CN104013335A - Antibacterial towel - Google Patents
Antibacterial towel Download PDFInfo
- Publication number
- CN104013335A CN104013335A CN201410288443.5A CN201410288443A CN104013335A CN 104013335 A CN104013335 A CN 104013335A CN 201410288443 A CN201410288443 A CN 201410288443A CN 104013335 A CN104013335 A CN 104013335A
- Authority
- CN
- China
- Prior art keywords
- parts
- hydrogen peroxide
- cloth
- antibacterial
- quality
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial towel, belonging to the technical field of toiletries. The antibacterial towel is produced by the following steps: dissolving cellulose sulfate into water, and uniformly stirring with an aloe water extract and seaweed with particle size being less than 1 micron to obtain a spinning solution; spinning and weaving by use of the spinning solution; and performing boiling, dyeing, washing, softening, dehydration, drying and trimming treatment on the cloth to obtain the antibacterial towel. The antibacterial towel disclosed by the invention has antibacterial and anti-inflammatory functions; moreover, the production cost is low, the raw materials are natural, and no harmful chemical component is contained in the antibacterial towel.
Description
Technical field
The invention belongs to bath accessory technical field, relate in particular to a kind of antibacterial towel.
Background technology
Traditional towel generally only possesses cleaning action, to the skin of human body without health care, skin-protecting function.At present, also someone starts to develop some functional towels, and such towel is subject to people's vast welcome deeply.Yet because functional towel is a kind of novel towel products, its production technology is not yet perfect, make such towel ubiquity production cost high, the problem that chemical Harmful ingredient content is too high.These problems make functional towel be difficult to be promoted.
Summary of the invention
The technical problem that the present invention solves is to provide a kind of antibacterial towel, effect antibacterial, anti-inflammatory that this antibacterial towel not only has, and also its production cost is low, and raw material is natural, not containing chemical harmful components.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
An antibacterial towel, comprises the raw material of following parts by weight: 60 parts～80 parts of cellulose sulfuric acid esters, 8 parts～12 parts of the marine algas that 10 parts～20 parts of aloe water extracts and particle diameter are less than 1 micron;
Its preparation method comprises the following steps:
A, by above-mentioned parts by weight, first cellulose sulfuric acid ester is dissolved in the water of 5 times～10 times of described cellulose sulfuric acid ester quality, then add aloe water extract, and the particle diameter marine alga that is less than 1 micron, stir, make spinning solution;
B, the spinning solution that A step is made carry out spinning, weave cotton cloth;
C, by B step knit cloth put into the digesting apparatus of the water that 1 times～2 times of described cloth quality are housed in advance, then to 30% hydrogen peroxide adding in described digesting apparatus, 4% NaOH and hydrogen peroxide stabilizer, be heated to boiling, boiling 1 minute～5 minutes, take out, being washed to pH value is 5.0～6.5; Wherein, the addition of described 30% hydrogen peroxide is 1% of described cloth quality, and the addition of described 4% NaOH is 10% of described cloth quality, and the addition of described hydrogen peroxide stabilizer is 10% of described 30% hydrogen peroxide quality;
D, by the cloth after C step process dye, wash, soften, dehydration, oven dry and strip limit process, and obtains the towel of this antibacterial energy.
Owing to adopting technique scheme, the beneficial effect that the present invention obtains is:
Effect antibacterial, anti-inflammatory that the antibacterial towel that the present invention makes not only has, and its production cost is low, and raw material is natural, not containing chemical harmful components.
The specific embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only confined to following examples.
Embodiment 1
This antibacterial towel comprises following raw materials: cellulose sulfuric acid ester 6.0kg, the marine alga 1.2kg that aloe water extract 2.0kg and particle diameter are less than 1 micron;
Its preparation method comprises the following steps:
A, first 6.0kg cellulose sulfuric acid ester is dissolved in 30kg water, then adds 2.0kg aloe water extract, and the 1.2kg particle diameter marine alga that is less than 1 micron, stir, make spinning solution;
B, the spinning solution that A step is made carry out spinning, weave cotton cloth;
C, by B step knit cloth put into the digesting apparatus of the water that 1 times of described cloth quality is housed in advance, then to 30% hydrogen peroxide adding in described digesting apparatus, 4% NaOH and hydrogen peroxide stabilizer, be heated to boiling, boiling 1 minute, takes out, and being washed to pH value is 5.0; Wherein, the addition of described 30% hydrogen peroxide is 1% of described cloth quality, and the addition of described 4% NaOH is 10% of described cloth quality, and the addition of described hydrogen peroxide stabilizer is 10% of described 30% hydrogen peroxide quality;
D, by the cloth after C step process dye, wash, soften, dehydration, oven dry and strip limit process, and obtains this antibacterial towel.
