CN107625652A - One kind melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask and preparation method thereof - Google Patents
One kind melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask and preparation method thereof Download PDFInfo
- Publication number
- CN107625652A CN107625652A CN201710872617.6A CN201710872617A CN107625652A CN 107625652 A CN107625652 A CN 107625652A CN 201710872617 A CN201710872617 A CN 201710872617A CN 107625652 A CN107625652 A CN 107625652A
- Authority
- CN
- China
- Prior art keywords
- parts
- prepared
- face mask
- nonwoven cloth
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask and preparation method thereof, according to mass percent, it is prepared from the following components：25 35 parts of string, 10 20 parts of terylene, 6 12 parts of viscose rayon, 59 parts of polypropylene fibre, preparation method are：String, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；Mixed material is melted into melt using screw extruder；Sizing turns into fiber；Fiber is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, forms continuous arlt's strata；Continuous arlt's strata is prepared into by non-woven fabrics using hot-rolling mill；The non-woven fabrics being prepared is soaked 35 65 minutes in fibroin liquid；One layer of Essence is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.The present invention has the advantages that anti-wrinkle effect is good, skin care effect is obvious.
Description
Technical field
The present invention relates to non-woven fabrics facial mask preparation field, and specifically a kind of melt-blown composite plant fabric nonwoven cloth is crease-resistant
Facial mask and preparation method thereof.
Background technology
Non-woven fabrics is a kind of non-woven cloth, and it is that fiber directly is passed through into gas using high polymer section, chopped fiber or long filament
Stream or mechanical networking, then reinforced by spun lacing, acupuncture, or hot rolling, the non-woven cloth finally formed by final finishing, tool
There is soft, ventilative and planar structure tencel product, advantage is not produce Soft flocks, tough, durable, as soft as silk.
Facial mask, the principle of facial mask, exactly using the of short duration time for being covered in face, it is temporarily isolating air and the dirt in the external world
Dye, skin temperature is improved, the pore expansion of skin, promotes sweat gland secretion and metabolism, the oxygen content of skin is increased, facial mask
Be advantageous to skin and exclude the product of epidermal cell metabolism and the oil substances of accumulation, the moisture in facial mask penetrates into skin table
The cuticula of skin, skin become soft, increase elasticity, want the skin care that facial mask has the effects such as whitening and moisturizing just to select specialty
Facial mask, skin is not stimulated specialty products and injury, are trusted with health, the mask sheet of one bag of bag of in the market, are all chemistry
Preparation bubbles out what is come, and sensitiveness skin is not suitable for using, certain when facial mask is selected it should be noted that specialty health is very heavy
Will.
With the continuous improvement of people's living standards, corresponding, the quality of life of people also gradually steps up, wherein, the present age
People have started to focus on skin care importance, especially like to be beautiful Ms, for skin wrinkle it is then heavier regard, it is at present, existing
Anti-wrinkle face mask generally existing anti-wrinkle effect difference the defects of, it is therefore desirable to be further improved.
The content of the invention
Anti-wrinkle effect of the prior art is poor, the unconspicuous defect of skin care effect the invention aims to solving, and carries
Solved the above problems for one kind melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask and preparation method thereof.
To achieve these goals, technical scheme is as follows：The invention discloses one kind melt-blown composite plant is fine
Non-woven fabrics anti-wrinkle face mask is tieed up, according to mass percent, is prepared from the following components：String 25-35 parts, terylene 10-20
Part, viscose rayon 6-12 parts, polypropylene fibre 5-9 parts.
Preferably, the invention discloses one kind to be meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, according to quality percentage
Than being prepared from the following components：30 parts of string, 15 parts of terylene, 9 parts of viscose rayon, 7 parts of polypropylene fibre.
Preferably, described string uses bamboo fibre or flax.
