CN105924007A - Fancy glaze and preparing method thereof - Google Patents
Fancy glaze and preparing method thereof Download PDFInfo
- Publication number
- CN105924007A CN105924007A CN201610359530.4A CN201610359530A CN105924007A CN 105924007 A CN105924007 A CN 105924007A CN 201610359530 A CN201610359530 A CN 201610359530A CN 105924007 A CN105924007 A CN 105924007A
- Authority
- CN
- China
- Prior art keywords
- glaze
- raw materials
- raw material
- fancy glaze
- fancy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fancy glaze and a preparing method thereof. The fancy glaze comprises 45% of melilite, 10% of white feldspar, 12% of calcite, 9% of quartz, 15% of frit, 1.5% of zinc oxide, 7% of copper ore and 0.5% of blue powder. The preparing method of the fancy glaze includes the following steps that the raw materials are added into a crusher and crushed, the crushed raw materials are sieved through a 150-mesh sieve to obtain mixed powder, and then mixed powder is put into a glaze pool to be ready for use; the blue powder and the copper ore are added into traditional raw materials, and under the matching effect of other chemical raw materials and natural raw materials and the high-temperature melting effect, the unique artistic effect of flowering-shape variation is generated, a fired finished product is in a flowering shape, and the quite good social benefits and the quite good economic benefits are achieved.
Description
Technical field
The present invention relates to porcelain field, be specifically related to a kind of fancy glaze and preparation method thereof.
Background technology
Pottery is originated in the Eastern Han Dynasty, is one of Song dynasty five your name's kiln porcelain, and the treasure in Han nationality's tradition technology in producing porcelain is referred to as national treasure, rarity.It is world-famous for unique transmutation art, have " gold have valency an ancient unit of weight priceless " and the good reputation of " there is ten thousand strings of cash in family, not as pottery one ".It it is the exclusive national treasure porcelain in god town, Countermeasure In Yuzhou City of Henan Province, by its simple and unsophisticated moulding, consummate technique, complicated join glaze, the magical transmutation of " entering kiln kiln discharge of the same colour ten thousand color ", with countless changes figure color and the marvellous charms such as the beautiful scenery of lakes and mountains, rosy clouds fog, people's beast flower, bird, insect, and fish, be described as first of China's " five your name's porcelain ".After founding of New, pottery is developed rapidly.Particularly since reform and opening-up, pottery production technology and level are obtained for epoch-making lifting, and pottery constantly appears the world as state's gift.
Pottery typically uses bavin to burn, coal burns, charcoal burns gentle burning and is prepared from, and the glaze colours that different burning process produces is the most different.Inside is blank, and outside is glaze, and different glaze makes pottery surface form different colors through high-temperature fusion, uses traditional glaze colours formula well can not represent change in shape as flower during melted.Reason is that conventional formulation is single, and the composition having is too much, and the change that can cause glaze colours is uncertain, and this is also that to cause pottery to enter kiln of the same colour, the secret of kiln discharge ten thousand coloured silk.
Therefore, it is pure that the present invention produces a kind of raw material, and proportioning is novel, simple fancy glaze of preparation method and preparation method thereof.
Summary of the invention
For the deficiencies in the prior art, the present invention provides a kind of raw material pure, and proportioning is novel, simple fancy glaze of preparation method and preparation method thereof, is used for solving defect of the prior art.
The technical scheme is that and be achieved in that: a kind of fancy glaze, it is to be prepared from by the raw material of following weight percents: melilite 44 to 46, Bai Changshi 9 to 11, calcite 11 to 13, quartz 8 to 10, frit 14 to 16, zinc oxide 1.4 to 1.6, Copper Ores 6 to 8, blue powder 0.4 to 0.6.
It is to be prepared from by the raw material of following weight percents: melilite 45, white feldspar 10, calcite 12, quartz 9, frit 15, zinc oxide 1.5, Copper Ores 7, blue powder 0.5.
The preparation method of a kind of fancy glaze as above, its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, the raw material after broken is crossed 150 mesh sieves, obtains mixed powder, be then placed in glaze pond by mixed powder standby.
The present invention has following good effect: the present invention adds blue powder and Copper Ores in traditional raw material, with under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of the change in shape that can produce that the flowers are in blossom, product fires finished form, and such as the flowers are in blossom, has good Social and economic benef@.
