CN107604641A - A kind of preparation of anion Composite Double functional fibre and its application method - Google Patents
A kind of preparation of anion Composite Double functional fibre and its application method Download PDFInfo
- Publication number
- CN107604641A CN107604641A CN201710781332.1A CN201710781332A CN107604641A CN 107604641 A CN107604641 A CN 107604641A CN 201710781332 A CN201710781332 A CN 201710781332A CN 107604641 A CN107604641 A CN 107604641A
- Authority
- CN
- China
- Prior art keywords
- weaving
- fiber
- polyester fiber
- functional fibre
- composite double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation of anion Composite Double functional fibre and its application method, belong to functional fibre technical field.A kind of preparation of anion Composite Double functional fibre of the present invention and its application method, the anion Composite Double functional fibre passes through during final finishing, weaving is combined with each other with negative-ion auxiliary agent, weaving with function additive and basic polyester fiber, formation has anion and functional terylene composite fibre, this method technique is simple, it is easy to streamline large-scale operation, easy control of process conditions in production process, production cost is low；A process for preparing the functional fibre come, can pass through repeatedly washing, also with good composite functional, be worth of widely use.
Description
Technical field
The present invention relates to a kind of preparation of anion Composite Double functional fibre and its application method, belong to functional fibre skill
Art field.
Background technology
At present, as textile technology and life taste, the raising of quality, the garment material of simple function can not expire
The life requirement of sufficient people.Multifunction is the inexorable trend of costume fabric development.
The development of functional fibre is the symbol of modern fiber science progress.Functional fibre, fibre in differentiation and high-performance are fine
The technological innovation for developing into traditional textile industry of dimension, the conversion to high-tech industry creates advantage, is human lives
Horizontal raising contributes.Functional fibre refers in addition to physical and mechanical properties possessed by general fiber, also have
The tencel of certain specific function.Such as:Fiber has health care function (antibacterial, mite killing, physiotherapy and eliminate the unusual smell)
；Safeguard function (radiation proof, antistatic, uvioresistant etc.)；The wet comfortable function (heat absorption, heat release, moisture absorption, moisture releasing etc.) of heat；Doctor
Treat and environment-friendly function (biocompatibility and biological degradability).Common functional fibre, complex manufacturing technology, cost of manufacture
It is higher, and function is not firm enough possessed by fiber, and by washing twice, the function of fiber will have a greatly reduced quality, and be unfavorable for
The manufacture of functional fibre and promote the use of.
It is an object of the invention to provide a kind of preparation of anion Composite Double functional fibre and its application method, this bear from
Sub- Composite Double functional fibre is by the way that during final finishing, weaving is washed with negative-ion auxiliary agent, weaving with function additive and basis
Together, formation has anion and functional terylene composite fibre to synthetic fibre fiber composite, and this method technique is simple, is easy to flow
Waterline large-scale operation, easy control of process conditions in production process, production cost are low；It is fine a process for preparing the function of coming
Dimension, repeatedly washing can be passed through, also with good composite functional, be worth of widely use.
The content of the invention
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation of anion Composite Double functional fibre
Method, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
Weaving is 1-5 with anion function auxiliary agent, weaving with the weight of function additive and water ratio in liquid:1-5:107, weaving is helped with function
The temperature of agent solution is 50-117 degrees Celsius, and weaving of the polyester fiber in fiber soaking box body is transported with side in function compounding agent solution
Dynamic side immersion, soak time is 3-8 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.1-1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is that 80-127 is Celsius
Degree, the baking time is 10-20 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into anion Composite Double functional fibre.
A kind of preparation method of preferable described anion Composite Double functional fibre, it is characterised in that the step（2）
Middle weaving is weaving function of driving mosquitoes auxiliary agent, weaving deodorization functions auxiliary agent, weaving formaldehyde-removing antibiotic deodorization with function additive
Accumulation of heat temperature storage heat-preserving function auxiliary agent is used in function additive, weaving moisture absorption sweat discharging functions auxiliary agent, weaving cool feeling function additive, weaving
Or phase-change constant-temperature function additive is used in weaving.
