CN106145683A - A kind of peacock blue pottery glaze and preparation method thereof - Google Patents

A kind of peacock blue pottery glaze and preparation method thereof Download PDF

Info

Publication number
CN106145683A
CN106145683A CN201610680409.1A CN201610680409A CN106145683A CN 106145683 A CN106145683 A CN 106145683A CN 201610680409 A CN201610680409 A CN 201610680409A CN 106145683 A CN106145683 A CN 106145683A
Authority
CN
China
Prior art keywords
glaze
plant ash
ash
oxide
peacock blue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610680409.1A
Other languages
Chinese (zh)
Inventor
温书强
Original Assignee
温书强
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 温书强 filed Critical 温书强
Priority to CN201610680409.1A priority Critical patent/CN106145683A/en
Publication of CN106145683A publication Critical patent/CN106145683A/en
Pending legal-status Critical Current

Abstract

A kind of peacock blue pottery glaze, it is made up of following raw materials according: turtledove Yamamoto medicine, Anhydrite, calcite, quartz, Talcum, Os Bovis seu Bubali ash, plant ash, frit, stannum oxide, zinc oxide, copper oxide, the peacock blue pottery glaze that the present invention makes is the most penetrating, there is third dimension, good fluidity, is difficult to bubble, good luster.

Description

A kind of peacock blue pottery glaze and preparation method thereof
Technical field
The invention belongs to pottery technical field, be specifically related to a kind of peacock blue pottery glaze and preparation method thereof.
Background technology
Pottery is thick for this with glaze, and at the bottom of its color or heavy glaze or in outstanding glaze or floating glaze table, the thick muddy work of glaze, glaze layer opalescence jade-like stone moistens, Being administrations with multiplied departments lives is intended to drip, and third dimension is extremely strong.Pottery is with transmutation as god, and natural transmutation is the elite place of pottery art, is also Pottery is rely the four seas of becoming famous, the rare part of porcelain woods of making a name.With executing a kind of glaze in firing, once burning till in multicoloured it is then " enter kiln of the same colour, kiln discharge ten thousand is color ".Protean transmutation effect, defines the mystery that colors changing hue is infinite, in red inner purple, purple During in dark blue, blue or green, residence is white, white general red, five colours imbibition, form a brightening, and have the title of ", without right, transmutation is unparalleled for pottery ".
An ancient unit of weight glaze is one layer of decorative layer on pottery surface, is to determine the principal element that pottery glaze colours generates, utilizes natural ore deposit Raw material or add some industrial chemicals and coordinate according to a certain percentage, melted and cover at base substrate under high temperature reducing atmospheres effect The rich jade-like stone profit gloss on surface and colorful vitreous body layer, have abundant dicoration, increases U.S. of pottery natural trend Sense, makes pottery have certain artistic value and enjoying value.
In coloured glaze, peafowl blue glaze is also referred to as peafowl green glaze or bright blue, is a kind of intermediate glaze with copper as coloring agent, because of face Color is similar to the cobalt blue of peafowl dodds and obtains this name.
In prior art, formula of peacock blue pottery glaze and preparation method thereof is the most little, and the peacock blue pottery prepared Glaze surface easily cracks, and glaze wearability and resistance to mechanical ability are poor, beautiful sense deficiency.
Summary of the invention
In order to solve the problems referred to above, the present invention provides a kind of peacock blue pottery glaze and preparation method thereof.
The technical solution used in the present invention is:
A kind of peacock blue pottery glaze, it is made up of following raw materials according: turtledove Yamamoto medicine, Anhydrite, calcite, quartz, Talcum, cattle Bone ash, plant ash, frit, stannum oxide, zinc oxide, copper oxide.
A kind of peacock blue pottery glaze, it is prepared by the raw materials in: turtledove Yamamoto medicine 30-40 part, Anhydrite 20-35 part, calcite 10-20 part, quartz 20-30 part, Talcum 20-30 part, Os Bovis seu Bubali ash 3-6 part, plant ash 3-5 part, frit 20- 30 parts, stannum oxide 1-2 part, zinc oxide 2-5 part, copper oxide 3-6 part.
The preparation method of a kind of peacock blue pottery glaze as above, comprises the following steps:
(1) pulverize: first take the turtledove Yamamoto medicine of above-mentioned weight portion, Anhydrite, calcite, quartz, Talcum are put in ball milling and pulverized, mixing Sieve after Jun Yun and be mix powder;