Detailed description of the invention
A kind of fancy glaze, it is to be prepared from by the raw material of following weight percents: melilite 44 to 46, white feldspar 9 to 11, calcite 11 to 13, quartz 8 to 10, frit 14 to 16, zinc oxide 1.4 to 1.6, Copper Ores 6 to 8, blue powder 0.4 to 0.6.
It is to be prepared from by the raw material of following weight percents: melilite 45, white feldspar 10, calcite 12, quartz 9, frit 15, zinc oxide 1.5, Copper Ores 7, blue powder 0.5.
Embodiment 1: a kind of fancy glaze, it is to be prepared from by the raw material of following weight percents: melilite 45, white feldspar 10, calcite 12, quartz 9, frit 15, zinc oxide 1.5, Copper Ores 7, blue powder 0.5.Its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, the raw material after broken is crossed 150 mesh sieves, obtains mixed powder, be then placed in glaze pond by mixed powder standby.Blue powder and Copper Ores is added in traditional raw material, with under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of the change in shape that can produce that the flowers are in blossom, product fires finished form, and such as the flowers are in blossom, has good Social and economic benef@.
Embodiment 2: a kind of fancy glaze, it is to be prepared from by the raw material of following weight percents: melilite 44, white feldspar 11, calcite 13, quartz 8, frit 15, zinc oxide 1.5, Copper Ores 7, blue powder 0.5.Its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, the raw material after broken is crossed 150 mesh sieves, obtains mixed powder, be then placed in glaze pond by mixed powder standby.Blue powder and Copper Ores is added in traditional raw material, with under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of the change in shape that can produce that the flowers are in blossom, product fires finished form, and such as the flowers are in blossom, has good Social and economic benef@.
Feldspar belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white and red etc., is the main component of glaze, and the formation mainly for glaze plays an important role.Yuzhou is distributed numerous mineral reserve.
Calcite mainly reduces glaze melt temperature, increases glossiness and the transparency of glaze colours, and preventing and treating glaze be full of cracks and accumulation, consumption can not be too much, otherwise can cause glaze crystallization devitrification, cause temperature to narrow, change very few, and cause glaze smoking.
Quartz is metamorphic rock, and its content is silica, the main glossiness increasing glaze, it is impossible to too much, can not lack, and glaze change color otherwise can be caused to reduce.
Copper Ores is topmost Copper Ores mineral, and typically by Cu, tri-kinds of element compositions of Fe, S, theoretical composition (%) Cu 34.56, Fe 30.52, S 34.92, theoretical chemistry formula is CuFeS2.Zinc oxide is a kind of oxide of zinc.It is insoluble in water, dissolves in acid and highly basic.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in the making of the products such as plastics, silicate product, synthetic rubber, lubricating oil, paint, ointment, adhesive, food, battery, fire retardant.The band gap of zinc oxide and exciton bind energy are relatively big, and transparency is high, have the normal temperature luminescent properties of excellence.
Frit has the feature such as insolubility and stability, and processing is standby after grinding, can be as the strong solvent of glaze, it is possible to be used alone.Blue powder is that chemical industry commonly uses raw material.
Above-mentioned natural material and industrial chemicals with the use of, under high-temperature fusion effect, it is possible to generate the unique artistic effect opening change in shape, product fires finished form as the flowers are in blossom, has good Social and economic benef@.
Claims (3)
1. a fancy glaze, it is characterised in that it is to be prepared from by the raw material of following weight percents: melilite 44 to 46, white feldspar 9 to 11, calcite 11 to 13, quartz 8 to 10, frit 14 to 16, zinc oxide 1.4 to 1.6, Copper Ores 6 to 8, blue powder 0.4 to 0.6.
Fancy glaze the most according to claim 1, it is characterised in that it is to be prepared from by the raw material of following weight percents: melilite 45, white feldspar 10, calcite 12, quartz 9, frit 15, zinc oxide 1.5, Copper Ores 7, blue powder 0.5.
3. the preparation method of a fancy glaze as claimed in claim 1, it is characterized in that, its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, and the raw material after broken is crossed 150 mesh sieves, obtain mixed powder, then mixed powder is placed in glaze pond standby.