A kind of application method of described anion Composite Double functional fibre, its step are：
（1）, the anion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-44 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-196 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into anion Composite Double functional fibre flocculus.
A kind of application method of anion Composite Double functional fibre, it is characterised in that use the compound difunctional fibre of anion
Tie up the fabric prepared.
It is an object of the invention to provide a kind of preparation of anion Composite Double functional fibre and its application method, this bear from
Sub- Composite Double functional fibre is by the way that during final finishing, weaving is washed with negative-ion auxiliary agent, weaving with function additive and basis
Together, formation has anion and functional terylene composite fibre to synthetic fibre fiber composite, and this method technique is simple, is easy to flow
Waterline large-scale operation, easy control of process conditions in production process, production cost are low；It is fine a process for preparing the function of coming
Dimension, repeatedly washing can be passed through, also with good composite functional, be worth of widely use.
Embodiment
Specific embodiment one：A kind of preparation method of anion Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
The weight ratio of weaving anion function auxiliary agent, weaving function of driving mosquitoes auxiliary agent and water is 1 in liquid:1:107, weaving is helped with function
The temperature of agent solution be 50 degrees Celsius, weaving of the polyester fiber in fiber soaking box body with function compounding agent solution while motion while
Immersion, soak time are 3 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 80 degrees Celsius, is dried
It is 10 minutes to roast the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into anion Composite Double functional fibre.
The application method of described a kind of anion Composite Double functional fibre, it is characterised in that its step is：
（1）, the anion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1：0.1, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 50 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into anion Composite Double functional fibre flocculus.
The application method of described a kind of anion Composite Double functional fibre, it is characterised in that use anion Composite Double
The fabric that functional fibre is prepared.
Specific embodiment two：A kind of preparation method of anion Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
The weight ratio of weaving anion function auxiliary agent, weaving deodorization functions auxiliary agent and water is 3 in liquid:2:107, weaving is helped with function
The temperature of agent solution be 94 degrees Celsius, weaving of the polyester fiber in fiber soaking box body with function compounding agent solution while motion while
Immersion, soak time are 4 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.44；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 107 degrees Celsius,
It is 13 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into anion Composite Double functional fibre.
A kind of application method of described anion Composite Double functional fibre, its step are：
（1）, the anion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1.4：0.4, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 34 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 187 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 54 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into anion Composite Double functional fibre flocculus.
The application method of described a kind of anion Composite Double functional fibre, it is characterised in that use anion Composite Double
The fabric that functional fibre is prepared.
Specific embodiment three：A kind of preparation method of anion Composite Double functional fibre, its step are：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
The weight ratio of weaving anion function auxiliary agent, weaving phase-change constant-temperature function additive and water is 5 in liquid: 5:107, weaving is used
The temperature of function additive solution is 117 degrees Celsius, and weaving of the polyester fiber in fiber soaking box body is with function compounding agent solution
Soaked in motion, soak time is 8 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber: 1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is 127 degrees Celsius,
It is 20 minutes to bakee the time；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into anion Composite Double functional fibre.
The application method of described a kind of anion Composite Double functional fibre, it is characterised in that its step is：
（1）, the anion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1： 2：0.5, which carries out uniformly mixing, unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 44 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 196 degrees Celsius, make
The fusing of eutectic polyester fiber is obtained, it is 60 seconds to bakee the time；
（5）, it is baked after, roll coiled, that is, be prepared into anion Composite Double functional fibre flocculus.
The application method of a kind of anion Composite Double functional fibre according to claim 1, it is characterised in that use
The fabric that anion Composite Double functional fibre is prepared.
It is an object of the invention to provide a kind of preparation of anion Composite Double functional fibre and its application method, this bear from
Sub- Composite Double functional fibre is by the way that during final finishing, weaving is washed with negative-ion auxiliary agent, weaving with function additive and basis
Together, formation has anion and functional terylene composite fibre to synthetic fibre fiber composite, and this method technique is simple, is easy to flow
Waterline large-scale operation, easy control of process conditions in production process, production cost are low；It is fine a process for preparing the function of coming
Dimension, repeatedly washing can be passed through, also with good composite functional, be worth of widely use.
