CN105948497A - Begonia red glaze and preparation method thereof - Google Patents
Begonia red glaze and preparation method thereof Download PDFInfo
- Publication number
- CN105948497A CN105948497A CN201610424418.4A CN201610424418A CN105948497A CN 105948497 A CN105948497 A CN 105948497A CN 201610424418 A CN201610424418 A CN 201610424418A CN 105948497 A CN105948497 A CN 105948497A
- Authority
- CN
- China
- Prior art keywords
- glaze
- red
- preparation
- begonia
- mixed powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a begonia red glaze and a preparation method thereof. The begonia red glaze is prepared from, by weight, 50% of red feldspar, 18% of yellow feldspar, 12% of calcite, 7% of copper ore, 6.8% of quartz, 5.5% of zinc oxide and 0.7% of talcum powder. The raw materials by weight are added into a crusher to be crushed, the crushed raw materials pass through a 150-mesh screen, mixed powder is obtained, and then the mixed powder is placed in a glaze pond for use; a traditional formula is quantized again, through the matching effect of the natural raw materials, under the effect of high temperature melting, a gorgeously changed special artistic effect with the glaze color just like begonia red can be generated, and god economic and social benefits are achieved.
Description
Technical field
The present invention relates to pottery field, be specifically related to a kind of crabapple red glaze and preparation method thereof.
Background technology
The development of pottery has close and remote contacting with the progress of the mankind, and it is the epoch mark of human civilization.Pottery in pottery, Tang, Song, unit, the baptism of bright, clear years are handled, define the artistic expression of uniqueness, an ancient unit of weight kiln has extremely beautiful color, glaze changes all the time in kiln, and has nature aesthetic feeling, and today is still inherited by various places porcelain kiln and imitates, and constantly bring forth new ideas, make this gorgeous flower playback extraordinary splendor of an ancient unit of weight kiln.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, the most still has the biggest achievement, typically uses bavin, coal, charcoal and natural gas to fire, and the glaze colours change that different burning process produces is also different.Outside is that glaze is producing gorgeous colorful change through high-temperature fusion, and reason is mainly at the formula of glaze, and this is the key factor affecting pottery finished product exogenic color, is also simultaneously that to cause pottery to enter kiln of the same colour, the key factor of kiln discharge ten thousand coloured silk.
Therefore, it is pure that the present invention produces a kind of raw material, and proportioning is novel, preparation method simple crabapple red glaze and preparation method thereof.
Summary of the invention
For the deficiencies in the prior art, the present invention provides a kind of raw material pure, and proportioning is novel, preparation method simple crabapple red glaze and preparation method thereof, is used for solving defect of the prior art.
The technical scheme is that and be achieved in that: a kind of crabapple red glaze, it is to be prepared from by the raw material of following weight percents: red Anhydrite 50, melilite 18, calcite 12, Copper Ores 7, quartz 6.8, zinc oxide 5.5, Pulvis Talci 0.7.
The preparation method of a kind of crabapple red glaze as above, its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, the raw material after broken is crossed 150 mesh sieves, obtains mixed powder, be then placed in glaze pond by mixed powder standby.
The present invention has a following good effect: the present invention carries out re-quantization to conventional formulation, natural raw material mating reaction, under high-temperature fusion effect, can produce glaze colours just as the unique artistic effect of the bright-colored change of crabapple red, have good Social and economic benef@.
Detailed description of the invention
A kind of crabapple red glaze, it is to be prepared from by the raw material of following weight percents: red Anhydrite 50, melilite 18, calcite 12, Copper Ores 7, quartz 6.8, zinc oxide 5.5, Pulvis Talci 0.7.
The preparation method of a kind of crabapple red glaze as above, its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, the raw material after broken is crossed 150 mesh sieves, obtains mixed powder, be then placed in glaze pond by mixed powder standby.
The present invention carries out re-quantization to conventional formulation, natural raw material mating reaction, under high-temperature fusion effect, can produce glaze colours just as the unique artistic effect of the bright-colored change of crabapple red, have good Social and economic benef@.
Anhydrite belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white and red etc., is the main component of glaze, and the formation mainly for glaze plays an important role.Yuzhou is distributed numerous mineral reserve.
Calcite mainly reduces glaze melt temperature, increases glossiness and the transparency of glaze colours, and preventing and treating glaze be full of cracks and accumulation, consumption can not be too much, otherwise can cause glaze crystallize devitrification, cause temperature to narrow, change very few, and cause glaze smoking.
Quartz is metamorphic rock, and its content is silicon dioxide, the main glossiness increasing glaze, it is impossible to too much, can not lack, and glaze change color otherwise can be caused to reduce.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in the making of the products such as plastics, silicate product, synthetic rubber, lubricating oil, paint, ointment, binding agent, food, battery, fire retardant.The band gap of zinc oxide and exciton bind energy are relatively big, and transparency is high, have the room temperature luminescent properties of excellence.
Copper Ores is topmost Copper Ores mineral, and typically by Cu, Fe, S tri-kinds is elementary composition, and theoretical composition (%) Cu 34.56, Fe 30.52, S 34.92, theoretical chemistry formula is CuFeS2.Zinc oxide is a kind of oxide of zinc.It is insoluble in water, dissolves in acid and highly basic.
Pulvis Talci is natural hydrous magnesium silicate mineral, is material of fluxing, it is possible to decrease the melt temperature of glaze and the reduction coefficient of expansion, promotes the formation of glaze-body interface, and increases opaque.
Above-mentioned natural material and industrial chemicals with the use of, under high-temperature fusion effect, the unique artistic effect that glaze colours such as crabapple red mottle bright-coloured changes can be produced, there is good Social and economic benef@.
Claims (2)
1. a crabapple red glaze, it is characterised in that it is to be prepared from by the raw material of following weight percents:
Red Anhydrite 50, melilite 18, calcite 12, Copper Ores 7, quartz 6.8, zinc oxide 5.5, Pulvis Talci 0.7.
2. the preparation method of a crabapple red glaze as claimed in claim 1, it is characterized in that, its preparation method is as follows: joined by the raw material of above-mentioned percentage by weight in disintegrating machine broken, and the raw material after broken is crossed 150 mesh sieves, obtain mixed powder, then mixed powder is placed in glaze pond standby.