CN108585498A - A kind of orchid chun glaze and preparation method thereof - Google Patents
A kind of orchid chun glaze and preparation method thereof Download PDFInfo
- Publication number
- CN108585498A CN108585498A CN201810852353.2A CN201810852353A CN108585498A CN 108585498 A CN108585498 A CN 108585498A CN 201810852353 A CN201810852353 A CN 201810852353A CN 108585498 A CN108585498 A CN 108585498A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- raw material
- temperature
- blue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of blue chun glazes and preparation method thereof, it is prepared by the raw material of following parts by weight：60 to 70 parts of feldspar, 25 to 30 parts of calcite, 15 to 20 parts of quartz, 2 to 5 parts of talcum, 2 to 5 parts of zinc, 1 to 3 part of barium, 0.5 to 2 part of bone meal, blue 0.5 to 1 part of powder；Although the raw material that the present invention uses is very common raw material, but it is made up of rational raw material and the adjustment of deal, also there is synergistic effect between each raw material, general porcelain is breached in order to realize the way of specific glaze colours and the artificial synthesized pigment of use, there is larger innovation on glaze and burning process, the pottery of output is bright-colored, increases the economic benefit and artistic effect of pottery.
Description
Technical field
The invention belongs to pottery technical fields, and in particular to a kind of orchid chun glaze and preparation method thereof.
Background technology
Pottery is originated in the Eastern Han Dynasty, is one of five big kiln porcelain of Song Dynasty, and the treasure in Chinese tradition technology in producing porcelain is referred to as
National treasure, rarity.It is world-famous for unique transmutation art, is known as " the valuable an ancient unit of weight of gold is priceless " and " there is ten thousand strings of cash in family, is not so good as pottery
One " good reputation.The exclusive porcelain in the Henan Province Xuchang City Yuzhou City towns god Hou, by its simple and unsophisticated moulding, consummate technique,
The complicated magical transmutation with glaze, " it is color to enter kiln kiln discharge ten thousand of the same colour ", the variations such as the beautiful scenery of lakes and mountains, rosy clouds fog, people's beast flower, bird, insect, and fish
Infinite figure color and marvellous charm are known as first of Chinese " five big porcelain ".
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has prodigious achievement, the external glaze of pottery to exist at present
By generating gorgeous colorful variation when high-temperature fusion, for reason mainly in the formula of glaze, this is influenced outside pottery finished product
An important factor for color, while being also the key factor for causing " pottery enters that kiln is of the same colour, and kiln discharge ten thousand is color ".
Therefore, research and development are a kind of is easy to fire, and proportioning is novel, and finished product glaze color glossiness is good, hacking uniformly blue chun glaze and its
Preparation method has high artistic value and extensive market prospects.
Invention content
In view of the deficiencies of the prior art, the present invention provides one kind to be easy to fire, and proportioning is novel, finished product glaze color glossiness
It is good, the uniform blue chun glaze and preparation method thereof of hacking.
The technical proposal of the invention is realized in this way：Blue chun glaze, it is prepared by the raw material of following parts by weight
's：60 to 70 parts of feldspar, 25 to 30 parts of calcite, 15 to 20 parts of quartz, 2 to 5 parts of talcum, 2 to 5 parts of zinc, 1 to 3 part of barium, bone meal
0.5 to 2 part, blue 0.5 to 1 part of powder.
Further, the blue chun glaze, it is prepared by the raw material of following parts by weight：65 parts of feldspar, side
Solve 25 parts of stone, 16 parts of quartz, 3 parts of talcum, 3 parts of zinc, 1.5 parts of barium, 1 part of bone meal, blue 0.5 part of powder.
