CN101343780B - Chinese aloe viscose fiber and preparation thereof - Google Patents
Chinese aloe viscose fiber and preparation thereof Download PDFInfo
- Publication number
- CN101343780B CN101343780B CN2008101412200A CN200810141220A CN101343780B CN 101343780 B CN101343780 B CN 101343780B CN 2008101412200 A CN2008101412200 A CN 2008101412200A CN 200810141220 A CN200810141220 A CN 200810141220A CN 101343780 B CN101343780 B CN 101343780B
- Authority
- CN
- China
- Prior art keywords
- aloe
- viscose
- spinning
- preparation
- viscose fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to an aloe viscose fiber and a manufacturing method thereof, relating to a fiber. The invention aims to provide the aloe viscose fiber with the functions of promoting the metabolism of skin cells and preventing the skin from being damaged and oxidized by ultraviolet ray as well as the preparation method thereof. The invention adopts the technical proposal that the aloe viscose fiber comprises the viscose fiber which contains aloe. The aloe in the aloe viscose fiber accounts for 1 to 50 percent of the fiber weight. The invention is used in the fiber production.
Description
Technical field:
The present invention relates to a kind of fiber, particularly a kind of aloe viscose and manufacture method thereof.
Background technology:
Containing in the aloe has 75 kinds of elements and human body cell desired substance almost completely identical, contain 7 kinds of 8 kinds of Amino acids of needed by human, 11 kinds of 12 kinds of less important Amino acids, vitamin A, E, C, B group, mineral matter reaches 10 kinds, Anthraquinone Complex, 8 big materials such as Saponins lignin, single marrow and polysaccharide.The natural bioactivity substance that they are a large amount of; can effectively purify the human epidermal free radical; brute force with cell tissue is composed the effect of living, protective effect; amino acid wherein and complex polysaccharide have constituted natural moisture preserving factor (NMF); can replenish the moisture that loses in the skin; recover the function of collagen protein, prevent facial wrinkles, keep soft and moist, smooth, the high resilience of skin.Material such as aloin and aloe-emodin has antiinflammatory action, and skin both capable of washing can prevent bacterial growth again, promotes cell metabolism and skin regeneration, eases the pain and itch, and some skin disease is had obvious curative effects.In addition; the amino acid that asparatate in the aloe, glycine, serine etc. help skin metabolism can form the invisible film of one deck on skin; can stop that long wave ultraviolet prevents because of redness, burning heat sensation that Exposure to Sunlight causes the injury and the oxidation of epidermis in the sunlight, protection skin exempts from burns.Thereby exploitation contains the fiber of aloe, with this fiber made clothes, people's skin is had good effect, and viscose has been widely used, aloe is added to makes the aloe viscose in the viscose glue vast market is arranged.
Summary of the invention:
The purpose of this invention is to provide a kind of have promote skin cell metabolism, stop ultraviolet ray the injury of skin and aloe viscose of oxidative function and preparation method thereof.Technical scheme of the present invention is that a kind of aloe viscose comprises viscose, it is characterized in that: contain extract solution from aloe in the viscose.Extract solution from aloe in the aloe viscose is the 1-50% of fibre weight.A kind of preparation method of aloe viscose, comprise cellulose sulfuric acid ester dissolving, filtration, mixed grinding and spinning work step, it is characterized in that: in the cellulose sulfonate course of dissolution, extract solution from aloe is added in the viscose glue, be blended into aloe rayon spinning liquid through stirring, the first fibre of this rayon spinning liquid is 7.5%-9.5%, containing alkali is 5 ± 0.5%, degree of ripeness is 9.2 ± 2ml, above-mentioned aloe rayon spinning liquid is filtered, viscose spinning bath and rayon spinning speed are carried out spinning routinely, make the aloe viscose through washing, bleach, oil, drying.
The weight that adds extract solution from aloe in the cellulose sulfonate course of dissolution is the 1-50% of aloe viscose weight.The general performance that aloe viscose of the present invention and viscose more not only have a viscose also has the skin cell metabolism of promotion and skin regeneration and can prevent the remarkable advantage of solar ultraviolet to the injury of skin.
