CN107586033A - A kind of pottery blueness glaze - Google Patents

A kind of pottery blueness glaze Download PDF

Info

Publication number
CN107586033A
CN107586033A CN201711056374.5A CN201711056374A CN107586033A CN 107586033 A CN107586033 A CN 107586033A CN 201711056374 A CN201711056374 A CN 201711056374A CN 107586033 A CN107586033 A CN 107586033A
Authority
CN
China
Prior art keywords
parts
glaze
pottery
raw material
blueness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711056374.5A
Other languages
Chinese (zh)
Inventor
任合超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yuzhou Huasheng Jun Co Ltd
Original Assignee
Yuzhou Huasheng Jun Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yuzhou Huasheng Jun Co Ltd filed Critical Yuzhou Huasheng Jun Co Ltd
Priority to CN201711056374.5A priority Critical patent/CN107586033A/en
Publication of CN107586033A publication Critical patent/CN107586033A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of pottery blueness glaze, and it is prepared by the raw material of following parts by weight:35 parts to 55 parts of the red feldspar in Yushan, 20 parts to 23 parts of quartz, 10 parts to 15 parts of calcite, 6 parts to 8 parts of frit, 0.8 part to 1.2 parts of cupric oxide, 5 parts to 6 parts of ox bone ash, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide;The present invention is improved to traditional formula with reference to current gas firing technique, proportioning mixing again is carried out to formula, by under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, the pottery glaze colours burnt out can produce the various unique artistic effect of overall blueness, have higher artistic value and extensive market prospects.