The blue chun glaze preparation method, it is characterised in that include the following steps：
S1：50kg raw materials are taken by said ratio, it is spare after dry；
S2：It is glaze to add water to be put into ball milling after grinding 48h the raw material after drying in S1；
S3：Glaze in S2 is imposed on biscuit, is then charged into kiln, kiln in-furnace temperature is made to be risen from room temperature through 60-70 minutes
To 700-800 DEG C, and keep temperature 1.5-2.5h；In-furnace temperature is set uniformly to be increased to 1000-1100 in 4h from 700-800 DEG C
DEG C, in the process, oxygen content in stove is kept to be not less than 40%；In-furnace temperature is set uniformly to be risen in 2-2.5h from 1000-1100 DEG C
Height keeps temperature 1-2h to 1240 DEG C, in the process, keeps oxygen content in stove to be not less than 40%, rear reduction temperature is extremely
Room temperature kiln discharge.
Technical scheme of the present invention has following good effect：Although the raw material that uses of the present invention for very common raw material,
It is to be made up of rational raw material and the adjustment of deal, also there is synergistic effect, breaching general porcelain is between each raw material
Realization specific glaze colours and the way for using artificial synthesized pigment, there is larger innovation, an ancient unit of weight of output on glaze and burning process
Porcelain is bright-colored, increases the economic benefit and artistic effect of pottery.
Specific implementation mode
The specific implementation mode of the present invention is further described with reference to embodiment, following embodiment is used for more
Clearly description technical scheme of the present invention, and protection scope of the present invention cannot be limited with this.
Embodiment 1：Blue chun glaze, it is prepared by the raw material of following parts by weight：65 parts of feldspar, calcite 25
Part, 16 parts of quartz, 3 parts of talcum, 3 parts of zinc, 1.5 parts of barium, 1 part of bone meal, blue 0.5 part of powder.
The blue chun glaze preparation method, it is characterised in that include the following steps：
S1：50kg raw materials are taken by said ratio, it is spare after dry；
S2：It is glaze to add water to be put into ball milling after grinding 48h the raw material after drying in S1；
S3：Glaze in S2 is imposed on biscuit, is then charged into kiln, kiln in-furnace temperature is made to be risen from room temperature through 60-70 minutes
To 700-800 DEG C, and keep temperature 1.5-2.5h；In-furnace temperature is set uniformly to be increased to 1000-1100 in 4h from 700-800 DEG C
DEG C, in the process, oxygen content in stove is kept to be not less than 40%；In-furnace temperature is set uniformly to be risen in 2-2.5h from 1000-1100 DEG C
Height keeps temperature 1-2h to 1240 DEG C, in the process, keeps oxygen content in stove to be not less than 40%, rear reduction temperature is extremely
Room temperature kiln discharge.
Although the raw material that the present invention uses for very common raw material, is made up of rational raw material and the tune of deal
It is whole, also there is synergistic effect between each raw material, breach general porcelain to realize specific glaze colours and use artificial synthesized pigment
Way, have larger innovation on glaze and burning process, the pottery of output is bright-colored, increase pottery economic benefit and
Artistic effect.
Embodiment 2：Blue chun glaze, it is prepared by the raw material of following parts by weight：60 parts of feldspar, calcite 25
Part, 15 parts of quartz, 2 parts of talcum, 2 parts of zinc, 13 parts of barium, 0.5 part of bone meal, blue 0.5 part of powder.
The blue chun glaze preparation method, it is characterised in that include the following steps：
S1：50kg raw materials are taken by said ratio, it is spare after dry；
S2：It is glaze to add water to be put into ball milling after grinding 48h the raw material after drying in S1；
S3：Glaze in S2 is imposed on biscuit, is then charged into kiln, kiln in-furnace temperature is made to be risen from room temperature through 60-70 minutes
To 700-800 DEG C, and keep temperature 1.5-2.5h；In-furnace temperature is set uniformly to be increased to 1000-1100 in 4h from 700-800 DEG C
DEG C, in the process, oxygen content in stove is kept to be not less than 40%；In-furnace temperature is set uniformly to be risen in 2-2.5h from 1000-1100 DEG C
Height keeps temperature 1-2h to 1240 DEG C, in the process, keeps oxygen content in stove to be not less than 40%, rear reduction temperature is extremely
Room temperature kiln discharge.
