CN107601878A - A kind of compound glaze of ox-blood glaze bottom green statin - Google Patents
A kind of compound glaze of ox-blood glaze bottom green statin Download PDFInfo
- Publication number
- CN107601878A CN107601878A CN201711066546.7A CN201711066546A CN107601878A CN 107601878 A CN107601878 A CN 107601878A CN 201711066546 A CN201711066546 A CN 201711066546A CN 107601878 A CN107601878 A CN 107601878A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- blood
- titanium dioxide
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of compound glaze of ox-blood glaze bottom green statin, and it is prepared by the raw material of following weight percents：30 parts to 90 parts of albite, 3 to 11 parts of alkali stone, 10 to 20 parts of lime stone, 2 to 5 parts of turtledove Yamamoto medicine, 0.3 to 0.5 part of tin oxide, 3 to 5 parts of ox bone ash, 0.1 to 0.3 part of titanium dioxide；The present invention adds titanium dioxide in traditional glaze, with under other chemical raw materials and natural raw material mating reaction, under high-temperature fusion effect, the artistic effect of the unique ox-blood glaze bottom green statin of glaze colours can be produced, color is more splendid colorful, has good social and economic benefit.
Description
Technical field
The present invention relates to glaze field, and in particular to a kind of compound glaze of ox-blood glaze bottom green statin.
Background technology
Ceramics development history be Chinese civilization history an important part, China as four major acids ancient country it
One, progress and development for human society are made that the contribution of brilliance, wherein the invention and development of ceramics are with more unique meaning
Justice, each Chao Gedai has different artistic styles and different technical characteristics on Chinese history." china " in English is existing Chinese
The meaning, there is the meaning of ceramics again, clearly demonstrate that China is exactly " native places of ceramics ".Porcelain manufacture skill is grasped early in European
Before art more than 1,000 years, Han nationality has just produced very exquisite ware.China is the country for applying pottery earliest in the world
One, and Chinese porcelain enjoys the high praise of common people because of its high practicality and artistry.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, typically using bavin, coal, charcoal
Fired with natural gas, glaze color change is also different caused by different burning process.Outside is glaze by being produced during high-temperature fusion
Raw gorgeous colorful change, for reason mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Glaze is exactly one layer of decorative layer on pottery surface, is to determine the principal element that pottery glaze colours is formed.Using natural
Raw mineral materials or some industrial chemicals of addition coordinate according to a certain percentage, are melted under high temperature reducing atmospheres effect and are covered in embryo
Moisten gloss and colorful vitreum layer rich in jade-like stone in body surface face.Kiln-transformation ceramic product is multicoloured color most for road alleged by people
The color wonderful stream picture with going out in length and breadth into the lines magically change of interest, be of the same colour into kiln, kiln discharge ten thousand is color, the delicate change of various colors and
It is reasonably combined, the abundant aesthetic feeling such as abundant, abundant, magnificent is produced, outside is glaze gorgeous by being produced during high-temperature fusion
Colorful change, mainly in the formula of glaze, this is an important factor for influenceing pottery finished product exogenic color reason, while is also to cause
Pottery enters that kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Therefore, a kind of raw material of present invention production is pure, and proportioning is novel, a kind of ox-blood glaze bottom green statin composite glaze of pure color
Material has extensive market prospects.
The content of the invention
In view of the shortcomings of the prior art, a kind of raw material of present invention offer is pure, and proportioning is novel, a kind of youth's kiln of pure color
The red compound glaze of bottom green statin.
The technical proposal of the invention is realized in this way：A kind of compound glaze of ox-blood glaze bottom green statin, it is by following weight
What the raw material of percentage was prepared：30 parts to 90 parts of albite, 3 to 11 parts of alkali stone, 10 to 20 parts of lime stone, turtledove Yamamoto medicine 2
To 5 parts, 0.3 to 0.5 part of tin oxide, 3 to 5 parts of ox bone ash, 0.1 to 0.3 part of titanium dioxide.
It is prepared by the raw material of following weight percents：60 parts of albite, 7 parts of alkali stone, 15 parts of lime stone, turtledove
3.5 parts of Yamamoto medicine, 0.4 part of tin oxide, 4 parts of ox bone ash, 0.2 part of titanium dioxide.
