CN109023714A - A kind of anti-blue light radiation protection mask substrate of high moisturizing and preparation method thereof and application - Google Patents
A kind of anti-blue light radiation protection mask substrate of high moisturizing and preparation method thereof and application Download PDFInfo
- Publication number
- CN109023714A CN109023714A CN201811037184.3A CN201811037184A CN109023714A CN 109023714 A CN109023714 A CN 109023714A CN 201811037184 A CN201811037184 A CN 201811037184A CN 109023714 A CN109023714 A CN 109023714A
- Authority
- CN
- China
- Prior art keywords
- blue light
- radiation protection
- mask substrate
- light radiation
- protection mask
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to personal technical field of skin care, especially a kind of anti-blue light radiation protection mask substrate of high moisturizing and preparation method thereof and application, its method the following steps are included: (1) fiber preparation: lutein and catechin are mixed by 1:1~5:1, it is added to after mixing according to the ratio of mass ratio 1:10 mixed and modified in the cellulose spinning fluid of preparation, wet spinning is carried out after blending, obtains functional fiber；(2) preparation of film cloth: being added above-mentioned functional fiber 20%~50%, alginate fibre 50%~80% is blended, and through fiber opening, mixing, combing networking, it is 20~50g/m that density, which is made, in spun lacing reinforcing2Non-woven cloth；Drying coiling and molding, then anti-blue light radiation protection mask substrate is made through clicking technique.
Description
Technical field
The present invention relates to personal technical field of skin care, specific field is a kind of high anti-blue light radiation protection facial mask base of moisturizing
Cloth.
Background technique
Currently, the organic TV of OLED with anti-blue ray radiation becomes new selection on the market, according to ginger treasured fine jade in " organic light emission
Diode " OLED (Organic Light-Emitting Diode) is proposed in a text, full name " Organic Light Emitting Diode ", is one
Kind display screen technology.
It is shown according to Baidu.com's encyclopaedia data, anti-blue light glasses and some anti-blue light screens or film, typically plated film
For reflection blue light to play the role of anti-blue light, anti-blue light goggles pouring-in class lutein in the arctic absorbs blue light, with putting the palms together before one four
The scientific and technological coated reflection blue light of layer, Multiple techniques so can be only achieved effective anti-blue light effect.
Anti- blue light TV can prevent the wavelength of blue light from damaging to eyes, but TV, which fails fully reflective absorb, to be owned
Blue light, meanwhile, when electric appliances long period such as various household electrical appliance, office equipment, mobile phone use, can all generate fainter
Electromagnetic field, anti-blue light action are not avoided that the accumulation of radiation.The electromagnetic radiation usually accumulated in life can little by little lead to skin
Skin is dry, and skin aging is accelerated to even result in skin cancer.
Anti- blue light glasses and anti-blue Light Film can easily protect eyes to be not subjected to the adverse effect of blue light, since glasses can only
Part shields to eyes, and the limited area of anti-blue Light Film, the blue light that can be shielded is less, still has blue light and passes through spoke
Penetrate and skin damaged, occur skin accelerate aging, relaxation and it is heavy have color spot, skin yellow and lack flexibility without pool, skin, add
Fast wrinkle occurs.
It is pointed out in Baidupedia, for anti-blue light, the good precious lutein of oral administration Australia Blackmores/ Australia be can promote
Blood vessel circulation, improves the malaise symptoms such as dry eyes and astringent eyes, while lasting supplement lutein can also prevent ultraviolet light and blue light
Injury, avoids the blurring of image and lesion.
103271865 A of patent CN " a kind of selenium-rich green tea facial mask " has invented a kind of producer of selenium-rich green tea powder film
Method is the selenium-rich green tea facial mask as made from some effective component grindings such as selenium-rich green tea powder and Bee Pollen, protects with whitening
Wet effect dispels facial crows feet and black freckle, moreover it is possible to promote the circulation of skin of face blood, enhance skin elasticity.
It is green that 107744494 A of patent CN " with green tea powder honey milk facial mask as main component " has invented a kind of production
The method of tea honey milk facial mask, using green tea powder honeybee milk as main component, green tea powder honey milk facial mask can be helped rapidly
Face's temperature is reduced, while can mildly protect injured skin, the honey and milk of addition can play the effect for promoting skin healing
Fruit.