Although the raw material that the present invention uses for very common raw material, is made up of rational raw material and the tune of deal
It is whole, also there is synergistic effect between each raw material, breach general porcelain to realize specific glaze colours and use artificial synthesized pigment
Way, have larger innovation on glaze and burning process, the pottery of output is bright-colored, increase pottery economic benefit and
Artistic effect.
Embodiment 3：Blue chun glaze, it is prepared by the raw material of following parts by weight：70 parts of feldspar, calcite 30
Part, 20 parts of quartz, 5 parts of talcum, 5 parts of zinc, 3 parts of barium, 2 parts of bone meal, blue 1 part of powder.
The blue chun glaze preparation method, it is characterised in that include the following steps：
S1：50kg raw materials are taken by said ratio, it is spare after dry；
S2：It is glaze to add water to be put into ball milling after grinding 48h the raw material after drying in S1；
S3：Glaze in S2 is imposed on biscuit, is then charged into kiln, kiln in-furnace temperature is made to be risen from room temperature through 60-70 minutes
To 700-800 DEG C, and keep temperature 1.5-2.5h；In-furnace temperature is set uniformly to be increased to 1000-1100 in 4h from 700-800 DEG C
DEG C, in the process, oxygen content in stove is kept to be not less than 40%；In-furnace temperature is set uniformly to be risen in 2-2.5h from 1000-1100 DEG C
Height keeps temperature 1-2h to 1240 DEG C, in the process, keeps oxygen content in stove to be not less than 40%, rear reduction temperature is extremely
Room temperature kiln discharge.
Although the raw material that the present invention uses for very common raw material, is made up of rational raw material and the tune of deal
It is whole, also there is synergistic effect between each raw material, breach general porcelain to realize specific glaze colours and use artificial synthesized pigment
Way, have larger innovation on glaze and burning process, the pottery of output is bright-colored, increase pottery economic benefit and
Artistic effect.
Feldspar belongs to silicate mineral salt, and internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white
Color and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Many ore is distributed in Yuzhou
It hides.Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of prevention glaze and accumulation, uses
Amount cannot be excessive, otherwise can lead to glaze crystallization devitrification, temperature is caused to narrow, and variation is very few, and glaze is caused to be smoked.Quartz is
Metamorphic rock, content are silica, and the main glossiness for increasing glaze cannot be excessive, can not lack, no it will cause glazes
Change color to reduce.Talcum is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion
Coefficient, promotes the formation of glaze-body interface, and increases opaque.
Claims (3)
1. a kind of orchid chun glaze, which is characterized in that it is prepared by the raw material of following parts by weight：60 to 70 parts of feldspar,
25 to 30 parts of calcite, 15 to 20 parts of quartz, 2 to 5 parts of talcum, 2 to 5 parts of zinc, 1 to 3 part of barium, 0.5 to 2 part of bone meal, blue powder 0.5
To 1 part.
2. orchid chun glaze according to claim 1, which is characterized in that it is prepared by the raw material of following parts by weight
's：65 parts of feldspar, 25 parts of calcite, 16 parts of quartz, 3 parts of talcum, 3 parts of zinc, 1.5 parts of barium, 1 part of bone meal, blue 0.5 part of powder.
3. a kind of blue chun glaze preparation method as claimed in claim 1 or 2, it is characterised in that include the following steps：
S1：50kg raw materials are taken by said ratio, it is spare after dry；
S2：It is glaze to add water to be put into ball milling after grinding 48h the raw material after drying in S1；
S3：Glaze in S2 is imposed on biscuit, is then charged into kiln, kiln in-furnace temperature is made to be risen from room temperature through 60-70 minutes
To 700-800 DEG C, and keep temperature 1.5-2.5h；In-furnace temperature is set uniformly to be increased to 1000-1100 in 4h from 700-800 DEG C
DEG C, in the process, oxygen content in stove is kept to be not less than 40%；In-furnace temperature is set uniformly to be risen in 2-2.5h from 1000-1100 DEG C
Height keeps temperature 1-2h to 1240 DEG C, in the process, keeps oxygen content in stove to be not less than 40%, rear reduction temperature is extremely
Room temperature kiln discharge.