Through evidence, the effect of the skin care such as that the antibacterial towel that the present embodiment makes has is antibacterial, anti-inflammatory, and under the warm condition of humidity, can not go mouldy yet, smelly.
Embodiment 2
This antibacterial towel comprises following raw materials: cellulose sulfuric acid ester 8.0kg, the marine alga 0.8kg that aloe water extract and particle diameter are less than 1 micron;
Its preparation method comprises the following steps:
A, first 8.0kg cellulose sulfuric acid ester is dissolved in 80kg water, then adds 1.0kg aloe water extract, and the 0.8kg particle diameter marine alga that is less than 1 micron, stir, make spinning solution;
B, the spinning solution that A step is made carry out spinning, weave cotton cloth;
C, by B step knit cloth put into the digesting apparatus of the water that 2 times of described cloth quality are housed in advance, then to 30% hydrogen peroxide adding in described digesting apparatus, 4% NaOH and hydrogen peroxide stabilizer, be heated to boiling, boiling 5 minutes, takes out, and being washed to pH value is 6.5; Wherein, the addition of described 30% hydrogen peroxide is 1% of described cloth quality, and the addition of described 4% NaOH is 10% of described cloth quality, and the addition of described hydrogen peroxide stabilizer is 10% of described 30% hydrogen peroxide quality;
D, by the cloth after C step process dye, wash, soften, dehydration, oven dry and strip limit process, and obtains this antibacterial towel.
Through evidence, the effect of the skin care such as that the antibacterial towel that the present embodiment makes has is antibacterial, anti-inflammatory, and under the warm condition of humidity, can not go mouldy yet, smelly.
Embodiment 3
This antibacterial towel comprises following raw materials: cellulose sulfuric acid ester 7.0kg, the marine alga 1.0kg that aloe water extract 1.7kg and particle diameter are less than 1 micron;
Its preparation method comprises the following steps:
A, first 7.0kg cellulose sulfuric acid ester is dissolved in 56kg water, then adds 1.7kg aloe water extract, and the 1.0kg particle diameter marine alga that is less than 1 micron, stir, make spinning solution;
B, the spinning solution that A step is made carry out spinning, weave cotton cloth;
C, by B step knit cloth put into the digesting apparatus that the water of cloth quality described in 1 times 8 is housed in advance, then to 30% hydrogen peroxide adding in described digesting apparatus, 4% NaOH and hydrogen peroxide stabilizer, be heated to boiling, boiling 4 minutes, takes out, and being washed to pH value is 6; Wherein, the addition of described 30% hydrogen peroxide is 1% of described cloth quality, and the addition of described 4% NaOH is 10% of described cloth quality, and the addition of described hydrogen peroxide stabilizer is 10% of described 30% hydrogen peroxide quality;
D, by the cloth after C step process dye, wash, soften, dehydration, oven dry and strip limit process, and obtains antibacterial towel.
Through evidence, the effect of the skin care such as that the antibacterial towel that the present embodiment makes has is antibacterial, anti-inflammatory, and under the warm condition of humidity, can not go mouldy yet, smelly.
Claims (1)
1. an antibacterial towel, is characterized in that comprising the raw material of following parts by weight: 60 parts～80 parts of cellulose sulfuric acid esters, 8 parts～12 parts of the marine algas that 10 parts～20 parts of aloe water extracts and particle diameter are less than 1 micron;
Its preparation method comprises the following steps:
A, by above-mentioned parts by weight, first cellulose sulfuric acid ester is dissolved in the water of 5 times～10 times of described cellulose sulfuric acid ester quality, then add aloe water extract, and the particle diameter marine alga that is less than 1 micron, stir, make spinning solution;
B, the spinning solution that A step is made carry out spinning, weave cotton cloth;
C, by B step knit cloth put into the digesting apparatus of the water that 1 times～2 times of described cloth quality are housed in advance, then to 30% hydrogen peroxide adding in described digesting apparatus, 4% NaOH and hydrogen peroxide stabilizer, be heated to boiling, boiling 1 minute～5 minutes, take out, being washed to pH value is 5.0～6.5; Wherein, the addition of described 30% hydrogen peroxide is 1% of described cloth quality, and the addition of described 4% NaOH is 10% of described cloth quality, and the addition of described hydrogen peroxide stabilizer is 10% of described 30% hydrogen peroxide quality;
D, by the cloth after C step process dye, wash, soften, dehydration, oven dry and strip limit process, and obtains this antibacterial towel.