Preferably, the invention also discloses a kind of above-mentioned preparation side for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask
Method, step are as follows：
(1), string, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；
(2) mixed material, is melted into melt using screw extruder；
(3) melt, is extruded by tow from spinneret orifice by spinning die head, under cold wind effect, by drawing-off air channel by silk
Beam cooling drafting forming turns into fiber；
(4) fiber, is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, is formed continuous netted
Fibrous layer；
(5) continuous arlt's strata, is prepared into by non-woven fabrics using hot-rolling mill；
(6) non-woven fabrics being prepared, is soaked into 35-65 minutes in fibroin liquid；
(7) one layer of Essence, is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
Glycerine 8-12 parts, triethanolamine 6-10 parts, natural perfume material 3-9 parts, trehalose 2-8 parts, Phenoxyethanol 3-9 parts, Fresh Cucumber Juice 5-10
Part, cider 5-20 parts, arginine 3-6 parts, carbomer 4-15 parts, extract solution from aloe 5-15 parts, honey 5-10 parts, pure water 3-
9 parts.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
10 parts of glycerine, 8 parts of triethanolamine, 6 parts of natural perfume material, 5 parts of trehalose, 6 parts of Phenoxyethanol, 7 parts of Fresh Cucumber Juice, 12 parts of cider,
4 parts of arginine, 10 parts of carbomer, 10 parts of extract solution from aloe, 7 parts of honey, 6 parts of pure water.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
8 parts of glycerine, 10 parts of triethanolamine, 3 parts of natural perfume material, 8 parts of trehalose, 3 parts of Phenoxyethanol, 10 parts of Fresh Cucumber Juice, 5 parts of cider,
6 parts of arginine, 4 parts of carbomer, 15 parts of extract solution from aloe, 5 parts of honey, 9 parts of pure water.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
12 parts of glycerine, 6 parts of triethanolamine, 9 parts of natural perfume material, 2 parts of trehalose, 9 parts of Phenoxyethanol, 5 parts of Fresh Cucumber Juice, 20 parts of cider,
3 parts of arginine, 15 parts of carbomer, 5 parts of extract solution from aloe, 10 parts of honey, 3 parts of pure water.
Preferably, the preparation method of described Essence is：According to above-mentioned parts by weight, by glycerine, triethanolamine, day
Right spices, trehalose, Phenoxyethanol, Fresh Cucumber Juice, cider, arginine, carbomer, extract solution from aloe, honey are added to pure
In water, stir and Essence is prepared.
The present invention has advantages below compared with prior art：
Melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask of the present invention is by by non-woven fabrics and above-mentioned elite liquid phase
Coordinate, non-woven fabrics has excellent toughness, gas permeability, beneficial to the absorption of facial mask nutritional ingredient, and is hardly damaged, and Essence
In containing abundant nutritional ingredient, there is excellent anti-wrinkle effect to skin.
Embodiment
The invention discloses one kind to be meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, according to mass percent, by following
Component is prepared：String 25-35 parts, terylene 10-20 parts, viscose rayon 6-12 parts, polypropylene fibre 5-9 parts.
Preferably, the invention discloses one kind to be meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, according to quality percentage
Than being prepared from the following components：30 parts of string, 15 parts of terylene, 9 parts of viscose rayon, 7 parts of polypropylene fibre.
Preferably, described string uses bamboo fibre or flax.
Preferably, the invention also discloses a kind of above-mentioned preparation side for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask
Method, step are as follows：
(1), string, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；
(2) mixed material, is melted into melt using screw extruder；
(3) melt, is extruded by tow from spinneret orifice by spinning die head, under cold wind effect, by drawing-off air channel by silk
Beam cooling drafting forming turns into fiber；
(4) fiber, is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, is formed continuous netted
Fibrous layer；
(5) continuous arlt's strata, is prepared into by non-woven fabrics using hot-rolling mill；
(6) non-woven fabrics being prepared, is soaked into 35-65 minutes in fibroin liquid；
(7) one layer of Essence, is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
Glycerine 8-12 parts, triethanolamine 6-10 parts, natural perfume material 3-9 parts, trehalose 2-8 parts, Phenoxyethanol 3-9 parts, Fresh Cucumber Juice 5-10
Part, cider 5-20 parts, arginine 3-6 parts, carbomer 4-15 parts, extract solution from aloe 5-15 parts, honey 5-10 parts, pure water 3-
9 parts.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
10 parts of glycerine, 8 parts of triethanolamine, 6 parts of natural perfume material, 5 parts of trehalose, 6 parts of Phenoxyethanol, 7 parts of Fresh Cucumber Juice, 12 parts of cider,
4 parts of arginine, 10 parts of carbomer, 10 parts of extract solution from aloe, 7 parts of honey, 6 parts of pure water.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
8 parts of glycerine, 10 parts of triethanolamine, 3 parts of natural perfume material, 8 parts of trehalose, 3 parts of Phenoxyethanol, 10 parts of Fresh Cucumber Juice, 5 parts of cider,
6 parts of arginine, 4 parts of carbomer, 15 parts of extract solution from aloe, 5 parts of honey, 9 parts of pure water.
Preferably, in described step (7), according to parts by weight, described Essence is prepared from the following components：
12 parts of glycerine, 6 parts of triethanolamine, 9 parts of natural perfume material, 2 parts of trehalose, 9 parts of Phenoxyethanol, 5 parts of Fresh Cucumber Juice, 20 parts of cider,
3 parts of arginine, 15 parts of carbomer, 5 parts of extract solution from aloe, 10 parts of honey, 3 parts of pure water.
