CN108314986A - 粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体及锂电池用外包装 - Google Patents
粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体及锂电池用外包装 Download PDFInfo
- Publication number
- CN108314986A CN108314986A CN201810088501.8A CN201810088501A CN108314986A CN 108314986 A CN108314986 A CN 108314986A CN 201810088501 A CN201810088501 A CN 201810088501A CN 108314986 A CN108314986 A CN 108314986A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- adhesive compositions
- lithium battery
- resin
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供树粘合剂用树脂,该树脂调制成粘合剂组成物,该粘合剂树脂组成物对高分子薄膜,金属箔等各种基材显示良好的粘接性,作为粘合剂层,通过卷对卷的工艺制造层状贴合型复合材料,用于软包装型锂电池的外包装。该高分子复合材料显示出良好的耐电解液腐蚀性,耐高温高湿水解性,耐化学药品性,耐热性,水蒸气阻隔性等良好特性。
Description
技术领域
本发明属于电池包装用膜材料技术领域,尤其涉及一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体及锂电池用外包装。
背景技术
聚氨酯树脂,因其独特的分子结构而具有较高的内聚能,可调的柔软度,与金属、木材、纤维、橡胶、塑料等极性表面存在极强的分子间相互作用,在涂装、包装、衣料服饰、电机、汽车以及建筑等领域作为粘合剂被广泛应用。
作为包装用途的聚氨酯型粘合剂,用在诸如食品,药品等保管保存用袋状包装材料的制造和使用过程中。这类袋状包装材料,通常选用铝箔等金属箔与塑料高分子膜,通过粘合剂形成层状贴合型复合材料。该复合材料具有遮光隔热,耐热,阻隔气体,以及耐受被包装物等特性。在新能源等产业领域,锂离子电池外包装材料选用上述的层状贴合型高分子复合材料制成袋状软包装体,与通常的金属壳相比,因其具有小型化,轻量化,超薄化,成型加工容易等特点,得到了极大的关注。
构成锂离子电池的重要组成成分之一的电解液,举例来说,是由LiPF6,LiBF4等极性锂盐溶解在碳酸脂等非水溶剂中构成。作为电解质的LiPF6,LiBF4等极性锂盐,遇水发生反应生成氟化氢。一旦生成氟化氢,构成电池的金属材料、电极材料会受到腐蚀,作为外包装的层状贴合型复合材料也因氟化氢造成层间粘合性下降而导致产品不良。为了解决该问题,用于锂电池的包装材料与通常的食品药品包装会有很大的区别。其层状构成依次采用,聚酯/尼龙构成的外层(耐热性树脂层),防止水分/氧气外部侵入及遮光用的铝箔作为阻隔层,以及聚烯烃树脂构成的内层(热封层)。特别是内层和阻隔层之间的粘合剂层(内层粘合剂层),基于锂电池的安全性及长期使用寿命考量,必须满足耐电解液性,水汽阻隔性,及耐湿热性等严格的指标。
