CN107685383A - A kind of production technology of Antique Imitation Tiles ceramics - Google Patents
A kind of production technology of Antique Imitation Tiles ceramics Download PDFInfo
- Publication number
- CN107685383A CN107685383A CN201710839471.5A CN201710839471A CN107685383A CN 107685383 A CN107685383 A CN 107685383A CN 201710839471 A CN201710839471 A CN 201710839471A CN 107685383 A CN107685383 A CN 107685383A
- Authority
- CN
- China
- Prior art keywords
- dry granular
- antique
- imitation tiles
- ceramics
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Embodiment of the present invention discloses a kind of production technology of Antique Imitation Tiles ceramics, it is combined by multiple technologies superposition, effectively embodies abundant color and strong third dimension, it is relatively simple can effectively to solve traditional Antique Imitation Tiles ceramics texture, lack stereovision, the problem of color is not abundant enough.This production technology includes step：A, it is that 5~7%, powder cabin is old to take raw material ball to wear into slurry to moisture 30~35%, powder by spraying to powder moisture；B, under 31000~32000KN pressure, mould is compressing, is dried at 180~250 DEG C to water content and is less than 0.5%；C, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；D, protection glaze is applied；E, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；F, at 1000~1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Description
Technical field
The present invention relates to ceramic tile field, more particularly to a kind of production technology of Antique Imitation Tiles ceramics.
Background technology
Antique Imitation Tiles ceramics are developed from color glazed brick, so-called modelled after an antique, refer to the effect of brick.The base substrate of brick can be porcelain
Matter, also have and make and form with Shi porcelain, thin Shi and Shi matter.Antique Imitation Tiles ceramic product is first introduced from foreign countries, is disappeared by domestic enterprise
What change, absorption and innovation were produced builds pottery new product.From technique, Antique Imitation Tiles are developed from color glazed brick, are substantially
A kind of Imitation Rock Porcelain Tiles of glazing.The use function and cultural connotation of Antique Imitation Tiles, have extended to bigger building decoration area.As one
Product of the kind containing graceful Cultural Elements, the application of Antique Imitation Tiles ceramics are very extensive.Antique Imitation Tiles ceramics fill for household
Build much, no matter be applied to indoor or outdoor, the effect that Antique Imitation Tiles play is all incomparable distinct and rich in characteristic.Together
Sample, even more transcendent in function performance for ground surface finishing, or wall decoration, Antique Imitation Tiles.
In the preparation technology of traditional Antique Imitation Tiles ceramics, generally raw material is crushed respectively, sieved, and be well mixed, mixed
Close material, obtain blank after ageing, after be put into mould, using plastic compression method be molded, obtain green compact, after green compact drying after glazing, then
Firing obtains Antique Imitation Tiles ceramics.The texture of traditional Antique Imitation Tiles ceramic surface is relatively simple, lacks stereovision, and color is not abundant enough,
It is difficult to the finishing requirements for meeting that consumer is increasingly personalized.
Antique Imitation Tiles ceramics are improved it can be seen that those skilled in the art needs badly to be adapted to present market.
The content of the invention
Embodiment of the present invention provides a kind of production technology of Antique Imitation Tiles ceramics, contrasts, imitates with traditional Antique Imitation Tiles ceramics
Ancient brick ceramics have its obvious technical advantage, and not only it is relatively abundanter that 3D effect, stereovision is presented in picture on surface；Multiple technologies are folded
Add and be combined, particularly the height of the technologies such as glaze, glaze spraying, ink, dry granular, polishing or half throwing is merged, makes Antique Imitation Tiles ceramic
Species is more abundant so that Antique Imitation Tiles ceramics are more imbued with dicoration.
To solve the above problems, a kind of production technology of Antique Imitation Tiles ceramics provided by the invention, including step：
A, it is that 5~7%, powder cabin is old to take raw material ball to wear into slurry to moisture 30~35%, powder by spraying to powder moisture；
B, under 31000~32000KN pressure, mould is compressing, dries to water content and is less than at 180~250 DEG C
0.5%；
C, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
D, protection glaze is applied；
E, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
F, at 1000~1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Preferably, after step c and before step D, in addition to dry granular is applied；
It is described to apply dry granular, specially modulate dry granular and dry granular is sprayed on to the surface of adobe by oil injection cabinet.
