CN107698156A - A kind of compound beautiful sense pottery glaze and preparation method thereof - Google Patents
A kind of compound beautiful sense pottery glaze and preparation method thereof Download PDFInfo
- Publication number
- CN107698156A CN107698156A CN201711065620.3A CN201711065620A CN107698156A CN 107698156 A CN107698156 A CN 107698156A CN 201711065620 A CN201711065620 A CN 201711065620A CN 107698156 A CN107698156 A CN 107698156A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- raw material
- pottery
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of compound gas to burn pottery glaze and preparation method thereof, and it is prepared by the raw material of following parts by weight：25 parts to 35 parts of melilite, 18 parts to 24 parts of calcite, 18 parts to 25 parts of quartz, 5 parts to 8 parts of fluorite, 5 parts to 8 parts of Copper Ores, 4 parts to 7 parts of glass, 4 parts to 7 parts of this medicine, 3 parts to 5 parts of ox bone ash, 1 part to 2 parts of tin oxide, 0.3 part to 0.8 part of talcum powder；In glaze dispensing, although the raw material used for very common raw material, is made up of rational raw material and the adjustment of deal, also there is synergy, glaze colours is uniform, bright in colour between each raw material, mobility is moderate, pottery made of glaze formula provided by the present invention, colour generation is uniform, and glossiness is good, uniform color, glaze paint are plump, have unique artistic effect, gentle, bright perception is given people, and glaze hacking is uniform, high yield rate.
Description
Technical field
The present invention relates to pottery field, and in particular to a kind of compound beautiful sense pottery glaze and preparation method thereof.
Background technology
Pottery is originated in the Eastern Han Dynasty, is one of five big kiln porcelain of Song Dynasty, the treasure in Chinese tradition technology in producing porcelain, is referred to as
National treasure, rarity.It is world-famous for the transmutation art of uniqueness, is known as " the valuable an ancient unit of weight of gold is priceless " and " there is ten thousand strings of cash in family, not as pottery
One " good reputation.It is the exclusive national treasure porcelain in Henan Province Xuchang City Yuzhou City god Hou towns, by its simple and unsophisticated moulding, consummate
Technique, the complicated magical transmutation, the beautiful scenery of lakes and mountains, rosy clouds fog, people's beast flower, bird, insect, and fish etc. with glaze, " it is color to enter kiln kiln discharge ten thousand of the same colour "
Varied figure color and marvellous charm, it is described as first of Chinese " five big porcelain ".
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, typically using bavin, coal, charcoal
Fired with natural gas, glaze color change is also different caused by different burning process.Outside is glaze by being produced during high-temperature fusion
Raw gorgeous colorful change, for reason mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Therefore, it is pure disclose a kind of raw material by the present invention, and proportioning novelty, preparation method is simple, meets the compound of environmental requirement
Jade sense pottery glaze and preparation method thereof.
The content of the invention
The invention discloses a kind of raw material is pure, proportioning is novel, and preparation method is simple, the moist compound beautiful sense pottery of glaze layer
Glaze and preparation method thereof.
The technical proposal of the invention is realized in this way：A kind of compound beautiful sense pottery glaze, it is by following parts by weight
Raw material be prepared：25 parts to 35 parts of melilite, 18 parts to 24 parts of calcite, 18 parts to 25 parts of quartz, 5 parts to 8 of fluorite
Part, 5 parts to 8 parts of Copper Ores, 4 parts to 7 parts of glass, 4 parts to 7 parts of this medicine, 3 parts to 5 parts of ox bone ash, 1 part to 2 parts of tin oxide, slide
0.3 part to 0.8 part of stone flour.
Described compound beautiful sense pottery glaze, it is prepared by the raw material of following parts by weight：31 parts of melilite,
22 parts of calcite, 20 parts of quartz, 7 parts of fluorite, 6 parts of Copper Ores, 6 parts of glass, 6 parts of this medicine, 4 parts of ox bone ash, 1.5 parts of tin oxide,
0.6 part of talcum powder.
The preparation method of described compound beautiful sense pottery glaze, comprises the following steps：
（1）Above-mentioned glaze is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is 1.15:2:3, ball milling
Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
Technical scheme has following good effect：In glaze dispensing, although the raw material used is very common
Raw material, but be made up of rational raw material and the adjustment of deal, also there is synergy between each raw material, glaze colours is uniform,
Lovely luster, mobility is moderate, and pottery made of glaze formula provided by the present invention, colour generation is uniform, and glossiness is good, and color and luster is equal
It is even, glaze paint is plump, has unique artistic effect, give people gentle, bright perception, and glaze hacking is uniform, high yield rate.
Embodiment
Embodiment 1：A kind of compound beautiful sense pottery glaze, it is prepared by the raw material of following parts by weight：Huang is long
31 parts of stone, 22 parts of calcite, 20 parts of quartz, 7 parts of fluorite, 6 parts of Copper Ores, 6 parts of glass, 6 parts of this medicine, 4 parts of ox bone ash, tin oxide
1.5 parts, 0.6 part of talcum powder.