相关技术方面,酸改性聚烯烃类等热塑性树脂,作为内层粘合剂,通过热熔挤出贴合工艺(热法)制造所得的锂电池软包装材料已被报道,使用溶液涂布的干法复合工艺所需的粘合剂也有相关的报道。但是,热法制造工艺存在装置复杂,制造效率低等问题。干法工艺中使用通用的聚酯型聚氨酯粘合剂,耐电解液性能尚有不足。一部分报道称使用聚烯烃多元醇以提高耐电解液性,由于其高昂的成本及供应受限等问题,并未引起产业界的关注。有些报道中,相关的耐热性,粘接强度的经时变化,粘结强度保持率,及复合材料的加工特性并未触及。
发明内容
本发明的目的是提供一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体及锂电池用外包装,其能通过高分子量聚酯制造粘合剂进而制造锂电池用外包装材料的方式,达到应用于锂电池包装的目的。本发明具有包装材料制造简单方便,以及应用于电池效果好,包装材料本身耐电解液腐蚀性、耐高温高湿水解性、耐化学药品性以及耐热性良好的优点。
本发明解决上述问题采用的技术方案是:粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,从外到内依次由耐热树脂薄膜层,外侧粘合剂层,金属箔阻隔层,内侧粘合剂层以及热塑性密封层组成,构成锂离子电池用软包装复合膜,所述内侧粘合剂层的粘合剂重量组成比例为粘结剂树脂:环氧树脂:固化剂=100:1-10:1-10,粘合剂层的厚度为1-10μm。
进一步优选的技术方案在于:所述粘结剂树脂为聚酯多元醇,其中芳香族多元酸含量为20-50mol%,脂肪族多元酸含量为50-80mol%,且至少包含一种碳原子数大于3的所述脂肪族多元醇,所述聚酯多元醇为的数均分子量为5000-50000,Tg小于20℃,酸值AV小于2mgKOH/g。
进一步优选的技术方案在于:所述粘合剂树脂为所述聚酯多元醇经过异氰酸酯改性所得的聚氨酯型聚酯多元醇,其数均分子量为5000-50000,Tg20℃以下。
进一步优选的技术方案在于:所述聚酯多元醇以及聚氨酯型聚酯多元醇,其组成中的脂肪族多元酸,至少有一种为二聚酸型脂肪族二羧酸,其组成比为50-80mol%。
进一步优选的技术方案在于:所述环氧树脂使用环氧值EEW为100-1000的双酚A型,双酚F型,双酚E型环氧树脂的一种或几种混合物。
进一步优选的技术方案在于:所述固化剂选用多官能团异氰酸酯类或者多官能团密胺类中的至少一种。
进一步优选的技术方案在于:所述外侧粘合剂层选择与所述内侧粘合剂层相同的组成成分。
一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体制造的锂电池用外包装材料,所述粘合剂组成物调制成涂布液,涂布到基材上,加热干燥后,通过卷对卷干法复合工艺获得层状贴合型复合材料。
进一步优选的技术方案在于:所述锂电池用外包装材料经过冷深冲加工及热封工艺形成锂电池包装袋。
进一步优选的技术方案在于:所述锂电池包装袋构成软包锂离子电池;所述锂电池包装袋用于数码电池,电动汽车及储能领域。
本发明的粘合剂组成物,由粘合剂用树脂作为必须成分,配合相应的固化剂及环氧树脂构成,以下为详细的说明:
1)粘合剂用树脂
本发明的粘合剂用树脂,特指多元酸及多元醇经过脱水缩合及酯交换反应等过程所得到的聚酯多元醇类,以及进一步的通过化学反应得到的改性聚酯多元醇类。现描述说明如下:
(1)多元酸类,比如芳香族多元酸,包括邻苯二甲酸,间苯二甲酸,对苯二甲酸,2,6-萘二甲酸,邻苯二甲酸酐,偏苯三酸酐等。优选间苯二甲酸,对苯二甲酸,偏苯三酸酐;脂肪族多元酸,包括乙二酸(草酸),1,3-丙二酸,1,4-丁二酸,1,5-戊二酸,1,6-己二酸,1,7-庚二酸,1,8-辛二酸,1,9-壬二酸,1,10-癸二酸等。植物来源的碳数36,含有非共轭的不饱和双键二聚酸。碳数54的三聚酸,以及加氢反应得到的完全氢化二聚酸,完全氢化三聚酸等。优选1,6-己二酸,1,8-辛二酸,1,10-癸二酸及二聚酸,三聚酸,氢化二聚酸,氢化三聚酸等。其中的组成比,芳香族多元酸20~50mol%,脂肪族多元酸50~80mol%,至少有一种脂肪族多元酸选自二聚酸,三聚酸,氢化二聚酸或氢化三聚酸。本发明优选氢化二聚酸,氢化二聚酸的含量20%摩尔以上为宜,优选30%摩尔以上。