106137905 A of patent CN " a kind of green tea mask and preparation method thereof " has invented a kind of green with natural nuisance-free
Tea tender leaf two leaves and a bud be raw material made of green tea mask, by tea-drying and be ground into green tea powder, be added pectin, Vitamin C,
Coatable green tea mask on the face, the health-care efficacy with green tea is made in the ingredients such as honey.
Lutein itself is a kind of polyphenoils, and harmful light such as blue light can be absorbed.Lutein has been incorporated as meals
Replenishers are eaten, are used as health care product for oral administration.Health ministry announces No. 12 file in 2008: health ministry ratifies leaf
Flavine ester be new resource food, can be widely applied to food and field of medicaments, daily dosage be less than 12mg.It is excessive to draw leaf
Flavine can cause extra burden to liver, cannot be well in control volume to its intake by taking.
Ultrafine green tea powder, the more big then silty of ultrafine green tea powder mesh number is made by the method pulverized in selenium-rich green tea facial mask
Absorption that is more thin more being easy to skin, but its active constituent content is then reduced.Through " constituent analysis of ultrafine green tea powder trophic function and its
Using " content of some effective components in green tea can be made to reduce during report pulverizes in document, catechin, reproducibility
Sugar, copper and selenium etc. are reduced as green tea powder mesh number increases.
Green tea mask, which can play skin, certain inoxidizability, since there is ingredient tea polyphenols stronger antioxygen to be turned into
With especially ester catechin EGCG, reproducibility is even up to 100 times of the different bad hematic acid of L-.4 kinds of main catechu are confirmed through encyclopaedia
In plain compound, oxidation resistance be EGCG (Epigallo-catechin gallate (EGCG)) > EGC (epigallocatechin) >
ECG (L-Epicatechin gallate) > EC (epicatechin) > BHA (butylated hydroxy anisole), and antioxygenic property is with temperature
It increases and enhances.Although green tea mask has certain inoxidizability, the content pettiness of its catechin is not enough to play very
Good anti-blue light antioxidation.Green tea mask on the market is used by way of coating, and mud membrane type uses complex steps,
Dry skin is easily caused after use, smears the overlong time even moisture of meeting suck-back skin.
Currently, common health functional mask majority is made of that chemical substance macromolecule glue, calcium carbonate make raw material, although
The metabolic object of face can be removed, but also has very big side effect, easily damage Skin Cell.Most health-care face mask is traditional Chinese medicine power
Film, the easy mould growth of Chinese medicine extract, bad anti-corrosion effect easily can cause to stimulate, very if being added to preservative to skin
The adverse reactions such as allergy, fash can extremely be caused.It is not at all surprising with green tea effect sexual health facial mask, but added mostly with a small amount of
Agent is added to exist, not targetedly extract Function to ultimate attainment, however on the market also without a specifically for indigo plant
The facial mask of light radiation research and development, it is therefore desirable to have the facial mask of a new type functional can also can use mobile phone heartily when in use, it is right
Skin of face has good anti-blue light.
Summary of the invention
The purpose of the present invention is to provide a kind of high anti-blue light radiation protection mask substrate of moisturizing and preparation method thereof and apply,
To solve the problems, such as to lack in the prior art one kind specifically for blue ray radiation facial mask.
To achieve the above object, the invention provides the following technical scheme:
A kind of production method of the anti-blue light radiation protection mask substrate of high moisturizing, comprising the following steps:
(1) preparation of fiber: lutein and catechin are mixed by 1:1~5:1, according to mass ratio 1:10 after mixing
Ratio be added to mixed and modified in the cellulose spinning fluid of preparation, wet spinning is carried out after blending, obtains functional fiber；
(2) preparation of film cloth: above-mentioned functional fiber 20%~50% is added, alginate fibre 50%~80% is total to
Mixed, through fiber opening, mixing, combing networking, it is 20~50g/m that density, which is made, in spun lacing reinforcing2Non-woven cloth；Drying winding
Molding, then anti-blue light radiation protection mask substrate is made through clicking technique.
The production method of the anti-blue light radiation protection mask substrate of high moisturizing of the present invention, the catechin in step (1) are logical
It crosses and is obtained by extraction, green tea is specially subjected to separating-purifying using gel filtration chromatography technology, gradient is made with 20% acetone/water
Elution, and isolate and purify to obtain catechin in conjunction with liquid chromatogram, obtained catechin purity is 99% or more.