The present invention has following good effect：The present invention adds titanium dioxide in traditional glaze, chemical with other
Under raw material and natural raw material mating reaction, under high-temperature fusion effect, the art of the unique ox-blood glaze bottom green statin of glaze colours can be produced
Effect, color is more splendid colorful, has good social and economic benefit.
Embodiment
A kind of compound glaze of ox-blood glaze bottom green statin, it is prepared by the raw material of following weight percents：Albite
30 parts to 90 parts, 3 to 11 parts of alkali stone, 10 to 20 parts of lime stone, 2 to 5 parts of turtledove Yamamoto medicine, 0.3 to 0.5 part of tin oxide, ox bone ash 3
To 5 parts, 0.1 to 0.3 part of titanium dioxide.
It is prepared by the raw material of following weight percents：60 parts of albite, 7 parts of alkali stone, 15 parts of lime stone, turtledove
3.5 parts of Yamamoto medicine, 0.4 part of tin oxide, 4 parts of ox bone ash, 0.2 part of titanium dioxide.
Embodiment 1：
A kind of compound glaze of ox-blood glaze bottom green statin, it is prepared by the raw material of following weight percents：30 parts of albite,
3 parts of alkali stone, 10 parts of lime stone, 2 parts of turtledove Yamamoto medicine, 0.3 part of tin oxide, 3 parts of ox bone ash, 0.1 part of titanium dioxide.
Embodiment 2
A kind of compound glaze of ox-blood glaze bottom green statin, it is prepared by the raw material of following weight percents：60 parts of albite,
7 parts of alkali stone, 15 parts of lime stone, 3.5 parts of turtledove Yamamoto medicine, 0.4 part of tin oxide, 4 parts of ox bone ash, 0.2 part of titanium dioxide.
Embodiment 3：
A kind of compound glaze of ox-blood glaze bottom green statin, it is prepared by the raw material of following weight percents：90 parts of albite,
11 parts of alkali stone, 20 parts of lime stone, 5 parts of turtledove Yamamoto medicine, 0.5 part of tin oxide, 5 parts of ox bone ash, 0.3 part of titanium dioxide.
Albite, feldspar belong to silicate mineral salt, and its internal content is potassium element, sodium element and calcium constituent etc., is divided into
Yellow, white and red etc., are the main components of glaze, and the formation mainly for glaze plays an important role.Yuzhou is distributed with
Numerous mineral reserve.
Lime stone, lime stone mainly reduce glaze melting temperature, increase the glossiness and transparency of glaze colours, prevent and treat glaze paint tortoise
Split and accumulate, dosage can not be excessive, otherwise can cause glaze paint crystallization devitrification, cause temperature to narrow, and change is very few, and causes glaze paint
Smoking.
Turtledove Yamamoto medicine, turtledove Yamamoto medicine predominant amount are silica.Plant ash is introduced primarily into calcium constituent and P elements, is good
Good cosolvent has strong basicity, has very light electrolysis in glaze, uses, has to glaze slip necessarily generally as dispersant
Suspension, the high temperature viscosity of melting temperature and glaze can be reduced, while there is milkiness to act on and the split-phase of chun glaze is promoted to make
With.
Tin oxide, tin oxide are cubic white, faint yellow or light gray, six sides or orthorhombic system powder.1630 DEG C of fusing point.
Ox bone ash, ox bone ash are made of ox bone calcining, can be used as cosolvent, make glaze paint gloss soft, while are also good
Good opacifiers, promote liquid phase separation.
Titanium dioxide, titanium dioxide main component are the Chinese white of titanium dioxide.It is a kind of polycrystalline compounds, its particle is in rule
Then arrange, there is grid system.
Claims (2)
1. the compound glaze of a kind of ox-blood glaze bottom green statin, it is characterised in that it is prepared by the raw material of following weight percents
's：30 parts to 90 parts of albite, 3 to 11 parts of alkali stone, 10 to 20 parts of lime stone, 2 to 5 parts of turtledove Yamamoto medicine, tin oxide 0.3 to 0.5
Part, 3 to 5 parts of ox bone ash, 0.1 to 0.3 part of titanium dioxide.
2. the compound glaze of ox-blood glaze bottom according to claim 1 green statin, it is characterised in that it is by following weight percents
Raw material be prepared：60 parts of albite, 7 parts of alkali stone, 15 parts of lime stone, 3.5 parts of turtledove Yamamoto medicine, 0.4 part of tin oxide, ox bone
4 parts of ash, 0.2 part of titanium dioxide.