(2)多元醇类,包括乙二醇,一缩二乙二醇,1,3-丙二醇,2-甲基-1,3-丙二醇,2,2-二甲基1,3-丙二醇,1,4-丁二醇,1,5-戊二醇,3-甲基-1,5-戊二醇,1,6-己二醇,1,7-庚二醇,1,8-辛二醇,1,9-壬二醇,1,10-癸二醇等小分子二醇,以及二聚酸还原所得碳数36的二元醇,分子量为500以上的聚烯烃二醇/完全氢化的聚烯烃二醇等。基于树脂物性调整等考量,优选碳原子数3以上多元醇。
(3)聚合反应,多元酸和多元醇混合后,按通常工艺高温下脱水缩合,得到聚酯多元醇。为提高反应速率可选用适当的催化剂,采用高温真空等条件,通过酯交换反应提高分子量。 所得的聚酯多元醇,其数均分子量5000~50000为宜,数均分子量低于5000,耐水解性不足;数均分子量高于50000,粘度过高,制造工艺复杂,易发生涂布不良,进一步优选数均分子量9000~30000。酸值2以下为宜,酸值高于2,树脂自身的耐水解性不足,优选酸值小于1。玻璃化温度Tg优选20℃以下。
(4)改性聚酯多元醇,前述聚酯多元醇树脂与下列至少一种多异氰酸酯通过改性反应得到聚氨酯型聚酯多元醇。 所选用的多异氰酸酯包括,1,4-四亚甲基二异氰酸酯,1,5-五亚甲基二异氰酸酯(PDI),1,6-六亚甲基二异氰酸酯(HDI),2,2,4-三甲基-1,6-六亚甲基二异氰酸酯。2,4,4-三甲基-1,6-六亚甲基二异氰酸酯,二聚酸型二异氰酸酯等脂肪族二异氰酸酯;1,4-环己烷基二异氰酸酯,异佛尔酮二异氰酸酯(IPDI),1-甲基-2,4-环己烷基二异氰酸酯,1-甲基-2,6-环己烷基二异氰酸酯,4,4-环己烷基甲烷二异氰酸酯,1,3-二(异氰酸酯基亚甲基)环己烷,1,4-二(异氰酸酯基亚甲基)环己烷等脂环族二异氰酸酯; 2,4(or2,6)-二异氰酸酯基甲苯(TDI),间二异氰酸酯基苯,对二异氰酸酯基苯,4,4-联苯基二异氰酸酯,4,4-二苯基甲烷二异氰酸酯(MDI),1,3-二苯甲基二异氰酸(XDI),二烷基二苯基甲烷二异氰酸酯,四烷基二苯基甲烷二异氰酸酯,1,5-萘基二异氰酸酯,3,3-二甲基-4,4-联苯基二异氰酸酯等芳香族二异氰酸酯类。进一步还包括异氰酸酯通过改性得到的加成体,三聚体,缩二脲,脲基甲酸酯型等,以及多聚MDI,末端异氰酸酯型预聚体等。优选异佛尔酮二异氰酸酯(IPDI),2,4(or2,6)-二异氰酸酯基甲苯(TDI),4,4-二苯基甲烷二异氰酸酯(MDI),1,3-二苯甲基二异氰酸(XDI)。所得的聚氨酯型聚酯多元醇数均分子量5000~50000为宜,优选9000~30000。游离异氰酸酯单体含量为0.1%以下为宜。
2)粘合剂组成物
本发明的粘合剂组成物包括本发明的粘合剂用树脂,配合优选的市售环氧树脂,市售多异氰酸酯型固化剂,市售的密胺型固化剂,溶剂,必要时加入添加剂构成。
(1)环氧树脂
本发明的粘合剂组成物,优选使用环氧值EEW为100~1000的市售双酚A型,双酚F型,双酚E型环氧树脂的一种或几种,以及相应的市售氢化双酚A型,氢化双酚F型,氢化双酚E型环氧树脂的一种或几种。进一步的优选双酚A型环氧树脂。环氧值大于1000,分子量偏大,与主树脂的相容性下降,粘结强度及耐候性不佳。
(2)固化剂