The specific embodiment:
The manufacture method of aloe viscose of the present invention has following examples:
Embodiment 1:
Product specification: 166.7dtex
Raw material: cotton pulp extract solution from aloe
Extract solution from aloe addition: 20% of aloe viscose weight
A added extract solution from aloe wherein in the cellulose sulfonate course of dissolution, mixed into aloe rayon spinning liquid through 4 hours.Its index is:
First fibre: 7.5～9.5%
Contain alkali: 5 ± 0.5%
Viscosity: 30～50 seconds
Degree of ripeness: 9.2 ± 2ml
The rayon spinning liquid that b will contain extract solution from aloe filters through conventional three roads, and then increase one deck poplin cloth filter cloth filters, under conventional acid bath condition, with 90.7 meters/minute speed spinning, again through washing, bleach, oil, dry the aloe viscose that obtains having plurality of health care functions.
Embodiment 2:
Product specification 133.3dtex
The addition of extract solution from aloe accounts for 30% of aloe viscose weight
After the aloe nutritional extract filtered with 400 order filter clothes, before spinning, make it add in the viscose glue uniformly through injector by dynamic and static the mixing very much, under conventional acid bath condition, with 90.7 meters/minute speed spinning, again through the aloe viscose that washs, oven dry obtains having multiple function.
Spinning technology parameter
Nervous drawing-off d tightly=2.692%
Drawing-off d dish=20% between dish
Silk mouthful drawing-off d mouth=-0.5%
Total draft D always=22.62%
Spinning bath is formed
Sulfuric acid: 132 ± 1g/L
Zinc sulfate: 11 ± 0.5g/L
Sodium sulphate: 275 ± 3g/L
Acid bath drop: 2≤2g/L
The washing process condition
Pickling concentration: 3 ± 0.2g/L
Pickling temperature: room temperature
Desulfurization concentration: 5 ± 0.5g/L
Desulfurization temperature: 60 ± 2 ℃
Embodiment 3:
1.67dtex viscose staple fibre
Extract solution from aloe accounts for 40% of aloe viscose weight
In the cellulose sulfonate course of dissolution, extract solution from aloe is added in the viscose glue by 40% addition, mixed the aloe rayon spinning liquid that becomes to have antibiotic sun-proof skin care effect through 4 hours.Its index is:
First fibre: 8.5～9.5%
Contain alkali: 5.5～6.0%
Viscosity: 30～50 seconds
Degree of ripeness: 8～15ml (10%NH
4The CL value)
The rayon spinning liquid that will contain extract solution from aloe filters through conventional three roads, and then increase one deck poplin cloth filter cloth filters, under specific acid bath condition,, oil through the cut-out detergent bleach again and dry the aloe nutritional viscose staple fibre that obtains having multiple function with 50～85 meters/minute speed spinning.
(1) spinning technology parameter
Spinning head stretching 51～55%
Godet stretching 13～15%
Plasticizing stretching 21～25%
Total stretching 85～95%
(2) (grams per liter) formed in spinning bath:
Sulfuric acid: 105 ± 1g/L
Zinc sulfate: 13 ± 0.5g/L
Sodium sulphate: 330 ± 10g/L
Acid bath drop :≤10g/L
(3) washing process condition
Desulfurization concentration: 2～8g/L
Desulfurization temperature: 70～80 ℃
Pickling concentration: 0.5～3g/L
Pickling temperature: 20～50 ℃.
Claims (2)
1. the preparation method of an aloe viscose, comprise cellulose sulfuric acid ester dissolving, filtration, mixed grinding and spinning work step, it is characterized in that: in the cellulose sulfonate course of dissolution, extract solution from aloe is added in the viscose glue, be blended into aloe rayon spinning liquid through stirring, the first fibre of this rayon spinning liquid is 7.5%-9.5%, containing alkali is 5 ± 0.5%, degree of ripeness is 9.2 ± 2ml, above-mentioned aloe rayon spinning liquid is filtered, viscose spinning bath and rayon spinning speed are carried out spinning routinely, make the aloe viscose through washing, oil, drying.
2. the preparation method of a kind of aloe viscose as claimed in claim 1 is characterized in that: the weight that adds extract solution from aloe in the cellulose sulfonate course of dissolution is the 1-50% of aloe viscose weight.