The production method of the anti-blue light radiation protection mask substrate of high moisturizing of the present invention, lutein described in step (1)
Using supercritical CO2Extraction is extracted from marigold, and extracting pressure 45Mpa, extraction temperature is set as 50 DEG C, separating pressure
For 8Mpa, separation temperature is 55 DEG C；It is subsequently added into separating still and carries out secondary separation extraction lutein, separating pressure is arranged at this time
For 4Mpa, separation temperature is 20 DEG C, remaining excess-col is impurity, then lutein resin can be obtained through potassium hydroxide saponification.
Lutein recovery rate is 95.7%.
The production method of the anti-blue light radiation protection mask substrate of high moisturizing of the present invention, spun lacing reinforces work in step (2)
Skill passes through the road 5-7 spun lacing；Wherein first of spun lacing water needle pressure is 1.5Mpa, and second spun lacing water needle pressure is 4.5Mpa, the
Three spun lacing water needle pressure are 5Mpa.
The high anti-blue light radiation protection mask substrate of moisturizing made from the above-mentioned production method of the present invention.
Facial mask prepared by the anti-blue light radiation protection mask substrate of high moisturizing of the present invention.
Wherein, lutein is a kind of carotenoid containing multiple conjugated double bonds, and structure determines that it is oxidized easily
And play antioxidation.Studies have shown that lutein can inhibit and inactivation activities oxygen cluster, alleviation cytolipin peroxidating damage
Wound, to reduce the apoptosis of retina cell.Lutein is also possible to turn by adjusting cell signal to the protective effect of light injury
It leads to realize.
Catechin is a kind of native oxidant that oxidation resistance is superpower, using electron paramagnetic resonance (ESR), chemiluminescence
(BCL) and in the different systems of spectrophotometry (SPM) detection catechin can big major clean-up operation superoxide anion.Catechin can also press down
Lipoxygenase and lipid peroxidation in skin mitochondria processed, to play aging effect, are prolonged with removing internal excessive free radicals
The generation of slow aging.
There is the effective component of anti-blue light by modified mask substrate, outside contamination can be completely cut off on the face when facial mask is fitted in,
Catechin and lutein, which contact with skin of face, to be absorbed its effective component and can put up a resistance to blue light shielding, and sweat can be promoted
Glandular secretion and metabolism, cause the oxygen content of skin to rise, and are conducive to the oil substances that skin excludes face's accumulation, together
When, the Essence of facial mask can penetrate into the cuticula of skin, be allowed to become soft fine and smooth, skin is more naturally bright flexible.
Anti- blue light radiation protection facial mask is using catechu cellulose fiber and lutein as the facial mask film cloth of raw material, the antioxygenic property energy of effective component
The blue ray radiation excessively aging caused by skin is resisted, can be used as blue light filtering containing lutein blue ray radiation is converted to nothing
Harmful heat absorbs blue light to prevent blue light illumination from causing oxidative stress.Sufficient catechin content can also function well as anti-
The health-care efficacies such as bacterium Peppermint Extract.Catechin inhibits hyaluronic acid by inhibiting the mechanism of action of histamine release from mast cells release
The activity of enzyme, thus also with the ability of antiallergy born of the same parents rash.
Alginate fibre has moisture-absorbing moisture-keeping performance, can play moisture pick-up properties by the contact with skin, skin can be made to inhale
The vitamin and mineral for receiving seaweed release, there is natural benefit, no allergic reaction to skin.The water absorbing capacity of alginate fibre
By force, good moisture-keeping functions can play beauty and health care functions with the moisture in tempered air.Furthermore there are also one for alginate fibre
Fixed radiation-proof effect can be formed since there is-COO- ,-OH groups in aqueous solution for sodium alginate with polyvalent metal ion
Complex.Ion in fibre substrate content increase to a certain extent when, the enhancing of interionic binding force, it is sufficient to overcome from
Electrostatic repulsion between son acts on and it is made to be connected with each other, and forms conductive particle subchain, improves the electromagnetic shielding of fabric and resists
Electrostatic capacity.
The beneficial effects of the present invention are: the present invention prepares new function with lutein, catechin and alginate fibre blending
For property fibration in mask substrate, micro lutein can absorb blue light；Simultaneously antioxidation can be played to skin with catechin
Without being accumulated by blue ray radiation, cause to have dry skin, accelerates skin aging；There is alginate fibre gel high moistening effect (to protect
Water rate is up to 1800% or more, i.e., 18 times or more) and excellent electron radiation shielding.