Obviously, above-described embodiment is only intended to clearly illustrate example, and is not the restriction to embodiment.It is right
For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of change or
Change.There is no necessity and possibility to exhaust all the enbodiments.And the obvious change thus extended out or
Among changing still in the protection domain of the invention.
Claims (4)
1. a kind of preparation method of anion Composite Double functional fibre, it is characterised in that its step is：
（1）, will be unpacked by vibratory equipment after polyester fiber carry out fiber fluffy processing, terylene after fluffy processing is fine
Dimension is sent on first circulation conveyer belt；
（2）, it is fluffy after polyester fiber fiber entered by first circulation conveyer belt soak casing, be provided with fiber soaking box body
Second circulation conveyer belt and the 3rd endless apron, second circulation conveyer belt are located at the top of the 3rd endless apron, and first follows
Endless conveying belt will be fluffy after polyester fiber be sent between second circulation conveyer belt and the 3rd endless apron, second circulation conveying
Band and the 3rd endless apron are immersed in weaving in fiber soaking box body with function compounding agent solution, and weaving function additive is molten
Weaving is 1-5 with anion function auxiliary agent, weaving with the weight of function additive and water ratio in liquid:1-5:107, weaving is helped with function
The temperature of agent solution is 50-117 degrees Celsius, and weaving of the polyester fiber in fiber soaking box body is transported with side in function compounding agent solution
Dynamic side immersion, soak time is 3-8 minutes；
（3）, the polyester fiber that soaked out of fiber soaking box body enter the 4th endless apron, on the 4th circulation conveying band
The fiber soaked is extruded with squeezing roller, the pressure of squeezing roller is 5 kilograms, washing after being extruded through squeezing roller
The weight of polyester fiber and solution ratio is 5 in synthetic fibre fiber:0.1-1；
（4）, the polyester fiber for preparing step 3 be put into steam drying box and bakeed, stoving temperature is that 80-127 is Celsius
Degree, the baking time is 10-20 minutes；
（5）, the polyester fiber after baking carry out packing encapsulation, that is, be prepared into anion Composite Double functional fibre.
A kind of 2. preparation method of anion Composite Double functional fibre according to claim 1, it is characterised in that the step
Suddenly（2）Middle weaving is weaving with function of driving mosquitoes auxiliary agent, weaving with deodorization functions auxiliary agent, weaving formaldehyde-removing antibiotic with function additive
Accumulation of heat temperature storage heat-preserving function is used in deodorization functions auxiliary agent, weaving moisture absorption sweat discharging functions auxiliary agent, weaving cool feeling function additive, weaving
Phase-change constant-temperature function additive is used in auxiliary agent or weaving.
A kind of 3. application method of anion Composite Double functional fibre according to claim 1, it is characterised in that its step
For：
（1）, the anion Composite Double functional fibre for preparing claim 1 and polyester fiber, eutectic polyester fiber be according to weight
Measure ratio 1：1-2：0.1-0.5 carries out uniformly mixing and unclamps combing；
（2）, according to needed for fabric grammes per square metre carry out multiple lapping in length and breadth successively, the grammes per square metre of every layer of lapping is at 15-44 grams；
（3）, then in step（2）The upper and lower surface for the Multilayer Network being paved into carries out glue spraying processing；
（4）, then after upper and lower surface glue spraying Multilayer Network be sent into baking oven in bakeed, stoving temperature be 180-196 it is Celsius
Degree so that eutectic polyester fiber melts, and the baking time is the 50-60 seconds；
（5）, it is baked after, roll coiled, that is, be prepared into anion Composite Double functional fibre flocculus.
4. the application method of a kind of anion Composite Double functional fibre according to claim 1, it is characterised in that using negative
The fabric that ion Composite Double functional fibre is prepared.