CN108863066A - A kind of black glaze of tea set and preparation method thereof - Google Patents
A kind of black glaze of tea set and preparation method thereof Download PDFInfo
- Publication number
- CN108863066A CN108863066A CN201810854022.2A CN201810854022A CN108863066A CN 108863066 A CN108863066 A CN 108863066A CN 201810854022 A CN201810854022 A CN 201810854022A CN 108863066 A CN108863066 A CN 108863066A
- Authority
- CN
- China
- Prior art keywords
- parts
- cobalt
- glaze
- raw material
- tea set
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to black glaze of a kind of tea set and preparation method thereof, it is prepared by the raw material of following weight percents：30~90 parts of feldspar, 4~24 parts of calcite, 2~4 parts of this medicine, 5~15 parts, 2~4 parts of talcum, 1~3 part of cobalt, 0.5~1.5 part of cobalt, 2~12 parts of iron ore of quartz；The present invention joined cobalt and chromium in traditional glaze, under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, can generate the unique artistic effect of glaze colours, color is more splendid colorful, has good social and economic benefit.
Description
Technical field
The present invention relates to glaze fields, and in particular to a kind of black glaze of tea set and preparation method thereof.
Background technique
Ceramics development history be Chinese civilization history an important component part, China as four major acids ancient country it
One, brilliant contribution is made that for mankind's social progress and development, wherein the invention and development of ceramics have more unique meaning
Justice, each Chao Gedai has different artistic styles and different technical characteristics on Chinese history." china " in English existing China
The meaning, and have the meaning of ceramics, clearly demonstrate that China is exactly " native places of ceramics ".Porcelain, which is grasped, early in European manufactures skill
As soon as before more than thousand years of art, Han nationality has produced very exquisite ware.China is the country for applying pottery earliest in the world
One, and Chinese porcelain due to its high practicability and artistry by the high praise of common people.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, generally uses bavin, coal, charcoal
It is fired with natural gas, the glaze color change that different burning process generates is also different.Outside is glaze production when by high-temperature fusion
Raw gorgeous colorful variation, for reason mainly in the formula of glaze, this is an important factor for influencing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Glaze is exactly one layer of decorative layer on pottery surface, is the principal element for determining pottery glaze colours and being formed.Using natural
Raw mineral materials or the certain industrial chemicals of addition cooperate according to a certain percentage, melt under high temperature reducing atmospheres effect and are covered on embryo
Moisten gloss and colorful vitreum layer rich in jade-like stone in body surface face.It is multicoloured color that kiln-transformation ceramic product, which is most road alleged by people,
It is color with the wonderful stream picture gone out in length and breadth at the lines magically change of interest, be it is of the same colour into kiln, kiln discharge ten thousand is color, the delicate variation of various colors and
It is reasonably combined, the aesthetic feeling abundant such as abundant, thick and solid, magnificent is generated, outside is glaze gorgeous by generating when high-temperature fusion
Colorful variation, mainly in the formula of glaze, this is an important factor for influencing pottery finished product exogenic color reason, while being also to cause
Pottery enters that kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Therefore, it is pure to produce a kind of raw material by the present invention, and proportion is novel, a kind of black glaze of tea set of pure color and its preparation
Method has extensive market prospects.
Summary of the invention
A kind of black glaze of tea set, it is prepared by the raw material of following weight percents：30~90 parts of feldspar, Fang Xie
4~24 parts of stone, 2~4 parts of this medicine, 5~15 parts of quartz, 2~4 parts of talcum, 1~3 part of cobalt, 0.5~1.5 part of cobalt, iron ore 2~12
Part.
Preferably, it is prepared by the raw material of following weight percents：60 parts of feldspar, 14 parts of calcite, this medicine 3
Part, 10 parts, 3 parts of talcum, 2 parts of cobalt, 1 part of chromium, 7 parts of iron ore of quartz.
