CN108044090A - 一种钢包包底砌筑方法 - Google Patents
一种钢包包底砌筑方法 Download PDFInfo
- Publication number
- CN108044090A CN108044090A CN201810052120.4A CN201810052120A CN108044090A CN 108044090 A CN108044090 A CN 108044090A CN 201810052120 A CN201810052120 A CN 201810052120A CN 108044090 A CN108044090 A CN 108044090A
- Authority
- CN
- China
- Prior art keywords
- working lining
- containment wall
- ladle
- permanent layer
- artistic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及钢包技术领域,具体涉及一种钢包包底砌筑方法。包括以下步骤,在浇注包壁永久层脱模之后,先按照烘烤曲线进行永久层烘烤,待耐材冷却至室温时,在包底永久层和包壁永久层结合处平放铺设一圈工艺砖;然后浇注包壁工作层,待包壁工作层成型后,去除包壁工作层包底处一圈部分浇注料(高度为工艺砖的高度,厚度到工艺砖即可);然后再浇注包底工作层,凝固后进行烘烤即可。本发明的一种钢包包底砌筑方法,采用先浇包壁工作层后浇包底工作层的模式,既保证安全,也能降低砌包时间,即保证了生产节奏。
Description
技术领域
本发明涉及钢包技术领域,具体涉及一种钢包包底砌筑方法。
背景技术
目前全国各大钢厂对钢包的砌筑采用整体浇注模式居多,然而对于包壁和包底工作层的浇注顺序又有不同方式。
先浇包壁后浇包底工作层,整个钢包的浇注时间短,但是容易出现安全事故,钢包容易出现穿包事故,在钢包倾翻时包底可能掉落(宝钢曾经发生过类似事故);先浇包底工作层后浇包壁,钢包倾翻时包底不会掉落,但浇注时间会增加24~36小时,影响生产周期。
本发明为解决钢包倾翻时包底不掉落,钢包不穿包,同时降低钢包的浇注时间,利于生产组织。
发明内容
本发明的目的在于提供一种钢包包底砌筑方法,采用先浇包壁工作层后浇包底工作层的模式,既保证安全,也能降低砌包时间,即保证了生产节奏。
一种钢包包底砌筑方法,包括以下步骤,
(1)在浇注包壁永久层脱模之后,先按照烘烤曲线进行永久层烘烤,待耐材冷却至室温时,在包底永久层和包壁永久层结合处平放铺设一圈工艺砖;
(2)然后浇注包壁工作层,待包壁工作层成型后,去除包壁工作层包底处一圈部分浇注料(高度为工艺砖的高度,厚度到工艺砖即可);
(3)然后再浇注包底工作层,凝固后进行烘烤即可。
步骤(1)中,所述工艺砖尺寸:高度为包底工作层的一半,厚度要小于包壁工作层约30-50mm,宽度约120mm。
步骤(1)中,所述工艺砖材质为刚玉质。
本发明具有以下有益效果:一种钢包包底砌筑方法,
1、采用先浇包壁工作层后浇包底工作层的顺序,保证了整个钢包的浇注周期短;
2、采用工艺砖的发明思路保证了钢包在倾翻时,包底工作层有包壁工作层作支撑,杜绝了包底不会脱落的风险;
3、由于工艺砖的作用,改变了钢水从包壁和包底工作层的缝隙直接进入到包底永久层,也降低了包底穿钢的风险。
附图说明
图1为本发明需要去除部分包壁工作层浇注料示意图;
图2为本发明包底工作层浇注后示意图。
其中:1、包壁永久层,2、工艺砖,3、包壁工作层,4、需要去除部分,5、包底永久层,6、包底工作层。
具体实施方式
一种钢包包底砌筑方法,包括以下步骤,
(1)在浇注包壁永久层脱模之后,先按照烘烤曲线进行永久层烘烤,待耐材冷却至室温时,在包底永久层和包壁永久层结合处平放铺设一圈工艺砖;
(2)然后浇注包壁工作层,待包壁工作层成型后,去除包壁工作层包底处一圈部分浇注料(高度为工艺砖的高度,厚度到工艺砖即可);
(3)然后再浇注包底工作层,凝固后进行烘烤即可。
步骤(1)中,所述工艺砖尺寸:高度为包底工作层的一半,厚度要小于包壁工作层约30-50mm,宽度约120mm。
步骤(1)中,所述工艺砖材质为刚玉质。
Claims (3)
1.一种钢包包底砌筑方法,其特征在于,包括以下步骤,
(1)在浇注包壁永久层脱模之后,先按照烘烤曲线进行永久层烘烤,待耐材冷却至室温时,在包底永久层和包壁永久层结合处平放铺设一圈工艺砖;
(2)然后浇注包壁工作层,待包壁工作层成型后,去除包壁工作层包底处一圈部分浇注料(高度为工艺砖的高度,厚度到工艺砖即可);
(3)然后再浇注包底工作层,凝固后进行烘烤即可。
2.根据权利要求1所述的一种钢包包底砌筑方法,其特征在于,步骤(1)中,所述工艺砖尺寸:高度为包底工作层的一半,厚度要小于包壁工作层约30-50mm,宽度约120mm。
3.根据权利要求1所述的一种钢包包底砌筑方法,其特征在于,步骤(1)中,所述工艺砖材质为刚玉质。