CN108166157A - Antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption and preparation method thereof - Google Patents
Antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption and preparation method thereof Download PDFInfo
- Publication number
- CN108166157A CN108166157A CN201711419662.2A CN201711419662A CN108166157A CN 108166157 A CN108166157 A CN 108166157A CN 201711419662 A CN201711419662 A CN 201711419662A CN 108166157 A CN108166157 A CN 108166157A
- Authority
- CN
- China
- Prior art keywords
- chitosan
- sodium alginate
- viscose rayon
- viscose
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses antibacterial spunlace non-woven cloth beauty mask base fabrics of a kind of moisture absorption and preparation method thereof, are related to field of nonwoven fabric technology, are made of the fiber of following weight percent：Sodium alginate viscose rayon 40 60%, chitosan viscose rayon 40 60%；Preparation method is first to prepare sodium alginate viscose rayon, chitosan viscose rayon, then carries out shredding respectively, combs, then cross lapping, and spun lacing reinforcing is carried out to the web completed, dry to get.The present invention is that sodium alginate and chitosan are added separately to spinning function viscose in viscose glue stoste; and using epoxychloropropane sodium alginate and chitosan are combined closely with viscose glue; sodium alginate viscose rayon and chitosan viscose rayon obtained have good gas permeability and water conservation hygroscopicity; bactericidal; non-woven fabrics made of being reinforced again through cross lapping spun lacing is used for facial mask substrate material; comfortable pro-skin; anti-inflammatory is antibacterial; it being capable of cleaning skin; effective protection skin weakens damage of the cosmetics to skin.
Description
Technical field
The present invention relates to the antibacterial spunlace non-woven cloth beauty mask base fabrics of field of nonwoven fabric technology more particularly to a kind of moisture absorption
And preparation method thereof.
Background technology
Nowadays, the maintenance of skin care particularly skin of face has become the daily required course of numerous people seeking beauties.Phase
For going to specialist cosmetology mechanism not only time-consuming the shortcomings that costly power, individual voluntarily maintains the selection for having become vast majority of people, especially
It is even more so for the Urban population all day among hectic.In numerous skin care item, facial mask with its it is convenient and
The advantages that preferable cosmetic result, is favored by numerous users.Wherein, refer to will be certain thickness non-woven for the mounted facial mask of film
The film cloth of cloth or other forms, is made the mask substrate for meeting shape of face size, coordinates suitable nutrient solution, and when use directly applies
In face.The hygroscopicity of existing mask substrate is general, and the essence liquid measure of load is few, and comfortable skin-friendly need into
One step improves.
Invention content
Technical problems based on background technology, the present invention propose a kind of antibacterial spunlace non-woven cloth beauty face of moisture absorption
Film base fabric and preparation method thereof, mask substrate moisture absorption water holding obtained, comfortable pro-skin, antibacterial anti-inflammatory being capable of effective protection faces
Skin weakens damage of the cosmetics to skin.
The antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption proposed by the present invention, by the fibre of following weight percent
Dimension composition：Sodium alginate viscose rayon 40-60%, chitosan viscose rayon 40-60%.
The invention also provides the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of above-mentioned moisture absorption, including following
Step：
The preparation of S1, sodium alginate viscose rayon：Sodium alginate is dissolved in water, pH to 8-9 is adjusted, adds in epoxy thereto
Chloropropane, temperature reaction obtain material A；Material A is added in viscose glue, stirs, obtains material B, material B is used into wet spinning,
Obtain sodium alginate viscose rayon；
The preparation of S2, chitosan viscose rayon：Chitosan is added to the water, adjusting pH to 5-6, stirring and dissolving, thereto
Epoxychloropropane is added in, temperature reaction obtains material C；Material C is adjusted into pH to 8-9, is then added in viscose glue, is stirred to react,
Material D is obtained, by material D using wet spinning, obtains chitosan viscose rayon；
It is prepared by S3, base fabric：Sodium alginate viscose rayon and chitosan viscose rayon are subjected to shredding respectively, combed, then
Cross lapping carries out spun lacing reinforcing to the web completed, dry to get.