And before step D, in addition to step preferably, after step c：Apply dry granular；
And
After step E and before step F, in addition to polishing；
It is described to apply dry granular, specially modulate dry granular and dry granular is sprayed on to the surface of adobe by oil injection cabinet；
The polishing, it is polished specifically by polishing machine and using the block combiner of different meshes；
The block combiner, including deep throwing or shallow throwing.
Preferably, the dry granular is a kind of or more in dumb light dry granular, light dry granular, colored dry granular and metal dry granular
Kind；
The grain composition of described dry granular is 110~210 mesh, is shaped as spheric granules.
Preferably, after step D and before step E, in addition to print one and half throws convex glaze；
And
After step E and before step F, in addition to polishing；
The print one and half throws convex glaze, and convex glaze is imprinted on to the surface of product specially by the way of screen printing；
The polishing, it is polished specifically by polishing machine and using the block combiner of different meshes；
The block combiner, including deep throwing or shallow throwing.
Preferably, cover-coat enamel modelled after an antique is applied described in step C, specific embodiment is glaze spraying or leaching glaze.
Preferably, the ink-jet described in step E, specially made using the ceramic glaze of inorganic material synthesis as agent material
With multichannel shower nozzle digital ink-jet.
Preferably, the multichannel is 8 passages.
As can be seen from the above technical solutions, embodiment of the present invention has advantages below：
The production technology of the Antique Imitation Tiles ceramics of the present invention, picture on surface is presented 3D effect, stereovision and relatively enriched, by more
Kind technology superposition is combined, and particularly the height of the technologies such as glaze, glaze spraying, ink, dry granular, polishing or half throwing is merged, allowed newly
Type Antique Imitation Tiles species is more abundant.The Antique Imitation Tiles ceramics manufactured by this production technology can effectively solve traditional Antique Imitation Tiles ceramics
The problem of surface texture is relatively simple, lacks stereovision, and color is not abundant enough.
Embodiment
Embodiment of the present invention provides a kind of production technology of Antique Imitation Tiles ceramics, and product level and third dimension are more prominent；
With traditional Antique Imitation Tiles ceramic phase ratio, this Antique Imitation Tiles ceramic surface can stamp various patterns modelled after an antique, and surface is in sand shape, there is sand
The natural texture of rock, comparison of light and shade is strong, and third dimension is strong, has adapted to the requirement of a variety of decorative effects.
A kind of production technology of Antique Imitation Tiles ceramics provided by the invention, including step：
A, it is that 5~7%, powder cabin is old to take raw material ball to wear into slurry to moisture 30~35%, powder by spraying to powder moisture；
B, under 31000~32000KN pressure, mould is compressing, dries to water content and is less than at 180~250 DEG C
0.5%；
C, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
D, protection glaze is applied；
E, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
F, at 1000~1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Preferably, after step c and before step D, in addition to step applies dry granular；
It is described to apply dry granular, specially modulate dry granular and dry granular is sprayed on to the surface of adobe by oil injection cabinet.
The present invention changes conventional way, increases the process for applying dry granular, and dry granular is sprayed on to the surface of product, profit by oil injection cabinet
Change the grain effect of Antique Imitation Tiles ceramics, difference in functionality with the temperature height of dry granular, the size of particle, the density degree of spray gun
Dry granular produce different effect.Not polished pure dry granular face effect, makes ceramic tile glaze paint form rough surface, Neng Gouti
The degree of lubrication of feel is risen, produces unglazed and anti-skidding using effect.
Preferably, after step c and before step D, in addition to dry granular is applied；
And
After step E and before step F, in addition to polishing；
It is described to apply dry granular, specially modulate dry granular and dry granular is sprayed on to the surface of adobe by oil injection cabinet；
The polishing, it is polished specifically by polishing machine and using the block combiner of different meshes；
The block combiner, including deep throwing or shallow throwing.
The present invention changes conventional way, increases the process for applying dry granular and polishing, dry granular is sprayed on into product by oil injection cabinet
Surface, change the grain effect of Antique Imitation Tiles ceramics using the temperature height of dry granular, the size of particle, the density degree of spray gun,
Dry granular effect after polishing, bright and clean and anti-skidding using effect can be produced, the effect of similar glaze paint is easily formed again to be regarded
Abundant stereovision on angle.
Preferably, the dry granular can be dumb light dry granular, light dry granular, colored dry granular and one kind in metal dry granular or
It is a variety of；
The mesh of grain composition 110~210 of described dry granular, is shaped as spheric granules.