本发明的粘合剂组成物,使用多官能团异氰酸酯型固化剂,多官能团密胺型固化剂,基于工艺条件,优选多官能团异氰酸酯型固化剂。包括1,6-六亚甲基二异氰酸酯(HDI),异佛尔酮二异氰酸酯(IPDI),2,4(or2,6)-二异氰酸酯基甲苯(TDI), 4,4-二苯基甲烷二异氰酸酯(MDI),1,3-二苯甲基二异氰酸(XDI)等通过改性得到的加成体,三聚体,缩二脲,脲基甲酸酯等多官能团异氰酸酯型固化剂,多聚MDI,市售末端异氰酸酯型的预聚体,以及使用本发明的聚酯多元醇,聚氨酯型聚酯多元醇通过改性得到的末端异氰酸酯型预聚体等等。作为固化剂,可以单独一种或者两种以上混合使用。从反应性及供应难易考量,优选HDI,IPDI的三聚体型,TDI的加成物型。
本发明的粘合剂组成物,其重量组成比例为:粘合剂树脂/环氧树脂/固化剂=100/1~10/1~10,粘合剂层厚度为1~10微米。
(3)溶剂
本发明的粘合剂组成物,使用粘合剂树脂,环氧树脂与固化剂直接混合所得无溶剂型,也可以使用添加有机溶剂调整所得溶液型。作为有机溶剂,对异氰酸酯应具有低的反应活性或者不反应为宜。具体举例如下:丙酮,甲乙酮,甲基异丁基酮,环己酮等酮类,甲苯,二甲苯等芳香烃类,正己烷,正庚烷,环己烷等脂肪烃/脂环烃类,二恶烷,四氢呋喃等醚类,乙酸乙酯,乙酸丁酯,乙酸异丁酯等酯类,N,N-二甲基甲酰胺,N,N-二甲基乙酰胺,N-甲基吡咯烷酮等酰胺类等。本发明优选乙酸乙酯,乙酸丁酯等酯类。上述溶剂可单独使用,或者两种以上混合使用。
4) 添加剂
本发明的粘合剂组成物,必要时可以加入二氧化钛,二氧化硅,滑石粉,碳酸钙,硅藻土,硫酸钡等无机类添加剂;松香树脂,萜烯树脂,石油树脂等增粘树脂类;以及紫外吸收剂,紫外稳定剂,抗氧化剂,阻燃剂,滑剂,流平剂,消泡剂,分散剂,防沉降剂等等。
本发明的粘合剂组成物配合溶剂,调整成一定的固含量及适宜粘度的溶液,作为涂布液用于卷对卷的涂布工艺中。固含量以15~50%为宜,粘度为50~1000mPas为宜,固含量过低或粘度过低,导致使用大量的有机溶剂,固含量过高或粘度过高,则导致粘结强度波动,涂布外观不良。
3)复合材料及锂电池外包装材料
使用本发明的粘合剂用树脂,粘合剂组成物作为必须材料可以用于层间粘合剂,通过卷对卷工艺得到层状复合材料,特别适合作为锂电池用外包装材料。锂电池用外包装材料从外到内依次为耐热高分子膜/外层粘合剂/金属箔/内层粘合剂/热塑性高分子膜。现分别描述如下:
(1)耐热高分子膜作为最外层,在锂电池外包装材中赋予成型性,同时在电池制造(热融合)过程及使用过程中赋予耐热性及耐刺穿性能。本发明中选择市售的单层或者多层复合的耐热性高分子膜,比如聚酯膜,尼龙膜及聚酰亚胺膜等。优选聚酯膜及尼龙膜。厚度10~40微米为宜,优选15~25微米。
(2)外层粘合剂 通过外层粘合剂把耐热高分子膜与芯材金属箔贴合在一起,可以优选市售的双组份聚氨酯型粘合剂,环氧型粘合剂,丙烯酸型粘合剂,硅胶型粘合剂等,进一步优选双组份聚氨酯型粘合剂。也可以选用本发明的粘合剂组成物构成的粘合剂层。粘合剂层厚度以1~10微米为宜。
(3)金属箔作为芯材赋予阻隔性及成型性。既可以防止水气,氧气等侵入电池内部,又能够遮光防止电解液劣化,同时要满足加工成型性。金属箔选择纯铝箔,铝-铁合金箔,铝-锰合金箔,铜箔,不锈钢箔等为宜,进一步优选铝-铁合金箔。必要时,金属箔表面可选择市售铬酸液等做钝化处理,以提高耐腐蚀性及密着性。金属箔厚度以10~50微米为宜,优选20~40微米。厚度过薄,轧制加工中的缺陷,表面针孔等过多,阻隔性不佳。厚度过厚,作为电池的重量比能量不适宜。
(4)内层粘合剂 使用本发明的粘合剂组成物构成的涂布液,通过涂布干燥过程得到粘合剂层,进而通过卷对卷工艺实现贴合。粘合剂层厚度以1~10微米为宜。