A kind of preparation method of the black glaze of tea set as described above, includes the following steps：
（1）The raw material of parts by weight described above is crushed, then carries out being sieved except iron, places into ball mill and ground,
It is spare after aging 48 hours finally again except iron crosses 200 meshes.
Specific embodiment
A kind of black glaze of tea set, it is prepared by the raw material of following weight percents：30~90 parts of feldspar, Fang Xie
4~24 parts of stone, 2~4 parts of this medicine, 5~15 parts of quartz, 2~4 parts of talcum, 1~3 part of cobalt, 0.5~1.5 part of cobalt, iron ore 2~12
Part.
Preferably, it is prepared by the raw material of following weight percents：60 parts of feldspar, 14 parts of calcite, this medicine 3
Part, 10 parts, 3 parts of talcum, 2 parts of cobalt, 1 part of chromium, 7 parts of iron ore of quartz.
A kind of preparation method of the black glaze of tea set as described above, includes the following steps：
（1）The raw material of parts by weight described above is crushed, then carries out being sieved except iron, places into ball mill and ground,
It is spare after aging 48 hours finally again except iron crosses 200 meshes.
The present invention has following good effect：The present invention joined cobalt and chromium in traditional glaze, chemical with other
Under raw material and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of glaze colours can be generated, color is more gorgeous
It is rotten colorful, there is good social and economic benefit.
Embodiment one
A kind of black glaze of tea set, it is prepared by the raw material of following weight percents：30 parts of feldspar, 4 parts of calcite, this
2 parts of medicine, 5 parts, 2 parts of talcum, 1 part of cobalt, 0.5 part of cobalt, 2 parts of iron ore of quartz.
A kind of preparation method of the black glaze of tea set as described above, includes the following steps：
（1）The raw material of parts by weight described above is crushed, then carries out being sieved except iron, places into ball mill and ground,
It is spare after aging 48 hours finally again except iron crosses 200 meshes.
Embodiment two
A kind of black glaze of tea set, it is prepared by the raw material of following weight percents：60 parts of feldspar, 14 parts of calcite,
3 parts of this medicine, 10 parts, 3 parts of talcum, 2 parts of cobalt, 1 part of chromium, 7 parts of iron ore of quartz.
A kind of preparation method of the black glaze of tea set as described above, includes the following steps：
（1）The raw material of parts by weight described above is crushed, then carries out being sieved except iron, places into ball mill and ground,
It is spare after aging 48 hours finally again except iron crosses 200 meshes.
Embodiment three
A kind of black glaze of tea set, it is prepared by the raw material of following weight percents：30~90 parts of feldspar, calcite 4
~24 parts, 2~4 parts of this medicine, 5~15 parts, 2~4 parts of talcum, 1~3 part of cobalt, 0.5~1.5 part of cobalt, 2~12 parts of iron ore of quartz.
A kind of preparation method of the black glaze of tea set as described above, includes the following steps：
（1）The raw material of parts by weight described above is crushed, then carries out being sieved except iron, places into ball mill and ground,
It is spare after aging 48 hours finally again except iron crosses 200 meshes.
Claims (3)
1. a kind of black glaze of tea set, which is characterized in that it is prepared by the raw material of following weight percents：Feldspar 30~
90 parts, 4~24 parts of calcite, 2~4 parts of this medicine, 5~15 parts of quartz, 2~4 parts of talcum, 1~3 part of cobalt, 0.5~1.5 part of cobalt, iron
2~12 parts of ore.
2. the black glaze of tea set according to claim 1, it is characterised in that：It is prepared by the raw material of following weight percents
Made of：60 parts of feldspar, 14 parts of calcite, 3 parts of this medicine, 10 parts, 3 parts of talcum, 2 parts of cobalt, 1 part of chromium, 7 parts of iron ore of quartz.
3. a kind of preparation method of the black glaze of tea set as claimed in claim 1 or 2, includes the following steps：
（1）The raw material of parts by weight described above is crushed, then carries out being sieved except iron, places into ball mill and ground,
It is spare after aging 48 hours finally again except iron crosses 200 meshes.