CN107572809A - A kind of pottery blue glaze - Google Patents
A kind of pottery blue glaze Download PDFInfo
- Publication number
- CN107572809A CN107572809A CN201711056462.5A CN201711056462A CN107572809A CN 107572809 A CN107572809 A CN 107572809A CN 201711056462 A CN201711056462 A CN 201711056462A CN 107572809 A CN107572809 A CN 107572809A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- raw material
- blue
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of pottery blue glaze, and it is prepared by the raw material of following parts by weight：35 parts to 38 parts of potassium feldspar, 22 parts to 25 parts of quartz, 17 parts to 20 parts of calcite, 8 parts to 10 parts of lime stone, your 5 parts to 9 parts of blue stone, 1.2 parts to 1.5 parts of tin oxide, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide；The present invention is matched again for conventional formulation, and the raw material in nature is coordinated into interaction, with chemical raw material under high-temperature fusion effect, can produce the unique artistic effect of the various change of glaze colours overall color, have very high artistic value and economic benefit.
Description
Technical field
The present invention relates to pottery field, is specifically related to a kind of pottery blue glaze.
Background technology
An ancient unit of weight kiln is northern celadon kiln system, still there is very big achievement at present, is typically burnt using bavin, coal, charcoal and natural gas
System, glaze color change is also different caused by different burning process.Outside is glaze by producing gorgeous color during high-temperature fusion
Variegation bright-coloured changes, and mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color reason, while is also to cause an ancient unit of weight
Porcelain enters that kiln is of the same colour, the color key factor of kiln discharge ten thousand.
" hacking crack ceramic product " is all liked that it has dense sense of history, line by vast consumption from ancient times to the present
Piece is original, simple and unsophisticated, pure, elegant, and fish scale-shaped cracking superposition, the defects of incomplete, rough is incorporated the aesthetic of ceramic product by it
Category, it is not difficult to find out, the appearance of the development history of crack glaze to Contemporary Ceramics has the influence power of uniqueness.Meanwhile Contemporary Ceramics
Different artistic effect and enjoying value have been createed for ceramic art.
Therefore, the present invention provides a kind of low cost, high finished product rate, and the pottery blue glaze for matching novelty has higher skill
Art is worth and extensive market prospects.
The content of the invention
It is an object of the invention to provide a kind of pottery with it is an object of the invention to provide a kind of low cost, high finished product rate, match somebody with somebody
Than the pottery blue glaze of novelty.
The technical proposal of the invention is realized in this way：
A kind of pottery blue glaze, it is prepared by the raw material of following parts by weight：35 parts to 38 parts of potassium feldspar, stone
22 parts to 25 parts of English, 17 parts to 20 parts of calcite, 8 parts to 10 parts of lime stone, your 5 parts to 9 parts of blue stone, 1.2 parts to 1.5 of tin oxide
Part, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide.
The pottery blue glaze is prepared by the raw material of following parts by weight：36 parts of potassium feldspar, 23 parts of quartz,
18 parts of calcite, 9 parts of lime stone, your 8 parts of blue stone, 1.4 parts of tin oxide, 3.5 parts of plant ash, 0.8 part of talcum powder, zinc oxide 0.6
Part.
Technical scheme has following good effect：
The present invention is matched again for conventional formulation, the raw material in nature is coordinated into interaction, with chemical raw material in height
Under warm melting, the unique artistic effect of the various change of glaze colours overall color can be produced, there is very high artistic value and warp
Ji benefit.
Embodiment
Embodiment 1：A kind of pottery blue glaze, it is prepared by the raw material of following parts by weight：Potassium feldspar 36
Part, 23 parts of quartz, 18 parts of calcite, 9 parts of lime stone, your 8 parts of blue stone, 1.4 parts of tin oxide, 3.5 parts of plant ash, talcum powder 0.8
Part, 0.6 part of zinc oxide.
The present embodiment is matched again for conventional formulation, and the raw material in nature is coordinated into interaction, former with chemistry
Material can produce the unique artistic effect of the various change of glaze colours overall color, have very high artistic valency under high-temperature fusion effect
Value and economic benefit.
Embodiment 2：A kind of pottery blue glaze, it is prepared by the raw material of following parts by weight：Potassium feldspar 35
Part, 22 parts of quartz, 17 parts of calcite, 8 parts of lime stone, your 5 parts of blue stone, 1.2 parts of tin oxide, 3.5 parts of plant ash, talcum powder 0.8
Part, 0.6 part of zinc oxide.
The present embodiment is matched again for conventional formulation, and the raw material in nature is coordinated into interaction, former with chemistry
Material can produce the unique artistic effect of the various change of glaze colours overall color, have very high artistic valency under high-temperature fusion effect
Value and economic benefit.
Embodiment 3：A kind of pottery blue glaze, it is prepared by the raw material of following parts by weight：Potassium feldspar 38
Part, 25 parts of quartz, 20 parts of calcite, 10 parts of lime stone, your 9 parts of blue stone, 1.5 parts of tin oxide, 5.5 parts of plant ash, talcum powder 1
Part, 0.7 part of zinc oxide.
The present embodiment is matched again for conventional formulation, and the raw material in nature is coordinated into interaction, former with chemistry
Material can produce the unique artistic effect of the various change of glaze colours overall color, have very high artistic valency under high-temperature fusion effect
Value and economic benefit.
Potassium feldspar belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., be divided into yellow,
White and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Many ore is distributed with Yuzhou
Hide.
Quartz is metamorphic rock, and its content is silica, the main glossiness for increasing glaze, it is impossible to it is excessive, it can not lack,
Otherwise glaze paint change color can be caused to reduce.
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of preventing and treating glaze paint and heap
Product, dosage can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint smoking.
Your blue stone of your ﹪ of blue stone 9 is a kind of stone material for preparing pottery glaze that Henan locality produces, and main component is dioxy
SiClx, the Henan People's Press《Chinese an ancient unit of weight stove research》One book page 123 is discussed in detail.
Talcum powder is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion system
Number, promotes the formation of glaze-body interface, and increase opaque.
Tin oxide is cubic white, faint yellow or light gray, six sides or orthorhombic system powder.1630 DEG C of fusing point.
Above-mentioned natural material is used cooperatively with industrial chemicals, and under high-temperature fusion effect, it is more to produce glaze colours overall color
The unique artistic effect of sample change, has very high artistic value and economic benefit.
Claims (2)
1. a kind of pottery blue glaze, it is characterised in that it is prepared by the raw material of following parts by weight：Potassium feldspar
35 parts to 38 parts, 22 parts to 25 parts of quartz, 17 parts to 20 parts of calcite, 8 parts to 10 parts of lime stone, your 5 parts to 9 parts of blue stone, oxygen
Change 1.2 parts to 1.5 parts of tin, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide.
2. pottery blue glaze according to claim 1, it is characterised in that it is the raw material preparation by following parts by weight
Form：36 parts of potassium feldspar, 23 parts of quartz, 18 parts of calcite, 9 parts of lime stone, your 8 parts of blue stone, 1.4 parts of tin oxide, plant ash
3.5 parts, 0.8 part of talcum powder, 0.6 part of zinc oxide.