CN106145677A - A kind of sky blue glaze of pottery - Google Patents
A kind of sky blue glaze of pottery Download PDFInfo
- Publication number
- CN106145677A CN106145677A CN201610513348.XA CN201610513348A CN106145677A CN 106145677 A CN106145677 A CN 106145677A CN 201610513348 A CN201610513348 A CN 201610513348A CN 106145677 A CN106145677 A CN 106145677A
- Authority
- CN
- China
- Prior art keywords
- glaze
- pottery
- sky blue
- raw material
- limestone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of sky blue glaze of pottery, it is to be prepared from by the raw material of following weight percents: potassium feldspar 40, calcite 20, quartz 22, limestone 10, stannum oxide 1.5, plant ash 5, Pulvis Talci 1, zinc oxide 0.5, conventional formulation is carried out re-quantization, natural raw material mating reaction, under high-temperature fusion effect, glaze colours entirety can be produced and present the unique artistic effect of sky blue color change, there is good Social and economic benef@.
Description
Technical field
The present invention relates to pottery field, be specifically related to a kind of sky blue glaze of pottery.
Background technology
The development of pottery has close and remote contacting with the progress of the mankind, and it is the epoch mark of human civilization.Pottery
Pottery in porcelain, has handled Tang, Song, unit, the baptism of bright, clear years, has defined the artistic expression of uniqueness, and an ancient unit of weight kiln has pole
Beautiful color, glaze changes all the time in kiln, and has nature aesthetic feeling, and today is still inherited by various places porcelain kiln and imitates, and constantly
Innovation, makes this gorgeous flower playback extraordinary splendor of an ancient unit of weight kiln.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, the most still has the biggest achievement, typically uses bavin, coal, charcoal
Firing with natural gas, the glaze colours change that different burning process produces is also different.Outside is that glaze is producing through high-temperature fusion
Raw gorgeous colorful change, reason is mainly at the formula of glaze, and this is the key factor affecting pottery finished product exogenic color, simultaneously
Also it is that to cause pottery to enter kiln of the same colour, the key factor of kiln discharge ten thousand coloured silk.
Therefore, it is pure that the present invention produces a kind of raw material, the sky blue glaze of pottery that proportioning is novel, has widely before market
Scape.
Summary of the invention
For the deficiencies in the prior art, the present invention provides a kind of raw material pure, and the sky blue glaze of pottery that proportioning is novel is used for
Solve defect of the prior art.
The technical scheme is that and be achieved in that: a kind of sky blue glaze of pottery, it is former by following weight percents
Material is prepared from: potassium feldspar 39 to 41, calcite 19 to 21, quartz 21 to 23, limestone 9 to
11, stannum oxide 1.4 to 1.6, plant ash 4 to 6, Pulvis Talci 0.9 to 1.1, zinc oxide 0.4 to 0.6.
It is to be prepared from by the raw material of following weight percents: potassium feldspar 40, calcite 20, quartz 22,
Limestone 10, stannum oxide 1.5, plant ash 5, Pulvis Talci 1, zinc oxide 0.5.
The present invention has following good effect: the present invention carries out re-quantization to conventional formulation, and natural raw material coordinates phase
Interaction, under high-temperature fusion effect, can produce glaze colours entirety and present the unique artistic effect of sky blue color change, has very well
Social and economic benef@.
Detailed description of the invention
Embodiment 1: a kind of sky blue glaze of pottery, it is to be prepared from by the raw material of following weight percents: potassium feldspar
40, calcite 20, quartz 22, limestone 10, stannum oxide 1.5, plant ash 5, Pulvis Talci 1, zinc oxide
0.5.
The present invention carries out re-quantization to conventional formulation, and natural raw material coordinates interaction, under high-temperature fusion effect, meeting
Produce glaze colours entirety and present the unique artistic effect of sky blue color change, there is good Social and economic benef@.
Embodiment 2: a kind of sky blue glaze of pottery, it is to be prepared from by the raw material of following weight percents: potassium feldspar
41, calcite 19, quartz 21, limestone 11, stannum oxide 1.4, plant ash 5, Pulvis Talci 1, zinc oxide
0.6.
The present invention carries out re-quantization to conventional formulation, and natural raw material coordinates interaction, under high-temperature fusion effect, meeting
Produce glaze colours entirety and present the unique artistic effect of sky blue color change, there is good Social and economic benef@.
Anhydrite belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white
Normal complexion is red, is the main component of glaze, and the formation mainly for glaze plays an important role.Yuzhou is distributed many ore
Hide.
Calcite mainly reduces glaze melt temperature, increases glossiness and the transparency of glaze colours, preventing and treating glaze be full of cracks and heap
Long-pending, consumption can not be too much, otherwise can cause glaze crystallize devitrification, cause temperature to narrow, change very few, and cause glaze smoking.
Quartz is metamorphic rock, and its content is silicon dioxide, the main glossiness increasing glaze, it is impossible to too much, can not lack,
Glaze change color otherwise can be caused to reduce.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in plastics, silicate product, synthetic rubber, profit
In the making of the products such as lubricating oil, paint, ointment, binding agent, food, battery, fire retardant.The band gap of zinc oxide and exciton
Binding energy is relatively big, and transparency is high, has the room temperature luminescent properties of excellence.
Plant ash is introduced primarily into the elements such as calcium phosphorus, is good cosolvent, has certain suspension to glaze slip, it is possible to decrease melting of glaze
Melting the high temperature viscosity of temperature and glaze, have opaque and the facilitation to an ancient unit of weight glaze split-phase simultaneously, consumption should control.
Stannum oxide is white, faint yellow or light gray is cubic, six sides or orthorhombic system powder.Fusing point 1630 DEG C.
Limestone main composition-calcium carbonate.Calx and limestone are largely used to construction material, the raw material of industry.Limestone is direct
It is processed into building stones and is fired into quick lime.The quick lime moisture absorption or add water and just become Calx, main component is Ca (OH)2,Can claim
For calcium hydroxide, Calx formulated one-tenth lime white, lime paste etc., as coating material and brick and tile binding agent.
Pulvis Talci is white or off-white color, fine, powder without grittiness, and hands touches with greasy feeling.Odorless, tasteless.This product exists
Water, dilute ore deposit be sour or the most insoluble in dilute alkali hydroxide solution.Can flux raw material, promote that glaze-body interface generates, reduce melted
Temperature and the coefficient of expansion, increase the opaque of an ancient unit of weight glaze simultaneously.
Above-mentioned natural material and industrial chemicals with the use of, under high-temperature fusion effect, glaze colours sky blue split-phase speckle can be produced
The unique artistic effect of bright-coloured change, has good Social and economic benef@.
Claims (2)
1. the sky blue glaze of pottery, it is characterised in that it is to be prepared from by the raw material of following weight percents: potassium feldspar
39 to 41, calcite 19 to 21, quartz 21 to 23, limestone 9 to 11, stannum oxide 1.4 to
1.6, plant ash 4 to 6, Pulvis Talci 0.9 to 1.1, zinc oxide 0.4 to 0.6.
The sky blue glaze of pottery the most according to claim 1, it is characterised in that it is by the raw material system of following weight percents
Standby: potassium feldspar 40, calcite 20, quartz 22, limestone 10, stannum oxide 1.5, plant ash 5, Talcum
Powder 1, zinc oxide 0.5.