(2) being placed in crucible by mix powder and carry out melting, crucible is generally located on the flue between kiln and chimney, under stove Separately set one and supplement dye chamber, when flue gas shortage of heat or kiln stop burn time, i.e. can use the roasting of aftercombustion room, at the bottom of crucible on have One aperture, blocks with admant English bead, to mix powder be melt into fluidised form melt matter time, bead is floated, and molten matter i.e. flows into down Quenching in the tank of face, makes molten matter split into crisp and transparent fritter;
(3) plant ash is eluriated: prepares several vat during elutriation, pours appropriate water into and be subsequently adding plant ash in one of them cylinder, Being sufficiently stirred for wooden stick, plant ash is all stirred out, the thing such as charcoal lump therein and grass cuttings will float to the water surface, so Afterwards floating thing is all pulled out, after dragging for clean floating thing, then stir vegetation buck, be allowed in suspended state, and some bigger soil The impurity such as grain, stone, slag will be deposited to cylinder bottom, with the container at a wide-mouth shallow end Herba Ceratophylli Demeersi wood ash water on upper strata is scooped out and pours into In the most several cylinders, wait and scoop to a certain extent, then add suitable quantity of water and continue stirring, until wash in a pan only washed in a pan dry afterwards standby;
(4) fritter molten matter split into is placed in ball milling pulverizing filtration together with plant ash, stannum oxide, zinc oxide, copper oxide, Finally obtain is glaze.
Turtledove Yamamoto medicine, is a kind of natural glaze stone, mainly originates in turtledove mountain area, Yuzhou Li Cun.
Os Bovis seu Bubali ash, is usually after calcining with Os Bovis seu Bubali and prepares, and Os Bovis seu Bubali can make cosolvent, and its hydrotropy effect is relatively slower, Glaze gloss can be made soft, be again the good opacifiers of an ancient unit of weight glaze simultaneously, liquid phase separation can be promoted.
Plant ash, is good cosolvent in an ancient unit of weight glaze, owing to plant ash has the strongest alkalescence, has electrolyte in glaze Effect, plant ash is generally scattered graininess, has certain suspension to glaze slip, introduces appropriate plant ash and can reduce glaze Melt temperature and the high temperature viscosity of glaze, have milkiness effect and the facilitation to an ancient unit of weight glaze split-phase simultaneously.
Talcum, is natural hydrous magnesium silicate mineral, and Talcum is commonly used to do the hydrotropy raw material of an ancient unit of weight glaze, can reduce the molten of an ancient unit of weight glaze Melt temperature and the coefficient of expansion, promote that glaze-body interface generates, the opaque of an ancient unit of weight glaze can also be increased simultaneously.
The invention has the beneficial effects as follows: the peacock blue pottery glaze that the present invention makes is the most penetrating, has third dimension, mobility Good, the most easy to foaming, good luster.
Detailed description of the invention
A kind of peacock blue pottery glaze, it is made up of following raw materials according: turtledove Yamamoto medicine, Anhydrite, calcite, quartz, cunning Stone, Os Bovis seu Bubali ash, plant ash, frit, stannum oxide, zinc oxide, copper oxide.
A kind of peacock blue pottery glaze, it is prepared by the raw materials in: turtledove Yamamoto medicine 30-40 part, Anhydrite 20-35 part, calcite 10-20 part, quartz 20-30 part, Talcum 20-30 part, Os Bovis seu Bubali ash 3-6 part, plant ash 3-5 part, frit 20- 30 parts, stannum oxide 1-2 part, zinc oxide 2-5 part, copper oxide 3-6 part.
The preparation method of a kind of peacock blue pottery glaze as above, comprises the following steps:
(1) pulverize: first take the turtledove Yamamoto medicine of above-mentioned weight portion, Anhydrite, calcite, quartz, Talcum are put in ball milling and pulverized, mixing Sieve after Jun Yun and be mix powder;
(2) being placed in crucible by mix powder and carry out melting, crucible is generally located on the flue between kiln and chimney, under stove Separately set one and supplement dye chamber, when flue gas shortage of heat or kiln stop burn time, i.e. can use the roasting of aftercombustion room, at the bottom of crucible on have One aperture, blocks with admant English bead, to mix powder be melt into fluidised form melt matter time, bead is floated, and molten matter i.e. flows into down Quenching in the tank of face, makes molten matter split into crisp and transparent fritter;