(5)热塑性高分子膜 作为最内层材料,具有耐电解液性质,以及热熔密封性。材料方面,优选市售聚烯烃类薄膜为宜,如聚乙烯,聚丙烯,乙烯-丙烯-丁二烯共聚物等,厚度30~100微米为宜,过薄,密封阻隔性不良,过厚则加工性不良。为提高粘合性能,该热塑性高分子膜与粘合剂贴合面宜采用单面电晕处理,优选表面达因值38以上。
4)外包装材料制造工艺
采用滚涂,刮涂,喷涂等方式,在金属箔阻隔层的单面涂布本发明的粘合剂组成物溶液,干燥后与外层耐热高分子膜贴合得到半成品。接下来,在该半成品的金属箔的另一面涂布本发明的粘合剂组成物溶液,干燥后与热封性内层膜的电晕处理面贴合得到层状贴合型高分子复合膜成品。
另一方面,也可以采用在外层耐热高分子膜上预先涂布本发明的粘合剂组成物溶液,干燥后和金属箔贴合而得到半成品。其余工艺同前。
粘合剂层的厚度1~10微米为宜,优选2~8微米。厚度低于1微米,粘接性不足,粘合剂层倾向于生成孔洞。此外,粘合剂层厚度超过10微米,层状复合材料的成型性呈现恶化的趋势。
涂布贴合工艺,或者称干法复合工艺,其烘干温度,贴合温度,贴合压力,依照构成材质等做适当调整。为完成交联固化反应,干法复合后经过适当的熟化过程为宜。温度30~60℃,时间3天~1周。
本发明的目的是提供一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体及锂电池用外包装,其能通过高分子量聚酯制造粘合剂进而制造锂电池用外包装材料的方式,达到应用于锂电池包装的目的。本发明具有包装材料制造简单方便,以及应用于电池效果好,包装材料本身耐电解液腐蚀性、耐高温高湿水解性、耐化学药品性以及耐热性良好的优点。
具体实施方式
以下所述仅为本发明的较佳实施例,非对本发明的范围进行限定。
合成例1:在本合成例中,在配置搅拌机,温度计,冷凝管,及氮气导管的四口反应瓶中,依次加入间苯二甲酸(IPA)166.克(1.0mol) ,1,6-己二醇(HDO)177.3克(1.5mol),2-甲基-1,3-丙二醇(MPG ) 90.1克 (1mol)及催化剂钛酸四丁酯0.1克(约0.3mmol),通氮气下,180-220度进行脱水酯化反应。待除去约36克定量生成的水后,加入氢化二聚酸(HDA)560.9克(1mol),220℃下启动高真空,40分钟内降至约15Pa,进一步酯交换反应得到数均分子量约11500的聚酯多元醇a。组成为IPA/HDA//HDO/MPG=50/50//65/35。(如表1所示)
合成例2:使用3-甲基-1,5-戊二醇(MPD)118.2.克(1.0mol)代替合成例1中的2-甲基-1,3-丙二醇(MPG),其他与合成例1相同,得到数均分子量约18000的聚酯多元醇b。组成为IPA/HDA//HDO/MPD=50/50//55/45。
合成例3:在配置搅拌机,温度计,冷凝管,及氮气导管的四口反应瓶中,依次加入间苯二甲酸(IPA)83.1克(0.5mol) ,1,6-己二醇(HDO)177.3克(1.5 mol),2-甲基-1,3-丙二醇(MPG ) 90.1克 (1.0 mol)及催化剂钛酸四丁酯0.1克(约0.3mmol),通氮气下 ,180-220度进行脱水酯化反应。待除去约18克定量生成的水后,加入氢化二聚酸(HDA)841.4克(1.5mol),220℃下启动高真空,40分钟内降至约15Pa,进一步酯交换反应得到数均分子量约12000的聚酯多元醇c。组成为IPA/HDA//HDO/MPG=25/75//67/33,其他未提及部分与合成例1相同。
合成例4:使用2-甲基-1,5-戊二醇(MPD)118.2克(1.0mol)代替合成例3中的2-甲基-1,3-丙二醇(MPG),其他与合成例3相同,得到数均分子量约16000的聚酯多元醇d。组成为IPA/HDA//HDO/MPD=25/75//58/42。