Preferably, in the S1, sodium alginate is dissolved in water, the sodium alginate aqueous solution of 3-5% is prepared, uses NaOH solution
PH to 8-9 is reconciled, the epoxychloropropane for accounting for sodium alginate weight 3-7% is added in thereto, is warming up to 70-80 DEG C, is stirred to react
2-3h, cooling, obtains material A；Material A is added in viscose glue, is stirred to react 2-3h, obtains material B, material B is used into Wet-spinning
Silk, obtains sodium alginate viscose rayon.
Preferably, material A is added in viscose glue by the ratio that the 4-6% of viscose glue is accounted for according to sodium alginate weight.
Preferably, in the S2, chitosan is added to the water, with second acid for adjusting pH to 5-6, stirring and dissolving prepares 3-5%
Chitosan aqueous solution, add in epoxychloropropane thereto, be warming up to 70-80 DEG C, be stirred to react 2-3h, obtain material C；By material
C adjusts pH to 8-9 with sodium hydroxide solution, is then added in viscose glue, is stirred to react 1-2h, obtain material D, material D is used
Wet spinning obtains chitosan viscose rayon.
Preferably, material A is added in viscose glue by the ratio that the 3-5% of viscose glue is accounted for according to chitosan weight.
Preferably, in the S3, the density of mating formation of web is 20-30g/m2。
Advantageous effect：The present invention is that sodium alginate and chitosan are added separately to spinning function viscose glue in viscose glue stoste
Silk, and using epoxychloropropane sodium alginate and chitosan are combined closely with viscose glue；Wherein, contain in epoxychloropropane molecule
There is high activity to be easy to the chlorion of substitution and be easy to the epoxy construction of ring-opening polymerisation, sodium alginate and shell are gathered using the structure
Sugar is modified processing；There is abundant hydroxyl on sodium alginate strand, it under alkaline condition, can be with epoxychloropropane
Reaction is crosslinked, is then combined again with viscose glue, so as to improve the problem of ammonium alginate viscosity is unstable, improves it
Viscosity stability, heat resistance and spinnability；Contain abundant amino and hydroxyl in chitosan molecule chain, in acid condition,
Can crosslink and react with epoxychloropropane, be then combined again with viscose glue, so as to make up chitosan molecule amount it is small,
The problems such as binding force between viscose rayon is weak；Sodium alginate, chitosan are respectively by epoxychloropropane and viscose glue with covalent
Key is strong bonded, and performance is stablized；Have very well containing hydrophilic radicals such as great amount of hydroxy group, amino on sodium alginate and chitosan
Hydrophily, hygroscopicity and biocompatibility and antibacterial, anti-inflammatory, itching-relieving efficacies, sodium alginate fiber is with negative electrical charge
Cellulose fibre, the healing of scytitis caused by can promoting infection or allergic reaction, chitin fiber is all fibres
Unique positively charged animal origin cellulose fiber, good to gram-positive bacteria bacteriostasis in dimension, additionally it is possible to pain of releiving, desalination
Scar, chelant heavy metal ion, by sodium alginate and chitosan respectively with viscose glue mixing wet spinning, it is intermolecular formed it is many micro-
Pore structure, sodium alginate viscose rayon and chitosan viscose rayon obtained have good gas permeability and water conservation hygroscopicity, to leather
Lan Shi positive bacterias, negative bacterium have good bactericidal effect, and sodium alginate viscose rayon and chitosan viscose rayon are handed over
Non-woven fabrics made of pitching the reinforcing of lapping spun lacing is used for facial mask substrate material, and comfortable pro-skin, high-hygroscopicity and gas permeability can make
Facial mask loads more Essences, skin of face is promoted to absorb more nutritional ingredients, and formed with the heavy metal ion of skin
Complex, anti-inflammatory is antibacterial, and so as to play cleaning skin, effective protection skin weakens damage of the cosmetics to skin, especially suitable
In sensibility skin quality, it can be used as medical facial mask substrate.
Specific embodiment
In the following, technical scheme of the present invention is described in detail by specific embodiment.
Embodiment 1
The antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption proposed by the present invention, by the fibre of following weight percent
Dimension composition：Sodium alginate viscose rayon 40%, chitosan viscose rayon 60%.