(3) plant ash is eluriated: prepares several vat during elutriation, pours appropriate water into and be subsequently adding plant ash in one of them cylinder, Being sufficiently stirred for wooden stick, plant ash is all stirred out, the thing such as charcoal lump therein and grass cuttings will float to the water surface, so Afterwards floating thing is all pulled out, after dragging for clean floating thing, then stir vegetation buck, be allowed in suspended state, and some bigger soil The impurity such as grain, stone, slag will be deposited to cylinder bottom, with the container at a wide-mouth shallow end Herba Ceratophylli Demeersi wood ash water on upper strata is scooped out and pours into In the most several cylinders, wait and scoop to a certain extent, then add suitable quantity of water and continue stirring, until wash in a pan only washed in a pan dry afterwards standby;
(4) fritter molten matter split into is placed in ball milling pulverizing filtration together with plant ash, stannum oxide, zinc oxide, copper oxide, Finally obtain is glaze.
Embodiment 1
A kind of peacock blue pottery glaze, it is prepared by the raw materials in: turtledove Yamamoto medicine 30 parts, Anhydrite 20 parts, side 10 parts of stone of solution, 20 parts of quartz, 20 parts of Talcum, Os Bovis seu Bubali ash 3 parts, plant ash 3 parts, frit 20 parts, stannum oxide 1 part, zinc oxide 2 parts, Copper oxide 3 parts.
The preparation method of a kind of peacock blue pottery glaze as above, comprises the following steps:
(1) pulverize: first take the turtledove Yamamoto medicine of above-mentioned weight portion, Anhydrite, calcite, quartz, Talcum are put in ball milling and pulverized, mixing Sieve after Jun Yun and be mix powder;
(2) being placed in crucible by mix powder and carry out melting, crucible is generally located on the flue between kiln and chimney, under stove Separately set one and supplement dye chamber, when flue gas shortage of heat or kiln stop burn time, i.e. can use the roasting of aftercombustion room, at the bottom of crucible on have One aperture, blocks with admant English bead, to mix powder be melt into fluidised form melt matter time, bead is floated, and molten matter i.e. flows into down Quenching in the tank of face, makes molten matter split into crisp and transparent fritter;
(3) plant ash is eluriated: prepares several vat during elutriation, pours appropriate water into and be subsequently adding plant ash in one of them cylinder, Being sufficiently stirred for wooden stick, plant ash is all stirred out, the thing such as charcoal lump therein and grass cuttings will float to the water surface, so Afterwards floating thing is all pulled out, after dragging for clean floating thing, then stir vegetation buck, be allowed in suspended state, and some bigger soil The impurity such as grain, stone, slag will be deposited to cylinder bottom, with the container at a wide-mouth shallow end Herba Ceratophylli Demeersi wood ash water on upper strata is scooped out and pours into In the most several cylinders, wait and scoop to a certain extent, then add suitable quantity of water and continue stirring, until wash in a pan only washed in a pan dry afterwards standby;
(4) fritter molten matter split into is placed in ball milling pulverizing filtration together with plant ash, stannum oxide, zinc oxide, copper oxide, Finally obtain is glaze.
Embodiment 2
A kind of peacock blue pottery glaze, it is prepared by the raw materials in: turtledove Yamamoto medicine 40 parts, Anhydrite 35 parts, side 20 parts of stone of solution, 30 parts of quartz, 30 parts of Talcum, Os Bovis seu Bubali ash 6 parts, plant ash 5 parts, frit 30 parts, stannum oxide 2 parts, zinc oxide 5 parts, Copper oxide 6 parts.
Preparation method is with embodiment 1.
Embodiment 3
A kind of peacock blue pottery glaze, it is prepared by the raw materials in: turtledove Yamamoto medicine 35 parts, Anhydrite 30 parts, side Solve 15 parts of stone, 25 parts of quartz, 25 parts of Talcum, Os Bovis seu Bubali ash 5 parts, plant ash 4 parts, frit 25 parts, stannum oxide 1.5 parts, zinc oxide 4 Part, copper oxide 5 parts.
Preparation method is with embodiment 1.
Embodiment 4
A kind of peacock blue pottery glaze, it is prepared by the raw materials in: turtledove Yamamoto medicine 35 parts, Anhydrite 25 parts, side Solve 15 parts of stone, 25 parts of quartz, 25 parts of Talcum, Os Bovis seu Bubali ash 4 parts, plant ash 4 parts, frit 25 parts, stannum oxide 1.5 parts, zinc oxide 3 Part, copper oxide 4 parts.
Preparation method is with embodiment 1.