Preferably, the preparation method of described Essence is：According to above-mentioned parts by weight, by glycerine, triethanolamine, day
Right spices, trehalose, Phenoxyethanol, Fresh Cucumber Juice, cider, arginine, carbomer, extract solution from aloe, honey are added to pure
In water, stir and Essence is prepared.
Embodiment 1
The invention discloses one kind to be meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, according to mass percent, by following
Component is prepared：30 parts of string, 15 parts of terylene, 9 parts of viscose rayon, 7 parts of polypropylene fibre.
Described string uses bamboo fibre.
The invention also discloses a kind of above-mentioned preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, step is such as
Under：
(1), string, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；
(2) mixed material, is melted into melt using screw extruder；
(3) melt, is extruded by tow from spinneret orifice by spinning die head, under cold wind effect, by drawing-off air channel by silk
Beam cooling drafting forming turns into fiber；
(4) fiber, is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, is formed continuous netted
Fibrous layer；
(5) continuous arlt's strata, is prepared into by non-woven fabrics using hot-rolling mill；
(6), the non-woven fabrics being prepared is soaked 50 minutes in fibroin liquid；
(7) one layer of Essence, is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.
In described step (7), according to parts by weight, described Essence is prepared from the following components：10 parts of glycerine,
8 parts of triethanolamine, 6 parts of natural perfume material, 5 parts of trehalose, 6 parts of Phenoxyethanol, 7 parts of Fresh Cucumber Juice, 12 parts of cider, 4 parts of arginine,
10 parts of carbomer, 10 parts of extract solution from aloe, 7 parts of honey, 6 parts of pure water.
The preparation method of described Essence is：According to above-mentioned parts by weight, by glycerine, triethanolamine, natural perfume material, sea
Algae sugar, Phenoxyethanol, Fresh Cucumber Juice, cider, arginine, carbomer, extract solution from aloe, honey are added in pure water, stirring
Essence uniformly is prepared.
Embodiment 2
The invention discloses one kind to be meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, according to mass percent, by following
Component is prepared：35 parts of string, 10 parts of terylene, 12 parts of viscose rayon, 5 parts of polypropylene fibre.
Described string uses bamboo fibre.
The invention also discloses a kind of above-mentioned preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, step is such as
Under：
(1), string, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；
(2) mixed material, is melted into melt using screw extruder；
(3) melt, is extruded by tow from spinneret orifice by spinning die head, under cold wind effect, by drawing-off air channel by silk
Beam cooling drafting forming turns into fiber；
(4) fiber, is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, is formed continuous netted
Fibrous layer；
(5) continuous arlt's strata, is prepared into by non-woven fabrics using hot-rolling mill；
(6), the non-woven fabrics being prepared is soaked 65 minutes in fibroin liquid；
(7) one layer of Essence, is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.
In described step (7), according to parts by weight, described Essence is prepared from the following components：8 parts of glycerine,
10 parts of triethanolamine, 3 parts of natural perfume material, 8 parts of trehalose, 3 parts of Phenoxyethanol, 10 parts of Fresh Cucumber Juice, 5 parts of cider, arginine 6
Part, 4 parts of carbomer, 15 parts of extract solution from aloe, 5 parts of honey, 9 parts of pure water.
The preparation method of described Essence is：According to above-mentioned parts by weight, by glycerine, triethanolamine, natural perfume material, sea
Algae sugar, Phenoxyethanol, Fresh Cucumber Juice, cider, arginine, carbomer, extract solution from aloe, honey are added in pure water, stirring
Essence uniformly is prepared.
Embodiment 3
The invention discloses one kind to be meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, according to mass percent, by following
Component is prepared：26 parts of string, 12 parts of terylene, 11 parts of viscose rayon, 7 parts of polypropylene fibre.
Described string uses flax.
The invention also discloses a kind of above-mentioned preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask, step is such as
Under：
(1), string, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；
(2) mixed material, is melted into melt using screw extruder；
(3) melt, is extruded by tow from spinneret orifice by spinning die head, under cold wind effect, by drawing-off air channel by silk
Beam cooling drafting forming turns into fiber；
(4) fiber, is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, is formed continuous netted
Fibrous layer；
(5) continuous arlt's strata, is prepared into by non-woven fabrics using hot-rolling mill；
(6), the non-woven fabrics being prepared is soaked 64 minutes in fibroin liquid；
(7) one layer of Essence, is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.
In described step (7), according to parts by weight, described Essence is prepared from the following components：12 parts of glycerine,
6 parts of triethanolamine, 9 parts of natural perfume material, 2 parts of trehalose, 9 parts of Phenoxyethanol, 5 parts of Fresh Cucumber Juice, 20 parts of cider, 3 parts of arginine,
15 parts of carbomer, 5 parts of extract solution from aloe, 10 parts of honey, 3 parts of pure water.