Wherein, dry granular is necessary for spherical, and sheet or other shapes can cause dry granular to be sticked together, can not show sandstone or
Stone effect.
Preferably, after step D and before step E, in addition to print one and half throws convex glaze；
And
After step E and before step F, in addition to polishing；
The print one and half throws convex glaze, and convex glaze is imprinted on to the surface of product specially by the way of screen printing；
The polishing, it is polished specifically by polishing machine and using the block combiner of different meshes；
The block combiner, including deep throwing or shallow throwing.
The present invention changes conventional way, the process that increase print one and half throws convex glaze, by convex glaze by the way of screen printing
The surface of product is imprinted on, changes the final effect of product using the effect of the transparency of convex glaze, half tone, different half tones will
Produce different effect.
Preferably, cover-coat enamel modelled after an antique is applied described in step C, specific embodiment is glaze spraying or leaching glaze.
Using different glazing modes, depending on the requirement of the fine and smooth degree of brick face feel, using the side of glaze spraying cabinet glaze spraying
Formula can obtain the effect that brick face is coarse, concave-convex sense is strong, and softer brick face effect can be obtained by the way of bell jar drenches glaze.
Preferably, the ink-jet described in step E, specially made using the ceramic glaze of inorganic material synthesis as agent material
With multichannel shower nozzle digital ink-jet.
Pattern printing is carried out using ink-jet printer；According to the pattern in brick face, texture, phase is carried out by image processing software
The adjustment of the function such as the shade answered, well arranged, then the file adjusted is uploaded to ink-jet printer, ink-jet printer
Ink or functional ink are subjected to print pattern according to the requirement of upper transmitting file using shower nozzle
Preferably, the multichannel is 8 passages.
Using multichannel shower nozzle yardage ink-jet, i.e., there are multiple shower nozzles, by different shower nozzles successively to nothing on ink jet technique
The ceramic glaze of machine materials synthesis, multichannel ink-jet is realized, the color and luster species of brick body can be enriched.This production technology preferably uses 8
Pass InkJet, color can be penetrated into adobe in order, and then step infiltration is outstanding for a step, can make forcing for a stone multiaspect
True effect.
Technological process：
Raw material enter factory → ball milling slurrying → powder by spraying → powder cabin it is old → compacting → drying → glazing (cover-coat enamel) → glazing
(protection glaze) → ink-jet → kiln firing → polishes → obtained finished product → finished product storage and treats outbound.
Below by embodiment and embodiment, the present invention will be described in detail：
Embodiment：
The production technology of Antique Imitation Tiles ceramics, including step：
A, it is that 5~7%, powder cabin is old to take raw material ball to wear into slurry to moisture 30~35%, powder by spraying to powder moisture；
B, under 31000~32000KN pressure, mould is compressing, dries to water content and is less than at 180~250 DEG C
0.5%；
C, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
Wherein, the embodiment for applying cover-coat enamel modelled after an antique is glaze spraying or leaching glaze.
D, protection glaze is applied；
E, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
Wherein, the ceramic glaze that ink-jet is synthesized using inorganic material is more using multichannel shower nozzle digital ink-jet as agent material
Passage is 8 passages.
F, at 1000~1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Raw material enters factory：That is raw material is taken in step A, the raw material type is consistent with the raw materials for production of traditional Antique Imitation Tiles ceramics, often
Kind raw material need homogenizing.
Ball milling slurrying：The formulation material prepared is put into ball mill, adds water to be ground, the slurry moisture after grinding is 30
Between~35%, 250 mesh sieves are crossed, are tailed over less than 1.5%.
Powder by spraying：Slurry is sent to spray tower atomization draining, its moisture is down to 5~7%.
Powder cabin is old：Qualified granular material is sent into powder cabin, sieved, tap a blast furnace into stock tank in carry out it is old to protect
Demonstrate,prove that each component is uniform, it is old by 42~48 hours under environment substantially sealed off, it is fully degenerated, in each powder cabin
Material performance is such as so that moisture is basically identical.
Compacting：Qualified powder by being sent into press, powder in the transfer hopper on press top by falling, through feeding vehicle cloth
Enter die cavity, under 31000~32000KN high pressure, upper mold core lowers into die cavity punching press powder, and subsequent upper mold core is somewhat lifted
It is exhausted, then upper mould progressive compacting still further below so that adobe reaches enough rupture strengths and good consistency.