Claims (3)

1. a peacock blue pottery glaze, it is characterised in that: it is made up of following raw materials according: turtledove Yamamoto medicine, Anhydrite, Fang Xie Stone, quartz, Talcum, Os Bovis seu Bubali ash, plant ash, frit, stannum oxide, zinc oxide, copper oxide.
One the most according to claim 1 peacock blue pottery glaze, it is characterised in that: it is by the raw material of following weight portion Make: turtledove Yamamoto medicine 30-40 part, Anhydrite 20-35 part, calcite 10-20 part, quartz 20-30 part, Talcum 20-30 part, Os Bovis seu Bubali Ash 3-6 part, plant ash 3-5 part, frit 20-30 part, stannum oxide 1-2 part, zinc oxide 2-5 part, copper oxide 3-6 part.
3. the preparation method of a peacock blue pottery glaze as claimed in claim 2, it is characterised in that: comprise the following steps:
Pulverize: first take the turtledove Yamamoto medicine of above-mentioned weight portion, Anhydrite, calcite, quartz, Talcum are put in ball milling and pulverized, and mixing is all Sieve after even and be mix powder;
Being placed in crucible by mix powder and carry out melting, crucible is generally located on the flue between kiln and chimney, another under stove If one supplements dye chamber, when flue gas shortage of heat or kiln stop burn time, i.e. can use the roasting of aftercombustion room, at the bottom of crucible on have one Aperture, blocks with admant English bead, to mix powder be melt into fluidised form melt matter time, bead is floated, and molten matter i.e. flows into following Quenching in tank, makes molten matter split into crisp and transparent fritter;
Plant ash is eluriated: prepares several vat during elutriation, pours appropriate water into and be subsequently adding plant ash, then use in one of them cylinder Wooden stick is sufficiently stirred for, and plant ash is all stirred out, and the thing such as charcoal lump therein and grass cuttings will float to the water surface, then Floating thing is all pulled out, after dragging for clean floating thing, then stirs vegetation buck, is allowed in suspended state, and some bigger grogs, stones The impurity such as son, slag will be deposited to cylinder bottom, with the container at a wide-mouth shallow end Herba Ceratophylli Demeersi wood ash water on upper strata is scooped out and pours into additionally In several cylinders, wait and scoop to a certain extent, then add suitable quantity of water and continue stirring, until wash in a pan only washed in a pan dry afterwards standby;
The fritter molten matter split into is placed in ball milling pulverizing together with plant ash, stannum oxide, zinc oxide, copper oxide and filters, After obtain be glaze.
CN201610680409.1A 2016-08-18 2016-08-18 A kind of peacock blue pottery glaze and preparation method thereof Pending CN106145683A (en)