CN108689609A - A kind of preparation method of orchid glaze - Google Patents
A kind of preparation method of orchid glaze Download PDFInfo
- Publication number
- CN108689609A CN108689609A CN201810858984.5A CN201810858984A CN108689609A CN 108689609 A CN108689609 A CN 108689609A CN 201810858984 A CN201810858984 A CN 201810858984A CN 108689609 A CN108689609 A CN 108689609A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- glaze
- weight
- remedies
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of blue glaze, it is prepared by the raw material of following parts by weight:60 parts of Bai Changshi, 2 parts of copper ash, 30 parts of bowl remedies, refreshing western 3.5 parts of the temple soil of Hou, 0.4 part of calcite, 4 parts of ox bone, 0.2 part of titanium dioxide;The present invention adds bowl remedies and titanium dioxide in traditional glaze, under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, will produce the unique artistic effect of glaze colours, color is more splendid colorful, has good social and economic benefit.
Description
Technical field
The present invention relates to glaze fields, and in particular to a kind of preparation method of orchid glaze.
Background technology
Ceramics development history be Chinese civilization history an important component part, China as four major acids ancient country it
One, remarkable contribution is made that for mankind's social progress and development, wherein the invention and development of ceramics have more unique meaning
Justice, each Chao Gedai has different artistic styles and different technical characteristics on Chinese history." in English;china"Existing China
The meaning, and have the meaning of ceramics, clearly demonstrate that China is exactly "The Gu Xiang " of ceramics;.Porcelain, which is grasped, early in European manufactures skill
As soon as before art more than thousand years, Han nationality has produced very exquisite ware.China is the country for applying pottery earliest in the world
One, and Chinese porcelain receives the high praise of common people because of its high practicability and artistry.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has prodigious achievement at present, generally uses bavin, coal, charcoal
It is fired with natural gas, the glaze color change that different burning process generates is also different.Outside is glaze by being produced when high-temperature fusion
Raw gorgeous colorful variation, for reason mainly in the formula of glaze, this is an important factor for influencing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Overglaze is exactly one layer of decorative layer on pottery surface, is the principal element for determining pottery glaze colours and being formed.Using natural
Raw mineral materials or the certain industrial chemicals of addition coordinate according to a certain percentage, are melted under high temperature reducing atmospheres effect and are covered in embryo
Moisten gloss and colorful vitreum layer rich in jade-like stone in body surface face.Kiln-transformation ceramic product is most that road alleged by people is multicoloured color
Color is of the same colour into kiln with the wonderful stream picture gone out in length and breadth at the lines magically change of interest, and kiln discharge ten thousand is color, the delicate variation of various colors and
It is reasonably combined, the abundant aesthetic feeling such as abundant, thick and solid, magnificent is generated, outside is glaze gorgeous by being generated when high-temperature fusion
Colorful variation, mainly in the formula of glaze, this is an important factor for influencing pottery finished product exogenic color reason, while being also to cause
Pottery enters that kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Therefore, a kind of raw material of present invention production is pure, and proportioning is novel, a kind of preparation method tool of blue glaze of pure color
There are extensive market prospects.
Invention content
In view of the deficiencies of the prior art, a kind of raw material of present invention offer is pure, and proportioning is novel, a kind of blue glaze of pure color
The preparation method of material.
The technical proposal of the invention is realized in this way:It is a kind of orchid glaze, it be by following parts by weight raw material prepare and
At:30 parts~90 parts of Bai Changshi, 1~3 part of copper ash, 20~40 parts of bowl remedies, refreshing western 2~5 parts of the temple soil of Hou, calcite 0.3~
0.5 part, 3~5 parts of ox bone, 0.1~0.3 part of titanium dioxide.
Preferably, it is prepared by the raw material of following parts by weight:60 parts of Bai Changshi, 2 parts of copper ash, bowl remedies 30
Part, refreshing western 3.5 parts of the temple soil of Hou, 0.4 part of calcite, 4 parts of ox bone, 0.2 part of titanium dioxide.
A kind of preparation method of blue glaze as described above, preparation method are as follows:
(1)After the raw material of above-described parts by weight is crushed, the raw material of crushing is put into ball mill, mixed raw material gross weight is added
The water of amount 50%, booting wet-milling 15 to 22 hours, wet-grinded slurry cross 150 mesh sieve, and after aging 48 hours, slurry reaches 40%
It is spare to 50%.
The present invention has following good effect:The present invention adds bowl remedies and titanium dioxide in traditional glaze, with
Under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of glaze colours, face will produce
Color is more splendid colorful, has good social and economic benefit.
Specific implementation mode
A kind of orchid glaze, it is prepared by the raw material of following parts by weight:30 parts~90 parts of Bai Changshi, copper ash 1~3
Part, 20~40 parts of bowl remedies, refreshing western 2~5 parts of the temple soil of Hou, 0.3~0.5 part of calcite, 3~5 parts of ox bone, titanium dioxide 0.1~0.3
Part.
