CN107694353A - 乙基纤维素与离子液体气体分离膜的制备方法 - Google Patents

乙基纤维素与离子液体气体分离膜的制备方法 Download PDF

Info

Publication number
CN107694353A
CN107694353A CN201710788135.2A CN201710788135A CN107694353A CN 107694353 A CN107694353 A CN 107694353A CN 201710788135 A CN201710788135 A CN 201710788135A CN 107694353 A CN107694353 A CN 107694353A
Authority
CN
China
Prior art keywords
ethyl cellulose
gas separation
separation membrane
preparation
ionic liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710788135.2A
Other languages
English (en)
Inventor
贾宏葛
张辉
徐双平
藏雨
王建军
朱广宇
徐晨曦
王庆宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qiqihar University
Original Assignee
Qiqihar University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qiqihar University filed Critical Qiqihar University
Priority to CN201710788135.2A priority Critical patent/CN107694353A/zh
Publication of CN107694353A publication Critical patent/CN107694353A/zh
Pending legal-status Critical Current

Abstract

本发明公开了乙基纤维素与离子液体气体分离膜的制备方法，其特征在于，将乙基纤维素(0.5g)，在乙醇(0.011mol,12.65ml)溶液中完全溶解，再加入1‑烯丙基‑3甲基咪唑四氟硼酸盐(0.002mol，0.5g)，在25℃下，搅拌反应24个小时，将反应溶液均匀分散在干净的玻璃板上，在25℃下溶剂挥发,制得乙基纤维素和1‑烯丙基‑3‑甲基咪唑四氟硼酸盐气体分离膜，对产品进行测试.本发明所得的分离膜在对混合气体N2/CO2时,有非常高的分离性能和透过性能。

Description

乙基纤维素与离子液体气体分离膜的制备方法
技术领域
本发明属高分子材料与工程领域,特别涉及乙基纤维素与1-烯丙基-3-甲基咪唑四氟硼酸盐气体分离制备膜的制备方法。
背景技术
气体分离膜作为分离温室气体的有效手段，它既经济有实用，而且绿色环保，符合低碳经济，符合可持续发展需要，将离子液体与高分子材料结合，得到的新型分离膜材料，成为当前离子液体研究领域的趋势之一，但离子液体与高分子材料间存在相容性很差易分层的问题，并且纯高分子分离膜气体选择性能低。
发明内容
本发明的目的在于提供乙基纤维素与1-烯丙基-3-甲基咪唑四氟硼酸盐共混膜的制备方法，解决了其相容性差和气体分离选择性低的问题，本发明专利采用的技术方案是：将乙基纤维素(0.5g)，在乙醇(0.011mol, 12.65ml)溶液中完全溶解，再加入1-烯丙基-3甲基咪唑四氟硼酸盐(0.002mol, 0.5g)，在25℃下,搅拌反应24个小时，将反应溶液均匀分散在干净的玻璃板上，在25℃下溶剂挥发,制得乙基纤维素和1-烯丙基-3-甲基咪唑四氟硼酸盐气体分离膜。
本发明的有益效果是提供乙基纤维素与1-烯丙基-3甲基咪唑四氟硼酸盐气体分离膜的制备方法，制备了选择性,透过性高的气体分离膜。
乙基纤维素与1-烯丙基-3-甲基咪唑四氟硼酸制备的气体分离膜的柔韧性增强,强度高，气体分离性能也有很大提高，N2的透过量达20.9Barrer较纯乙基纤维素膜相比增加10倍，CO2的透过量达810.9Barrer较纯乙基纤维素膜相比增加20倍，该膜分离系数平均值39，较纯乙基纤维素膜提高一倍。

Claims (1)

1.乙基纤维素与离子液体气体分离膜的制备方法，其特征在于，将乙基纤维素(0.5g)，在乙醇(0.011mol, 12.65ml)溶液中完全溶解，再加入1-烯丙基-3甲基咪唑四氟硼酸盐(0.002mol, 0.5g)，在25℃下,搅拌反应24个小时，将反应溶液均匀分散在干净的玻璃板上，在25℃下溶剂挥发,制得乙基纤维素和1-烯丙基-3-甲基咪唑四氟硼酸盐气体分离膜。
CN201710788135.2A 2017-09-05 2017-09-05 乙基纤维素与离子液体气体分离膜的制备方法 Pending CN107694353A (zh)