The invention also provides the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of above-mentioned moisture absorption, including following
Step：
The preparation of S1, sodium alginate viscose rayon：Sodium alginate is dissolved in water, adjusts pH to 8, adds in epoxy chlorine thereto
Propane, temperature reaction obtain material A；Material A is added in viscose glue, stirs, obtains material B, by material B using wet spinning, is obtained
Sodium alginate viscose rayon；
The preparation of S2, chitosan viscose rayon：Chitosan is added to the water, adjusts pH to 5, stirring and dissolving adds thereto
Enter epoxychloropropane, temperature reaction obtains material C；Material C is adjusted into pH to 8, is then added in viscose glue, is stirred to react, obtain object
Expect D, by material D using wet spinning, obtain chitosan viscose rayon；
It is prepared by S3, base fabric：Sodium alginate viscose rayon and chitosan viscose rayon are subjected to shredding respectively, combed, then
Cross lapping carries out spun lacing reinforcing to the web completed, dry to get.
Embodiment 2
The antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption proposed by the present invention, by the fibre of following weight percent
Dimension composition：Sodium alginate viscose rayon 50%, chitosan viscose rayon 50%.
The invention also provides the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of above-mentioned moisture absorption, including following
Step：
The preparation of S1, sodium alginate viscose rayon：Sodium alginate is dissolved in water, prepares 3% sodium alginate aqueous solution, is used
NaOH solution reconciles pH to 8, adds in the epoxychloropropane for accounting for sodium alginate weight 3% thereto, is warming up to 70 DEG C, is stirred to react
2h, cooling, obtains material A；Material A is added in viscose glue by 4% ratio that viscose glue is accounted for according to sodium alginate weight, is stirred to react
2h obtains material B, by material B using wet spinning, obtains sodium alginate viscose rayon；
The preparation of S2, chitosan viscose rayon：Chitosan is added to the water, with second acid for adjusting pH to 5, stirring and dissolving is prepared
3% chitosan aqueous solution, adds in epoxychloropropane thereto, is warming up to 70 DEG C, is stirred to react 2h, obtains material C；By material C
PH to 8 is adjusted with sodium hydroxide solution, material A is added to viscose glue by 3% ratio that viscose glue is then accounted for according to chitosan weight
In, 1h is stirred to react, obtains material D, by material D using wet spinning, obtains chitosan viscose rayon；
It is prepared by S3, base fabric：Sodium alginate viscose rayon and chitosan viscose rayon are subjected to shredding respectively, combed, then
Cross lapping, density of mating formation are 20g/m2, spun lacing reinforcing is carried out to the web completed, dry to get.
Embodiment 3
The antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption proposed by the present invention, by the fibre of following weight percent
Dimension composition：Sodium alginate viscose rayon 55%, chitosan viscose rayon 45%.
The invention also provides the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of above-mentioned moisture absorption, including following
Step：
The preparation of S1, sodium alginate viscose rayon：Sodium alginate is dissolved in water, prepares 4% sodium alginate aqueous solution, is used
NaOH solution reconciles pH to 8.5, adds in the epoxychloropropane for accounting for sodium alginate weight 5% thereto, is warming up to 75 DEG C, stirring is anti-
2.5h is answered, cools down, obtains material A；Material A is added in viscose glue by 5% ratio that viscose glue is accounted for according to sodium alginate weight, stirring
2.5h is reacted, obtains material B, by material B using wet spinning, obtains sodium alginate viscose rayon；
The preparation of S2, chitosan viscose rayon：Chitosan is added to the water, with second acid for adjusting pH to 5.5, stirring and dissolving is matched
The chitosan aqueous solution of system 4%, adds in epoxychloropropane, is warming up to 75 DEG C, is stirred to react 2.5h, obtain material C thereto；By object
Expect that C adjusts pH to 8.5 with sodium hydroxide solution, material A is added to by 4% ratio that viscose glue is then accounted for according to chitosan weight
In viscose glue, 1.5h is stirred to react, obtains material D, by material D using wet spinning, obtains chitosan viscose rayon；
It is prepared by S3, base fabric：Sodium alginate viscose rayon and chitosan viscose rayon are subjected to shredding respectively, combed, then
Cross lapping, density of mating formation are 25g/m2, spun lacing reinforcing is carried out to the web completed, dry to get.
Embodiment 4
The antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption proposed by the present invention, by the fibre of following weight percent
Dimension composition：Sodium alginate viscose rayon 60%, chitosan viscose rayon 40%.
