CN106348592A - Transmutation glaze and preparation method thereof - Google Patents
Transmutation glaze and preparation method thereof Download PDFInfo
- Publication number
- CN106348592A CN106348592A CN201610833585.4A CN201610833585A CN106348592A CN 106348592 A CN106348592 A CN 106348592A CN 201610833585 A CN201610833585 A CN 201610833585A CN 106348592 A CN106348592 A CN 106348592A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- raw material
- medicine
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to transmutation glaze and a preparation method thereof. The transmutation glaze is prepared from, by weight, 35-37 parts of melilite, 12-14 parts of feldspar, 11-13 parts of calcite, 4-6 parts of copper ore, 9-11 parts of quartz, 0.7-0.9 part of copper oxide, 17-19 parts of south-slope hard soil, 2-4 parts of Ru glaze stone, 2.1-2.3 parts of local glaze stone and 0.1-0.3 part of talcum powder.
Description
Technical field
The present invention relates to porcelain field is and in particular to a kind of furnace transmutation glaze and preparation method thereof.
Background technology
Pottery development history be Chinese civilization history an important ingredient, China as four major acids ancient country it
One, it is that progress and the development of human society is made that remarkable contribution, the wherein invention of pottery and development with more unique meaning
Justice, on Chinese history, each Chao Gedai has different artistic style and different technical characteristics." china " in English existing China
The meaning, has the meaning of pottery again, clearly demonstrate that China is exactly " native place of pottery ".Grasp porcelain early in European and manufacture skill
Before art more than 1,000 year, Han nationality has just produced very exquisite ware.China be apply earliest in the world pottery country it
One, and Chinese porcelain enjoys the high praise of common people because of its high practicality and artistry.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, typically adopts bavin, coal, charcoal
Fire with natural gas, the glaze color change that different burning process produces is also different.Outside is that glaze produces when through high-temperature fusion
The gorgeous colorful change of life, mainly in the formula of glaze, this is the key factor of impact pottery finished product exogenic color to reason, simultaneously
Be also cause pottery to enter kiln is of the same colour, the key factor of kiln discharge ten thousand coloured silk.
Glaze is exactly one layer of decorative layer on pottery surface, is to determine the principal element that pottery glaze colours is formed.Using natural
Raw mineral materials or some industrial chemicals of addition coordinate according to a certain percentage, melt and cover in embryo under high temperature reducing atmospheres effect
The rich jade-like stone profit gloss in body surface face and colorful vitreous body layer.There is abundant dicoration, increase pottery natural trend
Aesthetic feeling, makes pottery have certain artistic value and enjoying value.
A kind of present invention raw material of production is pure, and proportioning is novel, simple furnace transmutation glaze of preparation method and preparation method thereof.
Content of the invention
For the deficiencies in the prior art, the present invention provides a kind of raw material pure, and proportioning is novel, the simple transmutation of preparation method
Glaze and preparation method thereof, for solving defect of the prior art.
The technical scheme is that and be achieved in that: a kind of furnace transmutation glaze, it is by the raw material system of following weight percents
Standby: 35 parts to 37 parts of melilite, 12 parts to 14 parts of white Anhydrite, 11 parts to 13 parts of calcite, 4 parts to 6 parts of Copper Ores, stone
9 parts to 11 parts of English, 0.7 part to 0.9 part of copper oxide, 17 parts to 19 parts of southern slope pan soil, your 2 parts to 4 parts of medicine, 2.1 parts of this medicine to 2.3
Part, 0.1 to 0.3 part of Pulvis Talci.
Preferably, it is to be prepared from by the raw material of following weight percents: 36 parts of melilite, 13 parts of white Anhydrite, side
12 parts of stone of solution, 5 parts of Copper Ores, 10 parts of quartz, 0.8 part of copper oxide, 18 parts of southern slope pan soil, your 3 parts of medicine, 2.2 parts of this medicine, Pulvis Talci
0.2 part.
Its preparation method is as follows: the raw material of above-mentioned percentage by weight is added in disintegrating machine broken, former after crushing
Expected 150 mesh sieves, obtained mixed powder, then mixed powder was placed into standby in glaze material pond.
The present invention has following good effect: the present invention adds copper oxide and Copper Ores in traditional raw material, with
Under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the change of shape blueness split-phase that can produce that the flowers are in blossom
Unique artistic effect, product fires finished form as the flowers are in blossom, has good Social and economic benef@.Anhydrite belongs to silicate
Mineral salt, its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white and red etc., is the main of glaze
Composition, this product contains white Anhydrite and melilite, and the formation mainly for glaze plays an important role.Calcite mainly reduces glaze
Material melt temperature, increases glossiness and the transparency of glaze colours, prevents and treats glaze paint cracking and piles up, consumption can not be excessive, otherwise can lead
Cause glaze paint crystallize devitrification, cause temperature to narrow, change is very few, and causes glaze paint smoking.Quartz is metamorphic rock, and its content is dioxy
SiClx, the main glossiness increasing glaze it is impossible to excessive nor few, otherwise can cause glaze paint change color to reduce.Copper Ores
It is topmost Copper Ores mineral, typically by cu, tri- kinds of fe, s is elementary composition, theoretical composition (%) cu 34.56, fe 30.52,
S 34.92, theoretical chemistry formula is cufes2.Copper oxide is a kind of black oxide of copper, shows slightly both sexes, slightly hygroscopicity.Phase
It is 79.545 to molecular mass, density is 6.3～6.9 g/cm3, 1326 DEG C of fusing point.Water insoluble and ethanol, is dissolved in acid, chlorination
Ammonium and potassium cyanide solution, slow mechanism dissolved in ammonia solution, can react with highly basic.Copper oxide be mainly used in artificial silk processed, pottery, glaze and
Enamel, battery, petroleum sweetening agent, insecticide, also for hydrogen manufacturing, catalyst, green glass etc..