The preparation method of described Essence is：According to above-mentioned parts by weight, by glycerine, triethanolamine, natural perfume material, sea
Algae sugar, Phenoxyethanol, Fresh Cucumber Juice, cider, arginine, carbomer, extract solution from aloe, honey are added in pure water, stirring
Essence uniformly is prepared.
The women of 120 different age groups of selection is tried out the present invention, tries out comparing result such as table 1 before and after skin：
Table 1
As shown in Table 1, the melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask that the present invention is prepared can promote Ms
Skin more water moistens, and anti-wrinkle effect is relatively good.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is the present invention
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appended claims and its
Equivalent defines.
Claims (9)
1. one kind melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask, it is characterised in that：According to mass percent, by following components
It is prepared：String 25-35 parts, terylene 10-20 parts, viscose rayon 6-12 parts, polypropylene fibre 5-9 parts.
A kind of 2. melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 1, it is characterised in that：According to matter
Percentage is measured, is prepared from the following components：30 parts of string, 15 parts of terylene, 9 parts of viscose rayon, 7 parts of polypropylene fibre.
A kind of 3. melt-blown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 1 or 2, it is characterised in that：Institute
The string stated uses bamboo fibre or flax.
4. a kind of preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 1 or 2, it is special
Sign is：Step is as follows：
(1), string, terylene, viscose rayon, polypropylene fibre are mixed to obtain mixed material；
(2) mixed material, is melted into melt using screw extruder；
(3) melt, is extruded by tow from spinneret orifice by spinning die head, it is by drawing-off air channel that tow is cold under cold wind effect
But drafting forming turns into fiber；
(4) fiber, is passed through into diffusor duct, fiber is uniformly adsorbed onto on Web forming conveyer belt, forms continuous reticular fibre
Layer；
(5) continuous arlt's strata, is prepared into by non-woven fabrics using hot-rolling mill；
(6) non-woven fabrics being prepared, is soaked into 35-65 minutes in fibroin liquid；
(7) one layer of Essence, is respectively coated on the two sides of non-woven fabrics, then using packaging bag hermetic package.
5. a kind of preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 4, its feature
It is：In described step (7), according to parts by weight, described Essence is prepared from the following components：Glycerine 8-12 parts,
Triethanolamine 6-10 parts, natural perfume material 3-9 parts, trehalose 2-8 parts, Phenoxyethanol 3-9 parts, Fresh Cucumber Juice 5-10 parts, cider 5-
20 parts, arginine 3-6 parts, carbomer 4-15 parts, extract solution from aloe 5-15 parts, honey 5-10 parts, pure water 3-9 parts.
6. a kind of preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 4, its feature
It is：In described step (7), according to parts by weight, described Essence is prepared from the following components：10 parts of glycerine, three
8 parts of monoethanolamine, 6 parts of natural perfume material, 5 parts of trehalose, 6 parts of Phenoxyethanol, 7 parts of Fresh Cucumber Juice, 12 parts of cider, 4 parts of arginine, card
10 parts of ripple nurse, 10 parts of extract solution from aloe, 7 parts of honey, 6 parts of pure water.
7. a kind of preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 4, its feature
It is：In described step (7), according to parts by weight, described Essence is prepared from the following components：8 parts of glycerine, three second
10 parts of hydramine, 3 parts of natural perfume material, 8 parts of trehalose, 3 parts of Phenoxyethanol, 10 parts of Fresh Cucumber Juice, 5 parts of cider, 6 parts of arginine, card
4 parts of ripple nurse, 15 parts of extract solution from aloe, 5 parts of honey, 9 parts of pure water.
8. a kind of preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 4, its feature
It is：In described step (7), according to parts by weight, described Essence is prepared from the following components：12 parts of glycerine, three
6 parts of monoethanolamine, 9 parts of natural perfume material, 2 parts of trehalose, 9 parts of Phenoxyethanol, 5 parts of Fresh Cucumber Juice, 20 parts of cider, 3 parts of arginine, card
15 parts of ripple nurse, 5 parts of extract solution from aloe, 10 parts of honey, 3 parts of pure water.
9. a kind of preparation method for being meltblown composite plant fabric nonwoven cloth anti-wrinkle face mask according to claim 4, its feature
It is：The preparation method of described Essence is：According to above-mentioned parts by weight, by glycerine, triethanolamine, natural perfume material, marine alga
Sugar, Phenoxyethanol, Fresh Cucumber Juice, cider, arginine, carbomer, extract solution from aloe, honey are added in pure water, and stirring is equal
It is even that Essence is prepared.