CN106082665A - A kind of five colored glazes and preparation method thereof - Google Patents
A kind of five colored glazes and preparation method thereof Download PDFInfo
- Publication number
- CN106082665A CN106082665A CN201610424420.1A CN201610424420A CN106082665A CN 106082665 A CN106082665 A CN 106082665A CN 201610424420 A CN201610424420 A CN 201610424420A CN 106082665 A CN106082665 A CN 106082665A
- Authority
- CN
- China
- Prior art keywords
- raw material
- glaze
- preparation
- mixed powder
- broken
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of five colored glazes and preparation method thereof, it is to be prepared from by the raw material of following weight percents: melilite 32, red Anhydrite 26, calcite 10, quartz 21, frit 7, zinc oxide 3, copper oxide 1, the raw material of above-mentioned percentage by weight is joined in disintegrating machine broken, raw material after broken is crossed 160 mesh sieves, obtains mixed powder, then mixed powder is placed in glaze pond standby；With under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, can produce the unique artistic effect of glaze colours riot of color change, it is various that product fires finished product color change, has good Social and economic benef@.
Description
Technical field
The present invention relates to pottery field, be specifically related to a kind of five colored glazes and preparation method thereof.
Background technology
The development of pottery has close and remote contacting with the progress of the mankind, and it is the epoch mark of human civilization.Pottery
Pottery in porcelain, has handled Tang, Song, unit, the baptism of bright, clear years, has defined the artistic expression of uniqueness, and an ancient unit of weight kiln has pole
Beautiful color, glaze changes all the time in kiln, and has nature aesthetic feeling, and today is still inherited by various places porcelain kiln and imitates, and constantly
Innovation, makes this gorgeous flower playback extraordinary splendor of an ancient unit of weight kiln.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, the most still has the biggest achievement, typically uses bavin, coal, charcoal
Firing with natural gas, the glaze colours change that different burning process produces is also different.Outside is that glaze is producing through high-temperature fusion
Raw gorgeous colorful change, reason is mainly at the formula of glaze, and this is the key factor affecting pottery finished product exogenic color, simultaneously
Also it is that to cause pottery to enter kiln of the same colour, the key factor of kiln discharge ten thousand coloured silk.
It is pure that the present invention produces a kind of raw material, and proportioning is novel, simple five colored glazes of preparation method and preparation method thereof.
Summary of the invention
For the deficiencies in the prior art, the present invention provides a kind of raw material pure, and proportioning is novel, and preparation method is the most multicolored
Glaze and preparation method thereof, is used for solving defect of the prior art.
The technical scheme is that and be achieved in that: a kind of five colored glazes, it is to be prepared by the raw material of following weight percents
: melilite 32, red Anhydrite 26, calcite 10, quartz 21, frit 7, zinc oxide 3, copper oxide 1.
The preparation method of a kind of five colored glazes as above, its preparation method is as follows: by the raw material of above-mentioned percentage by weight
Join in disintegrating machine broken, the raw material after broken is crossed 160 mesh sieves, obtains mixed powder, then mixed powder is placed into glaze
In pond standby.
The present invention has following good effect: the present invention carries out re-quantization to traditional raw material, in high-temperature fusion effect
Under, the unique artistic effect that the glaze colours five colours change, surface is glittering and translucent can be produced, it is various that product fires finished product color change, tool
There is good Social and economic benef@.
Detailed description of the invention
A kind of five colored glazes, it is to be prepared from by the raw material of following weight percents: melilite 32, red Anhydrite
26, calcite 10, quartz 21, frit 7, zinc oxide 3, copper oxide 1.
The preparation method of a kind of five colored glazes as above, its preparation method is as follows: by the raw material of above-mentioned percentage by weight
Join in disintegrating machine broken, the raw material after broken is crossed 160 mesh sieves, obtains mixed powder, then mixed powder is placed into glaze
In pond standby.
Traditional raw material is carried out re-quantization, under high-temperature fusion effect, the change of the glaze colours five colours can be produced, surface is sparkling and crystal-clear picks
Saturating unique artistic effect, it is various that product fires finished product color change, has good Social and economic benef@.
Anhydrite belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white
Normal complexion is red, is the main component of glaze, and the formation mainly for glaze plays an important role.Yuzhou is distributed many ore
Hide.
Calcite mainly reduces glaze melt temperature, increases glossiness and the transparency of glaze colours, preventing and treating glaze be full of cracks and heap
Long-pending, consumption can not be too much, otherwise can cause glaze crystallize devitrification, cause temperature to narrow, change very few, and cause glaze smoking.
Quartz is metamorphic rock, and its content is silicon dioxide, the main glossiness increasing glaze, it is impossible to too much, can not lack,
Glaze change color otherwise can be caused to reduce.
Frit has the feature such as insolubility and stability, and processing is standby after grinding, can be as the strong solvent of glaze, it is possible to single
Solely use.Blue powder is that chemical industry commonly uses raw material.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in plastics, silicate product, synthetic rubber, profit
In the making of the products such as lubricating oil, paint, ointment, binding agent, food, battery, fire retardant.The band gap of zinc oxide and exciton
Binding energy is relatively big, and transparency is high, has the room temperature luminescent properties of excellence.
Copper oxide is the black oxide of a kind of copper, shows slightly both sexes, slightly hygroscopicity.Relative molecular mass is 79.545,
Density is 6.3～6.9 g/cm3, fusing point 1326 DEG C.Water insoluble and ethanol, is dissolved in acid, ammonium chloride and potassium cyanide solution, and ammonia is molten
Liquid slowly dissolves, can react with highly basic.Copper oxide is mainly used in artificial silk processed, pottery, glaze and enamel, battery, petroleum sweetening
Agent, insecticide, also for hydrogen manufacturing, catalyst, green glass etc..
Above-mentioned natural material and industrial chemicals with the use of, under high-temperature fusion effect, it is possible to generate an ancient unit of weight of riot of color
Porcelain unique artistic effect.
Claims (2)
1. a colored glaze, it is characterised in that it is to be prepared from by the raw material of following weight percents:
Melilite 32, red Anhydrite 26, calcite 10, quartz 21, frit 7, zinc oxide 3, copper oxide 1.
2. the preparation method of five colored glazes as claimed in claim 1, it is characterised in that its preparation method is as follows: by above-mentioned
The raw material of percentage by weight joins in disintegrating machine broken, the raw material after broken is crossed 160 mesh sieves, obtains mixed powder, then will
Mixed powder is placed in glaze pond standby.