3：2.2％、BaO：2.2％、ZnO：4.5％、TiO2：1.4％、Li2O：3.9％、I.L：4.5％。
坯体包括以下重量份的原料：长石21份、石英56份、高岭土26份、长辉石16份、方解石10份、电气石8份、盐土4份、竹粉3份、氧化铝7份、五氧化二钒4份、碳酸钙2份、氧化铈0.8份。
一种满釉陶瓷的制备方法，包括如下步骤：
(1)、将釉料原料中的钾长石、石英和蒙脱石先自然风化6天，然后与其他原料按配比称重混合，经破碎机破碎，过筛后，湿球磨制得釉料，其中，料：球：水＝1:2.2:1.9，球磨时间为22h；
(2)、将未施釉的坯体送入窑炉中，在780℃的温度下素烧3h；
(3)、对素烧后的坯体表面进行打磨、烘干；
(4)、在烘干后的坯体表面进行一次施釉，然后送入窑炉中，在1265℃的温度下进行一次烧制，烧制时间为13h，其中，一次施釉的施釉方式为浸釉，釉面层厚度为0.7mm；
(5)、待一次烧制后的坯体冷却至室温后，进行二次施釉，并送入窑炉中，在1070℃的温度下进行二次烧制，烧制时间为10h，冷却至室温，得满釉陶瓷，其中，二次施釉的施釉方式为浸釉，二次施釉的釉面层厚度为0.4mm。
具体的，坯体的制备方法包括如下步骤：
(1)、将坯体的原料按其配比称重后，混合破碎，过筛得粉料；
(2)、将制得粉料进行湿球磨，其中料：球：水＝1:1.8:1.4，球磨20小时制得泥料；
(3)、将泥料进行除气、陈泥后，干燥制成粗坯；
(4)、将粗坯经过粗修、细修、精修后得坯体。
所述满釉陶瓷经试验获得如下的性能参数：
抗弯强度：868MPa；
断裂韧性：36MPa/m；
维氏硬度：94GPa；
通过上述试验数据可知，本发明制得满釉陶瓷强度高、韧性好、硬度高，相比于现有技术的陶瓷相比，强度高、韧性好、硬度高、釉面光滑、不易伤到桌面，且不沾污垢、不吸味，易清洗，其生产成本低，且能达到实际生产应用中所需的各项性能。
其中，I.L指烧失量；
釉料以钾长石、石英和蒙脱石为基料，以高温熔块、磁铁矿、瓷石、白云石和木鱼石为辅，钾长石是熔剂原料，石英是瘠性原料，蒙脱石是可塑性原料，通过高温熔块保证制得的釉料在高温烧制时的质量稳定，使得烧制而成的陶瓷釉面光滑、不易伤到桌面，且不沾污垢、不吸味，易清洗。
以上所述，仅为本发明的较佳实施例而已，故不能以此限定本发明实施的范围，即依本发明申请专利范围及说明书内容所作的等效变化与修饰，皆应仍属本发明专利涵盖的范围内。

Claims (9)

1.一种满釉陶瓷，包括坯体和釉料，其特征在于：所述釉料包括以下重量份的原料：钾长石25-28份、石英46-52份、蒙脱石30-35份、磁铁矿15-18份、瓷石8-12份、高温熔块6-10份、白云石3-5份、木鱼石2-5份；
所述高温熔块的化学百分含量为：SiO2：46-50％、Al2O3：10-15％、MgO：6-8％、CaCO3：4-5.6％、Na2O：3.2-3.8％、Fe2O3：5.4-6.2％、La2O3：1.5-2.8％、BaO：1.8-2.4％、ZnO：4.2-4.8％、TiO2：0.8-1.8％、Li2O：3.5-4.2％、I.L：4-5％。
2.根据权利要求1所述的一种满釉陶瓷，其特征在于：所述坯体包括以下重量份的原料：长石18-25份、石英52-58份、高岭土25-28份、长辉石15-18份、方解石8-12份、电气石6-10份、盐土3-5份、竹粉2-4份、氧化铝5-8份、五氧化二钒3-5份、碳酸钙1-3份、氧化铈0.5-1.2份。
3.根据权利要求1或2所述的一种满釉陶瓷的制备方法，其特征在于：包括如下步骤：
(1)、将釉料原料中的钾长石、石英和蒙脱石先自然风化5-7天，然后与其他原料按配比称重混合，经破碎机破碎，过筛后，湿球磨制得釉料；
(2)、将未施釉的坯体送入窑炉中，在760-800℃的温度下素烧；
(3)、对素烧后的坯体表面进行打磨、烘干；
(4)、在烘干后的坯体表面进行一次施釉，然后送入窑炉中，在1250-1280℃的温度下进行一次烧制，烧制时间为12.5-13.5h；
(5)、待一次烧制后的坯体冷却至室温后，进行二次施釉，并送入窑炉中，在1050-1080℃的温度下进行二次烧制，烧制时间为9.5-10.5h，冷却至室温，得满釉陶瓷。
4.根据权利要求3所述的一种满釉陶瓷的制备方法，其特征在于：所述步骤(1)中，釉料湿球磨的条件为：料：球：水＝1:2-2.4:1.8-2，球磨时间为20-24h。
5.根据权利要求3所述的一种满釉陶瓷的制备方法，其特征在于：所述坯体的制备方法包括如下步骤：
(1)、将坯体的原料按其配比称重后，混合破碎，过筛得粉料；
(2)、将制得粉料进行湿球磨，其中料：球：水＝1:1.6-2:1.2-1.6，球磨18-22小时制得泥料；
(3)、将泥料进行除气、陈泥后，干燥制成粗坯；
(4)、将粗坯经过粗修、细修、精修后得坯体。
6.根据权利要求3所述的一种满釉陶瓷的制备方法，其特征在于：所述一次施釉的施釉方式为浸釉。
7.根据权利要求3所述的一种满釉陶瓷的制备方法，其特征在于：所述二次施釉的施釉方式为浸釉。
8.根据权利要求3所述的一种满釉陶瓷的制备方法，其特征在于：所述一次施釉的釉面层厚度为0.6-0.8mm。
9.根据权利要求3所述的一种满釉陶瓷的制备方法，其特征在于：所述二次施釉的釉面层厚度为0.3-0.5mm。
CN201810678626.6A 2018-06-27 2018-06-27 一种满釉陶瓷及其制备方法 Active CN108530034B (zh)