The preparation method of described compound beautiful sense pottery glaze, comprises the following steps：
（1）Above-mentioned glaze is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is 1.15:2:3, ball milling
Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
Embodiment 2：A kind of compound beautiful sense pottery glaze, it is prepared by the raw material of following parts by weight：Huang is long
25 parts of stone, 18 parts of calcite, 18 parts of quartz, 5 parts of fluorite, 5 parts of Copper Ores, 4 parts of glass, 4 parts of this medicine, 3 parts of ox bone ash, tin oxide
1 part, 0.3 part of talcum powder.
The preparation method of described compound beautiful sense pottery glaze, comprises the following steps：
（1）Above-mentioned glaze is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is 1.15:2:3, ball milling
Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
Embodiment 3：A kind of compound beautiful sense pottery glaze, it is prepared by the raw material of following parts by weight：Huang is long
35 parts of stone, 24 parts of calcite, 25 parts of quartz, 8 parts of fluorite, 8 parts of Copper Ores, 7 parts of glass, 7 parts of this medicine, 5 parts of ox bone ash, tin oxide
2 parts, 0.8 part of talcum powder.
The preparation method of described compound beautiful sense pottery glaze, comprises the following steps：
（1）Above-mentioned glaze is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is 1.15:2:3, ball milling
Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.
35 parts of melilite, 24 parts of calcite, 25 parts of quartz, 8 parts of fluorite, 8 parts of Copper Ores, 7 parts of glass, 7 parts of this medicine, ox bone
5 parts of ash, 2 parts of tin oxide, 0.8 part of talcum powder.
Melilite belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., be divided into yellow,
White and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Many ore is distributed with Yuzhou
Hide.
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of preventing and treating glaze paint and heap
Product, dosage can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint smoking.
Quartz is metamorphic rock, and its content is silica, the main glossiness for increasing glaze, it is impossible to it is excessive, it can not lack,
Otherwise glaze paint change color can be caused to reduce.
Fluorite is a kind of mineral, and isometric system, its main component is calcirm-fluoride, can reduce the melting temperature of glaze, increases glaze
Mobility, while there is milkiness effect, the glossiness of chun glaze can be improved, improve the suspension of glaze slip.
Copper Ores are most important Copper Ores mineral, typically by Cu, tri- kinds of element compositions of Fe, S, theory composition（%）Cu
34.56, Fe 30.52, S 34.92, theoretical chemistry formula are CuFeS2.
Glass be fused together by silica and other chemical substances formed (main production raw material is:Soda ash, stone
Lime stone, quartz).Contiguous network structure is formed in melting, viscosity, which gradually increases and hardened, in cooling procedure causes what it was crystallized
Silicates nonmetallic materials.
This medicine is a kind of natural glaze stone.Glass is introduced into glaze, is a kind of strong solvent.
Ox bone ash is made of ox bone calcining, can be used as cosolvent, makes glaze paint gloss, promotes liquid phase separation.
Tin oxide is cubic white, faint yellow or light gray, six sides or orthorhombic system powder.1630 DEG C of fusing point.
Talcum powder is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion system
Number, promotes the formation of glaze-body interface, and increase opaque.
Above-mentioned natural material is used cooperatively with industrial chemicals, and under high-temperature fusion effect, the pottery glaze colours burnt out can produce
The beautiful sense artistic effect that raw pottery glaze layer is gentle, gloss is unique, has higher artistic value and extensive market prospects.
Claims (3)
1. a kind of compound beautiful sense pottery glaze, it is characterised in that it is prepared by the raw material of following parts by weight：Huang is long
25 parts to 35 parts of stone, 18 parts to 24 parts of calcite, 18 parts to 25 parts of quartz, 5 parts to 8 parts of fluorite, 5 parts to 8 parts of Copper Ores, glass
4 parts to 7 parts, 4 parts to 7 parts of this medicine, 3 parts to 5 parts of ox bone ash, 1 part to 2 parts of tin oxide, 0.3 part to 0.8 part of talcum powder.
2. compound beautiful sense pottery glaze as claimed in claim 1, it is characterised in that it is by the raw material system of following parts by weight
For what is formed：31 parts of melilite, 22 parts of calcite, 20 parts of quartz, 7 parts of fluorite, 6 parts of Copper Ores, 6 parts of glass, 6 parts of this medicine, ox
4 parts of bone ash, 1.5 parts of tin oxide, 0.6 part of talcum powder.
3. the preparation method of the compound beautiful sense pottery glaze described in a kind of claim 1 or 2, it is characterised in that including following step
Suddenly：
（1）Above-mentioned glaze is mixed with water, carries out ball milling with ball mill, the ratio of water, glaze and ball is 1.15:2:3, ball milling
Time is 40 minutes；
（2）By step（1）Glaze slurry after middle ball milling is sieved by the screen cloth of 300 mesh, tails over control within 0.4%；
（3）By step（2）In the glaze slurry that is sieved be put into it is standby in glaze material pond.