CN107572794A - A kind of new stove chun glaze material - Google Patents
A kind of new stove chun glaze material Download PDFInfo
- Publication number
- CN107572794A CN107572794A CN201711059003.2A CN201711059003A CN107572794A CN 107572794 A CN107572794 A CN 107572794A CN 201711059003 A CN201711059003 A CN 201711059003A CN 107572794 A CN107572794 A CN 107572794A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- glass
- tin oxide
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of new stove chun glaze material, and it is prepared by the raw material of following weight percents：20 parts to 40 parts of Bai Changshi, 5 parts to 15 parts of calcite, 1 to 3 part of plant ash, 3 to 5 parts of turtledove this Chinese yam, 4 to 8 parts of glass, 0.3 to 0.5 part of tin oxide, 1 to 3 part of copper ash；The present invention adds glass and tin oxide in traditional burner chun glaze material, with under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of glaze colours can be produced, product firing finished product change is various, has good social and economic benefit.
Description
Technical field
The present invention relates to glaze, and in particular to a kind of new stove chun glaze material.
Background technology
Ceramics development history be Chinese civilization history an important part, China as four major acids ancient country it
One, progress and development for human society are made that the contribution of brilliance, wherein the invention and development of ceramics are with more unique meaning
Justice, each Chao Gedai has different artistic styles and different technical characteristics on Chinese history." china " in English is existing Chinese
The meaning, there is the meaning of ceramics again, clearly demonstrate that China is exactly " native places of ceramics ".Porcelain manufacture skill is grasped early in European
Before art more than 1,000 years, Han nationality has just produced very exquisite ware.China is the country for applying pottery earliest in the world
One, and Chinese porcelain enjoys the high praise of common people because of its high practicality and artistry.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, typically using bavin, coal, charcoal
Fired with natural gas, glaze color change is also different caused by different burning process.Outside is glaze by being produced during high-temperature fusion
Raw gorgeous colorful change, for reason mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Glaze is exactly one layer of decorative layer on pottery surface, is to determine the principal element that pottery glaze colours is formed.Using natural
Raw mineral materials or some industrial chemicals of addition coordinate according to a certain percentage, are melted under high temperature reducing atmospheres effect and are covered in embryo
Moisten gloss and colorful vitreum layer rich in jade-like stone in body surface face.With abundant dicoration, increase pottery natural trend
Aesthetic feeling, make pottery that there is certain artistic value and enjoying value.
A kind of raw material of present invention production is pure, and proportioning is novel, a kind of more splendid new stove chun glaze material behave excellently of color.
The content of the invention
In view of the shortcomings of the prior art, the present invention provides that a kind of raw material is pure, and proportioning is novel, and color is more splendid to behave excellently
A kind of new stove chun glaze material.
The technical proposal of the invention is realized in this way：A kind of new stove chun glaze material, it is the original by following weight percents
What material was prepared：20 parts to 40 parts of Bai Changshi, 5 parts to 15 parts of calcite, 1 to 3 part of plant ash, 3 to 5 parts of turtledove this Chinese yam, glass
4 to 8 parts of glass, 0.3 to 0.5 part of tin oxide, 1 to 3 part of copper ash.
Preferably, it is prepared by the raw material of following weight percents：30 parts of Bai Changshi, 10 parts of calcite, grass
2 parts of wood ash, 4 parts of turtledove this Chinese yam, 6 parts of glass, 0.4 part of tin oxide, 2 parts of copper ash.
The present invention has following good effect：The present invention adds glass and tin oxide in traditional burner chun glaze material,
With under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the unique artistic effect of glaze colours can be produced,
Product firing finished product change is various, and color is more splendid colorful, has good social and economic benefit.
Embodiment
A kind of new stove chun glaze material, it is prepared by the raw material of following weight percents：20 parts to 40 parts of Bai Changshi,
5 parts to 15 parts of calcite, 1 to 3 part of plant ash, 3 to 5 parts of turtledove this Chinese yam, 4 to 8 parts of glass, 0.3 to 0.5 part of tin oxide, copper ash 1
To 3 parts.
Preferably, it is prepared by the raw material of following weight percents：30 parts of Bai Changshi, 10 parts of calcite, grass
2 parts of wood ash, 4 parts of turtledove this Chinese yam, 6 parts of glass, 0.4 part of tin oxide, 2 parts of copper ash.
Embodiment 1：
A kind of new stove chun glaze material, it is prepared by the raw material of following weight percents：20 parts of Bai Changshi, 5 parts of calcite
Part, 1 part of plant ash, 3 parts of turtledove this Chinese yam, 4 parts of glass, 0.3 part of tin oxide, 1 part of copper ash.
Embodiment 2
A kind of new stove chun glaze material, it is prepared by the raw material of following weight percents：30 parts of Bai Changshi, calcite 10
Part, 2 parts of plant ash, 4 parts of turtledove this Chinese yam, 6 parts of glass, 0.4 part of tin oxide, 2 parts of copper ash.
Embodiment 3：
A kind of new stove chun glaze material, it is prepared by the raw material of following weight percents：40 parts of Bai Changshi, calcite 15
Part, 3 parts of plant ash, 5 parts of turtledove this Chinese yam, 8 parts of glass, 0.5 part of tin oxide, 3 parts of copper ash.
Feldspar belongs to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into yellow, white
Color and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Numerous mineral reserve are distributed with Yuzhou
Calcite mainly reduces glaze melting temperature, increases the glossiness and transparency of glaze colours, the cracking of preventing and treating glaze paint and accumulation, uses
Amount can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint smoking.
Plant ash is introduced primarily into the elements such as calcium phosphorus, supplementing calcium element and P elements, is good cosolvent, has one to glaze slip
Fixed suspension, the melting temperature of glaze and the high temperature viscosity of glaze can be reduced, while there is opaque and the promotion to chun glaze split-phase
Effect.
Turtledove Yamamoto medicine predominant amount is silica.Plant ash is introduced primarily into calcium constituent and P elements, is good hydrotropy
Agent has strong basicity, has very light electrolysis in glaze, is used generally as dispersant, there is certain suspension to glaze slip
Property, the high temperature viscosity of melting temperature and glaze can be reduced, while there is milkiness effect and the split-phase facilitation to chun glaze.
Glass is fused together by silica and other chemical substances and formed（Main production raw material is：Soda ash, stone
Lime stone, quartz）.Contiguous network structure is formed in melting, viscosity, which gradually increases and hardened, in cooling procedure causes what it was crystallized
Silicates nonmetallic materials, glass is added in glaze, is a kind of powerful cosolvent.
Claims (2)
1. a kind of new stove chun glaze material, it is characterised in that it is prepared by the raw material of following weight percents：Bai Changshi 20
Part to 40 parts, 5 parts to 15 parts of calcite, 1 to 3 part of plant ash, 3 to 5 parts of turtledove this Chinese yam, 4 to 8 parts of glass, tin oxide 0.3 to
0.5 part, 1 to 3 part of copper ash.
2. new stove chun glaze material according to claim 1, it is characterised in that it is the raw material preparation by following weight percents
Form：30 parts of Bai Changshi, 10 parts of calcite, 2 parts of plant ash, 4 parts of turtledove this Chinese yam, 6 parts of glass, 0.4 part of tin oxide, copper ash 2
Part.