Dry：Wet base after will be compressing at 180~250 DEG C is dried, make its moisture be reduced to 0.5% with
Under, so as to ensure that material strength meets production requirement.
Glazing (cover-coat enamel)：Glazing is carried out using using glaze spraying cabinet spray plane glaze or using bell jar leaching cover-coat enamel mode, is advantageous to
Improve the fine and smooth degree of brick face feel.
Glazing (protection glaze)：Glazing is carried out using using glaze spraying cabinet spray plane glaze or using bell jar leaching cover-coat enamel mode, can
Protect the service life of cover-coat enamel.
Ink-jet：Using the ceramic glaze of inorganic material synthesis as agent material, multichannel shower nozzle digital ink-jet is used.
Kiln is fired：By the way of roller kilns, temperature is 1000 °~1200 ° lower high-temperature firings, and that fires is modelled after an antique
Brick ceramics have strong rupture strength.
Polishing：Polishing mode is a variety of, and the matt that glossiness is 45 ° can be used to throw face, and it is 90 ° that can also use glossiness
Matt throw face.
Embodiment 1
The production technology of Antique Imitation Tiles ceramics, including step：
A1, take raw material ball wear into slurry to moisture 30%, powder by spraying to powder moisture be 5%, powder cabin it is old；
Under B1,31000 pressure, mould is compressing, is dried at 180 DEG C to water content and is less than 0.5%；
C1, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
Wherein, the embodiment for applying cover-coat enamel modelled after an antique is glaze spraying.
D1, apply protection glaze；
E1, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
Wherein, the ceramic glaze that ink-jet is synthesized using inorganic material is more using multichannel shower nozzle digital ink-jet as agent material
Passage is 8 passages.
F1, at 1000 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Embodiment 2
The production technology of Antique Imitation Tiles ceramics, including step：
A2, take raw material ball wear into slurry to moisture 30%, powder by spraying to powder moisture be 7%, powder cabin it is old；
Under B2,31000KN pressure, mould is compressing, is dried at 250 DEG C to water content and is less than 0.5%；
C2, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
Wherein, the embodiment for applying cover-coat enamel modelled after an antique is leaching glaze.
D2, apply protection glaze；
E2, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
Wherein, the ceramic glaze that ink-jet is synthesized using inorganic material is more using multichannel shower nozzle digital ink-jet as agent material
Passage is 8 passages.
F2, at 1000~1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Embodiment 3
The production technology of Antique Imitation Tiles ceramics, including step：
A3, take raw material ball wear into slurry to moisture 30%, powder by spraying to powder moisture be 5%, powder cabin it is old；
Under B3,32000KN pressure, mould is compressing, is dried at 250 DEG C to water content and is less than 0.5%；
C3, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
Wherein, the embodiment for applying cover-coat enamel modelled after an antique is leaching glaze.
D3, apply protection glaze；
E3, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
Wherein, the ceramic glaze that ink-jet is synthesized using inorganic material is more using multichannel shower nozzle digital ink-jet as agent material
Passage is 8 passages.
F3, at 1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
Embodiment 1, embodiment 2 and embodiment 3 produce three batch Antique Imitation Tiles ceramics, and 10 pieces are randomly selected from embodiment 1
Ceramic tile, numbering batch 1,10 blocks of ceramic tiles are randomly selected from embodiment 2, numbering batch 2,10 pieces are randomly selected from embodiment 3
Ceramic tile, numbering batch 3 are compared, observation Antique Imitation Tiles ceramics outward appearance, texture and hardness test：
Those skilled in the art observe：10 blocks of ceramic tiles of batch 1, color and luster is basically identical, and decorative pattern is similar；
Those skilled in the art observe：10 blocks of ceramic tiles of batch 2, color and luster is basically identical, and decorative pattern is similar；
Those skilled in the art observe：10 blocks of ceramic tiles of batch 3, color and luster is basically identical, and decorative pattern is similar；
Those skilled in the art observe：Each 1 piece of ceramic tile for choosing batch 1, batch 2 and batch 3 is compared, and color and luster is slightly not
Together, decorative pattern is similar.
Non- those skilled in the art's observation：30 blocks of ceramic tiles of batch 1, batch 2 and batch 3 are basically identical.
Hardness test：The ceramic tile hardness of batch 1, batch 2 and batch 3 meets ceramic tile Standard.
Reference examples
The production technology of Antique Imitation Tiles ceramics, including step：
A4~F4 select with embodiment 1A1~F1 identical methods, wherein difference is E1：
E4, stamp, pattern is printed on by adobe surface using silk screening techniques stamp line mode.