Description

A kind of pottery blueness glaze
Technical field
The present invention relates to pottery field, and in particular to a kind of pottery blueness glaze.
Background technology
Pottery is using glaze thickness as this, and in its color or heavy glaze bottom or outstanding glaze or floating glaze table, the thick muddy work of glaze, glaze layer opalescence jade-like stone moisten, Work of being administrations with multiplied departments is intended to drip, and third dimension is extremely strong.For pottery using transmutation as god, natural transmutation is the elite place of pottery art, and Pottery is rely the four seas of becoming famous, the rare part for porcelain woods of making a name.With applying a kind of glaze in firing, once burn till then in it is multicoloured i.e. " it is of the same colour entering kiln, kiln discharge ten thousand is color ".Protean transmutation effect, forms the infinite mystery of colors changing hue, it is red it is inner it is purple, purple in Resided in dark blue, blue or green it is white, white in it is general red, multicolored imbibition, form a brightening, and have the title of " pottery without right, transmutation is unparalleled ".
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, typically using bavin, coal, charcoal Fired with natural gas, glaze color change is also different caused by different burning process.Outside is glaze by being produced during high-temperature fusion Raw gorgeous colorful change, for reason mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color, simultaneously And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Therefore, the invention discloses a kind of raw material is pure, proportioning is novel, and finished product pottery blueness glaze lucuriant in design has Higher artistic value and extensive market prospects.
The content of the invention
The invention discloses a kind of raw material is pure, proportioning is novel, finished product pottery blueness glaze lucuriant in design.
The technical proposal of the invention is realized in this way:A kind of pottery blueness glaze, it is by the original of following parts by weight What material was prepared:35 parts to 55 parts of the red feldspar in Yushan, 20 parts to 23 parts of quartz, 10 parts to 15 parts of calcite, 6 parts to 8 of frit Part, 0.8 part to 1.2 parts of cupric oxide, 5 parts to 6 parts of ox bone ash, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, oxidation 0.5 to 0.7 part of zinc.
Described pottery blueness glaze is prepared by the raw material of following parts by weight:38 parts of the red feldspar in Yushan, stone 22 parts of English, 13 parts of calcite, 7 parts of frit, 1 part of cupric oxide, 5.5 parts of ox bone ash, 4 parts of plant ash, 0.9 part of talcum powder, zinc oxide 0.6 part.
Technical scheme has following good effect:The present invention combines current gas firing technique to traditional formula It is improved, proportioning is carried out again to formula and is mixed, by the raw material in nature and high temperature of the chemical raw material in natural gas kiln Under melting, the pottery glaze colours that burns out can produce the unique artistic effect of overall blueness, have higher artistic value and Extensive market prospects.
Embodiment
Embodiment 1:A kind of pottery blueness glaze, it is prepared by the raw material of following parts by weight:The red length in Yushan 38 parts of stone, 22 parts of quartz, 13 parts of calcite, 7 parts of frit, 1 part of cupric oxide, 5.5 parts of ox bone ash, 4 parts of plant ash, talcum powder 0.9 Part, 0.6 part of zinc oxide.
Embodiments of the invention are improved to traditional formula with reference to current gas firing technique, and formula is matched somebody with somebody again Than mixing, the pottery glaze that under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, will be burnt out Color can produce the unique artistic effect of overall blueness, have higher artistic value and extensive market prospects.
Embodiment 2:A kind of pottery black matrix locus coeruleus glaze, it is prepared by the raw material of following parts by weight:Yushan Red 35 parts of feldspar, 20 parts of quartz, 10 parts of calcite, 6 parts of frit, 0.8 part of cupric oxide, 5 parts of ox bone ash, 3.5 parts of plant ash, talcum 0.8 part of powder, 0.5 part of zinc oxide.
Embodiments of the invention are improved to traditional formula with reference to current gas firing technique, and formula is matched somebody with somebody again Than mixing, the pottery glaze that under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, will be burnt out Color can produce the unique artistic effect of overall blueness, have higher artistic value and extensive market prospects.
Embodiment 3:A kind of pottery black matrix locus coeruleus glaze, it is prepared by the raw material of following parts by weight:Yushan Red 55 parts of feldspar, 23 parts of quartz, 15 parts of calcite, 8 parts of frit, 1.2 parts of cupric oxide, 6 parts of ox bone ash, 5.5 parts of plant ash are sliding 1 part of stone flour, 0.7 part of zinc oxide.
Embodiments of the invention are improved to traditional formula with reference to current gas firing technique, and formula is matched somebody with somebody again Than mixing, the pottery glaze that under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, will be burnt out Color can produce the unique artistic effect of overall blueness, have higher artistic value and extensive market prospects.
The red feldspar in Yushan belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into Huang Color, white and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Crowd is distributed with Yuzhou More mineral reserve.
Quartz is metamorphic rock, and its content is silica, the main glossiness for increasing glaze, it is impossible to it is excessive, it can not lack, Otherwise glaze paint change color can be caused to reduce.
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of preventing and treating glaze paint and heap Product, dosage can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint smoking.
Frit has the features such as insolubility and stability, standby after processing grinding, can be as the strong solvent of glaze, also can be single Solely use.
Cupric oxide is a kind of black oxide of copper, shows slightly both sexes, slightly hygroscopicity.Relative molecular mass is 79.545, Density is 6.3~6.9 g/cm3,1326 DEG C of fusing point.Not soluble in water and ethanol, it is molten to be dissolved in acid, ammonium chloride and potassium cyanide solution, ammonia Slow mechanism dissolved in liquid, it can be reacted with highly basic.Cupric oxide is mainly used in artificial silk, ceramics, glaze and enamel processed, battery, petroleum sweetening Agent, insecticide, also for hydrogen manufacturing, catalyst, green glass etc..
Ox bone ash is made of ox bone calcining, can be used as cosolvent, makes glaze paint gloss, promotes liquid phase separation.
Plant ash is introduced primarily into the elements such as calcium phosphorus, is good cosolvent, there is certain suspension to glaze slip, can reduce glaze Melting temperature and glaze high temperature viscosity, while there is opaque and the facilitation to chun glaze split-phase, dosage should control.
Talcum powder is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion system Number, promotes the formation of glaze-body interface, and increase opaque.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in plastics, silicate product, synthetic rubber, profit In the making of the products such as lubricating oil, paint, ointment, adhesive, food, battery, fire retardant.The band gap and exciton of zinc oxide Binding energy is larger, and transparency is high, there is excellent normal temperature luminescent properties.
Above-mentioned natural material is used cooperatively with industrial chemicals, and under high-temperature fusion effect, it is more to produce the overall blueness of glaze colours The unique artistic effect of sample change, has very high artistic value and economic benefit.

Claims (2)

1. a kind of pottery blueness glaze, it is characterised in that it is prepared by the raw material of following parts by weight:The red length in Yushan 35 parts to 55 parts of stone, 20 parts to 23 parts of quartz, 10 parts to 15 parts of calcite, 6 parts to 8 parts of frit, 0.8 part to 1.2 parts of cupric oxide, 5 parts to 6 parts of ox bone ash, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide.
2. a kind of pottery blueness glaze according to claim 1, it is characterised in that it is by the raw material of following parts by weight It is prepared:38 parts of the red feldspar in Yushan, 22 parts of quartz, 13 parts of calcite, 7 parts of frit, 1 part of cupric oxide, 5.5 parts of ox bone ash, 4 parts of plant ash, 0.9 part of talcum powder, 0.6 part of zinc oxide.
CN201711056374.5A 2017-11-01 2017-11-01 A kind of pottery blueness glaze Pending CN107586033A (en)