CN107572810A - A kind of pottery red glaze - Google Patents
A kind of pottery red glaze Download PDFInfo
- Publication number
- CN107572810A CN107572810A CN201711056651.2A CN201711056651A CN107572810A CN 107572810 A CN107572810 A CN 107572810A CN 201711056651 A CN201711056651 A CN 201711056651A CN 107572810 A CN107572810 A CN 107572810A
- Authority
- CN
- China
- Prior art keywords
- parts
- red
- pottery
- glaze
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of pottery red glaze, and it is prepared by the raw material of following parts by weight:32 parts to 48 parts of the red feldspar in Yushan, 15 parts to 23 parts of quartz, 12 parts to 20 parts of calcite, 8 parts to 12 parts of iron ore, 5 parts to 8 parts of iron oxide red, 4 parts to 6 parts of this medicine, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide;The present invention is improved to traditional formula with reference to current gas firing technique, proportioning mixing again is carried out to formula, by under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, the pottery glaze colours burnt out can produce the red various unique artistic effect of pottery, have higher artistic value and extensive market prospects.
Description
Technical field
The present invention relates to pottery field, and in particular to a kind of pottery red glaze.
Background technology
Pottery is originated in the Eastern Han Dynasty, is one of five big kiln porcelain of Song Dynasty, the treasure in Han nationality's tradition technology in producing porcelain, is referred to as
National treasure, rarity.It is world-famous for the transmutation art of uniqueness, is known as " the valuable an ancient unit of weight of gold is priceless " and " there is ten thousand strings of cash in family, not as pottery
One " good reputation, be the exclusive national treasure porcelain in Pingdingshan City, Henan Province god Hou towns, by its simple and unsophisticated moulding, consummate technique,
The complicated change such as magical transmutation, the beautiful scenery of lakes and mountains, rosy clouds fog, people's beast flower, bird, insect, and fish with glaze, " it is color to enter kiln kiln discharge ten thousand of the same colour "
Infinite figure color and marvellous charm, it is described as first of Chinese " five big porcelain ".
When pottery is made, although present technology has been achieved for remarkable progress, but some defects be present,
Pottery, from sorting to finished product is fired, during which undergoes tens of road production processes in manufacturing process, and the careless of process can also make
Into all that has been achieved is spoiled, this is also pottery the reason for yield is extremely low all the time.The key of pottery is enamel, and enamel is being fired
Transmutation chatoyance afterwards determines the value of pottery, and red pottery enamel has red chicken blood, Vermilion, rose-red, crabapple red, persimmon leaf
Red, garnet, pink, pink, carmine, purplish red, Exocarpium Citri Rubrum, alum are red etc.;In addition because the main component of enamel is feldspar and height
Ridge soil so that an ancient unit of weight kiln easily ftractures after kiln discharge cooling, reduces treasure rate.The difference of enamel formula, the color burnt out
It is variant, and be to apply one layer of glaze on plain tire surface during tradition firing pottery, transmutation is occurred according to the firing environment chun glaze in kiln,
Some uncontrollable decorative patterns or color lump occur, the finished product burnt out is more difficult to be matched or configure complete.Therefore, it is badly in need of one
Kind can fire the pottery burning process of specific decorative pattern in ad-hoc location.
Therefore, the invention discloses a kind of raw material is pure, proportioning is novel, and color is vivid gorgeous, and hacking is uniform, glaze paint temperature
Profit, coloured glaze sense is strong, and the pottery red glaze for having higher artistic value has higher artistic value and extensive market prospects.
The content of the invention
The invention discloses a kind of raw material is pure, proportioning is novel, and finished product is lucuriant in design, has the pottery of higher artistic value red
Colour glaze.
The technical proposal of the invention is realized in this way:A kind of pottery red glaze, it is by the original of following parts by weight
What material was prepared:32 parts to 48 parts of the red feldspar in Yushan, 15 parts to 23 parts of quartz, 12 parts to 20 parts of calcite, 8 parts of iron ore is extremely
12 parts, 5 parts to 8 parts of iron oxide red, 4 parts to 6 parts of this medicine, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, zinc oxide
0.5 to 0.7 part.
Described pottery red glaze, it is prepared by the raw material of following parts by weight:45 parts of the red feldspar in Yushan,
18 parts of quartz, 15 parts of calcite, 10 parts of iron ore, 7 parts of iron oxide red, 5 parts of this medicine, 5 parts of plant ash, 1 part of talcum powder, zinc oxide
0.5 part.
Technical scheme has following good effect:The present invention combines current gas firing technique to traditional formula
It is improved, proportioning is carried out again to formula and is mixed, by the raw material in nature and high temperature of the chemical raw material in natural gas kiln
Under melting, the pottery glaze colours burnt out can produce the unique artistic effect of overall punctation, have higher artistic valency
Value and extensive market prospects.
Embodiment
Embodiment 1:A kind of pottery red glaze, it is prepared by the raw material of following parts by weight:The red length in Yushan
45 parts of stone, 18 parts of quartz, 15 parts of calcite, 10 parts of iron ore, 7 parts of iron oxide red, 5 parts of this medicine, 5 parts of plant ash, 1 part of talcum powder,
0.5 part of zinc oxide.
The present invention is improved to traditional formula with reference to current gas firing technique, and proportioning is carried out again to formula and is mixed,
By under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, the pottery glaze colours burnt out can produce
Overall red unique artistic effect, has higher artistic value and extensive market prospects.