Catechin that the present invention develops, lutein fibre spun-laced non-woven cloth mask substrate are not only soft, Breathable paste
Skin has good skin wetness sensation and efficient anti-blue light, anti-radiation, anti-oxidant, anti-aging, antiallergy and antibiotic effect.
Mask substrate has moisturizing simultaneously, and the functions such as activating cell and oxygen supply have the effects that nourishing, nutrition, health care to skin.
The lutein that the mask substrate uses, has broken the method for conventional lutein for oral administration, but the side for passing through face mask film
Method carries out osmotic absorption to skin, so that the textura epidermoidea of face not only has the function of shielding protection, moreover it is possible to play resistance and inhale
The external action for leading to face oxidation aging has been prevented in the effect for receiving blue light from the root, while when catechin and skin contact
Its oxidation resistant effect can be discharged, second has been carried out to skin and has protected the chronic hazard for resisting blue light to skin again.
The facial mask of mask substrate preparation of the present invention is a with functional Novel facial mask, and effective component is from natural
In environment protecting plant, there is natural degradable, gradually replace chemical reagent addition for natural green environmental protection additive and open newly
Approach.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1
A kind of production method of the anti-blue light radiation protection mask substrate of high moisturizing, comprising the following steps:
(1) preparation of fiber: lutein and catechin are mixed by 1:1, according to the ratio of mass ratio 1:10 after mixing
Example is added to mixed and modified in the cellulose spinning fluid of preparation, and wet spinning is carried out after blending, obtains functional fiber；
Wherein, green tea is subjected to separating-purifying using gel filtration chromatography technology, is washed with 20% acetone/water as gradient
It is de-, and isolate and purify to obtain catechin in conjunction with liquid chromatogram, obtained catechin purity is 99% or more.
Lutein uses supercritical CO2Extraction is extracted from marigold, extracting pressure 45Mpa, extraction temperature setting
It is 50 DEG C, separating pressure 8Mpa, separation temperature is 55 DEG C；It is subsequently added into separating still and carries out secondary separation extraction lutein,
Separating pressure is set as 4Mpa at this time, and separation temperature is 20 DEG C, remaining excess-col is impurity, then can through potassium hydroxide saponification
Obtain lutein resin.Lutein recovery rate is 95.7%.
(2) preparation of film cloth: being added above-mentioned functional fiber 20%, alginate fibre 80% is blended, through fiber opening,
Mixing, combing networking, spun lacing are reinforced, by 5 spun lacings, wherein first of spun lacing water needle pressure is 1.5Mpa, second spun lacing
Water needle pressure is 4.5Mpa, and third road spun lacing water needle pressure is 5Mpa.It is 20g/m that density, which is made,2Non-woven cloth；Drying volume
Anti- blue light radiation protection mask substrate is made around molding, then through clicking technique.
Embodiment 2
A kind of production method of the anti-blue light radiation protection mask substrate of high moisturizing, comprising the following steps:
(1) preparation of fiber: lutein and catechin are mixed by 3:1, according to the ratio of mass ratio 1:10 after mixing
Example is added to mixed and modified in the cellulose spinning fluid of preparation, and wet spinning is carried out after blending, obtains functional fiber；
Wherein, green tea is subjected to separating-purifying using gel filtration chromatography technology, is washed with 20% acetone/water as gradient
It is de-, and isolate and purify to obtain catechin in conjunction with liquid chromatogram, obtained catechin purity is 99% or more.
Lutein uses supercritical CO2Extraction is extracted from marigold, extracting pressure 45Mpa, extraction temperature setting
It is 50 DEG C, separating pressure 8Mpa, separation temperature is 55 DEG C；It is subsequently added into separating still and carries out secondary separation extraction lutein,
Separating pressure is set as 4Mpa at this time, and separation temperature is 20 DEG C, remaining excess-col is impurity, then can through potassium hydroxide saponification
Obtain lutein resin.Lutein recovery rate is 95.1%.
(2) preparation of film cloth: being added above-mentioned functional fiber 50%, alginate fibre 50% is blended, through fiber opening,
Mixing, combing networking, spun lacing, which is reinforced, passes through 6 spun lacings；Wherein first of spun lacing water needle pressure is 1.5Mpa, second spun lacing water
Needle force is 4.5Mpa, and third road spun lacing water needle pressure is 5Mpa.It is 50g/m that density, which is made,2Non-woven cloth；Drying winding
Molding, then anti-blue light radiation protection mask substrate is made through clicking technique.
