CN108410100A - 竹塑复合板材配方 - Google Patents
竹塑复合板材配方 Download PDFInfo
- Publication number
- CN108410100A CN108410100A CN201810347333.XA CN201810347333A CN108410100A CN 108410100 A CN108410100 A CN 108410100A CN 201810347333 A CN201810347333 A CN 201810347333A CN 108410100 A CN108410100 A CN 108410100A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo
- foaming
- plastic combined
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种竹塑复合板材配方,包括竹塑发泡层、花纹层、UV涂层,其中竹塑发泡层配方质量份组成为:聚氯乙烯(PVC)树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。本发明能实现毛竹的规模化利用。
Description
技术领域
本发明涉及一种高分子复合材料配方,特别是一种竹塑复合板材配方。
背景技术
PVC板材具有无甲醇、防腐蚀、重量轻、隔音、隔热等特点被广泛使用,大量毛竹未得到充分利用,将PVC、毛竹复合制成复合材料,能实现毛竹的规模化利用。
发明内容
本发明针对现有技术的不足,提出一种能实现毛竹的规模化利用的竹塑复合板材配方。
本发明通过下述技术方案实现技术目标。
竹塑复合板材配方,包括竹塑发泡层、花纹层、UV涂层,其改进之处在于:其中竹塑发泡层配方质量份组成为:聚氯乙烯(PVC) 树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC 发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。
本发明与现有技术相比,具有以下积极效果:
1、将PVC、毛竹复合制成复合材料,能实现毛竹规模化利用。
2、添加纳米活性碳酸钙,提高本发明的综合性能,而且减少制造成本。
具体实施方式
下面结合实施例对本发明作进一步说明。
竹塑复合板材配方,包括竹塑发泡层、花纹层、UV涂层,其中竹塑发泡层配方质量份组成为:聚氯乙烯(PVC) 树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC 发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。
Claims (1)
1.一种竹塑复合板材配方,包括竹塑发泡层、花纹层、UV涂层,其特征在于:其中竹塑发泡层配方质量份组成为:聚氯乙烯(PVC) 树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC 发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。