Embodiment 2:A kind of pottery red glaze, it is prepared by the raw material of following parts by weight:The red length in Yushan
32 parts of stone, 15 parts of quartz, 12 parts of calcite, 8 parts of iron ore, 5 parts of iron oxide red, 4 parts of this medicine, 3.5 parts of plant ash, talcum powder 0.8
Part, 0.5 part of zinc oxide.
The present invention is improved to traditional formula with reference to current gas firing technique, and proportioning is carried out again to formula and is mixed,
By under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, the pottery glaze colours burnt out can produce
Overall red unique artistic effect, has higher artistic value and extensive market prospects.
Embodiment 3:A kind of pottery red glaze, it is prepared by the raw material of following parts by weight:The red length in Yushan
48 parts of stone, 23 parts of quartz, 20 parts of calcite, 12 parts of iron ore, 8 parts of iron oxide red, 6 parts of this medicine, 5.5 parts of plant ash, talcum powder 1
Part, 0.7 part of zinc oxide.
The present invention is improved to traditional formula with reference to current gas firing technique, and proportioning is carried out again to formula and is mixed,
By under the high-temperature fusion effect of the raw material in nature and chemical raw material in natural gas kiln, the pottery glaze colours burnt out can produce
Overall red unique artistic effect, has higher artistic value and extensive market prospects.
The red feldspar in Yushan belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into Huang
Color, white and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Crowd is distributed with Yuzhou
More mineral reserve.
Quartz is metamorphic rock, and its content is silica, the main glossiness for increasing glaze, it is impossible to it is excessive, it can not lack,
Otherwise glaze paint change color can be caused to reduce.
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of preventing and treating glaze paint and heap
Product, dosage can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint smoking.
Iron ore is the important raw and processed materials of steel production enterprise, natural crystal is by crushing, grinding, magnetic separation, flotation, gravity treatment
Iron is gradually selected etc. program.It is the mineral aggregate for being capable of economic utilization containing iron simple substance or iron compound.It is every containing can be through
The ore for the ferro element that Ji utilizes is called iron ore.The species of iron ore is a lot, mainly has magnetic iron ore for ironmaking
(Fe3O4), bloodstone(Fe2O3)And siderite(FeCO3)Deng.Iron ore is that essential formation black is bright-colored in this patent
The important source material of change.
Iron oxide red, it is a kind of industrial chemicals, for painting, rubber, plastics, the coloring built etc..For painting, rubber,
Plastics, the coloring built etc., there is natural and artificial two kinds.Due to production method and the difference of operating condition, their crystalline substance
Body structure and physical behavior have very big difference, and color and luster is changed in orange light to blue light between purple light.Covering power and tinting strength, tinting power
It is all very big.There are superior fast light, resistance to elevated temperatures, and resistance to atmospheric effect, resistant foul smell body, all resistance to bases.In concentrated acid only
Have and be just gradually dissolved under heating state.Have many uses general, it is common to use special in industry such as building, rubber, plastics, coating
It is not that iron oxide red primer has antirust function, the red lead paint of high price can be replaced, save non-ferrous metal.It is advanced ground material again,
It is used in the polishing of hardware instrument, the optical glass of precision etc..
This medicine is a kind of natural glaze stone.Glass is introduced into glaze, is a kind of strong solvent.
Plant ash is introduced primarily into the elements such as calcium phosphorus, is good cosolvent, there is certain suspension to glaze slip, can reduce glaze
Melting temperature and glaze high temperature viscosity, while there is opaque and the facilitation to chun glaze split-phase, dosage should control.
Talcum powder is natural hydrous magnesium silicate mineral, is fluxing material, can reduce the melting temperature of glaze and reduce expansion system
Number, promotes the formation of glaze-body interface, and increase opaque.
Zinc oxide is a kind of conventional chemical addition agent, is widely used in plastics, silicate product, synthetic rubber, profit
In the making of the products such as lubricating oil, paint, ointment, adhesive, food, battery, fire retardant.The band gap and exciton of zinc oxide
Binding energy is larger, and transparency is high, there is excellent normal temperature luminescent properties.
Above-mentioned natural material is used cooperatively with industrial chemicals, and under high-temperature fusion effect, the pottery glaze colours burnt out can produce
Raw pottery red unique artistic effect, has higher artistic value and extensive market prospects.
Claims (2)
1. a kind of pottery red glaze, it is characterised in that it is prepared by the raw material of following parts by weight:The red length in Yushan
32 parts to 48 parts of stone, 15 parts to 23 parts of quartz, 12 parts to 20 parts of calcite, 8 parts to 12 parts of iron ore, 5 parts to 8 parts of iron oxide red,
4 parts to 6 parts of this medicine, 3.5 parts to 5.5 parts of plant ash, 0.8 part to 1 part of talcum powder, 0.5 to 0.7 part of zinc oxide.
2. pottery red glaze according to claim 1, it is characterised in that it is the raw material preparation by following parts by weight
Form:45 parts of the red feldspar in Yushan, 18 parts of quartz, 15 parts of calcite, 10 parts of iron ore, 7 parts of iron oxide red, 5 parts of this medicine, plant ash
5 parts, 1 part of talcum powder, 0.5 part of zinc oxide.