合成例5:在配置搅拌机,温度计,冷凝管,及氮气导管的四口反应瓶中,依次加入氢化二聚酸(HDA) 1121.克(2.0mol),1,6-己二醇(HDO)177.3克(1.5 mol),2-甲基-1,3-丙二醇(MPG) 90.1克 (1.0 mol)及催化剂钛酸四丁酯0.1克(约0.3mmol),通氮气下 ,180-220度进行脱水酯化反应。待除去约36克定量生成的水后, 220℃下启动高真空,40分钟内降至约15Pa,进一步酯化得到数均分子量约14800的聚酯多元醇e。组成为HDA//HDO/MPG=100//66/34,其他未提及部分与合成例1相同。
合成例6:使用己二酸146.1克(1mol)代替合成例1中的氢化二聚酸(HDA),其他与合成例1相同,得到数均分子量约10000的聚酯多元醇f。组成为IPA/AA//HDO/MPG=50/50//65/35。
合成例7:使用癸二酸202.3克(1mol)代替合成例1中的氢化二聚酸(HDA),其他与合成例1相同,得到数均分子量约11000的聚酯多元醇g。组成为IPA/SeA//HDO/MPG=50/50//67/33。
合成例8:称取500克(约0.1mol)合成例1中所得聚酯多元醇a,加入二苯基甲烷二异氰酸酯(MDI)7.5克(0.03mol),催化剂辛酸亚锡0.01克,80℃反应下反应约4小时,最终得到MDI改性的聚氨酯型聚酯多元醇混合物h,数均分子量约20500的改性聚酯多元醇。
在本发明中,表1如下:
表1 合成例组成
实施例1-6、比较例1-2:本发明的聚酯多元醇树脂a 100份,市售双酚A型环氧NPEL128(南亚)5份,聚异氰酸酯TPA100 4份,乙酸乙酯327份,得到固含量25%涂布液,粘度500mPas。常温下,在40微米厚的铝-铁合金箔上,使用丝棒涂布该粘合剂组成物,80℃烘干溶剂后,胶层干厚约4微米,随后与25微米厚度单面电晕的双向拉伸尼龙膜(NY)复合。接下来,与前述操作同样的,在铝箔的另一侧,涂布该粘合剂组成物,烘干后得到干厚4微米的胶层,与40微米的单面电晕流延聚丙烯薄膜(CPP)复合,经过50℃*5天的熟化后,最终得到113微米的铝塑复合膜A,对应实施例2-6为铝塑复合膜b-h,比较例1-2为铝塑复合膜f、g。
在本发明中,表2如下:
表2 实施例对比
表2续表
表2备注
1)剥离强度:铝塑复合膜切成15mm*15cm的样条,在万能拉力机上测定NY/Al及CPP/Al之间的剥离强度。测定条件,150mm/min, 180°剥离。
2)热封强度:铝塑复合膜切成15cm*10cm样片两枚,流延聚丙烯膜面相对叠合后,在热封机上热压(热封区域幅宽5mm,加热区上盘,下盘温度同为170℃,压力0.3MPa,时间4秒)。随后切成15mm样条,在拉力机上测定CPP之间的热封强度。测定条件,150mm/min, T型剥离。
3)耐电解液实验 铝塑复合膜真空下封入约10克市售锂电池用电解液,其典型组成为EC/DMC/DEC=1/1/1, LiPF6=1.5M,放在85℃烘箱中烘烤7天后,观察密封袋的外观有无分层,变色及渗漏等问题。剪开密封袋,除去电解液,擦拭CPP的表面后在室温下测定CPP/Al之间的剥离强度。
4)冷深冲成型性 采用单槽方案冲槽,模具尺寸45mm*65mm,槽深5.0mm,冲深加工后观察边角有无破损,起皱,分层,裂纹,及透光现象。
5)耐高温高湿性能 选用深冲5.0mm合格样品,在60℃,90%RH相对湿度的高温高湿箱中放置96小时后,观察有无分层,变色现象。