10 blocks of ceramic tiles in reference examples are randomly selected, are named as batch 4, randomly select 10 blocks of ceramic tiles in embodiment 1, are ordered
Entitled batch 5.
Observe ceramic tile appearance, hardness test：
Those skilled in the art observe：10 blocks of ceramic tiles of batch 4, color and luster slightly difference, decorative pattern are similar；
Those skilled in the art observe：10 blocks of ceramic tiles of batch 5, color and luster is basically identical, and decorative pattern is similar；
Those skilled in the art observe：Each 1 piece of ceramic tile for choosing batch 4 and selection batch 5 is compared, color and luster and decorative pattern difference
It is larger.
Non- those skilled in the art's observation：The color and luster and decorative pattern arranging effect of batch 4 and the ceramic tile of batch 5, batch 5 are more excellent.
Hardness test：The ceramic tile hardness of batch 4 and batch 5 meets ceramic tile Standard.
It is it can be seen that good by Antique Imitation Tiles ceramics, effect made from the production technology of the present invention.
Described above, embodiment of above and embodiment are merely illustrative of the technical solution of the present invention, rather than its limitations；
Although the present invention is described in detail with reference to aforementioned embodiments and embodiment, one of ordinary skill in the art should
Understand：It can still modify to the technical scheme described in foregoing embodiments, or to which part technical characteristic
Carry out equivalent substitution；And these modifications or replacement, the essence of appropriate technical solution is departed from each embodiment of the present invention
With the spirit and scope of embodiment technical scheme.
Claims (8)
1. a kind of production technology of Antique Imitation Tiles ceramics, it is characterised in that including step：
A, it is that 5~7%, powder cabin is old to take raw material ball to wear into slurry to moisture 30~35%, powder by spraying to powder moisture；
B, under 31000~32000KN pressure, mould is compressing, is dried at 180~250 DEG C to water content and is less than 0.5%；
C, cover-coat enamel modelled after an antique is applied, cover-coat enamel modelled after an antique is applied to the surface of adobe；
D, protection glaze is applied；
E, ink-jet printed, ink-jet printer carries out pattern printing, is printed on adobe surface；
F, at 1000~1200 DEG C, Antique Imitation Tiles ceramics are made in edging after firing.
2. the production technology of Antique Imitation Tiles according to claim 1 ceramics, it is characterised in that after step c and step D it
Before, in addition to step：Apply dry granular；
It is described to apply dry granular, specially modulate dry granular and dry granular is sprayed on to the surface of adobe by oil injection cabinet.
3. the production technology of Antique Imitation Tiles according to claim 1 ceramics, it is characterised in that after step c and step D it
Before, in addition to apply dry granular；
And
After step E and before step F, in addition to polishing；
It is described to apply dry granular, specially modulate dry granular and dry granular is sprayed on to the surface of adobe by oil injection cabinet；
The polishing, it is polished specifically by polishing machine and using the block combiner of different meshes；
The block combiner, including deep throwing or shallow throwing.
4. according to Claims 2 or 3 Antique Imitation Tiles ceramics production technology, the dry granular be dumb light dry granular, light dry granular,
One or more in colored dry granular and metal dry granular；
The grain composition of described dry granular is 110~210 mesh, is shaped as spheric granules.
5. the production technology of Antique Imitation Tiles according to claim 1 ceramics, it is characterised in that after step D and step E it
Before, in addition to the convex glaze of the throwing of print one and half；
And
After step E and before step F, in addition to polishing；
The print one and half throws convex glaze, and convex glaze is imprinted on to the surface of product specially by the way of screen printing；
The polishing, it is polished specifically by polishing machine and using the block combiner of different meshes；
The block combiner, including deep throwing or shallow throwing.
6. the production technology of Antique Imitation Tiles ceramics according to claim 1, it is characterised in that cover-coat enamel modelled after an antique is applied described in step C,
Specific embodiment is glaze spraying or leaching glaze.
7. the production technology of Antique Imitation Tiles ceramics according to claim 1, it is characterised in that the ink-jet described in step E, tool
Ceramic glaze of the body to be synthesized using inorganic material uses multichannel shower nozzle digital ink-jet as agent material.
8. the production technology of Antique Imitation Tiles ceramics according to claim 7, it is characterised in that the multichannel is 8 passages.