Preferably, it is prepared by the raw material of following parts by weight:60 parts of Bai Changshi, 2 parts of copper ash, bowl remedies 30
Part, refreshing western 3.5 parts of the temple soil of Hou, 0.4 part of calcite, 4 parts of ox bone, 0.2 part of titanium dioxide.A kind of system of blue glaze as described above
Preparation Method, preparation method are as follows:
(1)After the raw material of above-described parts by weight is crushed, the raw material of crushing is put into ball mill, mixed raw material gross weight is added
The water of amount 50%, booting wet-milling 15 to 22 hours, wet-grinded slurry cross 150 mesh sieve, and after aging 48 hours, slurry reaches 40%
It is spare to 50%.
Embodiment 1:
A kind of orchid glaze, it is prepared by the raw material of following parts by weight:30 parts of Bai Changshi, 1 part of copper ash, bowl remedies 20
Part, refreshing western 2 parts of the temple soil of Hou, 0.3 part of calcite, 3 parts of ox bone, 0.1 part of titanium dioxide.
A kind of preparation method of blue glaze as described above, preparation method are as follows:
(1)After the raw material of above-described parts by weight is crushed, the raw material of crushing is put into ball mill, mixed raw material gross weight is added
The water of amount 50%, booting wet-milling 15 to 22 hours, wet-grinded slurry cross 150 mesh sieve, and after aging 48 hours, slurry reaches 40%
It is spare to 50%.
Embodiment 2
A kind of orchid glaze, it is prepared by the raw material of following parts by weight:Preferably, it is by the raw material of following parts by weight
It is prepared:60 parts of Bai Changshi, 2 parts of copper ash, 30 parts of bowl remedies, refreshing western 3.5 parts of the temple soil of Hou, 0.4 part of calcite, 4 parts of ox bone,
0.2 part of titanium dioxide.
(1)After the raw material of above-described parts by weight is crushed, the raw material of crushing is put into ball mill, mixed raw material is added
The water of total weight 50%, booting wet-milling 15 to 22 hours, wet-grinded slurry cross 150 mesh sieve, and after aging 48 hours, slurry reaches
It is spare to 40% to 50%.
Embodiment 3:
A kind of orchid glaze, it is prepared by the raw material of following parts by weight:90 parts of Bai Changshi, 3 parts of copper ash, bowl remedies 40
Part, refreshing western 5 parts of the temple soil of Hou, 0.5 part of calcite, 5 parts of ox bone, 0.3 part of titanium dioxide.
A kind of preparation method of blue glaze as described above, preparation method are as follows:
(1)After the raw material of above-described parts by weight is crushed, the raw material of crushing is put into ball mill, mixed raw material gross weight is added
The water of amount 50%, booting wet-milling 15 to 22 hours, wet-grinded slurry cross 150 mesh sieve, and after aging 48 hours, slurry reaches 40%
It is spare to 50%.
Bai Changshi, feldspar belong to silicate mineral salt, and internal content is potassium element, sodium element and calcium constituent etc., is divided into
Yellow, white and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Yuzhou is distributed with
Numerous mineral reserve.
Copper ash, the self-control of copper ash, 98 ﹪ of main component copper monoxide content.
Bowl remedies, by the produced ore in the Countermeasure In Yuzhou City of Henan Province towns the god Hou mountains Wan Yao.
The refreshing western temple soil of Hou, is produced by the Countermeasure In Yuzhou City of Henan Province towns god Hou.
Calcite, calcite mainly reduce glaze melting temperature, increase the glossiness and transparency of glaze colours, prevent glaze tortoise
It splits and accumulates, dosage cannot be excessive, otherwise can lead to glaze crystallization devitrification, temperature is caused to narrow, and variation is very few, and causes glaze
Smoking.
Ox bone ash, ox bone ash are made of ox bone calcining, be can be used as cosolvent, are made glaze gloss, promote liquid phase separation.
Titanium dioxide, titanium dioxide main component are the white pigment of titanium dioxide.It is a kind of polycrystalline compounds, particle is in rule
It then arranges, there is grid system.
Claims (3)
1. a kind of orchid glaze, which is characterized in that it is prepared by the raw material of following parts by weight:Bai Changshi 30 parts~90
Part, 1~3 part of copper ash, 20~40 parts of bowl remedies, refreshing western 2~5 parts of the temple soil of Hou, 0.3~0.5 part of calcite, 3~5 parts of ox bone, titanium
0.1~0.3 part of white powder.
2. orchid glaze according to claim 1, which is characterized in that it is prepared by the raw material of following parts by weight:
60 parts of Bai Changshi, 2 parts of copper ash, 30 parts of bowl remedies, refreshing western 3.5 parts of the temple soil of Hou, 0.4 part of calcite, 4 parts of ox bone, titanium dioxide 0.2
Part.
3. the preparation method of orchid glaze according to claim 1 or 2, which is characterized in that preparation method is as follows:
(1)After the raw material of above-described parts by weight is crushed, the raw material of crushing is put into ball mill, mixed raw material gross weight is added
The water of amount 50%, booting wet-milling 15 to 22 hours, wet-grinded slurry cross 150 mesh sieve, and after aging 48 hours, slurry reaches 40%
It is spare to 50%.