CN107698157A - A kind of composite Jewel indigo plant pottery glaze and preparation method thereof - Google Patents
A kind of composite Jewel indigo plant pottery glaze and preparation method thereof Download PDFInfo
- Publication number
- CN107698157A CN107698157A CN201711066547.1A CN201711066547A CN107698157A CN 107698157 A CN107698157 A CN 107698157A CN 201711066547 A CN201711066547 A CN 201711066547A CN 107698157 A CN107698157 A CN 107698157A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- raw material
- pottery
- indigo plant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of composite Jewel indigo plant pottery glaze and its manufacture method, and it is prepared by the raw material of following parts by weight：30 parts to 40 parts of this medicine, 25 parts to 30 parts of feldspar, 20 parts to 25 parts of calcite, 20 parts to 30 parts of quartz, 7 parts to 10 parts of lime stone, 7 parts to 10 parts of Copper Ores, 3 parts to 5 parts of plant ash, 2 parts to 4 parts of zinc oxide, 1 part to 2 parts of tin oxide, 0.5 part to 1.5 parts of talcum powder；In glaze dispensing, although the raw material used for very common raw material, is made up of rational raw material and the adjustment of deal, also there is synergy, glaze colours is uniform, bright in colour between each raw material, mobility is moderate, pottery made of glaze formula provided by the present invention, colour generation is uniform, and glossiness is good, uniform color, glaze paint are plump, have unique artistic effect, the perception of deep, steady, dignified air is given people, and glaze hacking is uniform, high yield rate.
Description
Technical field
The present invention relates to pottery field, and in particular to a kind of composite Jewel indigo plant pottery glaze and preparation method thereof.
Background technology
Pottery is originated in the Eastern Han Dynasty, is one of five big kiln porcelain of Song Dynasty, the treasure in Chinese tradition technology in producing porcelain, is referred to as
National treasure, rarity.It is world-famous for the transmutation art of uniqueness, is known as " the valuable an ancient unit of weight of gold is priceless " and " there is ten thousand strings of cash in family, not as pottery
One " good reputation.It is the exclusive national treasure porcelain in Henan Province Xuchang City Yuzhou City god Hou towns, by its simple and unsophisticated moulding, consummate
Technique, the complicated magical transmutation, the beautiful scenery of lakes and mountains, rosy clouds fog, people's beast flower, bird, insect, and fish etc. with glaze, " it is color to enter kiln kiln discharge ten thousand of the same colour "
Varied figure color and marvellous charm, it is described as first of Chinese " five big porcelain ".
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, typically using bavin, coal, charcoal
Fired with natural gas, glaze color change is also different caused by different burning process.Outside is glaze by being produced during high-temperature fusion
Raw gorgeous colorful change, for reason mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Therefore, it is pure disclose a kind of raw material by the present invention, and proportioning novelty, preparation method is simple, rich in color bright-coloured compound
Sapphire blue pottery glaze and preparation method thereof has high artistic value and extensive market prospects.
The content of the invention
It is pure that the present invention disclose a kind of raw material, and proportioning is novel, and preparation method is simple, bright-coloured composite Jewel indigo plant rich in color
Pottery glaze and preparation method thereof.
The technical proposal of the invention is realized in this way：A kind of composite Jewel indigo plant pottery glaze, it is by following parts by weight
What several raw materials was prepared：30 parts to 40 parts of this medicine, 25 parts to 30 parts of feldspar, 20 parts to 25 parts of calcite, 20 parts of quartz is extremely
30 parts, 7 parts to 10 parts of lime stone, 7 parts to 10 parts of Copper Ores, 3 parts to 5 parts of plant ash, 2 parts to 4 parts of zinc oxide, 1 part of tin oxide
To 2 parts, 0.5 part to 1.5 parts of talcum powder.
Described composite Jewel indigo plant pottery glaze, it is prepared by the raw material of following parts by weight：35 parts of this medicine,
28 parts of feldspar, 22 parts of calcite, 21 parts of quartz, 8 parts of lime stone, 8 parts of Copper Ores, 4 parts of plant ash, 3 parts of zinc oxide, tin oxide 1
Part, 1 part of talcum powder.
The preparation method of described composite Jewel indigo plant pottery glaze, comprises the following steps：
（1）Glaze described in claim 1 is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is
1.25:2:3, Ball-milling Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
Technical scheme has following good effect：In glaze dispensing, although the raw material used is very common
Raw material, but be made up of rational raw material and the adjustment of deal, also there is synergy between each raw material, glaze colours is uniform,
Lovely luster, mobility is moderate, and pottery made of glaze formula provided by the present invention, colour generation is uniform, and glossiness is good, and color and luster is equal
It is even, glaze paint is plump, has unique artistic effect, give people the perception of deep, steady, dignified air, and glaze hacking is uniform, finished product
Rate is high.