The invention also provides the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of above-mentioned moisture absorption, including following
Step：
The preparation of S1, sodium alginate viscose rayon：Sodium alginate is dissolved in water, prepares 5% sodium alginate aqueous solution, is used
NaOH solution reconciles pH to 9, adds in the epoxychloropropane for accounting for sodium alginate weight 7% thereto, is warming up to 80 DEG C, is stirred to react
3h, cooling, obtains material A；Material A is added in viscose glue by 6% ratio that viscose glue is accounted for according to sodium alginate weight, is stirred to react
3h obtains material B, by material B using wet spinning, obtains sodium alginate viscose rayon；
The preparation of S2, chitosan viscose rayon：Chitosan is added to the water, with second acid for adjusting pH to 6, stirring and dissolving is prepared
5% chitosan aqueous solution, adds in epoxychloropropane thereto, is warming up to 80 DEG C, is stirred to react 3h, obtains material C；By material C
PH to 9 is adjusted with sodium hydroxide solution, material A is added to viscose glue by 5% ratio that viscose glue is then accounted for according to chitosan weight
In, 2h is stirred to react, obtains material D, by material D using wet spinning, obtains chitosan viscose rayon；
It is prepared by S3, base fabric：Sodium alginate viscose rayon and chitosan viscose rayon are subjected to shredding respectively, combed, then
Cross lapping, density of mating formation are 30g/m2, spun lacing reinforcing is carried out to the web completed, dry to get.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. the antibacterial spunlace non-woven cloth beauty mask base fabric of a kind of moisture absorption, which is characterized in that by the fiber of following weight percent
Composition：Sodium alginate viscose rayon 40-60%, chitosan viscose rayon 40-60%.
2. a kind of preparation method of the spunlace non-woven cloth beauty mask base fabric antibacterial based on moisture absorption described in claim 1, special
Sign is, includes the following steps：
The preparation of S1, sodium alginate viscose rayon：Sodium alginate is dissolved in water, pH to 8-9 is adjusted, adds in epoxy chloropropionate thereto
Alkane, temperature reaction obtain material A；Material A is added in viscose glue, stirs, obtains material B, by material B using wet spinning, is obtained extra large
Mosanom viscose rayon；
The preparation of S2, chitosan viscose rayon：Chitosan is added to the water, adjusts pH to 5-6, stirring and dissolving adds in thereto
Epoxychloropropane, temperature reaction obtain material C；Material C is adjusted into pH to 8-9, is then added in viscose glue, is stirred to react, obtain object
Expect D, by material D using wet spinning, obtain chitosan viscose rayon；
It is prepared by S3, base fabric：Sodium alginate viscose rayon and chitosan viscose rayon are subjected to shredding respectively, combed, is then intersected
Lapping carries out spun lacing reinforcing to the web completed, dry to get.
3. the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of moisture absorption according to claim 2, feature exist
In, in the S1, sodium alginate is dissolved in water, prepares the sodium alginate aqueous solution of 3-5%, pH to 8-9 is reconciled with NaOH solution,
The epoxychloropropane for accounting for sodium alginate weight 3-7% is added in thereto, 70-80 DEG C is warming up to, is stirred to react 2-3h, is cooled down, is obtained
Material A；Material A is added in viscose glue, is stirred to react 2-3h, obtains material B, by material B using wet spinning, obtains sodium alginate
Viscose rayon.
4. the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of moisture absorption according to claim 3, feature exist
In material A is added in viscose glue by the ratio that the 4-6% of viscose glue is accounted for according to sodium alginate weight.
5. the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of moisture absorption according to claim 2, feature exist
In in the S2, chitosan being added to the water, with second acid for adjusting pH to 5-6, the chitosan that stirring and dissolving prepares 3-5% is water-soluble
Liquid adds in epoxychloropropane thereto, is warming up to 70-80 DEG C, is stirred to react 2-3h, obtains material C；By material C sodium hydroxides
Solution adjusts pH to 8-9, is then added in viscose glue, is stirred to react 1-2h, obtains material D, by material D using wet spinning, obtains
Chitosan viscose rayon.
6. the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of moisture absorption according to claim 5, feature exist
In material A is added in viscose glue by the ratio that the 3-5% of viscose glue is accounted for according to chitosan weight.
7. the preparation method of the antibacterial spunlace non-woven cloth beauty mask base fabric of moisture absorption according to claim 2, feature exist
In in the S3, the density of mating formation of web is 20-30g/m2。