综上,使用本发明的粘合剂聚酯,粘合剂组成物,可以制造软包装锂电池用铝塑复合膜。测试结果表明,对比比较例1~2,本发明下,铝箔/CPP之间的剥离强度达到10N/15mm以上,特别的,耐电解液处理后,铝箔/CPP之间的剥离强度保持率达到90%以上。在固定冲压深度5mm情况下,铝塑膜本身无破裂发生。高温高湿处理后,铝塑复合膜无分层,起泡等外观不良发生。
上面对本发明的实施方式作了详细说明,但是本发明不限于上述实施方式,在所述技术领域普通技术人员所具备的知识范围内,还可以在不脱离本发明宗旨的前提下做出各种修改。这些都是不具有创造性的修改,只要在本发明的权利要求范围内都受到专利法的保护。
Claims (10)
1.粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,从外到内依次由耐热树脂薄膜层,外侧粘合剂层,金属箔阻隔层,内侧粘合剂层以及热塑性密封层组成,构成锂离子电池用软包装复合膜,其特征在于:所述内侧粘合剂层的粘合剂重量组成比例为粘合剂树脂:环氧树脂:固化剂=100:1-10:1-10,粘合剂层的厚度为1-10μm。
2.根据权利要求1所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,其特征在于:所述粘合剂树脂为聚酯多元醇,其中芳香族多元酸含量为20-50mol%,脂肪族多元酸含量为50-80mol%,且至少包含一种碳原子数大于3的所述脂肪族多元醇,所述聚酯多元醇为的数均分子量为5000-50000,Tg小于20℃,酸值AV小于2mgKOH/g。
3.根据权利要求2所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,其特征在于:所述粘合剂树脂为所述聚酯多元醇经过异氰酸酯改性所得的聚氨酯型聚酯多元醇,其数均分子量为5000-50000,Tg20℃以下。
4.根据权利要求3所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,其特征在于:所述聚酯多元醇以及聚氨酯型聚酯多元醇,其组成中的脂肪族多元酸,至少有一种为二聚酸型脂肪族二羧酸,其组成比为50-80mol%。
5.根据权利要求1所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,其特征在于:所述环氧树脂使用环氧值EEW为100-1000的双酚A型,双酚F型,双酚E型环氧树脂的一种或几种混合物。
6.根据权利要求1所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,其特征在于:所述固化剂选用多官能团异氰酸酯类或者多官能团密胺类中的至少一种。
7.根据权利要求1所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体,其特征在于:所述外侧粘合剂层选择与所述内侧粘合剂层相同的组成成分。
8.一种如权利要求1所述的粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体制造的锂电池用外包装,其特征在于:所述粘合剂组成物调制成涂布液,涂布到基材上,加热干燥后,通过卷对卷干法复合工艺获得层状贴合型复合材料。
9.根据权利要求8所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体制造的锂电池用外包装,其特征在于:所述锂电池用外包装材料经过冷深冲加工及热封工艺形成锂电池包装袋。
10.根据权利要求9所述的一种粘合剂用树脂,粘合剂组成物,使用该粘合剂组成物的层状贴合复合体制造的锂电池用外包装,其特征在于:所述锂电池包装袋构成软包锂离子电池;所述锂电池包装袋用于数码电池,电动汽车及储能领域。