Embodiment 3
A kind of production method of the anti-blue light radiation protection mask substrate of high moisturizing, comprising the following steps:
(1) preparation of fiber: lutein and catechin are mixed by 5:1, according to the ratio of mass ratio 1:10 after mixing
Example is added to mixed and modified in the cellulose spinning fluid of preparation, and wet spinning is carried out after blending, obtains functional fiber；
Wherein, green tea is subjected to separating-purifying using gel filtration chromatography technology, is washed with 20% acetone/water as gradient
It is de-, and isolate and purify to obtain catechin in conjunction with liquid chromatogram, obtained catechin purity is 99% or more.
Lutein uses supercritical CO2Extraction is extracted from marigold, extracting pressure 45Mpa, extraction temperature setting
It is 50 DEG C, separating pressure 8Mpa, separation temperature is 55 DEG C；It is subsequently added into separating still and carries out secondary separation extraction lutein,
Separating pressure is set as 4Mpa at this time, and separation temperature is 20 DEG C, remaining excess-col is impurity, then can through potassium hydroxide saponification
Obtain lutein resin.Lutein recovery rate is 94.3%.
(2) preparation of film cloth: being added above-mentioned functional fiber 40%, alginate fibre 60% is blended, through fiber opening,
Mixing, combing networking, spun lacing, which is reinforced, passes through 7 spun lacings；Wherein first of spun lacing water needle pressure is 1.5Mpa, second spun lacing water
Needle force is 4.5Mpa, and third road spun lacing water needle pressure is 5Mpa.It is 35g/m that density, which is made,2Non-woven cloth；Drying winding
Molding, then anti-blue light radiation protection mask substrate is made through clicking technique.
The mask substrate that embodiment 1-3 is respectively adopted prepares the anti-blue light radiation protection facial mask of high moisturizing, to the guarantor of three sections of facial masks
Wet effect is tested, and water retention is up to 1800% or more, i.e., 18 times or more.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of production method of the anti-blue light radiation protection mask substrate of high moisturizing, which comprises the following steps:
(1) preparation of fiber: lutein and catechin are mixed by 1:1~5:1, according to the ratio of mass ratio 1:10 after mixing
Example is added to mixed and modified in the cellulose spinning fluid of preparation, and wet spinning is carried out after blending, obtains functional fiber；
(2) preparation of film cloth: above-mentioned functional fiber 20%~50% is added, alginate fibre 50%~80% is blended, warp
Fiber opening, mixing, combing networking, it is 20~50g/m that density, which is made, in spun lacing reinforcing2Non-woven cloth；Drying coiling and molding,
Anti- blue light radiation protection mask substrate is made through clicking technique again.
2. the production method of the anti-blue light radiation protection mask substrate of high moisturizing according to claim 1, it is characterised in that: step
(1) green tea is specially carried out separating-purifying using gel filtration chromatography technology, with 20% by being obtained by extraction by the catechin in
Acetone/water make gradient elution, and isolate and purify to obtain catechin in conjunction with liquid chromatogram.
3. the production method of the anti-blue light radiation protection mask substrate of high moisturizing according to claim 2, it is characterised in that: gained
The catechin purity arrived is 99% or more.
4. the production method of the anti-blue light radiation protection mask substrate of high moisturizing according to claim 1, it is characterised in that: step
(1) lutein described in uses supercritical CO2Extraction is extracted from marigold, extracting pressure 45Mpa, extraction temperature setting
It is 50 DEG C, separating pressure 8Mpa, separation temperature is 55 DEG C；It is subsequently added into separating still and carries out secondary separation extraction lutein,
Separating pressure is set as 4Mpa at this time, and separation temperature is 20 DEG C, remaining excess-col is impurity, then can through potassium hydroxide saponification
Obtain lutein resin.
5. the production method of the anti-blue light radiation protection mask substrate of high moisturizing according to claim 4, it is characterised in that: described
Lutein recovery rate is 95.7%.
6. the production method of the anti-blue light radiation protection mask substrate of high moisturizing according to claim 1, it is characterised in that: step
(2) spun lacing reinforcement process passes through the road 5-7 spun lacing in；Wherein first of spun lacing water needle pressure is 1.5Mpa, second spun lacing water needle
Pressure is 4.5Mpa, and third road spun lacing water needle pressure is 5Mpa.
7. the high anti-blue light radiation protection mask substrate of moisturizing made from any production method of claim 1-6.
8. facial mask prepared by the anti-blue light radiation protection mask substrate of high moisturizing as claimed in claim 7.