Embodiment
Embodiment 1：A kind of composite Jewel indigo plant pottery glaze, it is prepared by the raw material of following parts by weight：This
35 parts of medicine, 28 parts of feldspar, 22 parts of calcite, 21 parts of quartz, 8 parts of lime stone, 8 parts of Copper Ores, 4 parts of plant ash, 3 parts of zinc oxide,
1 part of tin oxide, 1 part of talcum powder.
The preparation method of described composite Jewel indigo plant pottery glaze, comprises the following steps：
（1）Glaze described in claim 1 is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is
1.25:2:3, Ball-milling Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
Embodiment 2：A kind of composite Jewel indigo plant pottery glaze, it is prepared by the raw material of following parts by weight：This
30 parts of medicine, 25 parts of feldspar, 20 parts of calcite, 20 parts of quartz, 7 parts of lime stone, 7 parts of Copper Ores, 3 parts of plant ash, 2 parts of zinc oxide,
1 part of tin oxide, 0.5 part of talcum powder.
The preparation method of described composite Jewel indigo plant pottery glaze, comprises the following steps：
（1）Glaze described in claim 1 is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is
1.25:2:3, Ball-milling Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
Embodiment 3：A kind of composite Jewel indigo plant pottery glaze, it is prepared by the raw material of following parts by weight：This
40 parts of medicine, 30 parts of feldspar, 25 parts of calcite, 30 parts of quartz, 10 parts of lime stone, 7 parts of Copper Ores, 5 parts of plant ash, 4 parts of zinc oxide,
2 parts of tin oxide, 1.5 parts of talcum powder.
The preparation method of described composite Jewel indigo plant pottery glaze, comprises the following steps：
（1）Glaze described in claim 1 is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is
1.25:2:3, Ball-milling Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
40 parts of this medicine, 30 parts of feldspar, 25 parts of calcite, 30 parts of quartz, 10 parts of lime stone, 7 parts of Copper Ores, 5 parts of plant ash,
4 parts of zinc oxide, 2 parts of tin oxide, 1.5 parts of talcum powder.
This medicine is a kind of natural glaze stone.Glass is introduced into glaze, is a kind of strong solvent.
Feldspar belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white
Color and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Many ore is distributed with Yuzhou
Hide.
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of preventing and treating glaze paint and heap
Product, dosage can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint smoking.
Quartz is metamorphic rock, and its content is silica, the main glossiness for increasing glaze, it is impossible to it is excessive, it can not lack,
Otherwise glaze paint change color can be caused to reduce.
Plant ash is introduced primarily into the elements such as calcium phosphorus, is good cosolvent, there is certain suspension to glaze slip, can reduce glaze
Melting temperature and glaze high temperature viscosity, while there is opaque and the facilitation to chun glaze split-phase, dosage should control.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in plastics, silicate product, synthetic rubber, profit
In the making of the products such as lubricating oil, paint, ointment, adhesive, food, battery, fire retardant.The band gap and exciton of zinc oxide
Binding energy is larger, and transparency is high, there is excellent normal temperature luminescent properties.
Tin oxide is cubic white, faint yellow or light gray, six sides or orthorhombic system powder.1630 DEG C of fusing point.
Talcum powder is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion system
Number, promotes the formation of glaze-body interface, and increase opaque.
Above-mentioned natural material is used cooperatively with industrial chemicals, and under high-temperature fusion effect, the pottery glaze colours burnt out can produce
The unique artistic effect of raw pottery sapphire, has higher artistic value and extensive market prospects.
Claims (3)
1. a kind of composite Jewel indigo plant pottery glaze, it is characterised in that it is prepared by the raw material of following parts by weight：This
30 parts to 40 parts of medicine, 25 parts to 30 parts of feldspar, 20 parts to 25 parts of calcite, 20 parts to 30 parts of quartz, 7 parts to 10 parts of lime stone,
7 parts to 10 parts of Copper Ores, 3 parts to 5 parts of plant ash, 2 parts to 4 parts of zinc oxide, 1 part to 2 parts of tin oxide, 0.5 part to 1.5 of talcum powder
Part.
2. composite Jewel indigo plant pottery glaze as claimed in claim 1, it is characterised in that it is by the raw material of following parts by weight
It is prepared：35 parts of this medicine, 28 parts of feldspar, 22 parts of calcite, 21 parts of quartz, 8 parts of lime stone, 8 parts of Copper Ores, plant ash 4
Part, 3 parts of zinc oxide, 1 part of tin oxide, 1 part of talcum powder.
3. the preparation method of the composite Jewel indigo plant pottery glaze described in a kind of claim 1 or 2, it is characterised in that including following step
Suddenly：
（1）Glaze described in claim 1 is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is
1.25:2:3, Ball-milling Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.