Specific embodiment
A kind of furnace transmutation glaze, it is to be prepared from by the raw material of following weight percents: 35 parts to 37 parts of melilite, in vain
12 parts to 14 parts of Anhydrite, 11 parts to 13 parts of calcite, 4 parts to 6 parts of Copper Ores, 9 parts to 11 parts of quartz, 0.7 part of copper oxide to 0.9
Part, 17 parts to 19 parts of southern slope pan soil, your 2 parts to 4 parts of medicine, 2.1 parts to 2.3 parts of this medicine, 0.1 to 0.3 part of Pulvis Talci.
Preferably, it is to be prepared from by the raw material of following weight percents: 36 parts of melilite, 13 parts of white Anhydrite, side
12 parts of stone of solution, 5 parts of Copper Ores, 10 parts of quartz, 0.8 part of copper oxide, 18 parts of southern slope pan soil, your 3 parts of medicine, 2.2 parts of this medicine, Pulvis Talci
0.2 part.
Its preparation method is as follows: the raw material of above-mentioned percentage by weight is added in disintegrating machine broken, former after crushing
Expected 150 mesh sieves, obtained mixed powder, then mixed powder was placed into standby in glaze material pond.
Embodiment 1: a kind of furnace transmutation glaze is it is characterised in that it is to be prepared from by the raw material of following weight percents:
35 parts of melilite, 12 parts of white Anhydrite, 11 parts of calcite, 4 parts of Copper Ores, 9 parts of quartz, 0.7 part of copper oxide, 17 parts of southern slope pan soil,
Your 2 parts of medicine, 2.1 parts of this medicine, 0.1 part of Pulvis Talci.
Its preparation method is as follows: the raw material of above-mentioned percentage by weight is added in disintegrating machine broken, former after crushing
Expected 150 mesh sieves, obtained mixed powder, then mixed powder was placed into standby in glaze material pond.Oxidation is added in traditional raw material
Copper and Copper Ores, with other chemical raw materials and natural raw material mating reaction under, under high-temperature fusion effect, the shape that can produce that the flowers are in blossom
The unique artistic effect of the blue split-phase of shape change, product is fired finished form as the flowers are in blossom, is had good Social and economic benef@.
Embodiment 2: a kind of furnace transmutation glaze, it is to be prepared from by the raw material of following weight percents: 36 parts of melilite,
13 parts of Bai Changshi, 12 parts of calcite, 5 parts of Copper Ores, 10 parts of quartz, 0.8 part of copper oxide, 18 parts of southern slope pan soil, your 3 parts of medicine, this
2.2 parts of medicine, 0.2 part of Pulvis Talci.
Its preparation method is as follows: the raw material of above-mentioned percentage by weight is added in disintegrating machine broken, former after crushing
Expected 150 mesh sieves, obtained mixed powder, then mixed powder was placed into standby in glaze material pond.Oxidation is added in traditional raw material
Copper and Copper Ores, with other chemical raw materials and natural raw material mating reaction under, under high-temperature fusion effect, the shape that can produce that the flowers are in blossom
The unique artistic effect of the blue split-phase of shape change, product is fired finished form as the flowers are in blossom, is had good Social and economic benef@.
Embodiment 3: a kind of furnace transmutation glaze, it is to be prepared from by the raw material of following weight percents: 37 parts of melilite,
14 parts of Bai Changshi, 13 parts of calcite, 6 parts of Copper Ores, 11 parts of quartz, 0.9 part of copper oxide, 19 parts of southern slope pan soil, your 4 parts of medicine, this
22.3 parts of medicine, 0.3 part of Pulvis Talci.Its preparation method is as follows: the raw material of above-mentioned percentage by weight is added in disintegrating machine broken,
150 mesh sieves crossed by raw material after will be broken, obtain mixed powder, are then placed into mixed powder standby in glaze material pond.
Claims (3)
1. a kind of furnace transmutation glaze is it is characterised in that it is to be prepared from by the raw material of following weight percents: 35 parts of melilite
To 37 parts, 12 parts to 14 parts of white Anhydrite, 11 parts to 13 parts of calcite, 4 parts to 6 parts of Copper Ores, 9 parts to 11 parts of quartz, copper oxide
0.7 part to 0.9 part, 17 parts to 19 parts of southern slope pan soil, your 2 parts to 4 parts of medicine, 2.1 parts to 2.3 parts of this medicine, Pulvis Talci 0.1 to 0.3
Part.
2. furnace transmutation glaze according to claim 1 is it is characterised in that it is by the raw material preparation of following weight percents
Become: 36 parts of melilite, 13 parts of white Anhydrite, 12 parts of calcite, 5 parts of Copper Ores, 10 parts of quartz, 0.8 part of copper oxide, southern slope pan soil
18 parts, your 3 parts of medicine, 2.2 parts of this medicine, 0.2 part of Pulvis Talci.
3. a kind of preparation method of furnace transmutation glaze as claimed in claim 1 or 2 is it is characterised in that its preparation method is as follows: will
The raw material of above-mentioned percentage by weight is added in disintegrating machine and crushes, and 150 mesh sieves crossed by the raw material after crushing, and obtain mixed powder, so
Afterwards mixed powder is placed into standby in glaze material pond.